CN106592254A - Outdoor waterproof antibacterial superfine fiber synthetic leather and finishing method thereof - Google Patents
Outdoor waterproof antibacterial superfine fiber synthetic leather and finishing method thereof Download PDFInfo
- Publication number
- CN106592254A CN106592254A CN201611039253.5A CN201611039253A CN106592254A CN 106592254 A CN106592254 A CN 106592254A CN 201611039253 A CN201611039253 A CN 201611039253A CN 106592254 A CN106592254 A CN 106592254A
- Authority
- CN
- China
- Prior art keywords
- superfine fiber
- antibacterial
- water
- leather
- synthetic leather
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses outdoor waterproof antibacterial superfine fiber synthetic leather and a finishing method thereof, wherein a preparation method of the synthetic leather comprises the following steps: (1) immersing superfine fiber synthetic leather in a treatment liquid, and padding, wherein the liquid carrying rate of the superfine fiber synthetic leather is 50%-70%, and the treatment liquid comprises the following components in parts by weight: 7-10 parts of a C6 waterproof finishing agent, 3-7 parts of a water-based antibacterial agent, 1-3 parts of a water-based crosslinking agent, and 100 parts of deionized water, wherein the pH is 4-6; (2) drying the product of the step (1), cooling and coiling; and (3) roll-coating the front face and the reverse face of the superfine fiber synthetic leather of the step (2) with an oily antibacterial agent, drying, cooling and coiling, and thus obtaining the externally-applied waterproof antibacterial superfine fiber synthetic leather. The superfine fiber synthetic leather produced by the method has stable waterproof antibacterial quality, and overcomes the defect that the waterproof property and the antibacterial property cannot reach the standards at the same time; and the product has good breathability and moisture permeability and strong scratch resistance, and is suitable for outdoor protective shoes and protective gloves.
Description
Technical field
The present invention relates to the afterfinish method of suede superfine fiber synthetic leather.
Background technology
In recent years, suede superfine fiber synthetic leather increasingly liked by consumer, becomes superfine fiber chemical leather
Main product, at the same time, feature super fiber leather gradually climbs up stage, and the one seat of occuping market.As people are to family
Chasing after for outer activity is high, the requirement to outdoor protective articless also more and more higher, especially protective footwear and protective gloves, it is desirable to anti-
The functions such as water, ventilative, antibacterial, wear-resisting, scratch resistance.Existing water proof type super fiber leather and antimicrobial form super fiber leather commercially extensively flow
OK, but outdoor water-proof antibiotic super fiber leather technology and unstable.
Initially, the Final finishing technology bathed altogether using C8 waterproofing agents and antibacterial, can reach requirement, but contain in C8
The harmful substances such as PFOA and PFOS, do not meet consumer's environmental protection concept, therefore C8 products are not gradually contained PFOA's and PFOS
C6 products replace.
But fact proved, C6 waterproofing agents and antibacterial bathe altogether Final finishing technology and unstable, different batches of product it is anti-
There is larger difference between water and antibacterial effect.
The content of the invention
It is an object of the invention to provide a kind of outdoor water-proof antibiotic superfine fiber chemical leather and its method for sorting, with gram
Take the defect of prior art presence.
The method of the present invention, comprises the steps:
(1) superfine fiber chemical leather is immersed and will be padded in treatment fluid, after padding, the liquid carrying rate of super fiber leather is 50%~
70%;
Described treatment fluid includes the component of following parts by weight:
PH is 4~6;
Preparation method is as follows:
By the mixing of C6 water-proof aagents, waterborne antibacterial agent, water cross-linking agent and water, then the pH of mixed liquor is adjusted with acetic acid,
Obtain described treatment fluid;
Preferably, superfine fiber chemical leather is immersed in treatment fluid, is rolled through 4 leachings 4, the liquid carrying rate for controlling super fiber leather is
55%~65%, regulation speed is 5~8m/min;
(2) and then by the product of step (1) at 130~160 DEG C 5~15min of drying and processing, then cooled down, received
Volume.
