CN106590029A - Composite white pigment and preparation method thereof - Google Patents
Composite white pigment and preparation method thereof Download PDFInfo
- Publication number
- CN106590029A CN106590029A CN201611019495.8A CN201611019495A CN106590029A CN 106590029 A CN106590029 A CN 106590029A CN 201611019495 A CN201611019495 A CN 201611019495A CN 106590029 A CN106590029 A CN 106590029A
- Authority
- CN
- China
- Prior art keywords
- white pigment
- composite white
- ball
- composite
- pigment according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a composite white pigment. The composite white pigment is prepared from, by weight, 50-90 parts of calcium carbonate micropowder, 10-50 parts of transparent glass micropowder, 10-50 parts of ultrafine micropowder and 5-10 parts of water glass. The invention further provides a preparation method of the composite white pigment. The compound white pigment is prepared through the steps of paste preparing, high-energy ball-milling, drying and sample preparing. The composite white pigment is high in powder whiteness and covering power, stable in chemical property and low in production cost.
Description
Technical field
The present invention relates to a kind of production technical field of white powder pigment, and in particular to one kind is with Calcium Carbonate and controlled micro crystallization
Glass dust is the composite white pigment of primary raw material Jing high-energy ball milling preparation technologies.
Background technology
Titanium dioxide has excellent covering power, reducing power, fineness and a weatherability, and its have chemical inertness, it is nontoxic,
The performance such as harmless, becomes the maximum Chinese white of most widely used at present and consumption figure.However, titanium white production and
What the factor such as limited of problem of environmental pollution that actual application causes and titanium dioxide resource limited titanium dioxide industry enters one
Step upgrading and development.The mainly powder surface that titanium dioxide works in actual applications, and the nuclear structure of powder body is not played
Effect.A kind of effective way for solving the problem is prepared and using titanium dioxide substitute products.
Described titanium dioxide succedaneum, refers to the performance with titanium dioxide and cost is the titanium dioxide bottom of than, being capable of part or complete
Portion substitutes the inorganic powder material that titanium dioxide is employed.From 20 century 70s, titanium dioxide succedaneum has just had started to research
And exploitation, and achieve good economic benefit.Inorganic particle/TiO2Composite powder material possesses core (inorganic particle)-shell
(TiO2) structure, it is the optimal replacement of titanium dioxide so far while possessing similar pigment performance and cheap to titanium dioxide
Product.
Composite titanium dioxide is produced using inorganic particle method for coating, it is different according to handling process, can be generally divided at present
Two kinds of dry and wet.
Dry method is usually that surface activation process is carried out to inorganic powder particle using mechanochemical method, causes zwitterion
With reference to.Mechanochemical method is a kind of efficient, energy-conservation and comparatively environmentally friendly powder preparation method.It is powder body system
The method that favor is enjoyed in standby technique, realizes to realize between inorganic particle and titanium dioxide effectively using Mechanochemical Effect
Cladding.Chinese invention patent document such as Publication No. CN101100561A is disclosed and adopts dry production, uses whirlwind pulverizer
To powder body high speed shear, at a certain temperature, make powder body introduce zwitterion and combine, obtain a kind of composite titanium dioxide.
Wet method is in a liquid state, by chemical assistant or mechanical lapping, to be combined two kinds of powder body covered composite yarns
Thing.If the Chinese invention patent document of Publication No. CN1724595A is to white mineral powder-TiO2The system of composite white pigment
It is standby, using by after inorganic mineral powder slurrying with TiO2Suspension realize with the help of chemical assistant chemical reaction coat,
Form complex.The Chinese invention patent document of Publication No. CN101775239A discloses a kind of with the inorganic of high covering power
The preparation of composite white pigment, is by adding certain auxiliary agent, in wet ultra-fine grinding by titanium dioxide and white mineral powder
Two kinds of powder body are combined in equipment obtain complex.But wet method preparation is higher to equipment requirements, and the composite granule performance of preparation is not
It is good, and to environment in production process.
The composite titanium based on Calcium Carbonate, pyrophillite, Kaolin and barite etc. prepared using mechanochemical method
White lead, with preferably covering power, but acid resistance is poor, and the surface soundness of coating, overlay film or paint film is poor.
The content of the invention
In order to overcome the above-mentioned deficiencies of the prior art, the invention provides one kind is based on Calcium Carbonate and microcrystalline glass powder
Want the composite white pigment of raw material Jing high-energy ball milling preparation technologies.
