CN106630021A - Modified foamed titanium particle electrode with electrocatalysis carbazole removal function and preparation method thereof - Google Patents
Modified foamed titanium particle electrode with electrocatalysis carbazole removal function and preparation method thereof Download PDFInfo
- Publication number
- CN106630021A CN106630021A CN201611039113.8A CN201611039113A CN106630021A CN 106630021 A CN106630021 A CN 106630021A CN 201611039113 A CN201611039113 A CN 201611039113A CN 106630021 A CN106630021 A CN 106630021A
- Authority
- CN
- China
- Prior art keywords
- mixed liquor
- added
- conditions
- minutes
- under
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a modified foamed titanium particle electrode with an electrocatalysis carbazole removal function and a preparation method thereof. Foamed titanium, trichloromethane and ethyl alcohol are prepared into a substance A; the substance A is prepared into a substance E through being modified by a mixed solution prepared from silver nitrate, platinum nitrate, diethyl ether and Al(NO3)3; the substance E is prepared into a substance H through being modified by a mixed solution prepared from Cu(NO3)2, ethyl alcohol, InCl3, TiCl4, CoCl2 and MgCl2; the substance H is prepared into a substance K through being modified by a mixed solution prepared from sodium dodecyl sulfate, n-hexane, normal butanol, ammonium metavanadate, sodium citrate, CoCl2 and MgCl2; the substance K is prepared into a substance of the modified foamed titanium particle electrode with the electrocatalysis carbazole removal function through the mixed solution prepared from polyvinyl alcohol and HAuCl4.
Description
Technical field
The invention belongs to organic wastewater with difficult degradation thereby Electrocatalytic Oxidation processing technology field, more particularly to one kind are urged with electricity
Change the modified titanium foam granule electrode and preparation method for removing carbazole function.
Background technology
Electro-catalytic oxidation technology is a kind of very promising water technology for gradually growing up in recent years, mainly
Oxidative degradation is carried out to the organic pollution in waste water by producing the active groups with strong oxidizing property such as hydroxyl radical free radical, can
So that hardly degraded organic substance or bio-toxicity pollutant be converted into into biodegradable or innocuous substance, that improves waste water can be biochemical
Property, so as to be beneficial to follow-up biological treatment.Therefore, electrocatalytic oxidation water technology is processing high concentration, bio-refractory work
The features such as industry waste water aspect has non-secondary pollution, low cost, strong applicability, efficiency high.Electrode material is electrocatalytic oxidation skill
The core component of art, its performance has decisive influence for the treatment effeciency and operating cost of electro-catalytic oxidation technology, because
This electrocatalysis material for exploring and preparing good combination property is the research emphasis of current electro-catalytic oxidation technology.But traditional electrode
The resistance of material is larger, conductance is low so that its in the treatment of waste water current efficiency is low, stability not enough, short life, electrode material
Material is relatively costly, limits popularization and application of the electro-catalytic oxidation technology in water process and development, so new electrode materials
Research also needs to further reinforcement with preparation.Also lack at present and there is efficient electric catalytic elimination function to carbazole specific pollutants
Electrode material and preparation method.
The content of the invention
It is an object of the invention to provide a kind of modified titanium foam granule electrode and system that carbazole function is removed with electro-catalysis
Preparation Method, its preparation method is comprised the following steps that:
(1) 500mL beakers are put into after is washed with 1000mL deionized waters the 132g titanium foam particles that particle diameter is 4~6mm
In, 300mL molar concentrations are added for the hydrochloric acid solution of 0.1mol/L and soak 0.5h, liquid is removed after filtration and obtains substance A 01,
Substance A 01 is added to into the AgNO that 250mL molar concentrations are 2.51mol/L3In solution, shake in the shaking table that temperature is 65 DEG C
15 minutes, it is cooled to after room temperature and is filtered to remove liquid and obtains substance A 02, the Jing 900mL mass percent concentrations of substance A 02 is 95%
Ethanol washing after place 1.5h in 85 DEG C of drying box, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain
Substance A 1;
(2) it is in 1000mL conical flasks, in 1000r/ 9.88 grams of platinum nitrates and 800mL deionized waters to be added to into volume
Stir 3 minutes under the conditions of min, add 15mL red fuming nitric acid (RFNA)s, 4 parts of equivalent is divided into after shaking up, obtain mixed liquor K1, mixed liquor K2, mix
Close liquid K3, mixed liquor K4;
(3) by 776 milligrams of Al (NO3)3With the AgNO that 95mL molar concentrations are 0.82mol/L3Solution is added to mixed liquor K1
In, stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor L1;
(4) substance A 1 is added in mixed liquor L1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain substance A 2, substance A 2 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
Drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain substance A 3;
(5) by 796 milligrams of Al (NO3)3With the AgNO that 75mL molar concentrations are 0.72mol/L3Solution is added to mixed liquor K2
In, stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor L2;
(6) substance A 3 is added in mixed liquor L2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain substance A 4, substance A 4 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
Drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain substance A 5;
(7) by 816 milligrams of Al (NO3)3With the AgNO that 55mL molar concentrations are 0.62mol/L3Solution is added to mixed liquor K3
In, stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor L3;
(8) substance A 5 is added in mixed liquor L3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain substance A 6, substance A 6 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
Drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain substance A 7;
(9) by 836 milligrams of Al (NO3)3With the AgNO that 35mL molar concentrations are 0.52mol/L3Solution is added to mixed liquor K4
In, stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor L4;
(10) substance A 7 is added in mixed liquor L4, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains substance A 8, substance A 8 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain substance A;
(11) by 6.28 grams of AgNO3It is in 1000mL conical flasks, in 1000r/min bars to be added to volume with 750mL ether
Stir 3 minutes under part, 3 parts of equivalent is divided into after shaking up, obtain mixed liquor M1, mixed liquor M2, mixed liquor M3;
(12) by 322 milligrams of AgNO3With the Al (NO that 30mL molar concentrations are 0.47mol/L3)3Solution is added to mixed liquor
In M1, stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor N1;
(13) substance A is added in mixed liquor N1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain substance B, substance B is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
1.5h is placed in drying box, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, substance B 1 is obtained;
(14) by 342 milligrams of AgNO3With the Al (NO that 60mL molar concentrations are 0.67mol/L3)3Solution is added to mixed liquor
In M2, stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor N2;
(15) substance B 1 is added in mixed liquor N2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains substance B 2, substance B 2 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain substance C;
(16) by 362 milligrams of AgNO3With the Al (NO that 90mL molar concentrations are 0.87mol/L3)3Solution is added to mixed liquor
In M3, stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor N3;
(17) substance C is added in mixed liquor N3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain material D, material D is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
1.5h is placed in drying box, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material E is obtained;
(18) by 9.24 grams of Cu (NO3)2It is in 1000mL conical flasks, in 1000r/min to be added to volume with 900mL ethanol
Under the conditions of stir 3 minutes, add 5mL red fuming nitric acid (RFNA)s, 3 parts of equivalent is divided into after shaking up, obtain mixed liquor P1, mixed liquor P2, mixed liquor
P3;
(19) by 85mL molar concentrations for 0.61mol/L InCl3Solution is added in mixed liquor P1, in 1000r/min
Under the conditions of stir 3 minutes, obtain mixed liquor Q1;
(20) material E is added in mixed liquor Q1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain material F1, material F1 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
Drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material F2;
(21) by 70mL molar concentrations for 0.68mol/L Cu (NO3)2Solution is added in mixed liquor P2, in 1000r/
Stir 3 minutes under the conditions of min, obtain mixed liquor Q2;
(22) material F2 is added in mixed liquor Q2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material F3, material F3 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material F4;
(23) by 60mL molar concentrations for 0.51mol/L InCl3Solution is added in mixed liquor P3, in 1000r/min
Under the conditions of stir 3 minutes, obtain mixed liquor Q3;
(24) material F4 is added in mixed liquor Q3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material F5, material F5 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material F;
(25) by 5.28g TiCl4Volume is added to the sodium citrate solution that 750mL mass percent concentrations are 10%
In for 1000mL conical flasks, stir 3 minutes under the conditions of 1000r/min, 3 parts of equivalent is divided into after shaking up, obtain mixed liquor R1, mix
Close liquid R2, mixed liquor R3;
(26) by 40mL molar concentrations for 0.49mol/L CoCl2Solution and 60mL molar concentrations are for 1.02mol/L's
MgCl2Solution is added in mixed liquor R1, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor S1;
(27) material F is added in mixed liquor S1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain material G1, material G1 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
Drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material H1;
(28) by 50mL molar concentrations for 0.69mol/L CoCl2Solution and 50mL molar concentrations are for 0.82mol/L's
MgCl2Solution is added in mixed liquor R2, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor S2;
(29) material H1 is added in mixed liquor S2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material G2, material G2 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material H2;
