CN106633143A - Manufacturing method for heat active adhesive - Google Patents
Manufacturing method for heat active adhesive Download PDFInfo
- Publication number
- CN106633143A CN106633143A CN201610482969.6A CN201610482969A CN106633143A CN 106633143 A CN106633143 A CN 106633143A CN 201610482969 A CN201610482969 A CN 201610482969A CN 106633143 A CN106633143 A CN 106633143A
- Authority
- CN
- China
- Prior art keywords
- heat
- glue
- sealing cover
- finished product
- wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a manufacturing method for a heat active adhesive. The manufacturing method comprises the following steps: (A) manufacturing a plate roller provided with convex strips in the equal distance; (B) preparing glue; (C) coating the glue on the PE face of the PET/PE compound original film by the plate roller, drying, and forming a semi-finished product of the heat active adhesive with equal-distance adhesive tapes; and (D) slitting the semi-finished product of the heat active adhesive by a slitting machine, rolling by a rolling machine to obtain a finished product of the heat active adhesive. The heat active adhesive is sealed well by the plate roller coating glue and a carrier band so as to form a closed space. Because other positions of the heat active adhesive which do not need to be sealed are not coated by the glue, the cost and the resources are greatly saved firstly; secondly the transparency after packaging an electronic component is very good, the information, such as the appearance of the electronic component, can be clearly observed; and thirdly, the electronic component and the heat active adhesive are avoided to be adhered together, and the phenomenon of adhering components is solved.
Description
Technical field
The present invention relates to a kind of heat-sealing cover band, and in particular to a kind of manufacture method of heat-sealing cover band.
Background technology
At present electron trade is developed rapidly, and electronic devices and components usage amount is increasing, and packaging uses heat-sealing cover band demand
Constantly increase, because of existing market heat-sealing cover band PET/PE composite film surface entirety gluings, and with carrier band sealing does not have gluing.
So glue is not only wasted when with carrier band sealing process, waste of resource, and because glue is former during package interior electronic devices and components
Because causing heat-sealing cover band transparency not enough, the inspection letter such as electronic devices and components outward appearance and lot number is affected through heat-sealing cover band after packaging
Breath.And heat-sealing cover band entirety gluing, glue is in close contact with electronic devices and components long-time and forms bonding after packaging, holds when paster
Easily stick together the bad phenomenon of element, and electronic devices and components cannot be accurately captured when causing paster, and on the contrary electronic devices and components are glued
It is connected on heat-sealing cover band and takes away.
The content of the invention
The invention aims to solve the defect in prior art existing for heat-sealing cover band, there is provided a kind of heat-sealing cover band
Manufacture method solving the above problems.The present invention's is achieved through the following technical solutions：
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) roller for being provided with equidistant raised line is made；
(B) glue is prepared；
(C) pass through roller by glue application in PET/PE composite original films PE face, drying, form the heat with equidistant adhesive tape
Lidding tape semi-finished product；
(D) heat-sealing cover band semi-finished product are carried out into slitting by banding machine, then is wound by winder, obtain heat
Lidding tape finished product.
The order of step A and step B can be exchanged according to actual needs in said method.
Preferably, the glue is transparent by 65-75wt% ethylene bis stearamides, 15-25wt% resins and 10wt%
Powder is constituted；The preparation method of the glue is comprised the following steps：I) ethylene bis stearamide, resin are taken out in proportion solvent
In bucket, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content 30% while pour transparent powder into；II) solvent burden ratio is complete
Afterwards, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, in pouring stirred tank into, with 100rpm stirrings
2h, then starts to soak 24h, ethylene bis stearamide, resin, transparent powder is completely dissolved in solvent；IV) soak fully molten
Xie Hou, forms glue-like thing, and again in stirred tank with 100rpm stirring 20min；V) glue is made after being sufficiently stirred for, and
Filter, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, form free from admixture glue, be used in combination
Solvent barrel is contained, to be produced to use.
Preferably, the thickness of the pet layer of the PET/PE composite original films be 23 μm, the thickness of PE layers be 15 μm, the glue
The thickness of bar is 10 μm.
Preferably, also prepare wax including step c1 between step C and step D and step c2 is transferred in wax by reticulate pattern
PE face of the heat-sealing cover with semi-finished product.
Preferably, the wax is made up of the micro- wax powders of 85-97wt%PE and 3-15wt% silicone oil；The preparation method of the wax
Comprise the following steps：I) the micro- wax powders of PE and silicone oil are taken out in solvent barrel in proportion, and disperseed using solvent hexamethylene
Dissolving, is made into solid content 30%；II) prepare after be stirred 10min be stirred with 300rpm, you can；III) micro- wax powder system
Make because can only be fully dispersed, it is impossible to dissolve, then more than prepare after put in storage, it is to be produced receive after need again with 300rpm stirring 5min
Reach and directly used after being uniformly dispersed.
Preferably, the thickness of the wax is 1 μm.
Preferably, the center line in step D by the heat-sealing cover with semi-finished product by banding machine along the adhesive tape carries out slitting.