A kind of composite white pigment, the composite white pigment is made up of following parts by weight ingredient:
By adopting above-mentioned technical proposal, there is provided a kind of whiteness height, strong covering power, the compound white of stable chemical performance
Pigment.The application adds clear glass micropowder, improves the hiding rare of composite white pigment, adds super fine, improves multiple
The compactness and weatherability on Chinese white surface are closed, is allowed to more stable.
The calcium carbonate fine powder grain diameter size is 325~2500 mesh, and Blue Whiteness value is 92~97.
The clear glass micro powder granule size is 325~2500 mesh, and Blue Whiteness value is 90~95, and described
700~900 DEG C of heat treatments of bright glass micro mist Jing realize its controlled micro crystallization.Present invention introduces the glass micro mist of controlled micro crystallization, changes biography
The relatively low defect of the covering power of the one-component calcium carbonate superfine powder powder body of system.After controlled micro crystallization, its refractive index is obtained glass micro mist
Effectively improve.After microcrystalline glass powder is added, the covering power of composite granule can be effectively improved calcium carbonate fine powder system.
The clear glass micropowder controlled micro crystallization adopts sintering process, and its specific technological process is as follows:Dispensing → found → water
Quench → crush → sieve → shape → sinter → reprocess, wherein sintering temperature is 700~900 DEG C.Sintering process energy glass powder
Granule bonding is produced, then powder is produced intensity and is caused densification and recrystallization through material transport, the motive force of sintering
It is the crystal boundary energy of the surface energy more than polycrystalline sintered body of granular material.
The super fine be nano-calcium carbonate, nano titanium oxide, nano silicon and Nano silica sol in extremely
Few one kind.Preferably, the super fine is at least one in nano-calcium carbonate and nano titanium oxide.
The super fine grain diameter size is 5000~8000 mesh, and Blue Whiteness value is 92~97.Add in the present invention
Plus super fine, the surface soundness of coating, overlay film or paint film can be effectively improved, super fine can effectively be filled into bulky grain
The space of filler, improves blocking water and gas barrier properties for coating etc., improves the comprehensive effectiveness of coating.
The adsorptivity between different material in blending ingredients is effectively increased as binding agent using waterglass in the present invention
Can so that the chemical stability of end-product is effectively improved.
Preferably, the composite white pigment is made up of following parts by weight ingredient:
Experiment shows that, using the composite white pigment strong covering power of above-mentioned technical proposal, whiteness is high.
Preferably, the composite white pigment is made up of following parts by weight ingredient:
Nano-calcium carbonate is fine and smooth, uniform, whiteness is high, good in optical property, and experiment shows, using the compound of above-mentioned technical proposal
Chinese white strong covering power, whiteness is high.
Preferably, the composite white pigment is made up of following parts by weight ingredient:
Nano titanium oxide has very high chemical stability, and its refractive index effectively improves Jing after controlled micro crystallization.Experiment
Show, using the composite white pigment of above-mentioned technical proposal, strong covering power, whiteness is high, and whiteness value reaches more than 95%.
Preferably, the composite white pigment is made up of following parts by weight ingredient:
Experiment shows, using the composite white pigment of above-mentioned technical proposal, strong covering power, whiteness is high, and whiteness value reaches
More than 95%.
Preferably, the composite white pigment is made up of following parts by weight ingredient:
Experiment shows, using the composite white pigment of above-mentioned technical proposal, strong covering power, whiteness is high, and whiteness value reaches
More than 95%.
Present invention also offers a kind of preparation method of composite white pigment, comprises the following steps:
(1) slurrying:Oxide spinel calcium micropowder, clear glass micropowder, super fine and waterglass are mixed by weight, plus
Enter water and make suspended slurry, the addition of the water is 1~4 times of raw materials quality summation;
(2) high-energy ball milling:By suspended slurry high-energy ball milling together with mill ball obtained in step (1);
(3) it is dried:Material Jing after step (2) ball milling is dried through washing, sucking filtration;
(4) sample preparation:The dried material of step (3) is carried out into sample preparation crushing.
The present invention adopts high-energy ball milling preparation technology, effectively improves the surfactant property of different component material so that no
Improve with the absorbent properties between material component, again such that the chemical stability of end-product is improved.
To avoid impact of the metal medium to end-product composite granule, the mill ball is zirconia ball.
In step (2), to reach preferable wet method mechanical force ground and mixed uniformity, the suspended slurry and mill ball
Mass ratio is 50~100:1.