(30) by 60mL molar concentrations for 0.89mol/L CoCl2Solution and 40mL molar concentrations are for 0.52mol/L's
MgCl2Solution is added in mixed liquor R3, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor S3;
(31) material H2 is added in mixed liquor S3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material G3, material G3 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material H;
(32) 3.66g lauryl sodium sulfate, 40mL n-hexanes, 20 milliliters of n-butanols are added sequentially to volume and are
In 250mL conical flasks, 9.87g ammonium metavanadates and 150mL deionized waters are added, be placed in 70 DEG C of water-baths in 1000r/min bars
1h is stirred under part, the hydrochloric acid solution that 25mL molar concentrations are 2.40mol/L is subsequently adding, is shaken in the shaking table that temperature is 45 DEG C
0.5h, is cooled to after room temperature under the conditions of 7500r/min and 15min is centrifuged, and removes supernatant, uses 500mL mass percent concentrations
Ethanol for 95% is washed, and obtains material I;
(33) sodium citrate solution that material I and 800mL mass percent concentration is 15% is added to into volume is
In 1000mL conical flasks, stir 3 minutes under the conditions of 1000r/min, 4 parts of equivalent is divided into after shaking up, obtain mixed liquor T1, mixing
Liquid T2, mixed liquor T3, mixed liquor T4;
(34) by 35mL molar concentrations for 0.68mol/L CoCl2Solution and 65mL molar concentrations are for 0.93mol/L's
MgCl2Solution is added in mixed liquor T1, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor U1;
(35) material H is added in mixed liquor U1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain material J1, material J1 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
Drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material K1;
(36) by 45mL molar concentrations for 0.78mol/L CoCl2Solution and 55mL molar concentrations are for 0.83mol/L's
MgCl2Solution is added in mixed liquor T2, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor U2;
(37) material K1 is added in mixed liquor U2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material J2, material J2 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material K2;
(38) by 55mL molar concentrations for 0.88mol/L CoCl2Solution and 45mL molar concentrations are for 0.73mol/L's
MgCl2Solution is added in mixed liquor T3, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor U3;
(39) material K2 is added in mixed liquor U3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material J3, material J3 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material K3;
(40) by 65mL molar concentrations for 0.98mol/L CoCl2Solution and 35mL molar concentrations are for 0.63mol/L's
MgCl2Solution is added in mixed liquor T4, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor U4;
(41) material K3 is added in mixed liquor U4, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material J4, material J4 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material K;
(42) 14.56g polyvinyl alcohol and 800mL deionized waters are added to into volume in 1000mL conical flasks,
Stir 3 minutes under the conditions of 1000r/min, 4 parts of equivalent is divided into after shaking up, obtain mixed liquor V1, mixed liquor V2, mixed liquor V3, mixed
Close liquid V4;
(43) by 90mL molar concentrations for 1.09mol/L HAuCl4Solution is added in mixed liquor V1, in 1000r/min
Under the conditions of stir 3 minutes, obtain mixed liquor W1;
(44) material K is added in mixed liquor W1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain material L1, material L1 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
Drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material Z1;
(45) by 80mL molar concentrations for 0.89mol/L HAuCl4Solution is added in mixed liquor V2, in 1000r/min
Under the conditions of stir 3 minutes, obtain mixed liquor W2;
(46) material Z1 is added in mixed liquor W2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material L2, material L2 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material Z2;
(47) by 70mL molar concentrations for 0.69mol/L HAuCl4Solution is added in mixed liquor V3, in 1000r/min
Under the conditions of stir 3 minutes, obtain mixed liquor W3;
(48) material Z2 is added in mixed liquor W3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material L3, material L3 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material Z3;
(49) by 60mL molar concentrations for 0.49mol/L HAuCl4Solution is added in mixed liquor V4, in 1000r/min
Under the conditions of stir 3 minutes, obtain mixed liquor W4;
(50) material Z3 is added in mixed liquor W4, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material L4, material L4 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, the material for obtaining as has electricity
The modified titanium foam granule electrode of catalytic elimination carbazole function.
The invention has the beneficial effects as follows, the obtained modified titanium foam granule electrode tool that carbazole function is removed with electro-catalysis
Have that current efficiency is high, stability is strong, electrode life length, it is high to carbazole removal efficiency the features such as.
Specific embodiment
The present invention provides a kind of modified titanium foam granule electrode and preparation method that carbazole function is removed with electro-catalysis, under
Face illustrates to apply process in fact by an example.
Embodiment 1.
