CN106626628A - Fluoro-rubber adhesive tape and manufacturing method thereof - Google Patents

Fluoro-rubber adhesive tape and manufacturing method thereof Download PDF

Info

Publication number
CN106626628A
CN106626628A CN201611023720.5A CN201611023720A CN106626628A CN 106626628 A CN106626628 A CN 106626628A CN 201611023720 A CN201611023720 A CN 201611023720A CN 106626628 A CN106626628 A CN 106626628A
Authority
CN
China
Prior art keywords
fluorubber
adhesive plaster
parts
rubber
fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611023720.5A
Other languages
Chinese (zh)
Inventor
张光友
彭清涛
丛继信
范春华
李珍
李宝庭
王力
曹晔
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Bangwei High-Tech Special Textile Co., Ltd.
Original Assignee
HEALTH AND EPIDEMIC PREVENTION TEAM GENERAL ARMAMENT DEPARTMENT PLA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEALTH AND EPIDEMIC PREVENTION TEAM GENERAL ARMAMENT DEPARTMENT PLA filed Critical HEALTH AND EPIDEMIC PREVENTION TEAM GENERAL ARMAMENT DEPARTMENT PLA
Priority to CN201611023720.5A priority Critical patent/CN106626628A/en
Publication of CN106626628A publication Critical patent/CN106626628A/en
Pending legal-status Critical Current

Abstract

The invention discloses a fluoro-rubber adhesive tape and a manufacturing method thereof. The fluoro-rubber adhesive tape comprises a basic fabric and a rubber layer. The basic fabric is a grid fabric, rubber is arranged on two sides of the grid fabric and are fit through fabric mesh holes. The manufacturing method comprises the steps that the fluoro-rubber is plastified and mixed according to a formula, and mixed rubber having good processing properties is formed by adopting a thin-passing process for aiding; the mixed rubber is prepared into the continuous adhesive tape with the thickness of 0.15-0.20 mm through a calendaring process; the grid fabric is arranged between the two adhesive tapes for sulfur bulging, so that the purpose of fitting and vulcanizing the calendared rubber adhesive tape and the grid fabric is achieved, the vulcanizing temperature is 150-180 DEG C, and the time is 6-15 minutes. The fluoro-rubber adhesive tape produced by adopting the manufacturing method is retardant to flame, high in stripping firmness, resistant to high temperature and corrosion from acid, alkali, a strong oxidant, benzene and other organic solvents.