Preferably, the concrete mode of step C is：By roller by glue application in PET/PE composite original films PE face, gluing
Dried by the baking oven of 3m afterwards, 100～120 DEG C of oven temperature, 30～50m/min of gait of march, roller is then passed through again
By glue application in PET/PE composite original films PE face, dried by the baking oven of 3m again after gluing, oven temperature 100～120
DEG C, 30～50m/min of gait of march, so repeatedly after 7～15 times, you can fully drying makes that glue is firm to be attached on PE faces,
Form the band semi-finished product of the heat-sealing cover with equidistant adhesive tape.Compared with prior art, it is an advantage of the invention that：Present invention heat-sealing
Cover strip will form closed space by roller gluing glue and carrier band sealing well.Because of heat-sealing cover band, other are not required at sealing
Non- gluing, first is significantly cost-effective, resource；Transparency is very good after second packaging electronic devices and components, clearly sees electronics clearly
The information such as components and parts outward appearance, the 3rd can avoid electronic devices and components from being sticked together with heat-sealing cover band, solve adhesion element phenomenon.
Specific embodiment
With reference to specific embodiment, the invention will be further described, but not as limiting to the invention.
Embodiment 1
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) roller for being provided with equidistant raised line is made；Spacing between the width of the raised line and two raised lines can
To be configured, adjust according to production needs；
(B) glue is prepared；I) resin of the ethylene bis stearamide of 65 weight portions, 25 weight portions is taken out in proportion molten
In agent bucket, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content 30% while pour the transparent powder of 10 weight portions into；
II) after solvent burden ratio is complete, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, in pouring stirred tank into,
2h is stirred with 100rpm, then starts to soak 24h, ethylene bis stearamide, resin, transparent powder is completely dissolved in solvent；
IV) after soaking fully dissolving, glue-like thing is formed, and again in stirred tank with 100rpm stirring 20min；V) it is sufficiently stirred for
After make glue, and filter, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, form nothing
Impurity glue, and contained with solvent barrel, it is to be produced to use；
(C) pass through roller by glue application in PET/PE composite original films PE face, dried by the baking oven of 3m after gluing,
100～120 DEG C of oven temperature, 30～50m/min of gait of march is then compound former in PET/PE by glue application by roller again
Film PE faces, are dried by the baking oven of 3m again, 100～120 DEG C of oven temperature, 30～50m/min of gait of march, such as after gluing
After this is repeated 10 times, you can fully drying, make that glue is firm to be attached on PE faces, form the heat-sealing cover band with equidistant adhesive tape
Semi-finished product；
(D) heat-sealing cover band semi-finished product are carried out into slitting by banding machine, then is wound by winder, obtain heat
Lidding tape finished product.
Embodiment 2
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) glue is prepared；I) resin of the ethylene bis stearamide of 66 weight portions, 24 weight portions is taken out in proportion molten
In agent bucket, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content 30% while pour the transparent powder of 10 weight portions into；
II) after solvent burden ratio is complete, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, in pouring stirred tank into,
2h is stirred with 100rpm, then starts to soak 24h, ethylene bis stearamide, resin, transparent powder is completely dissolved in solvent；
IV) after soaking fully dissolving, glue-like thing is formed, and again in stirred tank with 100rpm stirring 20min；V) it is sufficiently stirred for
After make glue, and filter, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, form nothing
Impurity glue, and contained with solvent barrel, it is to be produced to use；
(B) roller for being provided with equidistant raised line is made；Spacing between the width of the raised line and two raised lines can
To be configured, adjust according to production needs；
(C) pass through roller by glue application in PET/PE composite original films PE face, dried by the baking oven of 3m after gluing,
Then 100 DEG C of oven temperature, gait of march 30m/min passes through again roller by glue application in PET/PE composite original films PE face, applies
Dried by the baking oven of 3m again after glue, 100 DEG C of oven temperature, gait of march 30m/min, after being so repeated 7 times, you can fill
Point drying, makes that glue is firm to be attached on PE faces, forms the band semi-finished product of the heat-sealing cover with equidistant adhesive tape；
(D) heat-sealing cover band semi-finished product are carried out into slitting by banding machine, then is wound by winder, obtain heat
Lidding tape finished product.
Embodiment 3
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) glue is prepared；I) resin of the ethylene bis stearamide of 67 weight portions, 23 weight portions is taken out in proportion molten
In agent bucket, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content 30% while pour the transparent powder of 10 weight portions into；
II) after solvent burden ratio is complete, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, in pouring stirred tank into,
2h is stirred with 100rpm, then starts to soak 24h, ethylene bis stearamide, resin, transparent powder is completely dissolved in solvent；
IV) after soaking fully dissolving, glue-like thing is formed, and again in stirred tank with 100rpm stirring 20min；V) it is sufficiently stirred for
After make glue, and filter, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, form nothing
Impurity glue, and contained with solvent barrel, it is to be produced to use；
(B) roller for being provided with equidistant raised line is made；Spacing between the width of the raised line and two raised lines can
To be configured, adjust according to production needs；
(C) pass through roller by glue application in PET/PE composite original films PE face, dried by the baking oven of 3m after gluing,
Then 100 DEG C of oven temperature, gait of march 30m/min passes through again roller by glue application in PET/PE composite original films PE face, applies
Dried by the baking oven of 3m again after glue, 100 DEG C of oven temperature, gait of march 30m/min, after being so repeated 7 times, you can fill
Point drying, makes that glue is firm to be attached on PE faces, forms the band semi-finished product of the heat-sealing cover with equidistant adhesive tape；
(D) heat-sealing cover is carried out into slitting by banding machine with semi-finished product along the center line of the adhesive tape, then by winding
Machine is wound, and obtains heat-sealing cover band finished product.
