CN106589646A - Novel polystyrene modified fluorescent material - Google Patents

Novel polystyrene modified fluorescent material Download PDF

Info

Publication number
CN106589646A
CN106589646A CN201611183993.6A CN201611183993A CN106589646A CN 106589646 A CN106589646 A CN 106589646A CN 201611183993 A CN201611183993 A CN 201611183993A CN 106589646 A CN106589646 A CN 106589646A
Authority
CN
China
Prior art keywords
parts
fluorescent material
modified fluorescent
polystyrene
methyl
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611183993.6A
Other languages
Chinese (zh)
Inventor
曾铁球
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FOSHAN CITY GAOMING DISTRICT PLASTICS INDUSTRY ASSOCIATION
Original Assignee
FOSHAN CITY GAOMING DISTRICT PLASTICS INDUSTRY ASSOCIATION
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FOSHAN CITY GAOMING DISTRICT PLASTICS INDUSTRY ASSOCIATION filed Critical FOSHAN CITY GAOMING DISTRICT PLASTICS INDUSTRY ASSOCIATION
Priority to CN201611183993.6A priority Critical patent/CN106589646A/en
Publication of CN106589646A publication Critical patent/CN106589646A/en
Pending legal-status Critical Current

Abstract

The invention provides a novel polystyrene modified fluorescent material and relates to the technical field of high polymer materials. The novel polystyrene modified fluorescent material is prepared from raw materials as follows: 120-140 parts of polystyrene, 13-19 parts of aluminum hydroxide, 7-14 parts of hexabromocyclododecane, 5-11 parts of phthalic acid diundecyl ester, 28-35 parts of epoxy oleic acid n-butyl ester, 23-29 parts of methyl acrylate, 12-17 parts of polyvinyl alcohol, 11-16 parts of polyvinyl acetate, 21-28 parts of glycerol trioleate, 3-7 parts of methyl palmitate, 15-20 parts of methyl triethoxysilane, 7-13 parts of diethyl n-butylmalonate, 25-32 parts of tributyl acetocitrate, 16-23 parts of nanometer magnesia, 32-39 parts of photo-induced energy-storage noctilucent powder, 7-16 parts of a plasticizer and 14-22 parts of a wear-resistant agent. The novel polystyrene modified fluorescent material has beneficial effects as follows: the polystyrene modified fluorescent material has the luminous function, and the location distinguishing degree in the dark place is increased.