Description

A kind of fluorubber adhesive plaster and preparation method thereof
Technical field
The present invention relates to chemical protection material production technical field, more particularly to a kind of fluorubber adhesive plaster and its making side Method.
Background technology
Fluorubber material is fire-retardant, corrosion-resistant, heat-resisting quantity is good, is usually used in chemical protection field, but fluorubber is excellent because of its Chemical stability cause the combination of itself and other materials difficult, the stripping of rubber and base fabric is shown as in adhesive plaster production process Fastness is low, protective materials delamination, the problem of foaming easily occurs.In order to strengthen the peel strength of fluororubber layer and base fabric, generally Rubber is carried out and with or base fabric pre-processed, existing complex treatment process and rubberized fabric barrier propterty can be caused big Width declines or makes its feel be hardened.Therefore, the rubberized fabric that prepared by existing process can not fully meet high-performance protective equipment Using need.
The content of the invention
To solve above-mentioned technical problem, it is an object of the invention to provide a kind of fluorubber adhesive plaster and preparation method thereof, described Fluorubber adhesive plaster can fire-retardant, high temperature resistant, resistance to strong acid, highly basic, strong oxidizer corrosion, manufacture craft high with the peel strength of base fabric Simply.
The purpose of the present invention is realized by following technical scheme：
A kind of fluorubber adhesive plaster, including：Base fabric and rubber layer；The base fabric is net fibric, in the both sides of net fibric Rubber is set, and the rubber fits through Fabric mesh.
A kind of preparation method of fluorubber adhesive plaster, including：
Fluorubber, magnesium hydroxide, calcium hydroxide, age resistor, vulcanizing agent and titanium dioxide are plasticated, kneaded, makes to be formed Elastomeric compound；
The elastomeric compound is rolled, continuous adhesive plaster of the thickness between 0.15mm～0.20mm is prepared；
Net fibric is placed between two-layer rubberized fabric, and drum-type sulfuration 6min is carried out in the case where temperature is for 150 DEG C～180 DEG C ～12min, makes calendering adhesive plaster reach sulfuration with the net fibric, fit, and forms fluorubber adhesive plaster.
Compared with prior art, one or more embodiments of the invention can have the advantage that：
The fluorubber adhesive plaster that the present invention is provided, with the contrast of preventing rubber material on the market, protection level is high, and functionality advantage is bright Aobvious, process is simple, low production cost can be used as the material of main part of high-level chemical protection clothes or product.
Description of the drawings
Fig. 1 is the section structure schematic diagram of fluorubber adhesive plaster.
Specific embodiment
To make the object, technical solutions and advantages of the present invention clearer, below in conjunction with embodiment and accompanying drawing to this It is bright to be described in further detail.
As shown in figure 1, for the section structure of fluorubber adhesive plaster, including base fabric 2 and rubber layer 1；The base fabric is knitted for grid Thing, in the both sides of net fibric rubber is arranged, and the rubber fits through Fabric mesh.
Above-mentioned elastomeric material is made up of following mass component：Fluorubber, magnesium hydroxide, calcium hydroxide, age resistor, sulfuration Agent and titanium dioxide, above-mentioned material mass component is：100 parts of fluorubber, 10～30 parts of magnesium hydroxide, 5～15 parts of calcium hydroxide is prevented 1～5 part of old agent, 5～10 parts of vulcanizing agent, 10～50 parts of titanium dioxide.
The vulcanizing agent be N, N- dicinnamylidene -1,6 hexamethylene diamines.
The present embodiment additionally provides a kind of preparation method of fluorubber adhesive plaster, following examples：
Embodiment 1
By 100 parts of fluorubber, 10 parts of magnesium hydroxide, 15 parts of calcium hydroxide, 3 parts of age resistor, 5 parts of vulcanizing agent, titanium dioxide 30 Part is plasticated, is kneaded, and makes to form elastomeric compound；
The elastomeric compound is rolled, sequential like adhesive plaster of the thickness in 0.15mm is prepared, rolling temperature is 80 DEG C, speed Spend for 20m/min；
Net fibric is placed between two-layer rubberized fabric, and drum-type sulfuration 10min is carried out in the case where temperature is for 170 DEG C, make pressure Prolong adhesive plaster to reach sulfuration with the net fibric, fit, form fluorubber adhesive plaster.
Fluorubber adhesive plaster thickness prepared by said method is 0.40mm, weight is 550g/m2.Fastness is peeled off with base fabric 0.81N/m, limited oxygen index is 29, and fracture strength is up to 350N/5cm, resistance to 98% sulfuric acid, 40% NaOH, 61% nitre Acid, 120min is impermeable, and outward appearance is good.Can be used to make heavy chemical protecting suit.
Embodiment 2
100 parts of fluorubber, 15 parts of calcium hydroxide, 2 parts of age resistor, 6 parts of vulcanizing agent, 20 parts of titanium dioxide are plasticated, mixed Refining, makes to form elastomeric compound.
Elastomeric compound is rolled into the sequential like adhesive plaster that thickness is 0.18mm by way of calendering, rolling temperature is 80 DEG C, Speed is 20m/min.
Sulfuration laminating：Aramid fiber net fibric is put between two-layer fluorubber adhesive plaster, enters bulging sulfuration, trilaminate material is slight Apply tension force, it is ensured that enter smooth when rousing sulphur equipment.Curing temperature is 180 DEG C, it is ensured that cure time is 10min.
The thickness of the fluorubber adhesive plaster that the present embodiment makes is 0.45mm, and limited oxygen index is 36.4, and fracture strength is reachable 500N/5cm, resistance to 98% concentrated sulfuric acid, 40% NaOH, 60% nitric acid, 200min is impermeable, and outward appearance is good.
The fluorubber adhesive plaster that above-described embodiment 2 is made carries out anti-strong oxidizer test, and test method is as follows：
Fluorubber adhesive plaster test surfaces are clamped on chemical agent penetration tester, fluorubber adhesive plaster opposite side places oxygen Change discoloration and indicate paper, strong oxidizer dinitrogen tetroxide 1mL is added by filling opening, stopper filling opening, observation indicates that paper color becomes Change to judge whether rubber blanket permeates.
Test result shows：The rubberized fabric is resistant to that strong oxidizer dinitrogen tetroxide solution 1h is not saturating, and rubberized fabric surface is slight Fade, illustrate that the fluorubber adhesive plaster has powerful oxidation corrosion resistance agent function.
Although disclosed herein embodiment as above, described content is only to facilitate understanding the present invention and adopting Embodiment, is not limited to the present invention.Technical staff in any the technical field of the invention, without departing from this On the premise of the disclosed spirit and scope of invention, any modification and change can be made in the formal and details implemented, But the scope of patent protection of the present invention, still must be defined by the scope of which is defined in the appended claims.

