CN106618010A - Degradable milk fiber quilt containing negative ions and preparation method of milk fiber quilt - Google Patents
Degradable milk fiber quilt containing negative ions and preparation method of milk fiber quilt Download PDFInfo
- Publication number
- CN106618010A CN106618010A CN201611247925.1A CN201611247925A CN106618010A CN 106618010 A CN106618010 A CN 106618010A CN 201611247925 A CN201611247925 A CN 201611247925A CN 106618010 A CN106618010 A CN 106618010A
- Authority
- CN
- China
- Prior art keywords
- fiber
- quilt
- anion
- degradable
- fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a degradable milk fiber quilt containing negative ions and a preparation method of the milk fiber quilt. The degradable milk fiber quilt containing the negative ions comprises quilt interior stuffing, wherein the quilt interior stuffing is prepared from the following components in percentage by weight: 40-60% of milk fibers, 10-30% of silk fibers, 10-20% of cotton fibers and 5-20% of nano germanium oxide composite zirconium poly(butylene succinate) fibers. The finished product (the degradable milk fiber quilt) prepared by the method can generate negative oxygen ions and hydroxyl negative ions which can take effects of sterilizing and refreshing air and can also promote cell activation, so that a skin aging speed is reduced.
Description
Technical field
The invention belongs to bedding technical field, and in particular to it is a kind of containing anion and degradable milk fibre by and
Its preparation method.
Background technology
In recent years, as people's living standard is improved constantly, operating pressure is increasing, and anion product acceptance is got over
Come higher, a series of anion product has wide market.Anion can not only facilitate human body to synthesize and vitamin storage,
Reinforcing and the physiological activity of human activin, therefore it is otherwise known as " air vitamin ", it is believed that it as the vitamin of food,
There is highly important impact to the vital movement of human body and other biological.
Milk protein fiber is, using cow's milk as base stock, through dehydration, de-oiling, degreasing, separation, purification, to be allowed to into
For a kind of MC with linear macromolecule structure;It is blended using high-tech means with polyacrylonitrile again, be crosslinked, is connect
Branch, is prepared into spinning solution;Finally by wet spinning into fibre, solidification, drawing-off, drying, curling, setting, chopped fiber cut-out(It is long
Silk winding).Security is taken with fabulous;With natural bacteriostatic function, than wool, cashmere anti-mould and anti-moth, intensity
Height, wears well washable, easily storage;Easily do after washing, permanent performance of product etc. can be still kept after washing.
But the Main Function of common quilt is that, for keeping out the cold, feature is single, it is impossible to meet the consumption need of different levels
Ask, such as cotton-wadded quilt it is abundant it is warming, be difficult breed bacteria, be a kind of current the most widely used quilt, but cotton-wadded quilt moisture-sensitive, easy plate
Knot, great inconvenience can be brought when using in winter, also do not possess health care.
The content of the invention
For defect present in prior art, the invention provides a kind of containing anion and degradable milk fibre quilt
And preparation method thereof, product prepared by the method can produce negative oxygen ion and hydroxyl group anion, negative oxygen ion and hydroxyl bear from
Son can sterilized and fresh air, cell activation can also be promoted, and then reduce skin senescence speed.
To achieve these goals, the technical solution used in the present invention is as follows:
The invention provides it is a kind of containing anion and degradable milk fibre quilt, including core filler, the core filling
Thing is made up of the component of following percentage by weight:Milk fibre 40-60%, silk fiber 10-30%, cotton fiber 10-20% and nanometer
The germanium oxide cruel fiber 5-20% of compound poly-succinic acid-butanediol.
According to above-mentioned containing anion and degradable milk fibre quilt, the core filler is by following percentage by weight
Component make:Milk fibre 40-50%, silk fiber 20-30%, cotton fiber 10-15% and nano oxidized germanium are combined poly-succinic
The cruel fiber 10-20% of butanediol.
According to above-mentioned containing anion and degradable milk fibre quilt, the core filler is by following percentage by weight
Component make:The compound poly-succinic acid-butanediol of milk fibre 50%, silk fiber 25%, cotton fiber 10% and nano oxidized germanium is cruel
Fiber 15%.
According to it is above-mentioned containing anion and degradable milk fibre quilt preparation method, comprise the following steps:
(1)Above-mentioned various fibers are carried out in proportion blending, blend fibre is obtained;
(2)Blend fibre is added at temperature 50-60 DEG C anion compound finishing agent, and while add hydrophilic softener,
Adjustment pH value is warmed up to 80 DEG C to 5-7, is then incubated 30 minutes, you can the finished product of blend fibre is obtained;
(3)The finished product of blend fibre is made into core filler through scutching cotton, carding process, so as to obtain containing anion and can drop
The milk fibre quilt of solution.