(3) by the super fiber leather of step (2), on three printing machines, roller coat oiliness antibacterial, the positive and negative of super fiber leather is respectively applied
One time, it is desirable to which roller coat amount is 2-10g/m2, then dry at 120 DEG C, finally cooled down, wound;
The operations such as described cooling, winding are known method, can be found in document:Qu Jianbo. synthetic leather material and technology
Learn [M]. Beijing:Chemical Industry Press, 2015. methods recorded.
The C6 water-proof aagents are perfluor hexane sulfonyl compound or sulfonate, the such as AFH6 of Rudoiph company, Du Pont
Teflon SLA, the TG-5671 of big King Company in one kind or arbitrary proportion mixture aqueous solution;
The waterborne antibacterial agent is silver ion type inorganic composite, and such as Rudoiph's antibacterial AGP, Hensel steps antibacterial HeiQ
The mixture aqueous solution of one kind or arbitrary proportion in Pure TF, Tao Shi antibacterial ET;
The water cross-linking agent is aromatic series closed type polyisocyanate, and the such as FU of solar corona company or Shanghai think to contain polymer
One or two the mixture of the water dispersed isocyanate cross-linking agent EC-600 of material;
The oiliness antibacterial is macromolecule organic antibacterial agent, the such as ATE's 9280, DOW Chemical of Germany Herst
One or two mixture in SKANE ò M-8.
Agent of the present invention is combined using Organic-inorganic composite antibacterial, and product has the high efficiency of organic antibacterial agent, holds
Continuous property has safety and the thermostability of inorganic antiseptic again;There is good water resistance again using C6 waterproofing agents, i.e. environmental protection.
Gained super fiber leather can reach following effect:
Water absorbance≤30%, penetration by water amount≤0.2g, vapor permeation amount >=5mg/cm2H (testing standards ISO
20345);Meanwhile, the effect of anti-K. pneumonia can reach more than 90% (testing standard ATCC 4352), resist golden yellow
The staphylococcic effect of color can reach more than 90% (testing standard ATCC 6538).
The super fiber leather steady quality of the method production, overcome waterproof and antibacterial can not while reach the defect of standard, and
And product air-and water-permeable vapour is good, scratch resistance strong, is well suited for for outdoor protective footwear and protective gloves.
Specific embodiment
Below by specific embodiment, the present invention is described in further detail, but the present invention is not only limited in these
Example.
Embodiment 1
(1) padding finishing agent:Superfine fibre suede is immersed in finishing agent, 4 leachings 4 are rolled, liquid carrying rate 55%, 130 DEG C
Drying and processing 10min, is then cooled down, is wound.
Described finishing agent, is made up of the component of following parts by weight:
It is 4.5 with second acid for adjusting pH
(2) antibacterial is printed:The positive and negative of super fiber leather respectively applies an oiliness antibacterial ATE 9280,
Roller coat amount is 2g/m2, then dry at 120 DEG C, finally cooled down, wound.
This technique gained super fiber leather can reach following effect:
Water absorbance 5.2%, penetration by water amount 0.02g, vapor permeation amount 10mg/cm2H (testing standard ISO 20345);
Meanwhile, anti-K. pneumonia is 95%, (testing standard ATCC 4352), and anti-Staphylococcus aureus are 93% (test
Standard ATCC 6538).
Embodiment 2
(1) padding finishing agent:Superfine fibre suede is immersed in finishing agent, 4 leachings 4 are rolled, liquid carrying rate 60%, 135 DEG C
Drying and processing 12min, is then cooled down, is wound.
Described finishing agent, is made up of the component of following parts by weight:
It is 5 with second acid for adjusting pH
(2) antibacterial is printed:The positive and negative of super fiber leather respectively applies an oiliness antibacterial ATE 9280, and roller coat amount is 7g/m2,
Then dry at 120 DEG C, finally cooled down, wound.
This technique gained super fiber leather can reach following effect:
Water absorbance 9.9%, penetration by water amount 0.15g, vapor permeation amount 13mg/cm2H (testing standard ISO 20345);
Meanwhile, anti-K. pneumonia is 92% (testing standard ATCC 4352), and anti-Staphylococcus aureus are 94% (test
Standard ATCC 6538).
