CN106633500A - Automobile foot mat pedal material and preparation method thereof - Google Patents
Automobile foot mat pedal material and preparation method thereof Download PDFInfo
- Publication number
- CN106633500A CN106633500A CN201611020652.7A CN201611020652A CN106633500A CN 106633500 A CN106633500 A CN 106633500A CN 201611020652 A CN201611020652 A CN 201611020652A CN 106633500 A CN106633500 A CN 106633500A
- Authority
- CN
- China
- Prior art keywords
- parts
- automobile foot
- foot mat
- reinforcing agent
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of automobile foot mat materials, in particular to an automobile foot mat pedal material and a preparation method thereof. The automobile foot mat pedal material is prepared from the following ingredients in parts by mass:100 parts of PVC (polyvinyl chloride) resin, 30 parts of reinforcing agents, 0.5 part of coupling agents, 5 parts of stabilizing agents and 1 part of lubricating agents. The preparation method of the automobile foot mat pedal material comprises the following steps that all the ingredients: 100 parts of the PVC resin, 30 parts of the reinforcing agents, 0.5 part of the coupling agents, 5 parts of the stabilizing agents and 1 part of the lubricating agents are weighed according to the mass parts; then, the materials except the reinforcing agent are put into a high-speed mixing machine for stirring for 10 to 15min; after being uniform, the materials enter a double-screw extruder to be extruded; the reinforcing agent enters an extruder material tube at a uniform speed from a second feeding opening of the extruder; after extrusion molding, cooling is performed to obtain the automobile foot mat pedal material, wherein the temperature of the material tube is 160 to 190 DEG C. The obtained automobile foot mat pedal material and the preparation method provided by the invention have the advantages that good waterproof performance is realized; meanwhile, good antiskid performance and wear-resistant performance are realized; the automobile foot mat pedal material is suitable for being used for manufacturing foot mat pedals.
Description
Technical field
The present invention relates to automatic foot-mat field of material technology, especially a kind of automobile foot pad pedal material and its preparation side
Method.
Background technology
At present automatic foot-mat on the market is mostly using cotton material or textile material, in use, water proofing property
Energy and skid resistance, anti-wear performance are poor.
The content of the invention
The invention aims to solve the not enough of above-mentioned technology and to provide a kind of water-proof skid-proof, anti-wear performance superior
Automobile foot pad pedal material and preparation method thereof.
In order to achieve the above object, a kind of automobile foot pad pedal material designed by the present invention, it is by following mass fraction
Component composition, 100 parts of polyvinyl chloride resin, 30 parts of reinforcing agent, 0.5 part of coupling agent, 5 parts of stabilizer, 1 part of lubricant.
Described reinforcing agent is glass fibre, and coupling agent is silane KH-550, and stabilizer is calcium zinc stabilizer, and lubricant is
Lubricant PE.
A kind of preparation method of automobile foot pad pedal material, by mass fraction each component, 100 parts of polyvinyl chloride resin, enhancing are weighed
30 parts of agent, 0.5 part of coupling agent, 5 parts of stabilizer, 1 part of lubricant, are then put into high-speed mixer by the material in addition to reinforcing agent
Middle stirring 10-15min, material uniformly after into double screw extruder extrusion, reinforcing agent extruder second charging aperture at the uniform velocity
Into extruder barrel, cool down after extrusion molding；Wherein the temperature of barrel is 160-190 DEG C.
A kind of automobile foot pad pedal material obtained by the present invention and preparation method thereof, it has good water resistance,
There is good anti-skidding, anti-wear performance simultaneously, be adapted to making foot pad pedal and use.
Specific embodiment
The present invention is further described by the following embodiment.
Embodiment 1：
A kind of automobile foot pad pedal material of the present embodiment description, is characterized in that：It is made up of the component of following mass fraction,
Polyvinyl chloride resin 100kg, reinforcing agent（Glass fibre）30kg, coupling agent silane KH-550 0.5kg, calcium zinc stabilizer 5kg, lubricant
PE 1kg。
Embodiment 2：
A kind of preparation method of automobile foot pad pedal material of the present embodiment description, by mass fraction each component, polyvinyl chloride resin are weighed
100kg, reinforcing agent（Glass fibre）30kg, coupling agent silane KH-550 0.5kg, calcium zinc stabilizer 5kg, lubricant PE 1kg,
Then the material in addition to reinforcing agent is put in high-speed mixer and stirs 10min, material uniformly enters afterwards double screw extruder
Extrusion, reinforcing agent at the uniform velocity enters extruder barrel in the second charging aperture of extruder, cools down after extrusion molding；Wherein barrel
Temperature be 160 DEG C.
Embodiment 3：
A kind of preparation method of automobile foot pad pedal material of the present embodiment description, by mass fraction each component, polyvinyl chloride resin are weighed
100kg, reinforcing agent（Glass fibre）30kg, coupling agent silane KH-550 0.5kg, calcium zinc stabilizer 5kg, lubricant PE 1kg,
Then the material in addition to reinforcing agent is put in high-speed mixer and stirs 15min, material uniformly enters afterwards double screw extruder
Extrusion, reinforcing agent at the uniform velocity enters extruder barrel in the second charging aperture of extruder, cools down after extrusion molding；Wherein barrel
Temperature be 190 DEG C.
Embodiment 4：
A kind of preparation method of automobile foot pad pedal material of the present embodiment description, by mass fraction each component, polyvinyl chloride resin are weighed
100kg, reinforcing agent（Glass fibre）30kg, coupling agent silane KH-550 0.5kg, calcium zinc stabilizer 5kg, lubricant PE 1kg,
Then the material in addition to reinforcing agent is put in high-speed mixer and stirs 12min, material uniformly enters afterwards double screw extruder
Extrusion, reinforcing agent at the uniform velocity enters extruder barrel in the second charging aperture of extruder, cools down after extrusion molding；Wherein barrel
Temperature be 180 DEG C.
Claims (3)
1. a kind of automobile foot pad pedal material, is characterized in that：It is made up of the component of following mass fraction, 100 parts of polyvinyl chloride resin,
30 parts of reinforcing agent, 0.5 part of coupling agent, 5 parts of stabilizer, 1 part of lubricant.
2. a kind of automobile foot pad pedal material according to claim 1, is characterized in that：Described reinforcing agent is glass fibers
Dimension, coupling agent is silane KH-550, and stabilizer is calcium zinc stabilizer, and lubricant is lubricant PE.
3. a kind of preparation method of automobile foot pad pedal material, is characterized in that：Each component, polyvinyl chloride resin 100 are weighed by mass fraction
Part, 30 parts of reinforcing agent, 0.5 part of coupling agent, 5 parts of stabilizer, 1 part of lubricant, are then put into height by the material in addition to reinforcing agent
Stir 10-15min in fast mixer, material uniformly after enter the second of extruder into double screw extruder extrusion, reinforcing agent
Material mouth at the uniform velocity enters extruder barrel, cools down after extrusion molding；Wherein the temperature of barrel is 160-190 DEG C.