According to it is above-mentioned containing anion and degradable milk fibre quilt preparation method, step(2)In, the anion
Compounding finishing agent is made up of the raw material Jing emulsifications of following percentage by weight with ultrasonically treated;
(1)Raw material:Granularity is the tourmaline Ultramicro-powder 1-3% of 100-200nm, ammonium polyacrylate 0.5-2%, sodium laurate 2-3%,
Triethanolamine 1-3% and water 90-95.5%;
(2)Pretreatment:The water of the amount of weighing up is put in container, is then slowly added into ammonium polyacrylate, sodium laurate and triethanolamine
And be stirred continuously, then it is slow added into tourmaline micro mist and is stirred continuously;
(3)Emulsification treatment:Pretreated liquid is the emulsified process 30-50min of 4500-5000r/min in emulsification rotating speed;Breast
Change adopts high-shear emulsion machine, emulsifying rate to accelerate to 4500-5000r/min with 90-110r/min in processing;
(4)It is ultrasonically treated:Liquid after emulsification treatment ultrasonically treated 8-15min in the case where power is 1000-1200w, you can obtain
Anion compounds finishing agent.
Compared with prior art, it is an advantage of the current invention that:
The present invention develops the functional health fiber of more high-tech content on the basis of conventional type milk fibre;The fiber is because having
The addition of germanium material, less than in the case of human surface temperature, 32 DEG C can the far infrared ripple that send of high emissivity promote
Enter blood circulation;Simultaneously the negative oxygen ion of its generation, hydroxyl group anion reach sterilization and the effect of fresh air, are promoting cell
Activation, reduction skin senescence speed;And the micro Ge element in the germanic milk fibre of skin-proximal also can pass through skin and inhale
Receive, enter and formed in vivo organic germanium, play anti-cancer, anticancer that generally acknowledged organic germanium rises, the pre- beneficial internal health such as anti-aging
Effect.
Specific embodiment
Following examples are that detailed specific description is carried out to present invention, but present disclosure is not limited such as
This.
Embodiment 1
The invention provides it is a kind of containing anion and degradable milk fibre quilt, including core filler, the core filling
Thing is made up of the component of following percentage by weight:Milk fibre 40-60%, silk fiber 10-30%, cotton fiber 10-20% and nanometer
The germanium oxide cruel fiber 5-20% of compound poly-succinic acid-butanediol.
It is above-mentioned containing anion and degradable milk fibre quilt preparation method, comprise the following steps:
(1)Above-mentioned various fibers are carried out in proportion blending, blend fibre is obtained;
(2)Blend fibre is added at temperature 50-60 DEG C anion compound finishing agent, and while add hydrophilic softener,
Adjustment pH value is warmed up to 80 DEG C to 5-7, is then incubated 30 minutes, you can the finished product of blend fibre is obtained;
(3)The finished product of blend fibre is made into core filler through scutching cotton, carding process, so as to obtain containing anion and can drop
The milk fibre quilt of solution.
Above-mentioned steps(2)In, the anion compounding finishing agent is to be emulsified by the raw material Jing of following percentage by weight and super
Sonication is made;
(1)Raw material:Granularity is the tourmaline Ultramicro-powder 1-3% of 100-200nm, ammonium polyacrylate 0.5-2%, sodium laurate 2-3%,
Triethanolamine 1-3% and water 90-95.5%;
(2)Pretreatment:The water of the amount of weighing up is put in container, is then slowly added into ammonium polyacrylate, sodium laurate and triethanolamine
And be stirred continuously, then it is slow added into tourmaline micro mist and is stirred continuously;
(3)Emulsification treatment:Pretreated liquid is the emulsified process 30-50min of 4500-5000r/min in emulsification rotating speed;Breast
Change adopts high-shear emulsion machine, emulsifying rate to accelerate to 4500-5000r/min with 90-110r/min in processing;
(4)It is ultrasonically treated:Liquid after emulsification treatment ultrasonically treated 8-15min in the case where power is 1000-1200w, you can obtain
Anion compounds finishing agent.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
It is more than 4200/cubic centimetre.
Embodiment 2
The invention provides it is a kind of containing anion and degradable milk fibre quilt, including core filler, the core filling
Thing is made up of the component of following percentage by weight:Milk fibre 50%, silk fiber 25%, cotton fiber 10% and nano oxidized germanium are answered
Close the cruel fiber 15% of poly-succinic acid-butanediol.