Embodiment 3
(1) padding finishing agent:Superfine fibre suede is immersed in finishing agent, 4 leachings 4 are rolled, liquid carrying rate 60%, 135 DEG C
Drying and processing 10min, is then cooled down, is wound.
Described finishing agent, is made up of the component of following parts by weight:
It is 5 with second acid for adjusting pH
(2) antibacterial is printed:The positive and negative of super fiber leather respectively applies an oiliness antibacterial SKANE ò M-8, and roller coat amount is 10g/
m2, then dry at 120 DEG C, finally cooled down, wound.
This technique gained super fiber leather can reach following effect:
Water absorbance 4.3%, penetration by water amount 0.02g, vapor permeation amount 11mg/cm2H (testing standard ISO 20345);
Meanwhile, anti-K. pneumonia is 91% (testing standard ATCC 4352), and anti-Staphylococcus aureus are 92% (test
Standard ATCC 6538).
Embodiment 4
(1) padding finishing agent:Superfine fibre suede is immersed in finishing agent, 4 leachings 4 are rolled, liquid carrying rate 65%, 140 DEG C
Drying and processing 8min, is then cooled down, is wound.
Described finishing agent, is made up of the component of following parts by weight:
It is 5.5 with second acid for adjusting pH
(2) antibacterial is printed:The positive and negative of super fiber leather respectively applies an oiliness antibacterial SKANE ò M-8, and roller coat amount is 5g/
m2, then dry at 120 DEG C, finally cooled down, wound.
This technique gained super fiber leather can reach following effect:
Water absorbance 3.3%, penetration by water amount 0.08g, vapor permeation amount 8.5mg/cm2H (testing standards ISO
20345);Anti- K. pneumonia is 92% (testing standard ATCC 4352), and anti-Staphylococcus aureus are 95% (survey
The quasi- ATCC 6538 of test-object).
Claims (9)
1. outdoor water-proof antibiotic superfine fiber chemical leather method for sorting, it is characterised in that comprise the steps:
(1) superfine fiber chemical leather is immersed and is padded in treatment fluid, the liquid carrying rate of super fiber leather is 50%~70%;
Described treatment fluid includes the component of following parts by weight:
PH is 4~6;
(2) and then by the product of step (1) dry, then cooling, winding;
(3) by the positive and negative of the super fiber leather of step (2), roller coat oiliness antibacterial, drying, cooling, winding are outer that is, described in acquisition
Use water-proof antibiotic superfine fiber chemical leather.
2. method according to claim 1, it is characterised in that the C6 water-proof aagents are perfluor hexane sulfonyl compound
Or sulfonate.
3. method according to claim 1, it is characterised in that the waterborne antibacterial agent is silver ion type inorganic composite.
4. method according to claim 1, it is characterised in that the water cross-linking agent is aromatic series closed type polyisocyanate
Ester.
5. method according to claim 1, it is characterised in that the oiliness antibacterial is macromolecule organic antibacterial agent.
6. method according to claim 1, it is characterised in that superfine fiber chemical leather is immersed in treatment fluid, through 4 leachings
4 roll, and the liquid carrying rate for controlling super fiber leather is 55%~65%, and regulation speed is 5~8m/min.
7. method according to claim 1, it is characterised in that in step (3), by the positive and negative of the super fiber leather of step (2),
Roller coat oiliness antibacterial, roller coat amount is 2-10g/m2, then dry at 120 DEG C.
8. the outdoor water-proof antibiotic superfine fiber chemical leather for being prepared according to any one of claim 1~7 method.
9. outdoor water-proof antibiotic superfine fiber chemical leather according to claim 8, it is characterised in that water absorbance≤
30%, penetration by water amount≤0.2g, vapor permeation amount >=5mg/cm2H (testing standard ISO 20345);Meanwhile, anti-K
The effect of pneumobacilluses can reach more than 90% (testing standard ATCC 4352), and the effect of anti-Staphylococcus aureus can reach
More than 90% (testing standard ATCC 6538).