Embodiment 4
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) roller for being provided with equidistant raised line is made；Spacing between the width of the raised line and two raised lines can
To be configured, adjust according to production needs；
(B) glue is prepared；I) resin of the ethylene bis stearamide of 68 weight portions, 22 weight portions is taken out in proportion molten
In agent bucket, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content 30% while pour the transparent powder of 10 weight portions into；
II) after solvent burden ratio is complete, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, in pouring stirred tank into,
2h is stirred with 100rpm, then starts to soak 24h, ethylene bis stearamide, resin, transparent powder is completely dissolved in solvent；
IV) after soaking fully dissolving, glue-like thing is formed, and again in stirred tank with 100rpm stirring 20min；V) it is sufficiently stirred for
After make glue, and filter, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, form nothing
Impurity glue, and contained with solvent barrel, it is to be produced to use；
(C) pass through roller by glue application in PET/PE composite original films PE face, dried by the baking oven of 3m after gluing,
100～120 DEG C of oven temperature, 30～50m/min of gait of march is then compound former in PET/PE by glue application by roller again
Film PE faces, are dried by the baking oven of 3m again, 100～120 DEG C of oven temperature, 30～50m/min of gait of march, such as after gluing
After this repeats 7～15 times, you can fully drying, make that glue is firm to be attached on PE faces, form the heat-sealing with equidistant adhesive tape
Cover strip semi-finished product；
(c1) wax is prepared；I) the micro- wax powders of 85 weight portion PE and 15 weight portion silicone oil are taken out in solvent barrel in proportion, and
Dispersing and dissolving is carried out using solvent hexamethylene, solid content 30% is made into；II) prepare after be stirred and be stirred with 300rpm
10min, you can；III) micro- wax powder making because can only be fully dispersed, it is impossible to dissolve, then more than prepare after put in storage, it is to be produced to receive
After need again with 300rpm stirring 5min reach be uniformly dispersed after directly use；
(c2) wax is transferred in into PE face of the heat-sealing cover with semi-finished product by reticulate pattern；
(D) heat-sealing cover is carried out into slitting by banding machine with semi-finished product along the center line of the adhesive tape, then by winding
Machine is wound, and obtains heat-sealing cover band finished product.
Embodiment 5
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) roller for being provided with equidistant raised line is made；Spacing between the width of the raised line and two raised lines can
To be configured, adjust according to production needs；
(B) glue is prepared；I) resin of the ethylene bis stearamide of 69 weight portions, 21 weight portions is taken out in proportion molten
In agent bucket, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content 30% while pour the transparent powder of 10 weight portions into；
II) after solvent burden ratio is complete, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, in pouring stirred tank into,
2h is stirred with 100rpm, then starts to soak 24h, ethylene bis stearamide, resin, transparent powder is completely dissolved in solvent；
IV) after soaking fully dissolving, glue-like thing is formed, and again in stirred tank with 100rpm stirring 20min；V) it is sufficiently stirred for
After make glue, and filter, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, form nothing
Impurity glue, and contained with solvent barrel, it is to be produced to use；
(C) pass through roller by glue application in PET/PE composite original films PE face, dried by the baking oven of 3m after gluing
Dry, then 110 DEG C of oven temperature, gait of march 30m/min passes through again roller by glue application in PET/PE composite original films PE
Face, is dried by the baking oven of 3m again, 110 DEG C of oven temperature, gait of march 30m/min after gluing, after being so repeated 10 times,
Can fully dry, make that glue is firm to be attached on PE faces, form the band semi-finished product of the heat-sealing cover with equidistant adhesive tape；It is described
The thickness of the pet layer of PET/PE composite original films is 23 μm, the thickness of PE layers is 15 μm, and the thickness of the adhesive tape is 10 μm；
(c1) wax is prepared；I) the micro- wax powders of 86 weight portion PE and 14 weight portion silicone oil are taken out in solvent barrel in proportion, and
Dispersing and dissolving is carried out using solvent hexamethylene, solid content 30% is made into；II) prepare after be stirred and be stirred with 300rpm
10min, you can；III) micro- wax powder making because can only be fully dispersed, it is impossible to dissolve, then more than prepare after put in storage, it is to be produced to receive
After need again with 300rpm stirring 5min reach be uniformly dispersed after directly use；
(c2) wax is transferred in into PE face of the heat-sealing cover with semi-finished product by reticulate pattern；The thickness of the wax is 1 μm；
(D) heat-sealing cover is carried out into slitting by banding machine with semi-finished product along the center line of the adhesive tape, then by winding
Machine is wound, and obtains heat-sealing cover band finished product.