It is above-mentioned containing anion and degradable milk fibre quilt preparation method, comprise the following steps:
(1)Above-mentioned various fibers are carried out in proportion blending, blend fibre is obtained;
(2)Blend fibre adds at 58 DEG C of temperature anion compounding finishing agent, and while add hydrophilic softener, adjustment
PH value is warmed up to 80 DEG C to 5.5, is then incubated 30 minutes, you can the finished product of blend fibre is obtained;
(3)The finished product of blend fibre is made into core filler through scutching cotton, carding process, so as to obtain containing anion and can drop
The milk fibre quilt of solution.
Above-mentioned steps(2)In, the anion compounding finishing agent is to be emulsified by the raw material Jing of following percentage by weight and super
Sonication is made;
(1)Raw material:Granularity is tourmaline Ultramicro-powder 1%, ammonium polyacrylate 1.5%, sodium laurate 2%, the triethanolamine 2% of 160nm
With water 93.5%;
(2)Pretreatment:The water of the amount of weighing up is put in container, is then slowly added into ammonium polyacrylate, sodium laurate and triethanolamine
And be stirred continuously, then it is slow added into tourmaline micro mist and is stirred continuously;
(3)Emulsification treatment:Pretreated liquid is the emulsified process 40min of 4800r/min in emulsification rotating speed;In emulsification treatment
Using high-shear emulsion machine, emulsifying rate accelerates to 4800r/min with 90r/min;
(4)It is ultrasonically treated:Liquid after emulsification treatment ultrasonically treated 14min in the case where power is 1100w, you can obtain anion
Compounding finishing agent.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4400/cubic centimetre.
Embodiment 3
The present embodiment part same as Example 1 is no longer repeated, and difference is the core filler by following weight hundred
The component for dividing ratio is made:The compound poly-succinic fourth two of milk fibre 40%, silk fiber 30%, cotton fiber 10% and nano oxidized germanium
The cruel fiber 20% of alcohol.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4380/cubic centimetre.
Embodiment 4
The present embodiment part same as Example 1 is no longer repeated, and difference is the core filler by following weight hundred
The component for dividing ratio is made:The compound poly-succinic fourth two of milk fibre 45%, silk fiber 25%, cotton fiber 15% and nano oxidized germanium
The cruel fiber 15% of alcohol.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4530/cubic centimetre.
Embodiment 5
The present embodiment part same as Example 1 is no longer repeated, and difference is the core filler by following weight hundred
The component for dividing ratio is made:The compound poly-succinic fourth two of milk fibre 43%, silk fiber 27%, cotton fiber 12% and nano oxidized germanium
The cruel fiber 18% of alcohol.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4280/cubic centimetre.
Embodiment 6
The present embodiment part same as Example 1 is no longer repeated, and difference is the core filler by following weight hundred
The component for dividing ratio is made:The compound poly-succinic fourth two of milk fibre 42%, silk fiber 28%, cotton fiber 13% and nano oxidized germanium
The cruel fiber 17% of alcohol.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4360/cubic centimetre.
Embodiment 7
The present embodiment part same as Example 1 is no longer repeated, and difference is the core filler by following weight hundred
The component for dividing ratio is made:The compound poly-succinic fourth two of milk fibre 46%, silk fiber 24%, cotton fiber 14% and nano oxidized germanium
The cruel fiber 16% of alcohol.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4480/cubic centimetre.
Embodiment 8
The present embodiment part same as Example 1 is no longer repeated, and difference is the core filler by following weight hundred
The component for dividing ratio is made:The compound poly-succinic fourth two of milk fibre 48%, silk fiber 22%, cotton fiber 16% and nano oxidized germanium
The cruel fiber 14% of alcohol.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4260/cubic centimetre.
Embodiment 9
The present embodiment part same as Example 1 is no longer repeated, and difference is the core filler by following weight hundred
The component for dividing ratio is made:The compound poly-succinic fourth two of milk fibre 52%, silk fiber 20%, cotton fiber 18% and nano oxidized germanium
The cruel fiber 10% of alcohol.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4380/cubic centimetre.
Embodiment 10
The present embodiment part same as Example 1 is no longer repeated, and difference is the core filler by following weight hundred
The component for dividing ratio is made:The compound poly-succinic fourth two of milk fibre 54%, silk fiber 16%, cotton fiber 20% and nano oxidized germanium
The cruel fiber 10% of alcohol.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4290/cubic centimetre.
