CN106587658B - A kind of glass fiber infiltration agent and application thereof - Google Patents
A kind of glass fiber infiltration agent and application thereof Download PDFInfo
- Publication number
- CN106587658B CN106587658B CN201610963776.2A CN201610963776A CN106587658B CN 106587658 B CN106587658 B CN 106587658B CN 201610963776 A CN201610963776 A CN 201610963776A CN 106587658 B CN106587658 B CN 106587658B
- Authority
- CN
- China
- Prior art keywords
- agent
- film forming
- size
- forming agent
- glass fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides a kind of glass fiber infiltration agents, the size includes coupling agent, lubricant, film forming agent A, film forming agent B, pH adjusting agent and water, coupling agent is containing vinyl, metacryloxy, one of amino or the silane coupling agent of epoxy group are a variety of, film forming agent A is polyester resin emulsion, film forming agent B is epoxy resin latex, wherein, the solid masses of size accounts for the 4~12% of size gross mass, the present invention is compounded using the film forming agent of different type and high-content, and with suitable coupling agent, lubricant and pH adjusting agent match fast wetting-out rate is prepared, the good size of com-patibilising effect.Soft using yarn made from the size, wetting-out rate is fast, and possesses excellent pultrusion performance, while having good resin compatible.The present invention also provides purposes of the size on the pultrusion molding process of the enhanced umbrella frame of alkali-free glass fibre.
Description
Technical field
The present invention relates to size field more particularly to a kind of glass fiber infiltration agent with and application thereof.
Background technique
From the nineties, China starts to introduce pultrusion molding process from the U.S. to produce glass fiber compound material profile,
Moulding process flow process is as follows: the woven glass roving fabric as reinforcing material is soaking under the action of extruding equipment tractive force
After being sufficiently impregnated in glue groove, a series of conjunction by preforming templates is oriented to, and is tentatively formed, finally enters and be heated
Metal die, solidification is reacted under certain temperature action, to obtain continuous, smooth surface, dimensionally stable, high intensity
Composite material section bar.
Glass fibre as pultrusion molding process will do it size coating processing, and size using and selecting not only
It is most important to the processability of glass fiber compound material profile, and have an effect on the phase of subsequent glass fibre with matrix resin
The mechanical performance of capacitive and product.For example, by taking the actual production of enhanced umbrella frame as an example, the choosing of size during being somebody's turn to do
Select it is most important, if selection it is improper, on the one hand, easily there is the problems such as yarn is really up to the mark or wetting-out rate is slow in glass fibre, in turn
Product in pultrusion molding process is led to problems such as surface missing yarn, surface groove mark, face crack occur;On the other hand, it will affect glass
The compatibility of glass fiber and matrix resin, and then the mechanical performance of product is influenced, and umbrella frame is especially curved to mechanical performance
Bent intensity requirement is higher, because the performance is directly related with the wind loading rating of umbrella.
Also, the demand of high-end customer is had been unable to meet using the product that medium-alkali glass fibre is enhanced in the market: in
Alkali containing glass fibre generally uses saving of platinum alloy to be produced, and easily leads to unstable product quality, and medium-alkali glass fibre alkali metal
Content is high, easily there is the problems such as product aging is fast, and the quality of item for using alkali-free glass fibre to enhance is more preferably, especially intensity
Etc. mechanical performances be far superior to medium-alkali glass fibre.
Therefore, it is asked to solve the fiberglass reinforced articles mechanical performance for pultrusion and produce molding technology
Topic, develop a kind of dedicated glass fiber infiltration agent, especially for enhancing umbrella frame e-glass fiber infiltrant
It is extremely urgent and significant to the actual production of the fiberglass reinforced articles for pultrusion.
Summary of the invention
Present invention seek to address that problem as described above.The object of the present invention is to provide a kind of glass fiber infiltration agents, should
Size keeps glass fiber yarn soft, wetting-out rate is fast, possesses excellent by the physics and chemical property of change fiberglass surfacing
Different pultrusion performance, while there is good resin compatible, greatly improve the mechanical performance of composite article.