Embodiment 6
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) glue is prepared；I) resin of the ethylene bis stearamide of 70 weight portions, 20 weight portions is taken out in proportion molten
In agent bucket, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content 30% while pour the transparent powder of 10 weight portions into；
II) after solvent burden ratio is complete, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, in pouring stirred tank into,
2h is stirred with 100rpm, then starts to soak 24h, ethylene bis stearamide, resin, transparent powder is completely dissolved in solvent；
IV) after soaking fully dissolving, glue-like thing is formed, and again in stirred tank with 100rpm stirring 20min；V) it is sufficiently stirred for
After make glue, and filter, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, form nothing
Impurity glue, and contained with solvent barrel, it is to be produced to use；
(B) roller for being provided with equidistant raised line is made；Spacing between the width of the raised line and two raised lines can
To be configured, adjust according to production needs；
(C) pass through roller by glue application in PET/PE composite original films PE face, dried by the baking oven of 3m after gluing,
Then 110 DEG C of oven temperature, gait of march 40m/min passes through again roller by glue application in PET/PE composite original films PE face, applies
Dried by the baking oven of 3m again after glue, 110 DEG C of oven temperature, gait of march 40m/min, after being so repeated 10 times, you can
Fully drying, makes that glue is firm to be attached on PE faces, forms the band semi-finished product of the heat-sealing cover with equidistant adhesive tape；The PET/PE
The thickness of the pet layer of composite original film is 23 μm, the thickness of PE layers is 15 μm, and the thickness of the adhesive tape is 10 μm；
(c1) wax is prepared；I) the micro- wax powders of 87 weight portion PE and 13 weight portion silicone oil are taken out in solvent barrel in proportion, and
Dispersing and dissolving is carried out using solvent hexamethylene, solid content 30% is made into；II) prepare after be stirred and be stirred with 300rpm
10min, you can；III) micro- wax powder making because can only be fully dispersed, it is impossible to dissolve, then more than prepare after put in storage, it is to be produced to receive
After need again with 300rpm stirring 5min reach be uniformly dispersed after directly use；
(c2) wax is transferred in into PE face of the heat-sealing cover with semi-finished product by reticulate pattern；The thickness of the wax is 1 μm；
(D) heat-sealing cover is carried out into slitting by banding machine with semi-finished product along the center line of the adhesive tape, then by winding
Machine is wound, and obtains heat-sealing cover band finished product.
Embodiment 7
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) glue is prepared；I) resin of the ethylene bis stearamide of 71 weight portions, 19 weight portions is taken out in proportion molten
In agent bucket, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content 30% while pour the transparent powder of 10 weight portions into；
II) after solvent burden ratio is complete, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, in pouring stirred tank into,
2h is stirred with 100rpm, then starts to soak 24h, ethylene bis stearamide, resin, transparent powder is completely dissolved in solvent；
IV) after soaking fully dissolving, glue-like thing is formed, and again in stirred tank with 100rpm stirring 20min；V) it is sufficiently stirred for
After make glue, and filter, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, formed
Free from admixture glue, and contained with solvent barrel, it is to be produced to use；
(B) roller for being provided with equidistant raised line is made；Spacing between the width of the raised line and two raised lines can
To be configured, adjust according to production needs；
(C) pass through roller by glue application in PET/PE composite original films PE face, dried by the baking oven of 3m after gluing,
Then 110 DEG C of oven temperature, gait of march 50m/min passes through again roller by glue application in PET/PE composite original films PE face, applies
Dried by the baking oven of 3m again after glue, 110 DEG C of oven temperature, gait of march 50m/min, after being so repeated 10 times, you can
Fully drying, makes that glue is firm to be attached on PE faces, forms the band semi-finished product of the heat-sealing cover with equidistant adhesive tape；The PET/PE
The thickness of the pet layer of composite original film is 23 μm, the thickness of PE layers is 15 μm, and the thickness of the adhesive tape is 10 μm；
(c1) wax is prepared；I) the micro- wax powders of 88 weight portion PE and 12 weight portion silicone oil are taken out in solvent barrel in proportion, and
Dispersing and dissolving is carried out using solvent hexamethylene, solid content 30% is made into；II) prepare after be stirred and be stirred with 300rpm
10min, you can；III) micro- wax powder making because can only be fully dispersed, it is impossible to dissolve, then more than prepare after put in storage, it is to be produced to receive
After need again with 300rpm stirring 5min reach be uniformly dispersed after directly use；
(c2) wax is transferred in into PE face of the heat-sealing cover with semi-finished product by reticulate pattern；The thickness of the wax is 1 μm；
(D) heat-sealing cover is carried out into slitting by banding machine with semi-finished product along the center line of the adhesive tape, then by winding
Machine is wound, and obtains heat-sealing cover band finished product.
Embodiment 8
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) roller for being provided with equidistant raised line is made；Spacing between the width of the raised line and two raised lines can
To be configured, adjust according to production needs；
(B) glue is prepared；I) resin of the ethylene bis stearamide of 72 weight portions, 18 weight portions is taken out in proportion molten
In agent bucket, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content 30% while pour the transparent powder of 10 weight portions into；
II) after solvent burden ratio is complete, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, in pouring stirred tank into,
2h is stirred with 100rpm, then starts to soak 24h, ethylene bis stearamide, resin, transparent powder is completely dissolved in solvent；
IV) after soaking fully dissolving, glue-like thing is formed, and again in stirred tank with 100rpm stirring 20min；V) it is sufficiently stirred for
After make glue, and filter, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, form nothing
Impurity glue, and contained with solvent barrel, it is to be produced to use；
(C) pass through roller by glue application in PET/PE composite original films PE face, dried by the baking oven of 3m after gluing,
Then 120 DEG C of oven temperature, gait of march 30m/min passes through again roller by glue application in PET/PE composite original films PE face, applies
Dried by the baking oven of 3m again after glue, 120 DEG C of oven temperature, gait of march 30m/min, after being so repeated 10 times, you can
Fully drying, makes that glue is firm to be attached on PE faces, forms the band semi-finished product of the heat-sealing cover with equidistant adhesive tape；The PET/PE
The thickness of the pet layer of composite original film is 23 μm, the thickness of PE layers is 15 μm, and the thickness of the adhesive tape is 10 μm；
(c1) wax is prepared；I) the micro- wax powders of 89 weight portion PE and 11 weight portion silicone oil are taken out in solvent barrel in proportion, and
Dispersing and dissolving is carried out using solvent hexamethylene, solid content 30% is made into；II) prepare after be stirred and be stirred with 300rpm
10min, you can；III) micro- wax powder making because can only be fully dispersed, it is impossible to dissolve, then more than prepare after put in storage, it is to be produced to receive
After need again with 300rpm stirring 5min reach be uniformly dispersed after directly use；
(c2) wax is transferred in into PE face of the heat-sealing cover with semi-finished product by reticulate pattern；The thickness of the wax is 1 μm；
(D) heat-sealing cover is carried out into slitting by banding machine with semi-finished product along the center line of the adhesive tape, then by winding
Machine is wound, and obtains heat-sealing cover band finished product.
