CN106626667A - Micro-foaming material with three-layered structure - Google Patents
Micro-foaming material with three-layered structure Download PDFInfo
- Publication number
- CN106626667A CN106626667A CN201610830914.XA CN201610830914A CN106626667A CN 106626667 A CN106626667 A CN 106626667A CN 201610830914 A CN201610830914 A CN 201610830914A CN 106626667 A CN106626667 A CN 106626667A
- Authority
- CN
- China
- Prior art keywords
- foaming
- micro
- toughener
- hips
- foaming material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a micro-foaming material with a three-layered structure. The micro-foaming material with the three-layered structure is formed by extruding, rolling and compounding three-layered structures and is respectively divided into an upper layer, a middle layer and a lower layer; the upper layer and the lower layer are mixed materials of HIPS and a toughener; the material of the middle layer contains HIPS, a foaming agent, a toughener, an antioxidant, a nucleating agent and the like; and a physical foaming technique is utilized, so that foam expansion is controlled to be 0.3-1 time; the material has the original structure; the structure is simple; foaming of the inside is uniform, the micro-foaming material is impact-resistant, the membrane internal stress of the material is reduced or eliminated, the accuracy is high, the production cost is low, the micro-foaming material is non-toxic and non-pollution, the production benefit is increased, the problem of warping and flattening of the material is improved effectively, and the quality of the product is high.
Description
Technical field
The present invention relates to a kind of micro-foaming material of three-decker.
Background technology
Today's society has been stepped into industrial 4.0 epoch, mobile phone, IT, communication, and the industry such as household electrical appliances is developed rapidly, supporting with it
Electronic product packaging material industry also develop rapidly therewith.Because electronic product is day by day high, essence, point, fast direction is developed, this
It is both a kind of challenge for electronic packaging materials industry, is also a kind of opportunity, opportunity is that electronic packaging materials market is thrown away
Further widen, challenge is that this trend proposes higher level requirement to electronic packaging materials.
First it is the impact resistance to packaging material, the requirement of ruggedness.Next to that control of the client to material cost will
Ask, be finally that product need to meet green, the requirement of environmental protection.
Present micro-foaming material started till now comparative maturity from 1997 in injection molding technology application aspect, but
Micro-foaming material at home and abroad belongs to blank in extruding technology application aspect, so needing to be improved packaging material, introduces
The processing technology of fretting map.
The content of the invention
To solve the above problems, the present invention proposes a kind of micro-foaming material of three-decker.
A kind of micro-foaming material of three-decker, including micro-foaming material body, described micro-foaming material body is adopted
Three-decker extrusion, pressure of prolonging are compound prepared, respectively upper strata, intermediate layer and lower floor;Described the upper and lower be HIPS and
The mixing material of toughener;Foaming agent and a certain proportion of toughener are added with described intermediate layer material;And utilize physics
Foaming technique, makes coefficient of foaming control at 0.3-1 times so that material keeps original structure;HIPS is in described upper strata
70%--90%, toughener is 10%--30%;HIPS in described intermediate layer is 50%--90%, and foaming agent is 1%--
10%, toughener is 1%--10%, and antioxidant is 0.2%--1%, nucleator:0.1%--1%;In described lower floor
HIPS is 70%--90%, and toughener is 10%--30%.
Further, the percentage elongation in the performance indications of described micro-foaming material body reaches 20%.
Further, the tensile strength of the performance indications of described micro-foaming material body is between 8-12Mpa.
Compared with prior art, it has the advantages that the present invention:The fretting map material of the three-decker of the present invention
Material, effectively reduces the cost of raw material and Product transport cost;The product with more thin structure, stretching in performance indications can be designed
Long rate reaches 20% or so, and the tensile strength of performance indications is between 8-12Mpa;Effectively reduce the density of material;Wherein add
Foaming agent and a certain proportion of toughener, by physical foaming method so that foamed interlayer uniform foam cell, can be at utmost
Ensure the impact resistance of product, while causing material internal almost uneven without stress and contraction by fretting map technology, subtract
Less or eliminate material film internal stress, the warpage issues of material are effectively improved, so as to improve product quality;Surface is not changed
The performance indications of layer, it is ensured that the performance processing of later process, degree of accuracy is high, and low production cost is nontoxic, pollution-free.
Description of the drawings
Fig. 1 is the overlooking the structure diagram of first embodiment of the invention.
1- micro-foaming material bodies;2- lower floors;3- upper stratas;4- intermediate layers;5- toughener;6- foaming agent;7-HIPS and increasing
Tough dose of mixing material.
