CN106609056A - Waterborne epoxy anticorrosion paint - Google Patents
Waterborne epoxy anticorrosion paint Download PDFInfo
- Publication number
- CN106609056A CN106609056A CN201510703282.6A CN201510703282A CN106609056A CN 106609056 A CN106609056 A CN 106609056A CN 201510703282 A CN201510703282 A CN 201510703282A CN 106609056 A CN106609056 A CN 106609056A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- waterborne epoxy
- corrosion
- resistant epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a waterborne epoxy anticorrosion paint. The waterborne epoxy anticorrosion paint comprises, by weight, 20 to 50 parts of waterborne epoxy resin emulsion, 1 to 5 parts of a waterborne epoxy curing agent, 10 to 20 parts of hydroxybutyl acrylate, 5 to 20 parts of polyurethane resin, 1 to 5 parts of mica powder, 1 to 5 parts of zinc phosphate and 0.5 to 2 parts of an antifoaming agent. The waterborne epoxy anticorrosion paint provided by the invention overcomes the disadvantages of traditional paints and has the advantages of strong anticorrosion performance, good compatibility, good storage stability, no pollution and high film quality.
Description
Technical field
The invention is related to chemical material field, more particularly to a kind of water corrosion-resistant epoxy paint.
Background technology
Containing substantial amounts of phenyl ring and ehter bond in epoxy molecule structure, system intensity is big, and molecular structure is caused
Close, cohesive energy is big, therefore the coating prepared using epoxy resin has, chemically-resistant strong with centralized procurement adhesive force
Medium and Corrosion Protection are excellent, are widely used in heavy antisepsis field.The big portion of anticorrosive paint in the market
It is solvent based coating to divide, due to containing some hydrophilic compositions in water paint, under causing Corrosion Protection
Drop, but, as the requirement to environmental protection is more and more stricter, the demand of water-based anticorrosive paint is more and more urgent,
Therefore the excellent water paint of antiseptic property receives attention.
The content of the invention
To solve above-mentioned technical problem, the technical solution used in the present invention is:
A kind of water corrosion-resistant epoxy paint, the water corrosion-resistant epoxy paint, in terms of parts by weight, including
Following component:20~50 parts of aqueous epoxy resin emulsion, 1~5 part of soluble epoxide curing agent, propylene
10~20 parts of sour hydroxy butyl ester, 5~20 parts of polyurethane resin, 1~5 part of mica powder, trbasic zinc phosphate 1~5
Part, 0.5~2 part of defoamer, 20~40 parts of water.
Further, the water corrosion-resistant epoxy paint, in terms of parts by weight, including following component:It is aqueous
30 parts of epoxy resin latex, 2 parts of soluble epoxide curing agent, 15 parts of hy-droxybutyl, polyurethane
10 parts of resin, 3 parts of mica powder, 2 parts of trbasic zinc phosphate, 1 part of defoamer, 30 parts of water.
Further, the aqueous epoxy curing agent is micella decentralized or emulsion-type curing agent.
The present invention has the advantages and positive effects that:The water corrosion-resistant epoxy paint of the present invention, compensate for
The deficiency of traditional coating, anticorrosive property is strong, and paint compatibility is good, and excellent storage stability is pollution-free, applies
Film quality is high.
Specific embodiment
The present invention is further detailed below by specific embodiment.
Embodiment 1
A kind of water corrosion-resistant epoxy paint, the water corrosion-resistant epoxy paint, in terms of parts by weight, including
Following component:30 parts of aqueous epoxy resin emulsion, 2 parts of soluble epoxide curing agent, acrylic acid hydroxyl fourth
15 parts of ester, 10 parts of polyurethane resin, 3 parts of mica powder, 2 parts of trbasic zinc phosphate, 1 part of defoamer, water 30
Part.
Embodiment 2
A kind of water corrosion-resistant epoxy paint, the water corrosion-resistant epoxy paint, in terms of parts by weight, including
Following component:50 parts of aqueous epoxy resin emulsion, 5 parts of soluble epoxide curing agent, acrylic acid hydroxyl fourth
20 parts of ester, 20 parts of polyurethane resin, 5 parts of mica powder, 1 part of trbasic zinc phosphate, 2 parts of defoamer, water 40
Part.
Embodiment 3
A kind of water corrosion-resistant epoxy paint, the water corrosion-resistant epoxy paint, in terms of parts by weight, including
Following component:20 parts of aqueous epoxy resin emulsion, 1 part of soluble epoxide curing agent, acrylic acid hydroxyl fourth
10 parts of ester, 5 parts of polyurethane resin, 1 part of mica powder, 5 parts of trbasic zinc phosphate, 0.5 part of defoamer, water
20 parts.
One embodiment of the present of invention has been described in detail above, but the content is only the present invention's
Preferred embodiment, it is impossible to be considered as the practical range for limiting the present invention.It is all according to the present patent application scope
The impartial change made and improvement etc., all should still belong within the patent covering scope of the present invention.
Claims (3)
1. a kind of water corrosion-resistant epoxy paint, it is characterised in that:The water corrosion-resistant epoxy paint, with weight
Amount number meter, including following component:20~50 parts of aqueous epoxy resin emulsion, soluble epoxide solidification
1~5 part of agent, 10~20 parts of hy-droxybutyl, 5~20 parts of polyurethane resin, mica powder 1~5
Part, 1~5 part of trbasic zinc phosphate, 0.5~2 part of defoamer, 20~40 parts of water.
2. a kind of water corrosion-resistant epoxy paint according to claim 1, it is characterised in that:The water
Property corrosion-resistant epoxy paint, in terms of parts by weight, including following component:30 parts of aqueous epoxy resin emulsion,
2 parts of soluble epoxide curing agent, 15 parts of hy-droxybutyl, 10 parts of polyurethane resin, mica powder 3
Part, 2 parts of trbasic zinc phosphate, 1 part of defoamer, 30 parts of water.
3. a kind of water corrosion-resistant epoxy paint according to claim 1, it is characterised in that:The water
Property epoxy hardener is micella decentralized or emulsion-type curing agent.