The rotational speed of ball-mill is 3000~5000r/min.Rotating speed is too high, and one side energy consumption is larger, on the other hand, is unfavorable for
The preferable physics covered effect of above-mentioned mixed powder.
With the increase of Ball-milling Time, powder particle is gradually refined, but Ball-milling Time is long, and powder particle can be rolled into a ball again
It is poly-, there is the phenomenon of particle size increase, preferably, Ball-milling Time is 30~60min.
The present invention prepare composite white pigment grain diameter size be 1200~2500 mesh, Blue Whiteness value be 88.2~
95.7。
Compared with prior art, the invention provides one kind based on calcium carbonate superfine powder micropowder, microcrystalline glass micropowder,
Super fine is the composite white pigment of body material Jing high-energy ball milling preparation technologies, and gained composite white pigment powder body is white
Degree is high, strong covering power, stable chemical performance, and production cost is relatively low.
Description of the drawings
Fig. 1 is the preparation technology flow chart of composite white pigment of the present invention.
Specific embodiment
Embodiment 1
A kind of composite white pigment, the composite white pigment is made up of following parts by weight ingredient:
Prepared by following steps:
(1) slurrying:By 90g calcium carbonate fine powders, 10g clear glass micropowders, 10g nano-calcium carbonates, 10g nano titanium oxides
Mix by weight with 10g waterglass, add 150g water to make suspended slurry;
(2) high-energy ball milling:Suspended slurry obtained in step (1) is poured in ball grinder, 5.6g zirconia ball conducts are added
Mill ball, carries out high-energy ball milling, and rotational speed of ball-mill is 3000r/min, and Ball-milling Time is 60min;
(3) it is dried:Material Jing after step (2) ball milling is put in blowing-type drying baker after sucking filtration and is done through washing
Dry, baking temperature is 120 DEG C, and drying time is 2h;
(4) sample preparation:The dried material of step (3) is carried out into sample preparation crushing.
The preparation technology flow chart of composite white pigment of the present invention is as shown in Figure 1.
Embodiment 2
A kind of composite white pigment, the composite white pigment is made up of following parts by weight ingredient:
Prepared by following steps:
(1) slurrying:By 80g calcium carbonate fine powders, 20g clear glass micropowders, 30g nano-calcium carbonates, 20g nano silicons
Mix by weight with 10g waterglass, add 150g water to make suspended slurry;
(2) high-energy ball milling:Suspended slurry obtained in step (1) is poured in ball grinder, 6.0g zirconia ball conducts are added
Mill ball, carries out high-energy ball milling, and rotational speed of ball-mill is 5000r/min, and Ball-milling Time is 40min;
(3) it is dried:Material Jing after step (2) ball milling is put in blowing-type drying baker after sucking filtration and is done through washing
Dry, baking temperature is 120 DEG C, and drying time is 2h;
(4) sample preparation:The dried material of step (3) is carried out into sample preparation crushing.
Embodiment 3
A kind of composite white pigment, the composite white pigment is made up of following parts by weight ingredient:
Prepared by following steps:
(1) slurrying:By 80g calcium carbonate fine powders, 30g clear glass micropowders, 10g nano-calcium carbonates, 20g nano silicons
Mix by weight with 9g waterglass, add 300g water to make suspended slurry;
(2) high-energy ball milling:Suspended slurry obtained in step (1) is poured in ball grinder, 9.0g zirconia ball conducts are added
Mill ball, carries out high-energy ball milling, and rotational speed of ball-mill is 5000r/min, and Ball-milling Time is 30min;
(3) it is dried:Material Jing after step (2) ball milling is put in blowing-type drying baker after sucking filtration and is done through washing
Dry, baking temperature is 120 DEG C, and drying time is 2h;
(4) sample preparation:The dried material of step (3) is carried out into sample preparation crushing.
Embodiment 4
A kind of composite white pigment, the composite white pigment is made up of following parts by weight ingredient:
Prepared by following steps:
(1) slurrying:By 70g calcium carbonate fine powders, 30g clear glass micropowders, 5g nano-calcium carbonates, 5g Nano silica sols and 5g
Waterglass mixes by weight, adds 450g water to make suspended slurry;
(2) high-energy ball milling:Suspended slurry obtained in step (1) is poured in ball grinder, 5.7g zirconia ball conducts are added
Mill ball, carries out high-energy ball milling, and rotational speed of ball-mill is 3000r/min, and Ball-milling Time is 50min;
(3) it is dried:Material Jing after step (2) ball milling is put in blowing-type drying baker after sucking filtration and is done through washing
Dry, baking temperature is 120 DEG C, and drying time is 2h;
(4) sample preparation:The dried material of step (3) is carried out into sample preparation crushing.