(1) 500mL beakers are put into after is washed with 1000mL deionized waters the 132g titanium foam particles that particle diameter is 4~6mm
In, 300mL molar concentrations are added for the hydrochloric acid solution of 0.1mol/L and soak 0.5h, liquid is removed after filtration and obtains substance A 01,
Substance A 01 is added to into the AgNO that 250mL molar concentrations are 2.51mol/L3In solution, shake in the shaking table that temperature is 65 DEG C
15 minutes, it is cooled to after room temperature and is filtered to remove liquid and obtains substance A 02, the Jing 900mL mass percent concentrations of substance A 02 is 95%
Ethanol washing after place 1.5h in 85 DEG C of drying box, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain
Substance A 1;
(2) it is in 1000mL conical flasks, in 1000r/ 9.88 grams of platinum nitrates and 800mL deionized waters to be added to into volume
Stir 3 minutes under the conditions of min, add 15mL red fuming nitric acid (RFNA)s, 4 parts of equivalent is divided into after shaking up, obtain mixed liquor K1, mixed liquor K2, mix
Close liquid K3, mixed liquor K4;
(3) by 776 milligrams of Al (NO3)3With the AgNO that 95mL molar concentrations are 0.82mol/L3Solution is added to mixed liquor K1
In, stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor L1;
(4) substance A 1 is added in mixed liquor L1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain substance A 2, substance A 2 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
Drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain substance A 3;
(5) by 796 milligrams of Al (NO3)3With the AgNO that 75mL molar concentrations are 0.72mol/L3Solution is added to mixed liquor K2
In, stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor L2;
(6) substance A 3 is added in mixed liquor L2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain substance A 4, substance A 4 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
Drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain substance A 5;
(7) by 816 milligrams of Al (NO3)3With the AgNO that 55mL molar concentrations are 0.62mol/L3Solution is added to mixed liquor K3
In, stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor L3;
(8) substance A 5 is added in mixed liquor L3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain substance A 6, substance A 6 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
Drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain substance A 7;
(9) by 836 milligrams of Al (NO3)3With the AgNO that 35mL molar concentrations are 0.52mol/L3Solution is added to mixed liquor K4
In, stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor L4;
(10) substance A 7 is added in mixed liquor L4, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains substance A 8, substance A 8 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain substance A;
(11) by 6.28 grams of AgNO3It is in 1000mL conical flasks, in 1000r/min bars to be added to volume with 750mL ether
Stir 3 minutes under part, 3 parts of equivalent is divided into after shaking up, obtain mixed liquor M1, mixed liquor M2, mixed liquor M3;
(12) by 322 milligrams of AgNO3With the Al (NO that 30mL molar concentrations are 0.47mol/L3)3Solution is added to mixed liquor
In M1, stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor N1;
(13) substance A is added in mixed liquor N1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain substance B, substance B is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
1.5h is placed in drying box, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, substance B 1 is obtained;
(14) by 342 milligrams of AgNO3With the Al (NO that 60mL molar concentrations are 0.67mol/L3)3Solution is added to mixed liquor
In M2, stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor N2;
(15) substance B 1 is added in mixed liquor N2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains substance B 2, substance B 2 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain substance C;
(16) by 362 milligrams of AgNO3With the Al (NO that 90mL molar concentrations are 0.87mol/L3)3Solution is added to mixed liquor
In M3, stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor N3;
(17) substance C is added in mixed liquor N3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain material D, material D is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
1.5h is placed in drying box, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material E is obtained;
(18) by 9.24 grams of Cu (NO3)2It is in 1000mL conical flasks, in 1000r/min to be added to volume with 900mL ethanol
Under the conditions of stir 3 minutes, add 5mL red fuming nitric acid (RFNA)s, 3 parts of equivalent is divided into after shaking up, obtain mixed liquor P1, mixed liquor P2, mixed liquor
P3;
(19) by 85mL molar concentrations for 0.61mol/L InCl3Solution is added in mixed liquor P1, in 1000r/min
Under the conditions of stir 3 minutes, obtain mixed liquor Q1;
(20) material E is added in mixed liquor Q1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain material F1, material F1 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
Drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material F2;
(21) by 70mL molar concentrations for 0.68mol/L Cu (NO3)2Solution is added in mixed liquor P2, in 1000r/
Stir 3 minutes under the conditions of min, obtain mixed liquor Q2;
(22) material F2 is added in mixed liquor Q2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material F3, material F3 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material F4;
(23) by 60mL molar concentrations for 0.51mol/L InCl3Solution is added in mixed liquor P3, in 1000r/min
Under the conditions of stir 3 minutes, obtain mixed liquor Q3;
(24) material F4 is added in mixed liquor Q3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material F5, material F5 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material F;
(25) by 5.28g TiCl4Volume is added to the sodium citrate solution that 750mL mass percent concentrations are 10%
In for 1000mL conical flasks, stir 3 minutes under the conditions of 1000r/min, 3 parts of equivalent is divided into after shaking up, obtain mixed liquor R1, mix