Embodiment 11
The present embodiment part same as Example 1 is no longer repeated, and difference is the core filler by following weight hundred
The component for dividing ratio is made:The compound poly-succinic fourth two of milk fibre 60%, silk fiber 20%, cotton fiber 15% and nano oxidized germanium
The cruel fiber 5% of alcohol.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4370/cubic centimetre.
Embodiment 12
The present embodiment part same as Example 1 is no longer repeated, and difference is the core filler by following weight hundred
The component for dividing ratio is made:The compound poly-succinic fourth two of milk fibre 59%, silk fiber 12%, cotton fiber 10% and nano oxidized germanium
The cruel fiber 19% of alcohol.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4420/cubic centimetre.
Embodiment 13
The present embodiment part same as Example 1 is no longer repeated, and difference is the core filler by following weight hundred
The component for dividing ratio is made:The compound poly-succinic fourth two of milk fibre 55%, silk fiber 25%, cotton fiber 15% and nano oxidized germanium
The cruel fiber 5% of alcohol.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4510/cubic centimetre.
Embodiment 14
The present embodiment part same as Example 1 is no longer repeated, and difference is the core filler by following weight hundred
The component for dividing ratio is made:The compound poly-succinic fourth two of milk fibre 48%, silk fiber 26%, cotton fiber 13% and nano oxidized germanium
The cruel fiber 13% of alcohol.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4450/cubic centimetre.
Embodiment 15
The present embodiment part same as Example 1 is no longer repeated, and difference is the core filler by following weight hundred
The component for dividing ratio is made:The compound poly-succinic fourth two of milk fibre 47%, silk fiber 18%, cotton fiber 20% and nano oxidized germanium
The cruel fiber 15% of alcohol.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4370/cubic centimetre.
Embodiment 16
The present embodiment part same as Example 1 is no longer repeated, and it is by such as that difference is the anion compounding finishing agent
The raw material Jing emulsifications of lower percentage by weight are made with ultrasonically treated;
(1)Raw material:Granularity is tourmaline Ultramicro-powder 1%, ammonium polyacrylate 2%, sodium laurate 3%, the and of triethanolamine 3% of 120nm
Water 91%;
(2)Pretreatment:The water of the amount of weighing up is put in container, is then slowly added into ammonium polyacrylate, sodium laurate and triethanolamine
And be stirred continuously, then it is slow added into tourmaline micro mist and is stirred continuously;
(3)Emulsification treatment:Pretreated liquid is the emulsified process 45min of 4600r/min in emulsification rotating speed;In emulsification treatment
Using high-shear emulsion machine, emulsifying rate accelerates to 4600r/min with 100r/min;
(4)It is ultrasonically treated:Liquid after emulsification treatment ultrasonically treated 9min in the case where power is 1050w, you can obtain anion and answer
With finishing agent.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4280/cubic centimetre.
Embodiment 17
The present embodiment part same as Example 1 is no longer repeated, and it is by such as that difference is the anion compounding finishing agent
The raw material Jing emulsifications of lower percentage by weight are made with ultrasonically treated;
(1)Raw material:Granularity is tourmaline Ultramicro-powder 3%, ammonium polyacrylate 1%, sodium laurate 3%, the and of triethanolamine 3% of 190nm
Water 90%;
(2)Pretreatment:The water of the amount of weighing up is put in container, is then slowly added into ammonium polyacrylate, sodium laurate and triethanolamine
And be stirred continuously, then it is slow added into tourmaline micro mist and is stirred continuously;
(3)Emulsification treatment:Pretreated liquid is the emulsified process 30-50min of 4700r/min in emulsification rotating speed;At emulsification
High-shear emulsion machine, emulsifying rate is adopted to accelerate to 4700r/min with 110r/min in reason;
(4)It is ultrasonically treated:Liquid after emulsification treatment ultrasonically treated 12min in the case where power is 1150w, you can obtain anion
Compounding finishing agent.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4280/cubic centimetre.
Embodiment 18
The present embodiment part same as Example 1 is no longer repeated, and it is by such as that difference is the anion compounding finishing agent
The raw material Jing emulsifications of lower percentage by weight are made with ultrasonically treated;
(1)Raw material:Granularity is tourmaline Ultramicro-powder 1.5%, ammonium polyacrylate 0.5%, the sodium laurate 2%, triethanolamine of 200nm
2% and water 94%;
(2)Pretreatment:The water of the amount of weighing up is put in container, is then slowly added into ammonium polyacrylate, sodium laurate and triethanolamine
And be stirred continuously, then it is slow added into tourmaline micro mist and is stirred continuously;
(3)Emulsification treatment:Pretreated liquid is the emulsified process 45min of 4800r/min in emulsification rotating speed;In emulsification treatment
Using high-shear emulsion machine, emulsifying rate accelerates to 4800r/min with 105r/min;
(4)It is ultrasonically treated:Liquid after emulsification treatment ultrasonically treated 8min in the case where power is 1200w, you can obtain anion and answer
With finishing agent.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4330/cubic centimetre.