Embodiment 9
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) roller for being provided with equidistant raised line is made；Spacing between the width of the raised line and two raised lines can
To be configured, adjust according to production needs；
(B) glue is prepared；I) resin of the ethylene bis stearamide of 73 weight portions, 17 weight portions is taken out in proportion
In solvent barrel, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content while pour the transparent powder of 10 weight portions into
30%；II) after solvent burden ratio is complete, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, pour stirring into
In kettle, 2h is stirred with 100rpm, then start to soak 24h, be completely dissolved in ethylene bis stearamide, resin, transparent powder molten
In agent；IV) after soaking fully dissolving, glue-like thing is formed, and again in stirred tank with 100rpm stirring 20min；V) fully
Glue is made after stirring, and is filtered, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, shape
Into free from admixture glue, and contained with solvent barrel, it is to be produced to use；
(C) pass through roller by glue application in PET/PE composite original films PE face, dried by the baking oven of 3m after gluing,
Then 120 DEG C of oven temperature, gait of march 40m/min passes through again roller by glue application in PET/PE composite original films PE face, applies
Dried by the baking oven of 3m again after glue, 120 DEG C of oven temperature, gait of march 40m/min, after being so repeated 10 times, you can
Fully drying, makes that glue is firm to be attached on PE faces, forms the band semi-finished product of the heat-sealing cover with equidistant adhesive tape；The PET/PE
The thickness of the pet layer of composite original film is 23 μm, the thickness of PE layers is 15 μm, and the thickness of the adhesive tape is 10 μm；
(c1) wax is prepared；I) the micro- wax powders of 90 weight portion PE and 10 weight portion silicone oil are taken out in solvent barrel in proportion, and
Dispersing and dissolving is carried out using solvent hexamethylene, solid content 30% is made into；II) prepare after be stirred and be stirred with 300rpm
10min, you can；III) micro- wax powder making because can only be fully dispersed, it is impossible to dissolve, then more than prepare after put in storage, it is to be produced to receive
After need again with 300rpm stirring 5min reach be uniformly dispersed after directly use；
(c2) wax is transferred in into PE face of the heat-sealing cover with semi-finished product by reticulate pattern；The thickness of the wax is 1 μm；
(D) heat-sealing cover is carried out into slitting by banding machine with semi-finished product along the center line of the adhesive tape, then by winding
Machine is wound, and obtains heat-sealing cover band finished product.
Embodiment 10
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) glue is prepared；I) resin of the ethylene bis stearamide of 74 weight portions, 16 weight portions is taken out in proportion
In solvent barrel, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content while pour the transparent powder of 10 weight portions into
30%；II) after solvent burden ratio is complete, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, pour stirring into
In kettle, 2h is stirred with 100rpm, then start to soak 24h, be completely dissolved in ethylene bis stearamide, resin, transparent powder molten
In agent；IV) after soaking fully dissolving, glue-like thing is formed, and again in stirred tank with 100rpm stirring 20min；V) fully
Glue is made after stirring, and is filtered, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, shape
Into free from admixture glue, and contained with solvent barrel, it is to be produced to use；
(B) roller for being provided with equidistant raised line is made；Spacing between the width of the raised line and two raised lines can
To be configured, adjust according to production needs；
(C) pass through roller by glue application in PET/PE composite original films PE face, dried by the baking oven of 3m after gluing,
Then 120 DEG C of oven temperature, gait of march 50m/min passes through again roller by glue application in PET/PE composite original films PE face, applies
Dried by the baking oven of 3m again after glue, 120 DEG C of oven temperature, gait of march 50m/min, after being so repeated 10 times, you can
Fully drying, makes that glue is firm to be attached on PE faces, forms the band semi-finished product of the heat-sealing cover with equidistant adhesive tape；The PET/PE
The thickness of the pet layer of composite original film is 23 μm, the thickness of PE layers is 15 μm, and the thickness of the adhesive tape is 10 μm；
(c1) wax is prepared；I) the micro- wax powders of 91 weight portion PE and 9 weight portion silicone oil are taken out in solvent barrel in proportion, and make
Dispersing and dissolving is carried out with solvent hexamethylene, solid content 30% is made into；II) prepare after be stirred and be stirred with 300rpm
10min, you can；III) micro- wax powder making because can only be fully dispersed, it is impossible to dissolve, then more than prepare after put in storage, it is to be produced to receive
After need again with 300rpm stirring 5min reach be uniformly dispersed after directly use；
(c2) wax is transferred in into PE face of the heat-sealing cover with semi-finished product by reticulate pattern；The thickness of the wax is 1 μm；
(D) heat-sealing cover is carried out into slitting by banding machine with semi-finished product along the center line of the adhesive tape, then by winding
Machine is wound, and obtains heat-sealing cover band finished product.