The present invention provides a kind of glass fiber infiltration agent, and the size includes coupling agent, lubricant, film forming agent A, film forming
Agent B, pH adjusting agent and water, the coupling agent are the silane coupling agent containing vinyl, metacryloxy, amino or epoxy group
One of or it is a variety of, the film forming agent A is polyester resin emulsion, the film forming agent B is epoxy resin latex, wherein described
The solid masses of size accounts for the 4~12% of size gross mass;Also, the solid masses of each component accounts for the size solid
The percentage of gross mass is as follows:
Also, the pH value control of the size is 2~7.
The percentage that the solid masses of each component accounts for the size solid gross mass is as follows:
Wherein, the solid masses of each component account for the size solid gross mass percentage it is as follows:
Wherein, the coupling agent includes three ethoxy of γ-methacryloxypropyl trimethoxy silane and γ-aminopropyl
Base silane, also, the solid masses of the γ-methacryloxypropyl trimethoxy silane accounts for size solid gross mass
6~8%, the solid masses of the gamma-aminopropyl-triethoxy-silane accounts for the 1~3% of size solid gross mass.
Wherein, the film forming agent A is Emulsion of UPR, and number-average molecular weight is 500~1000.
Wherein, the film forming agent B is epoxy resin latex, and number-average molecular weight is 300~800.
Wherein, the coupling agent is γ-methacryloxypropyl trimethoxy silane, gamma-aminopropyl-triethoxy
One in silane, γ-(2,3- glycidoxy) propyl trimethoxy silicane and vinyl three ('beta '-methoxy ethyoxyl) silane
Kind is a variety of;The lubricant is PEG series lubricant agent;The pH adjusting agent is one in acetic acid, citric acid, hydrochloric acid and formic acid
Kind is a variety of.
Wherein, the size is made of coupling agent, lubricant, film forming agent, pH adjusting agent and water, and the film forming
Agent is the composition of Emulsion of UPR and epoxy resin latex, and the solid masses of each component accounts for the size solid
The percentage of gross mass is as follows:
Also, the pH value control of the size is 3~6.
Wherein, the number-average molecular weight of the Emulsion of UPR is 500~1000, the epoxy resin latex
Number-average molecular weight is 300~800.
Wherein, the glass fiber infiltration agent is the glass fiber infiltration agent for enhancing umbrella frame.
The present invention is especially suitable for the pultrusion molding process of umbrella frame, and particularly, the present invention also provides above-mentioned sizes
Purposes on the pultrusion molding process of the enhanced umbrella frame of alkali-free glass fibre.
The glass fiber infiltration agent provided according to the present invention, main innovative point are the film forming agents by high-content, in right amount
Coupling agent, lubricant and pH adjusting agent wetting-out rate is fast to be prepared, the good size of com-patibilising effect, specifically, leaching
Profit agent includes coupling agent, lubricant, film forming agent A, film forming agent B, pH adjusting agent and water, and the coupling agent is containing vinyl, first
One of silane coupling agent of base propenyloxy group, amino or epoxy group is a variety of, the film forming agent A be polyester resin emulsion,
The film forming agent B is epoxy resin latex, wherein the solid masses of the size accounts for the 4~12% of size gross mass;And
And the solid masses of each component account for the size solid gross mass percentage it is as follows:
Also, the pH value control of the size is 2~7.
The effect of each component and content are described as follows in the size:
Coupling agent, also known as bridging agent, containing organic from inorganic two different functional groups, Inorganic functional groups can be with for its own
The hydroxyl of glass surface reacts, and another organo-functional group can react with enhanced matrix resin, serves as a connection.
The use of coupling agent can play the coupled action between glass fibre and matrix resin, on the one hand can reduce glass fibre in wire drawing
On the other hand the extent of damage in the process still influences the key of glass fiber strength and composite article intensity.