Close liquid R2, mixed liquor R3;
(26) by 40mL molar concentrations for 0.49mol/L CoCl2Solution and 60mL molar concentrations are for 1.02mol/L's
MgCl2Solution is added in mixed liquor R1, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor S1;
(27) material F is added in mixed liquor S1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain material G1, material G1 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
Drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material H1;
(28) by 50mL molar concentrations for 0.69mol/L CoCl2Solution and 50mL molar concentrations are for 0.82mol/L's
MgCl2Solution is added in mixed liquor R2, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor S2;
(29) material H1 is added in mixed liquor S2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material G2, material G2 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material H2;
(30) by 60mL molar concentrations for 0.89mol/L CoCl2Solution and 40mL molar concentrations are for 0.52mol/L's
MgCl2Solution is added in mixed liquor R3, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor S3;
(31) material H2 is added in mixed liquor S3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material G3, material G3 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material H;
(32) 3.66g lauryl sodium sulfate, 40mL n-hexanes, 20 milliliters of n-butanols are added sequentially to volume and are
In 250mL conical flasks, 9.87g ammonium metavanadates and 150mL deionized waters are added, be placed in 70 DEG C of water-baths in 1000r/min bars
1h is stirred under part, the hydrochloric acid solution that 25mL molar concentrations are 2.40mol/L is subsequently adding, is shaken in the shaking table that temperature is 45 DEG C
0.5h, is cooled to after room temperature under the conditions of 7500r/min and 15min is centrifuged, and removes supernatant, uses 500mL mass percent concentrations
Ethanol for 95% is washed, and obtains material I;
(33) sodium citrate solution that material I and 800mL mass percent concentration is 15% is added to into volume is
In 1000mL conical flasks, stir 3 minutes under the conditions of 1000r/min, 4 parts of equivalent is divided into after shaking up, obtain mixed liquor T1, mixing
Liquid T2, mixed liquor T3, mixed liquor T4;
(34) by 35mL molar concentrations for 0.68mol/L CoCl2Solution and 65mL molar concentrations are for 0.93mol/L's
MgCl2Solution is added in mixed liquor T1, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor U1;
(35) material H is added in mixed liquor U1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain material J1, material J1 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
Drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material K1;
(36) by 45mL molar concentrations for 0.78mol/L CoCl2Solution and 55mL molar concentrations are for 0.83mol/L's
MgCl2Solution is added in mixed liquor T2, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor U2;
(37) material K1 is added in mixed liquor U2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material J2, material J2 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material K2;
(38) by 55mL molar concentrations for 0.88mol/L CoCl2Solution and 45mL molar concentrations are for 0.73mol/L's
MgCl2Solution is added in mixed liquor T3, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor U3;
(39) material K2 is added in mixed liquor U3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material J3, material J3 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material K3;
(40) by 65mL molar concentrations for 0.98mol/L CoCl2Solution and 35mL molar concentrations are for 0.63mol/L's
MgCl2Solution is added in mixed liquor T4, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor U4;
(41) material K3 is added in mixed liquor U4, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material J4, material J4 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material K;
(42) 14.56g polyvinyl alcohol and 800mL deionized waters are added to into volume in 1000mL conical flasks,
Stir 3 minutes under the conditions of 1000r/min, 4 parts of equivalent is divided into after shaking up, obtain mixed liquor V1, mixed liquor V2, mixed liquor V3, mixed
Close liquid V4;
(43) by 90mL molar concentrations for 1.09mol/L HAuCl4Solution is added in mixed liquor V1, in 1000r/min
Under the conditions of stir 3 minutes, obtain mixed liquor W1;
(44) material K is added in mixed liquor W1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room temperature
After be filtered to remove liquid and obtain material L1, material L1 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
Drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material Z1;
(45) by 80mL molar concentrations for 0.89mol/L HAuCl4Solution is added in mixed liquor V2, in 1000r/min
Under the conditions of stir 3 minutes, obtain mixed liquor W2;
(46) material Z1 is added in mixed liquor W2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material L2, material L2 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material Z2;
(47) by 70mL molar concentrations for 0.69mol/L HAuCl4Solution is added in mixed liquor V3, in 1000r/min
Under the conditions of stir 3 minutes, obtain mixed liquor W3;
(48) material Z2 is added in mixed liquor W3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material L3, material L3 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, obtain material Z3;
(49) by 60mL molar concentrations for 0.49mol/L HAuCl4Solution is added in mixed liquor V4, in 1000r/min
Under the conditions of stir 3 minutes, obtain mixed liquor W4;
(50) material Z3 is added in mixed liquor W4, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to room
Liquid is filtered to remove after temperature and obtains material L4, material L4 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% 85
DEG C drying box in place 1.5h, be subsequently placed in Muffle furnace the roasting 1h under the conditions of 480 DEG C, the material for obtaining as has electricity
The modified titanium foam granule electrode of catalytic elimination carbazole function.