Embodiment 19
The present embodiment part same as Example 1 is no longer repeated, and it is by such as that difference is the anion compounding finishing agent
The raw material Jing emulsifications of lower percentage by weight are made with ultrasonically treated;
(1)Raw material:Granularity is tourmaline Ultramicro-powder 1%, ammonium polyacrylate 0.5%, sodium laurate 2%, the triethanolamine 1% of 140nm
With water 95.5%;
(2)Pretreatment:The water of the amount of weighing up is put in container, is then slowly added into ammonium polyacrylate, sodium laurate and triethanolamine
And be stirred continuously, then it is slow added into tourmaline micro mist and is stirred continuously;
(3)Emulsification treatment:Pretreated liquid is the emulsified process 30-50min of 5000r/min in emulsification rotating speed;At emulsification
High-shear emulsion machine, emulsifying rate is adopted to accelerate to 5000r/min with 100r/min in reason;
(4)It is ultrasonically treated:Liquid after emulsification treatment ultrasonically treated 15min in the case where power is 1000w, you can obtain anion
Compounding finishing agent.
Foundation《SFJJ-QWX25-2006 negative ion concentrations check detailed rules and regulations》Test, negative ion concentration is in product of the present invention
4260/cubic centimetre.
Above-described is only the preferred embodiment of the present invention, it is noted that for a person skilled in the art,
Under the premise of without departing from general idea of the present invention, some changes and improvements can also be made, these should also be considered as the present invention's
Protection domain.
Claims (5)
1. containing anion and degradable milk fibre quilt, including core filler, it is characterised in that the core filler by
The component of following percentage by weight is made:Milk fibre 40-60%, silk fiber 10-30%, cotton fiber 10-20% and nano oxidized
The germanium cruel fiber 5-20% of compound poly-succinic acid-butanediol.
2. it is according to claim 1 containing anion and degradable milk fibre quilt, it is characterised in that the core filling
Thing is made up of the component of following percentage by weight:Milk fibre 40-50%, silk fiber 20-30%, cotton fiber 10-15% and nanometer
The germanium oxide cruel fiber 10-20% of compound poly-succinic acid-butanediol.
3. it is according to claim 1 containing anion and degradable milk fibre quilt, it is characterised in that the core filling
Thing is made up of the component of following percentage by weight:Milk fibre 50%, silk fiber 25%, cotton fiber 10% and nano oxidized germanium are answered
Close the cruel fiber 15% of poly-succinic acid-butanediol.
4. it is according to claim 1 containing anion and degradable milk fibre quilt preparation method, it is characterised in that bag
Include following steps:
(1)Above-mentioned various fibers are carried out in proportion blending, blend fibre is obtained;
(2)Blend fibre is added at temperature 50-60 DEG C anion compound finishing agent, and while add hydrophilic softener,
Adjustment pH value is warmed up to 80 DEG C to 5-7, is then incubated 30 minutes, you can the finished product of blend fibre is obtained;
(3)The finished product of blend fibre is made into core filler through scutching cotton, carding process, so as to obtain containing anion and can drop
The milk fibre quilt of solution.
5. it is according to claim 4 containing anion and degradable milk fibre quilt preparation method, it is characterised in that:Step
Suddenly(2)In, the anion compounding finishing agent is made up of the raw material Jing emulsifications of following percentage by weight with ultrasonically treated;
(1)Raw material:Granularity is the tourmaline Ultramicro-powder 1-3% of 100-200nm, ammonium polyacrylate 0.5-2%, sodium laurate 2-3%,
Triethanolamine 1-3% and water 90-95.5%;
(2)Pretreatment:The water of the amount of weighing up is put in container, is then slowly added into ammonium polyacrylate, sodium laurate and triethanolamine
And be stirred continuously, then it is slow added into tourmaline micro mist and is stirred continuously;
(3)Emulsification treatment:Pretreated liquid is the emulsified process 30-50min of 4500-5000r/min in emulsification rotating speed;Breast
Change adopts high-shear emulsion machine, emulsifying rate to accelerate to 4500-5000r/min with 90-110r/min in processing;
(4)It is ultrasonically treated:Liquid after emulsification treatment ultrasonically treated 8-15min in the case where power is 1000-1200w, you can obtain
Anion compounds finishing agent.