Embodiment 11
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) glue is prepared；I) resin of the ethylene bis stearamide of 75 weight portions, 15 weight portions is taken out in proportion molten
In agent bucket, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content 30% while pour the transparent powder of 10 weight portions into；
II) after solvent burden ratio is complete, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, in pouring stirred tank into,
2h is stirred with 100rpm, then starts to soak 24h, ethylene bis stearamide, resin, transparent powder is completely dissolved in solvent；
IV) after soaking fully dissolving, glue-like thing is formed, and again in stirred tank with 100rpm stirring 20min；V) it is sufficiently stirred for
After make glue, and filter, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, form nothing
Impurity glue, and contained with solvent barrel, it is to be produced to use；
(B) roller for being provided with equidistant raised line is made；Spacing between the width of the raised line and two raised lines can
To be configured, adjust according to production needs；
(C) pass through roller by glue application in PET/PE composite original films PE face, dried by the baking oven of 3m after gluing,
Then 100 DEG C of oven temperature, gait of march 30m/min passes through again roller by glue application in PET/PE composite original films PE face, applies
Dried by the baking oven of 3m again after glue, 100 DEG C of oven temperature, gait of march 30m/min, after being so repeated 10 times, you can
Fully drying, makes that glue is firm to be attached on PE faces, forms the band semi-finished product of the heat-sealing cover with equidistant adhesive tape；The PET/PE
The thickness of the pet layer of composite original film is 23 μm, the thickness of PE layers is 15 μm, and the thickness of the adhesive tape is 10 μm；
(c1) wax is prepared；I) the micro- wax powders of 92 weight portion PE and 8 weight portion silicone oil are taken out in solvent barrel in proportion, and make
Dispersing and dissolving is carried out with solvent hexamethylene, solid content 30% is made into；II) prepare after be stirred and be stirred with 300rpm
10min, you can；III) micro- wax powder making because can only be fully dispersed, it is impossible to dissolve, then more than prepare after put in storage, it is to be produced to receive
After need again with 300rpm stirring 5min reach be uniformly dispersed after directly use；
(c2) wax is transferred in into PE face of the heat-sealing cover with semi-finished product by reticulate pattern；The thickness of the wax is 1 μm；
(D) heat-sealing cover is carried out into slitting by banding machine with semi-finished product along the center line of the adhesive tape, then by winding
Machine is wound, and obtains heat-sealing cover band finished product.
Embodiment 12
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) glue is prepared；I) resin of the ethylene bis stearamide of 65 weight portions, 25 weight portions is taken out in proportion molten
In agent bucket, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content 30% while pour the transparent powder of 10 weight portions into；
II) after solvent burden ratio is complete, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, in pouring stirred tank into,
2h is stirred with 100rpm, then starts to soak 24h, ethylene bis stearamide, resin, transparent powder is completely dissolved in solvent；
IV) after soaking fully dissolving, glue-like thing is formed, and again in stirred tank with 100rpm stirring 20min；V) it is sufficiently stirred for
After make glue, and filter, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, form nothing
Impurity glue, and contained with solvent barrel, it is to be produced to use；
(B) roller for being provided with equidistant raised line is made；Spacing between the width of the raised line and two raised lines can
To be configured, adjust according to production needs；
(C) pass through roller by glue application in PET/PE composite original films PE face, dried by the baking oven of 3m after gluing,
Then 100 DEG C of oven temperature, gait of march 40m/min passes through again roller by glue application in PET/PE composite original films PE face, applies
Dried by the baking oven of 3m again after glue, 100 DEG C of oven temperature, gait of march 40m/min, after being so repeated 10 times, you can
Fully drying, makes that glue is firm to be attached on PE faces, forms the band semi-finished product of the heat-sealing cover with equidistant adhesive tape；The PET/PE
The thickness of the pet layer of composite original film is 23 μm, the thickness of PE layers is 15 μm, and the thickness of the adhesive tape is 10 μm；
(c1) wax is prepared；I) the micro- wax powders of 93 weight portion PE and 7 weight portion silicone oil are taken out in solvent barrel in proportion, and make
Dispersing and dissolving is carried out with solvent hexamethylene, solid content 30% is made into；II) prepare after be stirred and be stirred with 300rpm
10min, you can；III) micro- wax powder making because can only be fully dispersed, it is impossible to dissolve, then more than prepare after put in storage, it is to be produced to receive
After need again with 300rpm stirring 5min reach be uniformly dispersed after directly use；
(c2) wax is transferred in into PE face of the heat-sealing cover with semi-finished product by reticulate pattern；The thickness of the wax is 1 μm；
(D) heat-sealing cover is carried out into slitting by banding machine with semi-finished product along the center line of the adhesive tape, then by winding
Machine is wound, and obtains heat-sealing cover band finished product.