It is presented herein below with the modified titanium foam granule electrode obtained in the inventive method with electro-catalysis removal carbazole function
Electro-catalytic Oxidation Process test has been carried out to the waste water containing carbazole in electric catalysis reactor, the present invention has been further illustrated.
Electricity is seated in by having the modified titanium foam granule electrode that electro-catalysis removes carbazole function obtained in the inventive method
In catalytic reactor, Degrading experiment is carried out to the waste water containing carbazole, as a result shown the electrocatalytic reaction loaded by the electrode
Device can efficiently remove the carbazole in waste water, be 5.0 in pH when the carbazole concentration in waste water is 55.4mg/L, and voltage is
14V, process time is that the carbazole concentration after process in water outlet is reduced to 1.1mg/L under the conditions of 45min.
Claims (1)
1. it is a kind of with electro-catalysis remove carbazole function modified titanium foam granule electrode preparation method, it is characterised in that should
Method is comprised the following steps that:
(1) it is put in 500mL beakers after is washed with 1000mL deionized waters the 132g titanium foam particles that particle diameter is 4~6mm, plus
Enter 300mL molar concentrations be 0.1mol/L hydrochloric acid solution and soak 0.5h, after filtration remove liquid obtain substance A 01, by thing
Matter A01 is added to the AgNO that 250mL molar concentrations are 2.51mol/L3In solution, 15 points are shaken in the shaking table that temperature is 65 DEG C
Clock, is cooled to after room temperature and is filtered to remove liquid and obtains substance A 02, and the Jing 900mL mass percent concentrations of substance A 02 are 95% second
1.5h is placed in 85 DEG C of drying box after alcohol washing, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material is obtained
A1;
(2) it is in 1000mL conical flasks, in 1000r/min bars 9.88 grams of platinum nitrates and 800mL deionized waters to be added to into volume
Stir 3 minutes under part, add 15mL red fuming nitric acid (RFNA)s, 4 parts of equivalent is divided into after shaking up, obtain mixed liquor K1, mixed liquor K2, mixed liquor
K3, mixed liquor K4;
(3) by 776 milligrams of Al (NO3)3With the AgNO that 95mL molar concentrations are 0.82mol/L3Solution is added in mixed liquor K1,
Stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor L1;
(4) substance A 1 is added in mixed liquor L1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to mistake after room temperature
Filter liquid and obtain substance A 2, substance A 2 is dry at 85 DEG C Jing after the ethanol washing that 100mL mass percent concentrations are 95%
1.5h is placed in dry case, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, substance A 3 is obtained;
(5) by 796 milligrams of Al (NO3)3With the AgNO that 75mL molar concentrations are 0.72mol/L3Solution is added in mixed liquor K2,
Stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor L2;
(6) substance A 3 is added in mixed liquor L2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to mistake after room temperature
Filter liquid and obtain substance A 4, substance A 4 is dry at 85 DEG C Jing after the ethanol washing that 100mL mass percent concentrations are 95%
1.5h is placed in dry case, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, substance A 5 is obtained;
(7) by 816 milligrams of Al (NO3)3With the AgNO that 55mL molar concentrations are 0.62mol/L3Solution is added in mixed liquor K3,
Stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor L3;
(8) substance A 5 is added in mixed liquor L3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to mistake after room temperature
Filter liquid and obtain substance A 6, substance A 6 is dry at 85 DEG C Jing after the ethanol washing that 100mL mass percent concentrations are 95%
1.5h is placed in dry case, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, substance A 7 is obtained;
(9) by 836 milligrams of Al (NO3)3With the AgNO that 35mL molar concentrations are 0.52mol/L3Solution is added in mixed liquor K4,
Stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor L4;
(10) substance A 7 is added in mixed liquor L4, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, after being cooled to room temperature
It is filtered to remove liquid and obtains substance A 8, substance A 8 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
1.5h is placed in drying box, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, substance A is obtained;
(11) by 6.28 grams of AgNO3With 750mL ether volume is added in 1000mL conical flasks, to stir under the conditions of 1000r/min
Mix 3 minutes, 3 parts of equivalent is divided into after shaking up, obtain mixed liquor M1, mixed liquor M2, mixed liquor M3;
(12) by 322 milligrams of AgNO3With the Al (NO that 30mL molar concentrations are 0.47mol/L3)3Solution is added in mixed liquor M1,
Stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor N1;
(13) substance A is added in mixed liquor N1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to mistake after room temperature
Filter liquid and obtain substance B, substance B is Jing after the ethanol washing that 100mL mass percent concentrations are 95% in 85 DEG C of drying
1.5h is placed in case, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, substance B 1 is obtained;
(14) by 342 milligrams of AgNO3With the Al (NO that 60mL molar concentrations are 0.67mol/L3)3Solution is added in mixed liquor M2,
Stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor N2;
(15) substance B 1 is added in mixed liquor N2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, after being cooled to room temperature
It is filtered to remove liquid and obtains substance B 2, substance B 2 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
1.5h is placed in drying box, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, substance C is obtained;
(16) by 362 milligrams of AgNO3With the Al (NO that 90mL molar concentrations are 0.87mol/L3)3Solution is added in mixed liquor M3,
Stir 3 minutes under the conditions of 1000r/min, obtain mixed liquor N3;
(17) substance C is added in mixed liquor N3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to mistake after room temperature
Filter liquid and obtain material D, material D is Jing after the ethanol washing that 100mL mass percent concentrations are 95% in 85 DEG C of drying
1.5h is placed in case, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material E is obtained;
(18) by 9.24 grams of Cu (NO3)2It is in 1000mL conical flasks, in 1000r/min conditions to be added to volume with 900mL ethanol
Lower stirring 3 minutes, adds 5mL red fuming nitric acid (RFNA)s, and 3 parts of equivalent is divided into after shaking up, and obtains mixed liquor P1, mixed liquor P2, mixed liquor P3;
(19) by 85mL molar concentrations for 0.61mol/L InCl3Solution is added in mixed liquor P1, under the conditions of 1000r/min
Stirring 3 minutes, obtains mixed liquor Q1;
(20) material E is added in mixed liquor Q1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to mistake after room temperature
Filter liquid and obtain material F1, material F1 is dry at 85 DEG C Jing after the ethanol washing that 100mL mass percent concentrations are 95%
1.5h is placed in dry case, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material F2 is obtained;
(21) by 70mL molar concentrations for 0.68mol/L Cu (NO3)2Solution is added in mixed liquor P2, in 1000r/min bars
Stir 3 minutes under part, obtain mixed liquor Q2;
(22) material F2 is added in mixed liquor Q2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, after being cooled to room temperature
It is filtered to remove liquid and obtains material F3, material F3 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
1.5h is placed in drying box, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material F4 is obtained;
(23) by 60mL molar concentrations for 0.51mol/L InCl3Solution is added in mixed liquor P3, under the conditions of 1000r/min
Stirring 3 minutes, obtains mixed liquor Q3;
(24) material F4 is added in mixed liquor Q3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, after being cooled to room temperature
It is filtered to remove liquid and obtains material F5, material F5 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
1.5h is placed in drying box, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material F is obtained;
(25) by 5.28g TiCl4Being added to volume with the sodium citrate solution that 750mL mass percent concentrations are 10% is
In 1000mL conical flasks, stir 3 minutes under the conditions of 1000r/min, 3 parts of equivalent is divided into after shaking up, obtain mixed liquor R1, mixing
Liquid R2, mixed liquor R3;
(26) by 40mL molar concentrations for 0.49mol/L CoCl2Solution and the MgCl that 60mL molar concentrations are 1.02mol/L2It is molten
Liquid is added in mixed liquor R1, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor S1;
(27) material F is added in mixed liquor S1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to mistake after room temperature
Filter liquid and obtain material G1, material G1 is dry at 85 DEG C Jing after the ethanol washing that 100mL mass percent concentrations are 95%
1.5h is placed in dry case, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material H1 is obtained;
(28) by 50mL molar concentrations for 0.69mol/L CoCl2Solution and the MgCl that 50mL molar concentrations are 0.82mol/L2It is molten
Liquid is added in mixed liquor R2, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor S2;
(29) material H1 is added in mixed liquor S2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, after being cooled to room temperature
It is filtered to remove liquid and obtains material G2, material G2 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
1.5h is placed in drying box, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material H2 is obtained;
(30) by 60mL molar concentrations for 0.89mol/L CoCl2Solution and the MgCl that 40mL molar concentrations are 0.52mol/L2It is molten
Liquid is added in mixed liquor R3, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor S3;
(31) material H2 is added in mixed liquor S3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, after being cooled to room temperature
It is filtered to remove liquid and obtains material G3, material G3 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
1.5h is placed in drying box, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material H is obtained;
(32) 3.66g lauryl sodium sulfate, 40mL n-hexanes, 20 milliliters of n-butanols are added sequentially to into volume for 250mL cones
In shape bottle, 9.87g ammonium metavanadates and 150mL deionized waters are added, be placed in 70 DEG C of water-baths and stirred under the conditions of 1000r/min
1h, is subsequently adding the hydrochloric acid solution that 25mL molar concentrations are 2.40mol/L, and in the shaking table that temperature is 45 DEG C 0.5h is shaken, cold