Claims (7)

1. a kind of fluorubber adhesive plaster, it is characterised in that include：Base fabric and rubber layer；The base fabric is net fibric, is knitted in grid The both sides of thing arrange rubber, and the rubber fits through Fabric mesh.
2. fluorubber adhesive plaster as claimed in claim 1, it is characterised in that the elastomeric material include fluorubber, magnesium hydroxide, Calcium hydroxide, age resistor, vulcanizing agent and titanium dioxide, above-mentioned material mass component is：100 parts of fluorubber, magnesium hydroxide 10～30 Part, 5～15 parts of calcium hydroxide, 1～5 part of age resistor, 5～10 parts of vulcanizing agent, 10～50 parts of titanium dioxide.
3. fluorubber adhesive plaster as claimed in claim 1, it is characterised in that the vulcanizing agent is N, N- dicinnamylidene -1,6 oneself Diamines.
4. a kind of preparation method of fluorubber adhesive plaster, it is characterised in that methods described includes：
Fluorubber, magnesium hydroxide, calcium hydroxide, age resistor, vulcanizing agent and titanium dioxide are plasticated, kneaded, makes to form mixing Glue；
The elastomeric compound is rolled, continuous adhesive plaster of the thickness between 0.15mm～0.20mm is prepared；
Net fibric is placed between two-layer rubberized fabric, and temperature be 150 DEG C～180 DEG C at carry out drum-type sulfuration 6min～ 12min, makes calendering adhesive plaster reach sulfuration with the net fibric, fit, and forms fluorubber adhesive plaster.
5. the preparation method of fluorubber adhesive plaster as claimed in claim 4, it is characterised in that the constituent of the elastomeric compound For：100 parts of fluorubber, 10～30 parts of magnesium hydroxide, 5～15 parts of calcium hydroxide, 1～5 part of age resistor, 5～10 parts of vulcanizing agent, titanium 10～50 parts of white powder.
6. the preparation method of fluorubber adhesive plaster as claimed in claim 4, it is characterised in that the vulcanizing agent is N, bis- meat of N- Gui Ji -1,6 hexamethylene diamines.
7. the preparation method of fluorubber adhesive plaster as claimed in claim 4, it is characterised in that the fluorubber adhesive plaster thickness is Between 0.35mm～0.45mm, weight be 400g/m2～850g/m2。
CN201611023720.5A 2016-11-14 2016-11-14 Fluoro-rubber adhesive tape and manufacturing method thereof Pending CN106626628A (en)