Embodiment 13
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) roller for being provided with equidistant raised line is made；Spacing between the width of the raised line and two raised lines can
To be configured, adjust according to production needs；
(B) glue is prepared；I) resin of the ethylene bis stearamide of 68 weight portions, 22 weight portions is taken out in proportion molten
In agent bucket, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content 30% while pour the transparent powder of 10 weight portions into；
II) after solvent burden ratio is complete, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, in pouring stirred tank into,
2h is stirred with 100rpm, then starts to soak 24h, ethylene bis stearamide, resin, transparent powder is completely dissolved in solvent；
IV) after soaking fully dissolving, glue-like thing is formed, and again in stirred tank with 100rpm stirring 20min；V) it is sufficiently stirred for
After make glue, and filter, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, form nothing
Impurity glue, and contained with solvent barrel, it is to be produced to use；
(C) pass through roller by glue application in PET/PE composite original films PE face, dried by the baking oven of 3m after gluing,
Then 100 DEG C of oven temperature, gait of march 50m/min passes through again roller by glue application in PET/PE composite original films PE face, applies
Dried by the baking oven of 3m again after glue, 100 DEG C of oven temperature, gait of march 50m/min, after being so repeated 10 times, you can
Fully drying, makes that glue is firm to be attached on PE faces, forms the band semi-finished product of the heat-sealing cover with equidistant adhesive tape；The PET/PE
The thickness of the pet layer of composite original film is 23 μm, the thickness of PE layers is 15 μm, and the thickness of the adhesive tape is 10 μm；
(c1) wax is prepared；I) the micro- wax powders of 94 weight portion PE and 6 weight portion silicone oil are taken out in solvent barrel in proportion, and make
Dispersing and dissolving is carried out with solvent hexamethylene, solid content 30% is made into；II) prepare after be stirred and be stirred with 300rpm
10min, you can；III) micro- wax powder making because can only be fully dispersed, it is impossible to dissolve, then more than prepare after put in storage, neck to be produced
Need with after again with 300rpm stirring 5min reach be uniformly dispersed after directly use；
(c2) wax is transferred in into PE face of the heat-sealing cover with semi-finished product by reticulate pattern；The thickness of the wax is 1 μm；
(D) heat-sealing cover is carried out into slitting by banding machine with semi-finished product along the center line of the adhesive tape, then by winding
Machine is wound, and obtains heat-sealing cover band finished product.
Embodiment 14
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) roller for being provided with equidistant raised line is made；Spacing between the width of the raised line and two raised lines can
To be configured, adjust according to production needs；
(B) glue is prepared；I) resin of the ethylene bis stearamide of 70 weight portions, 20 weight portions is taken out in proportion molten
In agent bucket, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content 30% while pour the transparent powder of 10 weight portions into；
II) after solvent burden ratio is complete, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, in pouring stirred tank into,
2h is stirred with 100rpm, then starts to soak 24h, ethylene bis stearamide, resin, transparent powder is completely dissolved in solvent；
IV) after soaking fully dissolving, glue-like thing is formed, and again in stirred tank with 100rpm stirring 20min；V) it is sufficiently stirred for
After make glue, and filter, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, form nothing
Impurity glue, and contained with solvent barrel, it is to be produced to use；
(C) pass through roller by glue application in PET/PE composite original films PE face, dried by the baking oven of 3m after gluing,
100～120 DEG C of oven temperature, 30～50m/min of gait of march is then compound former in PET/PE by glue application by roller again
Film PE faces, are dried by the baking oven of 3m again, 100～120 DEG C of oven temperature, 30～50m/min of gait of march, such as after gluing
After this repeats 7～15 times, you can fully drying, make that glue is firm to be attached on PE faces, form the heat-sealing with equidistant adhesive tape
Cover strip semi-finished product；The thickness of the pet layer of the PET/PE composite original films is 23 μm, the thickness of PE layers is 15 μm, the adhesive tape
Thickness is 10 μm；
(c1) wax is prepared；I) the micro- wax powders of 95 weight portion PE and 5 weight portion silicone oil are taken out in solvent barrel in proportion, and
Dispersing and dissolving is carried out using solvent hexamethylene, solid content 30% is made into；II) prepare after be stirred and be stirred with 300rpm
10min, you can；III) micro- wax powder making because can only be fully dispersed, it is impossible to dissolve, then more than prepare after put in storage, it is to be produced to receive
After need again with 300rpm stirring 5min reach be uniformly dispersed after directly use；
(c2) wax is transferred in into PE face of the heat-sealing cover with semi-finished product by reticulate pattern；The thickness of the wax is 1 μm；
(D) heat-sealing cover is carried out into slitting by banding machine with semi-finished product along the center line of the adhesive tape, then by winding
Machine is wound, and obtains heat-sealing cover band finished product.
Embodiment 15
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) glue is prepared；I) resin of the ethylene bis stearamide of 72 weight portions, 18 weight portions is taken out in proportion molten
In agent bucket, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content 30% while pour the transparent powder of 10 weight portions into；
II) after solvent burden ratio is complete, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, in pouring stirred tank into,
2h is stirred with 100rpm, then starts to soak 24h, ethylene bis stearamide, resin, transparent powder is completely dissolved in solvent；
IV) after soaking fully dissolving, glue-like thing is formed, and again in stirred tank with 100rpm stirring 20min；V) it is sufficiently stirred for
After make glue, and filter, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, form nothing
Impurity glue, and contained with solvent barrel, it is to be produced to use；
(B) roller for being provided with equidistant raised line is made；Spacing between the width of the raised line and two raised lines can
To be configured, adjust according to production needs；
(C) pass through roller by glue application in PET/PE composite original films PE face, dried by the baking oven of 3m after gluing,
Then 120 DEG C of oven temperature, gait of march 50m/min passes through again roller by glue application in PET/PE composite original films PE face, applies
Dried by the baking oven of 3m again after glue, 120 DEG C of oven temperature, gait of march 50m/min, after being so repeated 15 times, you can
Fully drying, makes that glue is firm to be attached on PE faces, forms the band semi-finished product of the heat-sealing cover with equidistant adhesive tape；The PET/PE
The thickness of the pet layer of composite original film is 23 μm, the thickness of PE layers is 15 μm, and the thickness of the adhesive tape is 10 μm；
(c1) wax is prepared；I) the micro- wax powders of 96 weight portion PE and 4 weight portion silicone oil are taken out in solvent barrel in proportion, and make
Dispersing and dissolving is carried out with solvent hexamethylene, solid content 30% is made into；II) prepare after be stirred and be stirred with 300rpm
10min, you can；III) micro- wax powder making because can only be fully dispersed, it is impossible to dissolve, then more than prepare after put in storage, it is to be produced to receive
After need again with 300rpm stirring 5min reach be uniformly dispersed after directly use；
(c2) wax is transferred in into PE face of the heat-sealing cover with semi-finished product by reticulate pattern；The thickness of the wax is 1 μm；
(D) heat-sealing cover is carried out into slitting by banding machine with semi-finished product along the center line of the adhesive tape, then by winding
Machine is wound, and obtains heat-sealing cover band finished product.