But 15min is centrifuged under the conditions of 7500r/min to after room temperature, removes supernatant, be 95% with 500mL mass percent concentrations
Ethanol is washed, and obtains material I;
(33) sodium citrate solution that material I and 800mL mass percent concentration is 15% is added to into volume for 1000mL cones
In shape bottle, stir 3 minutes under the conditions of 1000r/min, 4 parts of equivalent is divided into after shaking up, obtain mixed liquor T1, mixed liquor T2, mix
Close liquid T3, mixed liquor T4;
(34) by 35mL molar concentrations for 0.68mol/L CoCl2Solution and the MgCl that 65mL molar concentrations are 0.93mol/L2It is molten
Liquid is added in mixed liquor T1, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor U1;
(35) material H is added in mixed liquor U1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to mistake after room temperature
Filter liquid and obtain material J1, material J1 is dry at 85 DEG C Jing after the ethanol washing that 100mL mass percent concentrations are 95%
1.5h is placed in dry case, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material K1 is obtained;
(36) by 45mL molar concentrations for 0.78mol/L CoCl2Solution and the MgCl that 55mL molar concentrations are 0.83mol/L2It is molten
Liquid is added in mixed liquor T2, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor U2;
(37) material K1 is added in mixed liquor U2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, after being cooled to room temperature
It is filtered to remove liquid and obtains material J2, material J2 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
1.5h is placed in drying box, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material K2 is obtained;
(38) by 55mL molar concentrations for 0.88mol/L CoCl2Solution and the MgCl that 45mL molar concentrations are 0.73mol/L2It is molten
Liquid is added in mixed liquor T3, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor U3;
(39) material K2 is added in mixed liquor U3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, after being cooled to room temperature
It is filtered to remove liquid and obtains material J3, material J3 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
1.5h is placed in drying box, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material K3 is obtained;
(40) by 65mL molar concentrations for 0.98mol/L CoCl2Solution and the MgCl that 35mL molar concentrations are 0.63mol/L2It is molten
Liquid is added in mixed liquor T4, is stirred 3 minutes under the conditions of 1000r/min, obtains mixed liquor U4;
(41) material K3 is added in mixed liquor U4, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, after being cooled to room temperature
It is filtered to remove liquid and obtains material J4, material J4 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
1.5h is placed in drying box, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material K is obtained;
(42) it is in 1000mL conical flasks, in 1000r/min 14.56g polyvinyl alcohol and 800mL deionized waters to be added to into volume
Under the conditions of stir 3 minutes, 4 parts of equivalent is divided into after shaking up, obtain mixed liquor V1, mixed liquor V2, mixed liquor V3, mixed liquor V4;
(43) by 90mL molar concentrations for 1.09mol/L HAuCl4Solution is added in mixed liquor V1, in 1000r/min conditions
Lower stirring 3 minutes, obtains mixed liquor W1;
(44) material K is added in mixed liquor W1, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, be cooled to mistake after room temperature
Filter liquid and obtain material L1, material L1 is dry at 85 DEG C Jing after the ethanol washing that 100mL mass percent concentrations are 95%
1.5h is placed in dry case, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material Z1 is obtained;
(45) by 80mL molar concentrations for 0.89mol/L HAuCl4Solution is added in mixed liquor V2, in 1000r/min conditions
Lower stirring 3 minutes, obtains mixed liquor W2;
(46) material Z1 is added in mixed liquor W2, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, after being cooled to room temperature
It is filtered to remove liquid and obtains material L2, material L2 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
1.5h is placed in drying box, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material Z2 is obtained;
(47) by 70mL molar concentrations for 0.69mol/L HAuCl4Solution is added in mixed liquor V3, in 1000r/min conditions
Lower stirring 3 minutes, obtains mixed liquor W3;
(48) material Z2 is added in mixed liquor W3, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, after being cooled to room temperature
It is filtered to remove liquid and obtains material L3, material L3 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
1.5h is placed in drying box, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, material Z3 is obtained;
(49) by 60mL molar concentrations for 0.49mol/L HAuCl4Solution is added in mixed liquor V4, in 1000r/min conditions
Lower stirring 3 minutes, obtains mixed liquor W4;
(50) material Z3 is added in mixed liquor W4, is shaken 15 minutes in the shaking table that temperature is 45 DEG C, after being cooled to room temperature
It is filtered to remove liquid and obtains material L4, material L4 is Jing after the ethanol washing that 100mL mass percent concentrations are 95% at 85 DEG C
1.5h is placed in drying box, the roasting 1h under the conditions of 480 DEG C is subsequently placed in Muffle furnace, the material for obtaining as has electro-catalysis
Remove the modified titanium foam granule electrode of carbazole function.