Embodiment 5
A kind of composite white pigment, the composite white pigment is made up of following parts by weight ingredient:
Prepared by following steps:
(1) slurrying:By 70g calcium carbonate fine powders, 40g clear glass micropowders, 10g nano-calcium carbonates, 10g nano titanium oxides
Mix by weight with 10g waterglass, add 300g water to make suspended slurry;
(2) high-energy ball milling:Suspended slurry obtained in step (1) is poured in ball grinder, 8.6g zirconia ball conducts are added
Mill ball, carries out high-energy ball milling, and rotational speed of ball-mill is 4000r/min, and Ball-milling Time is 30min;
(3) it is dried:Material Jing after step (2) ball milling is put in blowing-type drying baker after sucking filtration and is done through washing
Dry, baking temperature is 120 DEG C, and drying time is 2h;
(4) sample preparation:The dried material of step (3) is carried out into sample preparation crushing.
Embodiment 6
A kind of composite white pigment, the composite white pigment is made up of following parts by weight ingredient:
Prepared by following steps:
(1) slurrying:By 65g calcium carbonate fine powders, 35g clear glass micropowders, 10g nano-calcium carbonates, 5g nano silicons
Mix by weight with 7g waterglass, add 200g water to make suspended slurry;
(2) high-energy ball milling:Suspended slurry obtained in step (1) is poured in ball grinder, 6.5g zirconia ball conducts are added
Mill ball, carries out high-energy ball milling, and rotational speed of ball-mill is 3500r/min, and Ball-milling Time is 40min;
(3) it is dried:Material Jing after step (2) ball milling is put in blowing-type drying baker after sucking filtration and is done through washing
Dry, baking temperature is 120 DEG C, and drying time is 2h;
(4) sample preparation:The dried material of step (3) is carried out into sample preparation crushing.
Embodiment 7
A kind of composite white pigment, the composite white pigment is made up of following parts by weight ingredient:
Prepared by following steps:
(1) slurrying:By 65g calcium carbonate fine powders, 40g clear glass micropowders, 10g nano titanium oxides and 9g waterglass by weight
Amount part mixing, adds 200g water to make suspended slurry;
(2) high-energy ball milling:Suspended slurry obtained in step (1) is poured in ball grinder, 7.6g zirconia ball conducts are added
Mill ball, carries out high-energy ball milling, and rotational speed of ball-mill is 4000r/min, and Ball-milling Time is 30min;
(3) it is dried:Material Jing after step (2) ball milling is put in blowing-type drying baker after sucking filtration and is done through washing
Dry, baking temperature is 120 DEG C, and drying time is 2h;
(4) sample preparation:The dried material of step (3) is carried out into sample preparation crushing.
Embodiment 8
A kind of composite white pigment, the composite white pigment is made up of following parts by weight ingredient:
Prepared by following steps:
(1) slurrying:By 60g calcium carbonate fine powders, 35g clear glass micropowders, 10g nano silicons and 8g waterglass by weight
Amount part mixing, adds 150g water to make suspended slurry;
(2) high-energy ball milling:Suspended slurry obtained in step (1) is poured in ball grinder, 4.5g zirconia ball conducts are added
Mill ball, carries out high-energy ball milling, and rotational speed of ball-mill is 4000r/min, and Ball-milling Time is 40min;
(3) it is dried:Material Jing after step (2) ball milling is put in blowing-type drying baker after sucking filtration and is done through washing
Dry, baking temperature is 120 DEG C, and drying time is 2h;
(4) sample preparation:The dried material of step (3) is carried out into sample preparation crushing.
Embodiment 9
A kind of composite white pigment, the composite white pigment is made up of following parts by weight ingredient:
Prepared by following steps:
(1) slurrying:By 60g calcium carbonate fine powders, 40g clear glass micropowders, 5g nano-calcium carbonates, 5g nano silicons and
7g waterglass mixes by weight, adds 250g water to make suspended slurry;
(2) high-energy ball milling:Suspended slurry obtained in step (1) is poured in ball grinder, 5.0g zirconia ball conducts are added
Mill ball, carries out high-energy ball milling, and rotational speed of ball-mill is 3500r/min, and Ball-milling Time is 40min;
(3) it is dried:Material Jing after step (2) ball milling is put in blowing-type drying baker after sucking filtration and is done through washing
Dry, baking temperature is 120 DEG C, and drying time is 2h;
(4) sample preparation:The dried material of step (3) is carried out into sample preparation crushing.