Specific embodiment
First embodiment, as shown in figure 1, including micro-foaming material body (1), described micro-foaming material body (1) is adopted
Prolonged with three-decker extrusion and press compound prepared, respectively upper strata (3), intermediate layer (4) and lower floor (2);Described upper strata (3) and under
Layer (2) is the mixing material (7) of HIPS and toughener;Containing foaming agent (6) and certain proportion in described intermediate layer material
Toughener (5);And physical foaming technology is utilized, coefficient of foaming is controlled at 0.3-1 times so that material keeps original structure;
HIPS is 70%--90% in described upper strata (3), and toughener is 10%--30%;HIPS in described intermediate layer (4) is
50%--90%, foaming agent is 1%--10%, and toughener is 1%--10%, and antioxidant is 0.2%--1%, nucleator:
0.1%--1%;HIPS in described lower floor (2) is 70%--90%, and toughener is 10%--30%.
Percentage elongation in the performance indications of described micro-foaming material body reaches 20%.
The tensile strength of the performance indications of described micro-foaming material body is between 8-12Mpa.
Second embodiment, as shown in figure 1, including micro-foaming material body (1), described micro-foaming material body (1) is adopted
Prolonged with three-decker extrusion and press compound prepared, respectively upper strata (3), intermediate layer (4) and lower floor (2);Described upper strata (3) and under
Layer (2) is the mixing material (7) of HIPS and toughener;Containing foaming agent (6) and certain proportion in described intermediate layer material
Toughener (5);And physical foaming technology is utilized, coefficient of foaming is controlled at 0.3-1 times so that material keeps original structure;
HIPS is 70%--85% in described upper strata (3), and toughener is 15%--30%;HIPS in described intermediate layer (4) is
50%--90%, foaming agent is 1%--10%, and toughener is 1%--10%, and antioxidant is 0.2%--1%, nucleator:
0.1%--1%;HIPS in described lower floor (2) is 70%-85%, and toughener is 15%--30%.
Percentage elongation in the performance indications of described micro-foaming material body reaches 20%.
The tensile strength of the performance indications of described micro-foaming material body is between 8-12Mpa
Compared with prior art, it has the advantages that the present invention:The fretting map material of the three-decker of the present invention
Material, effectively reduces the consuming of the cost of raw material and petroleum-based energy;The product with more thin structure can be designed, in performance indications
Percentage elongation reaches 20% or so, and the tensile strength of performance indications is between 8-12Mpa;Effectively reduce the density of material;Wherein add
Plus foaming agent and a certain proportion of toughener, by physical foaming method so that foamed interlayer uniform foam cell, can be with maximum journey
Degree ensures the impact resistance of product, while cause material internal almost uneven without stress and contraction by fretting map technology,
The film internal stress of material is reduced or eliminated, the warpage issues of material are effectively improved, so as to improve product quality;Table is not changed
The performance indications of surface layer, it is ensured that the performance processing of later process, degree of accuracy is high, and low production cost is nontoxic, pollution-free.
Embodiment described above is only that the preferred embodiment of the present invention is described, not to the structure of the present invention
Think and scope is defined.On the premise of without departing from design concept of the present invention, technology of this area ordinary person to the present invention
Various modifications and improvement that scheme is made, all should drop into protection scope of the present invention, the technology contents that the present invention is claimed,
All record in detail in the claims.
Claims (3)
1. a kind of micro-foaming material of three-decker, it is characterised in that:Including micro-foaming material body (1), described fretting map
Material body (1) extruded using three-decker, prolong pressure, compound prepared, respectively upper strata (3), intermediate layer (4) and lower floor (2);Institute
The upper strata (3) and lower floor (2) stated are the mixing material (7) of HIPS and toughener;Containing foaming in described intermediate layer material
Agent (6) and a certain proportion of toughener (5);And physical foaming technology is utilized, coefficient of foaming is controlled at 0.3-1 times so that material
Material keeps original structure;HIPS is 70%--90% in described upper strata (3), and toughener is 10%--30%;Described centre
HIPS in layer (4) is 50%--90%, and foaming agent is 1%--10%, and toughener is 1%--10%, and antioxidant is
0.2%--1%, nucleator:0.1%--1%;HIPS in described lower floor (2) is 70%--90%, and toughener is 10%--
30%.
2. the micro-foaming material of three-decker according to claim 1, it is characterised in that:Described micro-foaming material body
(1) the percentage elongation in performance indications reaches 20% or so.
3. the micro-foaming material of three-decker according to claim 1, it is characterised in that:Described micro-foaming material body
(1) the tensile strength in performance indications is between 8-12Mpa.