CN106627411A - Fabrication process of automobile brand sign - Google Patents

Abstract

The invention discloses a fabrication process of an automobile brand sign comprising the following steps: mixing 10 parts of acrylonitrile, 20 parts of butadiene and 15 parts of styrene to make a new material named acrylonitrile butadiene styrene (ABS); drying the ABS for 60-80 minutes; melting the ABS after drying and pouring the ABS into a mold for the preparation of molding; polishing the automobile brand sign after the preparation of molding to be smooth, cleaning the same with water and drying the same; trimming the automobile brand sign after drying with cutting tools and carrying out the processes of drilling and grinding inner arcs, outer arcs and chamfers; punching location holes with a punch press on the automobile brand sign which is trimmed and spraying paints on the automobile brand sign with a thickness of 40-50 mum; and then drying the automobile brand sign by means of a dryer with a drying temperature of 100 DEG C and a drying time of 20 minutes. The fabrication process of the automobile brand sign has the advantages of prolonging the service life of the automobile brand sign and preventing the problems such as yellowing, fading and deformation of the automobile brand sign in the case of exposure or rain.

Description

A kind of processing technology of vehicle label

Technical field

The invention belongs to automobile part production technique field, more particularly to a kind of processing technology of vehicle label.

Background technology

Vehicle label refers to the mark of various automobile brands, and these marks often become the representative of Automobile Enterprises. Automobile should have the mark of oneself, to show the manufacturer of automobile, vehicle, engine power, hold Factory number of mounted mass, electromotor and car load etc..

Vehicle label represents the image of a motor corporation, and except shape is unique, color has outside the style of oneself, marks The material of board is also critically important, due to the running environment and storage environment of automobile, it is to avoid not being exposed to the sun for the sun, The invasion and attack of rainwater, can so make label turn yellow, and even shape of fading has so take on a new look, currently manufactured label There is many drawbacks in technique, resistance to corrosion is poor, to doing high cost, complex manufacturing technology, accordingly, it would be desirable to A kind of new technique is making label

The content of the invention

The technical problem to be solved in the present invention is, for the deficiencies in the prior art, to propose a kind of system of vehicle label Make technique.

The technical problem to be solved in the present invention is achieved through the following technical solutions, a kind of system of vehicle label Make technique, be characterized in, comprise the following steps：

(1) by propylene is fine 10 parts, 20 parts of butadiene, 15 parts of mixing of styrene, make a kind of new material Material ABS；

(2) ABS is dried into 60-80 minutes；

(3) ABS for completing drying melts, and pours mould into, is prepared molding；

(4) logo for preparing molding is polished smooth, is then rinsed with water, carried out drying and processing；

(5) label after drying is carried out into finishing process with cutter, and is drilled, grinding inner arc, outer arc And chamfering；

(6) by location hole in the label punch press after finishing, painted, the thickness of spray painting is 40～50um；

(7) dried with dehydrator again, the dry temperature of flood is 100 DEG C, the flood dry time is 20 minutes；

(8) acceptance(check).

Compared with prior art, the present invention greatly reduces development cost, and conforming product rate is high, extends mark The service life of board, prevents from being exposed to the sun or the label jaundice in the case of raining, and fades, the problems such as deformation, It is with low cost and technological process is simple.

Specific embodiment

The concrete technical scheme of the present invention described further below, it is further in order to those skilled in the art Ground understands the present invention, and does not constitute the restriction of its power.

A kind of embodiment 1, processing technology of vehicle label, is characterized in, comprises the following steps：

(1) by propylene is fine 10 parts, 20 parts of butadiene, 15 parts of mixing of styrene, make a kind of new material Material ABS；

(2) ABS is dried into 60-80 minutes；

(3) ABS for completing drying melts, and pours mould into, is prepared molding；

(4) logo for preparing molding is polished smooth, is then rinsed with water, carried out drying and processing；

(5) label after drying is carried out into finishing process with cutter, and is drilled, grinding inner arc, outer arc And chamfering；

(6) by location hole in the label punch press after finishing, painted, the thickness of spray painting is 40～50um；

(7) dried with dehydrator again, the dry temperature of flood is 100 DEG C, the flood dry time is 20 minutes；

(8) acceptance(check).

Claims (1)

1. a kind of processing technology of vehicle label, it is characterised in that comprise the following steps：

(1) by propylene is fine 10 parts, 20 parts of butadiene, 15 parts of mixing of styrene, make a kind of new Materials A BS；

(2) ABS is dried into 60-80 minutes；

(3) ABS for completing drying melts, and pours mould into, is prepared molding；

(4) logo for preparing molding is polished smooth, is then rinsed with water, carried out drying and processing；

(5) label after drying is carried out into finishing process with cutter, and is drilled, it is grinding inner arc, outer Arc and chamfering；

(6) by location hole in the label punch press after finishing, being painted, the thickness of spray painting is 40～ 50um；

(7) dried with dehydrator again, the dry temperature of flood is 100 DEG C, the flood dry time is 20 minutes；

(8) acceptance(check).