Embodiment 10
A kind of composite white pigment, the composite white pigment is made up of following parts by weight ingredient:
Prepared by following steps:
(1) slurrying:By 50g calcium carbonate fine powders, 50g clear glass micropowders, 5g nano titanium oxides and 5g waterglass by weight
Amount part mixing, adds 150g water to make suspended slurry;
(2) high-energy ball milling:Suspended slurry obtained in step (1) is poured in ball grinder, 6.0g zirconia ball conducts are added
Mill ball, carries out high-energy ball milling, and rotational speed of ball-mill is 4000r/min, and Ball-milling Time is 30min;
(3) it is dried:Material Jing after step (2) ball milling is put in blowing-type drying baker after sucking filtration and is done through washing
Dry, baking temperature is 120 DEG C, and drying time is 2h;
(4) sample preparation:The dried material of step (3) is carried out into sample preparation crushing.
Comparative example
A kind of composite white pigment, the composite white pigment is made up of following parts by weight ingredient:
Prepared by following steps:
(1) slurrying:By 90g calcium carbonate fine powders, 10g nano-calcium carbonates, 10g nano titanium oxides and 10g waterglass by weight
Amount part mixing, adds 150g water to make suspended slurry;
(2) high-energy ball milling:Suspended slurry obtained in step (1) is poured in ball grinder, 5.6g zirconia ball conducts are added
Mill ball, carries out high-energy ball milling, and rotational speed of ball-mill is 3000r/min, and Ball-milling Time is 60min;
(3) it is dried:Material Jing after step (2) ball milling is put in blowing-type drying baker after sucking filtration and is done through washing
Dry, baking temperature is 120 DEG C, and drying time is 2h;
(4) sample preparation:The dried material of step (3) is carried out into sample preparation crushing.
The composition and physical parameter of composite titanium dioxide prepared by various embodiments of the present invention is as shown in table 1.
Table 1
As seen from the above table:1st, nano titanium oxide constituent content is higher in above-described embodiment, and the whiteness of composite granule has one
Fixed raising;2nd, the content of superfine glass micropowder component is higher in above-described embodiment, and covering power performance is significantly improved.
Claims (10)
1. a kind of composite white pigment, it is characterised in that the composite white pigment is made up of following parts by weight ingredient:
2. composite white pigment according to claim 1, it is characterised in that the calcium carbonate fine powder grain diameter size is
325~2500 mesh, Blue Whiteness value is 92~97;The clear glass micro powder granule size be 325~2500 mesh, blue light
Whiteness value is 90~95, and described 700~900 DEG C of heat treatments of clear glass micropowder Jing realize its controlled micro crystallization.
3. composite white pigment according to claim 1, it is characterised in that the super fine is nano-calcium carbonate, receives
At least one in rice titanium dioxide, nano silicon and Nano silica sol.
4. composite white pigment according to claim 1, it is characterised in that the composite white pigment is by following weight portion
Into being grouped into:
5. composite white pigment according to claim 1, it is characterised in that the composite white pigment is by following weight portion
Into being grouped into:
6. composite white pigment according to claim 1, it is characterised in that the composite white pigment is by following weight portion
Into being grouped into:
7. composite white pigment according to claim 1, it is characterised in that the composite white pigment is by following weight portion
Into being grouped into:
8. composite white pigment according to claim 1, it is characterised in that the composite white pigment is by following weight portion
Into being grouped into:
9. a kind of preparation method of the composite white pigment according to any one of claim 1~8, it is characterised in that include
Following steps:
(1) slurrying:Oxide spinel calcium micropowder, clear glass micropowder, super fine and waterglass are mixed by weight, water is added
Suspended slurry is made, the addition of the water is 1~4 times of raw materials quality summation;
(2) high-energy ball milling:By suspended slurry high-energy ball milling together with mill ball obtained in step (1);
(3) it is dried:Material Jing after step (2) ball milling is dried through washing, sucking filtration;
(4) sample preparation:The dried material of step (3) is carried out into sample preparation crushing.
10. the preparation method of composite white pigment according to claim 9, it is characterised in that in step (2) is described outstanding
Turbid slurry is 50~100 with the mass ratio of mill ball:1, rotational speed of ball-mill be 3000~5000r/min, Ball-milling Time be 30~
60min。