Description

A kind of ethylene modified fluorescent material of novel polyphenyl
Technical field
The present invention relates to technical field of polymer materials, the especially a kind of ethylene modified fluorescent material of novel polyphenyl.
Background technology
Polystyrene (Polystyrene, abridge PS) was referred to by gathering that styrene monomer Jing free radical polymerizations synthesize Compound, the product of traditional polystyrene has high transparency, and light transmittance can reach more than 90%, with electrical insulating property The advantages of good, easy coloring of energy, good processing fluidity, good rigidity and resistance to chemical attack.But it is also fewer at present to be related to polyphenyl Ethene has the data introduction in terms of fluorescence, which has limited polystyrene material application in this regard.
The content of the invention
Instant invention overcomes shortcoming of the prior art, there is provided a kind of ethylene modified fluorescent material of novel polyphenyl, gather this Phenylethene modified fluorescent material has lighting function, improves location identification degree in the dark.
In order to solve above-mentioned technical problem, the present invention is achieved by the following technical solutions:
A kind of ethylene modified fluorescent material of novel polyphenyl, constitutive material includes:Polystyrene 120-140 parts, aluminium hydroxide 13-19 parts, HBCD 7-14 parts, phthalic acid double 11 ester 5-11 parts, epoxyoleic acid butyl ester 28-35 part, propylene Sour methyl esters 23-29 parts, polyvinyl alcohol 12-17 parts, polyvinyl acetate 11-16 parts, glycerol trioleate 21-28 parts, palmitic acid Methyl esters 3-7 parts, MTES 15-20 parts, diethyl butylmalonate 7-13 parts, citroflex A-4 25-32 parts, excessively nano magnesia 16-23 parts, photo-induced energy storage luminescent powder 32-39 parts, plasticizer 7-16 parts, anti-wear agent 14-22 parts.
Further, a kind of described ethylene modified fluorescent material of novel polyphenyl, constitutive material includes:Polystyrene 130 Part, 15 parts of aluminium hydroxide, 11 parts of HBCD, phthalic acid double 8 parts of 11 ester, 32 parts of epoxyoleic acid butyl ester, propylene 28 parts of sour methyl esters, 15 parts of polyvinyl alcohol, 15 parts of polyvinyl acetate, 24 parts of glycerol trioleate, 5 parts of methyl hexadecanoate, methyl 18 parts of triethoxysilane, 11 parts of diethyl butylmalonate, excessively 28 parts of citroflex A-4, nano magnesia 19 Part, 35 parts of photo-induced energy storage luminescent powder, 11 parts of plasticizer, 19 parts of anti-wear agent.
Further, a kind of preparation method of the described ethylene modified fluorescent material of novel polyphenyl, comprises the following steps:
(1) by polystyrene, aluminium hydroxide, HBCD, double 11 esters of phthalic acid, epoxyoleic acid butyl ester, Methyl acrylate, polyvinyl alcohol, polyvinyl acetate, glycerol trioleate, methyl hexadecanoate, MTES, just Diethyl butylmalonate, citroflex A-4 and mistake nano magnesia are put in blender and are blended, the temperature of blending Degree is 63-68 DEG C, and the blending time is 40-45min;
(2) step (1) material, photo-induced energy storage luminescent powder, plasticizer and anti-wear agent are together put in mixer, with The speed of 88-95r/min, stirs 50-60min;
(3) the material double screw extruder in step (2) is extruded, pelletizing obtains pellet, as described novel polyphenyl Ethylene modified fluorescent material.
Compared with prior art, the invention has the beneficial effects as follows:
The Polystyrene fluorescent material that the present invention makes can absorb luminous energy, store, and can stop After light irradiation, then lentamente discharged in the way of fluorescence, the material can be applied and used under environment dimmed suddenly, be improved The location recognition degree of the material product.
Specific embodiment
The preferred embodiments of the present invention are illustrated below, it will be appreciated that preferred embodiment described herein is only used In the description and interpretation present invention, it is not intended to limit the present invention.
The preparation method of the ethylene modified fluorescent material of novel polyphenyl of the present invention, comprises the following steps:
(1) by polystyrene, aluminium hydroxide, HBCD, double 11 esters of phthalic acid, epoxyoleic acid butyl ester, Methyl acrylate, polyvinyl alcohol, polyvinyl acetate, glycerol trioleate, methyl hexadecanoate, MTES, just Diethyl butylmalonate, citroflex A-4 and mistake nano magnesia are put in blender and are blended, the temperature of blending Degree is 65 DEG C, and the blending time is 43min;
(2) step (1) material, photo-induced energy storage luminescent powder, plasticizer and anti-wear agent are together put in mixer, with The speed of 92r/min, stirs 55min;
(3) the material double screw extruder in step (2) is extruded, pelletizing obtains pellet, as described novel polyphenyl Ethylene modified fluorescent material.
Embodiment 1
A kind of ethylene modified fluorescent material of novel polyphenyl, constitutive material includes:130 parts of polystyrene, 15 parts of aluminium hydroxide, 11 parts of HBCD, phthalic acid double 8 parts of 11 ester, 32 parts of epoxyoleic acid butyl ester, 28 parts of methyl acrylate, polyethylene 15 parts of alcohol, 15 parts of polyvinyl acetate, 24 parts of glycerol trioleate, 5 parts of methyl hexadecanoate, 18 parts of MTES, 11 parts of diethyl butylmalonate, excessively 28 parts of citroflex A-4,19 parts of nano magnesia, photo-induced energy storage luminescent powder 35 parts, 11 parts of plasticizer, 19 parts of anti-wear agent.
Embodiment 2
A kind of ethylene modified fluorescent material of novel polyphenyl, constitutive material includes:120 parts of polystyrene, 13 parts of aluminium hydroxide, 7 parts of HBCD, phthalic acid double 5 parts of 11 ester, 28 parts of epoxyoleic acid butyl ester, 23 parts of methyl acrylate, polyethylene 12 parts of alcohol, 11 parts of polyvinyl acetate, 21 parts of glycerol trioleate, 3 parts of methyl hexadecanoate, 15 parts of MTES, 7 parts of diethyl butylmalonate, excessively 25 parts of citroflex A-4,16 parts of nano magnesia, photo-induced energy storage luminescent powder 32 parts, 7 parts of plasticizer, 14 parts of anti-wear agent.
Embodiment 3
A kind of ethylene modified fluorescent material of novel polyphenyl, constitutive material includes:140 parts of polystyrene, 19 parts of aluminium hydroxide, 14 parts of HBCD, phthalic acid double 11 parts of 11 ester, 35 parts of epoxyoleic acid butyl ester, 29 parts of methyl acrylate, poly- second 17 parts of enol, 16 parts of polyvinyl acetate, 28 parts of glycerol trioleate, 7 parts of methyl hexadecanoate, MTES 20 Part, excessively 13 parts of diethyl butylmalonate, 32 parts of citroflex A-4,23 parts of nano magnesia, photo-induced energy storage night 39 parts of light powder, 16 parts of plasticizer, 22 parts of anti-wear agent.
With wattage be the incandescent lamp of 40W to embodiment 1, embodiment 2 and the sample irradiation 30min of embodiment 3, then by embodiment 1st, embodiment 2 and the sample of embodiment 3 are placed into dark place, and observable sends light, and three's average duration is 10.8h.
Finally it should be noted that:The preferred embodiments of the present invention are these are only, the present invention is not limited to, although The present invention is described in detail with reference to embodiment, for a person skilled in the art, it still can be to aforementioned Technical scheme described in each embodiment is modified, or equivalent is carried out to which part technical characteristic, but it is all Within the spirit and principles in the present invention, any modification, equivalent substitution and improvements made etc. should be included in the protection of the present invention Within the scope of.

