CN106589793A - Automotive windscreen - Google Patents
Automotive windscreen Download PDFInfo
- Publication number
- CN106589793A CN106589793A CN201611228275.6A CN201611228275A CN106589793A CN 106589793 A CN106589793 A CN 106589793A CN 201611228275 A CN201611228275 A CN 201611228275A CN 106589793 A CN106589793 A CN 106589793A
- Authority
- CN
- China
- Prior art keywords
- parts
- nanometer
- acid
- phenolic resin
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an automotive windscreen and relates to the technical field of automotive parts. The automotive windscreen comprises the following raw materials, by weight, of 30-40 parts of glass fiber yarns, 10-15 parts of phenolic resin, 1-5 parts of nanometer rubber, 0.5-1 part of turpentine, 1-5 parts of pinonic acid, 1-5 parts of nanometer calcareous shale, 1-5 parts of silicon dioxide, 1-5 parts of boric acid, 1-5 parts of ethylenediamine and 1-10 parts of water. According to the automotive windscreen, the phenolic resin, the nanometer rubber, the turpentine, the pinonic acid, the nanometer calcareous shale, the silicon dioxide and the boric acid are added, and therefore, the properties, such as strength, heat resistance, aging resistance and water resistance, of product materials are increased.
Description
Technical field
The present invention relates to technical field of automobile, especially a kind of windshield.
Background technology
Automobile door protection panel is that a kind of surface area is big, the single structure part of arc, and it requires to possess excellent intensity, resistance to
Hot, resistance to ag(e)ing and resistance to water etc..However, with the continuous development of automobile industry, it is wanted to windshield performance
Seek also more and more higher.
The content of the invention
The invention provides a kind of windshield, wants so as to meet automobile industry to windshield performance
Ask.
In order to solve above-mentioned technical problem, the technical solution adopted in the present invention is:
It is prepared from the following raw materials in parts by weight:
30 parts~40 parts of glass fiber yarn, 10 parts~15 parts of phenolic resin, 1 part~5 parts of nano-rubber, turpentine oil 0.5 part~1
Part, 1 part~5 parts of 1 part~5 part, nanometer calcareous shale of pinonic acid, silica 1 part~5 part, 1 part~5 parts of boric acid, ethylenediamine 1
Part~5 parts and 1 part~10 parts of water.
In above-mentioned technical proposal, more specifically technical scheme can also be:36 parts of glass fiber yarn, 14 parts of phenolic resin,
1 part of nano-rubber, 0.5 part of turpentine oil, 5 parts of 5 part, nanometer calcareous shale of pinonic acid, silica 1 part, 3 parts of boric acid, ethylenediamine 5
6 parts of part and water.
Due to adopting above-mentioned technical proposal, the beneficial effect that the present invention is obtained to be:
It is of the invention main by addition phenolic resin, nano-rubber, turpentine oil, pinonic acid, nanometer calcareous shale, silica and
Boric acid, so as to improve the performance such as intensity, heat resistance, resistance to ag(e)ing and resistance to water of resulting material.
Specific embodiment
Below in conjunction with specific embodiment, the invention will be further described, and protection scope of the present invention is not only limited to
In following examples.
Embodiment 1 --- windshield
It is made using following raw material:
Glass fiber yarn 3600g, phenolic resin 1400g, nano-rubber 100g, turpentine oil 0.500g, pinonic acid 500g, nanometer calcium
Matter shale 500g, silica 1 00g, boric acid 300g, ethylenediamine 500g and water 600g.
Embodiment 2 --- windshield
It is made using following raw material:
Glass fiber yarn 3000g, phenolic resin 1000g, nano-rubber 300g, turpentine oil 0.700g, pinonic acid 300g, nanometer calcium
Matter shale 100g, silica 300g, boric acid 100g, ethylenediamine 100g and water 100g.
Embodiment 3 --- windshield
It is made using following raw material:
Glass fiber yarn 4000g, phenolic resin 1500g, nano-rubber 500g, turpentine oil 100g, pinonic acid 100g, nanometer are calcareous
Shale 300g, silica 500g, boric acid 500g, ethylenediamine 300g and water 1000g.
The mechanical property of product is as shown in table 1 obtained by 1~embodiment of above-described embodiment 3.
Table 1
。
Claims (2)
1. a kind of windshield, it is characterised in that be prepared from the following raw materials in parts by weight:
30 parts~40 parts of glass fiber yarn, 10 parts~15 parts of phenolic resin, 1 part~5 parts of nano-rubber, turpentine oil 0.5 part~1
Part, 1 part~5 parts of 1 part~5 part, nanometer calcareous shale of pinonic acid, silica 1 part~5 part, 1 part~5 parts of boric acid, ethylenediamine 1
Part~5 parts and 1 part~10 parts of water.
2. windshield according to claim 1, it is characterised in that:36 parts of glass fiber yarn, 14 parts of phenolic resin,
1 part of nano-rubber, 0.5 part of turpentine oil, 5 parts of 5 part, nanometer calcareous shale of pinonic acid, silica 1 part, 3 parts of boric acid, ethylenediamine 5
6 parts of part and water.