Embodiment 16
A kind of manufacture method of heat-sealing cover band, comprises the following steps：
(A) glue is prepared；I) resin of the ethylene bis stearamide of 75 weight portions, 15 weight portions is taken out in proportion molten
In agent bucket, toluene solvant dissolving is poured into, one side pneumatic stirring reaches solid content 30% while pour the transparent powder of 10 weight portions into；
II) after solvent burden ratio is complete, 5min is first stirred with 300rpm using Pneumatic blender；III) stir after 5min, in pouring stirred tank into,
2h is stirred with 100rpm, then starts to soak 24h, ethylene bis stearamide, resin, transparent powder is completely dissolved in solvent；
IV) after soaking fully dissolving, glue-like thing is formed, and again in stirred tank with 100rpm stirring 20min；V) it is sufficiently stirred for
After make glue, and filter, filtered using 200 mesh filter bags, glue impurities in water and crystal thing etc. are filtered out, form nothing
Impurity glue, and contained with solvent barrel, it is to be produced to use；
(B) roller for being provided with equidistant raised line is made；Spacing between the width of the raised line and two raised lines can
To be configured, adjust according to production needs；
(C) pass through roller by glue application in PET/PE composite original films PE face, dried by the baking oven of 3m after gluing,
Then 120 DEG C of oven temperature, gait of march 50m/min passes through again roller by glue application in PET/PE composite original films PE face, applies
Dried by the baking oven of 3m again after glue, 120 DEG C of oven temperature, gait of march 50m/min, after being so repeated 15 times, you can
Fully drying, makes that glue is firm to be attached on PE faces, forms the band semi-finished product of the heat-sealing cover with equidistant adhesive tape；The PET/
The thickness of the pet layer of PE composite original films is 23 μm, the thickness of PE layers is 15 μm, and the thickness of the adhesive tape is 10 μm；
(c1) wax is prepared；I) the micro- wax powders of 97 weight portion PE and 3 weight portion silicone oil are taken out in solvent barrel in proportion, and make
Dispersing and dissolving is carried out with solvent hexamethylene, solid content 30% is made into；II) prepare after be stirred and be stirred with 300rpm
10min, you can；III) micro- wax powder making because can only be fully dispersed, it is impossible to dissolve, then more than prepare after put in storage, it is to be produced to receive
After need again with 300rpm stirring 5min reach be uniformly dispersed after directly use；
(c2) wax is transferred in into PE face of the heat-sealing cover with semi-finished product by reticulate pattern；The thickness of the wax is 1 μm；
(D) heat-sealing cover is carried out into slitting by banding machine with semi-finished product along the center line of the adhesive tape, then by winding
Machine is wound, and obtains heat-sealing cover band finished product.
Preferred embodiments of the present invention are the foregoing is only, embodiments of the present invention and protection model is not thereby limited
Enclose, to those skilled in the art, should can appreciate that all equivalents with done by present specification are replaced
Resulting scheme is changed and obviously changed, should be included in protection scope of the present invention.
Claims (8)
1. a kind of manufacture method of heat-sealing cover band, it is characterised in that comprise the following steps：
(A) roller for being provided with equidistant raised line is made；
(B) glue is prepared；
(C) pass through roller by glue application in PET/PE composite original films PE face, drying, form the heat-sealing cover with equidistant adhesive tape
Band semi-finished product；
(D) heat-sealing cover band semi-finished product are carried out into slitting by banding machine, then is wound by winder, obtain heat-sealing cover
Band finished product.
2. the manufacture method of heat-sealing cover band according to claim 1, it is characterised in that the glue is by 65-75wt%
Ethylene bis stearamide, 15-25wt% resins and 10wt% transparent powders composition.
3. the manufacture method of heat-sealing cover band according to claim 1, it is characterised in that the PET/PE composite original films
The thickness of pet layer is 23 μm, the thickness of PE layers is 15 μm, and the thickness of the adhesive tape is 10 μm.
4. the manufacture method of heat-sealing cover band according to claim 1, it is characterised in that also wrap between step C and step D
Include step c1 and prepare wax and step c2 and wax is transferred in into PE face of the heat-sealing cover with semi-finished product by reticulate pattern.
5. the manufacture method of heat-sealing cover band according to claim 4, it is characterised in that the wax is by 85-97wt%PE
Micro- wax powder and 3-15wt% silicone oil are constituted.
6. the manufacture method of heat-sealing cover band according to claim 4, it is characterised in that the thickness of the wax is 1 μm.
7. the manufacture method of heat-sealing cover band according to claim 1, it is characterised in that by the heat-sealing cover band in step D
Center line of the semi-finished product by banding machine along the adhesive tape carries out slitting.
8. according to the manufacture method of the arbitrary described heat-sealing cover band of claim 1 to 7, it is characterised in that step A and step B
Order is exchanged.