Claims (3)

1. the ethylene modified fluorescent material of a kind of novel polyphenyl, it is characterised in that constitutive material includes:Polystyrene 120-140 parts, Aluminium hydroxide 13-19 parts, HBCD 7-14 parts, phthalic acid double 11 ester 5-11 parts, epoxyoleic acid butyl esters 28-35 Part, methyl acrylate 23-29 parts, polyvinyl alcohol 12-17 parts, polyvinyl acetate 11-16 parts, glycerol trioleate 21-28 parts, Methyl hexadecanoate 3-7 parts, MTES 15-20 parts, diethyl butylmalonate 7-13 parts, acetyl citrate Tributyl 25-32 parts, excessively nano magnesia 16-23 parts, photo-induced energy storage luminescent powder 32-39 parts, plasticizer 7-16 parts, anti-wear agent 14-22 parts.
2. a kind of ethylene modified fluorescent material of novel polyphenyl according to claim 1, it is characterised in that constitutive material bag Include:130 parts of polystyrene, 15 parts of aluminium hydroxide, 11 parts of HBCD, phthalic acid double 8 parts of 11 ester, epoxyoleic acids 32 parts of butyl ester, 28 parts of methyl acrylate, 15 parts of polyvinyl alcohol, 15 parts of polyvinyl acetate, 24 parts of glycerol trioleate, palmitic acid 5 parts of methyl esters, 18 parts of MTES, 11 parts of diethyl butylmalonate, 28 parts of citroflex A-4, mistake 19 parts of nano magnesia, 35 parts of photo-induced energy storage luminescent powder, 11 parts of plasticizer, 19 parts of anti-wear agent.
3. a kind of preparation method of the ethylene modified fluorescent material of novel polyphenyl according to claim 1 and 2, its feature exists In comprising the following steps:
(1) by polystyrene, aluminium hydroxide, HBCD, phthalic acid double 11 esters, epoxyoleic acid butyl ester, propylene Sour methyl esters, polyvinyl alcohol, polyvinyl acetate, glycerol trioleate, methyl hexadecanoate, MTES, normal-butyl Diethyl malonate, citroflex A-4 and mistake nano magnesia are put in blender and are blended, and the temperature of blending is 63-68 DEG C, the blending time is 40-45min;
(2) step (1) material, photo-induced energy storage luminescent powder, plasticizer and anti-wear agent are together put in mixer, with 88- The speed of 95r/min, stirs 50-60min;
(3) the material double screw extruder in step (2) is extruded, pelletizing obtains pellet, as described novel polyphenyl ethene Modified fluorescent material.
CN201611183993.6A 2016-12-20 2016-12-20 Novel polystyrene modified fluorescent material Pending CN106589646A (en)