Common coupling agent is silane coupling agent, inventors discovered through research that, contain vinyl, metacryloxy, ammonia
Base or the coupling agent of epoxy group and film forming agent provided by the present application, lubricant cooperate, can effectively improve glass fibre with
The compatibility of resin.The solid masses accounting of coupling agent should not be too large, and the solid masses that the present invention limits coupling agent accounts for size
3~15%, preferably 5~15%, more preferably the 5~13% of solid gross mass.Further, inventor has found γ-methyl
Acryloyloxypropyltrimethoxysilane, gamma-aminopropyl-triethoxy-silane, γ-(2,3- glycidoxy) propyl front three
Oxysilane and vinyl three ('beta '-methoxy ethyoxyl) silane are highly suitable for the present invention, the infiltration prepared using the coupling agent
Agent, can make glass fibre composite article, and especially enhancing umbrella frame has better mechanical performance.
Most preferably, inventor is had found by numerous studies, and γ-methacryloxy third is used in above-mentioned coupling agent
Base trimethoxy silane and gamma-aminopropyl-triethoxy-silane progress compounding effect are best, glass fiber reinforced composite product tool
The standby bending strength being obviously improved, and unsuitable excessively high, the γ-ammonia of too high amount of content of gamma-aminopropyl-triethoxy-silane
Propyl-triethoxysilicane will lead to yarn and be hardened, and wetting-out rate is slack-off, most preferably, γ-methacryloxypropyl three
The solid masses of methoxy silane accounts for the 6~8% of size solid gross mass, the solid matter of gamma-aminopropyl-triethoxy-silane
Amount accounts for the 1~3% of size solid gross mass.
Lubricant is primarily to guarantee glass fibre in wire drawing, post-processing and the lubricant effect for the processes such as using.Profit
Lubrication prescription content is excessively few to be then not achieved lubricant effect, excessively will affect the caking property between precursor, reduce the stiffness of yarn so that
In will affect being impregnated in matrix resin and compatibility, the mechanical performance to final composite material is caused to have negative effect, this
The solid content of invention lubricant accounts for the 1~10% of size solid amount, and more preferable 1~8%.Lubricant of the present invention is selected
PEG series lubricant agent, PEG series lubricant agent have preferable emulsifiable property, water solubility and low surface tension, have good lubrication
Effect.It further, can inventors have found that PEG600, PEG1000 and PEG3000 high lubricating effect and molecular weight is smaller
Preferably meet the requirement of the high wetting-out rate of the present invention.
Film forming agent is the main component of size, plays conclusive influence to the processing performance of glass fibre, plays guarantor
The effect for protecting glass fibre, the compatibility for improving glass fibre and matrix resin, should guarantee glass fibre in pultrusion
Quick impregnability in technique guarantee again glass fibre and matrix resin compatibility and final composite article machinery it is strong
Degree, therefore, the selection of film forming agent is emphasis of the invention.
Common film forming agent have polyaminoester emulsion, polyester resin emulsion, polyvinyl acetate emulsion, acrylic acid ester emulsion and
Epoxy emulsion, inventor is by a large amount of the study found that film forming agent of the invention is suitble to only have polyester resin emulsion and epoxy cream
Liquid, other kinds of film forming agent can make yarn be hardened, and be unfavorable for the pultrusion molding process of reinforcing material.On the other hand, in this hair
In bright, in order to further increase the wetting-out rate of glass fibre, exceptionally except the necessary group such as coupling agent, lubricant, pH adjusting agent,
Should not be again containing other auxiliary agents such as antistatic agents, therefore, film former content is higher, and solid masses accounts for size solid amount
70~90%, preferably 72~90%, more preferably 75~90%.
Further, film forming agent of the present invention uses the compounded combination of polyester resin emulsion and epoxy emulsion, can meet infiltration
The coating requirement of agent, wherein the solid content of polyester resin emulsion accounts for the 10~80% of size solid amount, preferably 30~
50%;The solid content of epoxy emulsion accounts for the 10~80% of size solid amount, preferably 30~50%, more preferable 35~
50%.
The present invention also further has studied the molecular weight of film forming agent emulsion and the relationship of size performance, and invention is when use
When the agent emulsion molecular weight that forms a film is smaller, corresponding glass fiber yarn is soft, and convergence is poor, but wetting-out rate is fast;And use molecule
When measuring big lotion, corresponding glass fiber yarn is hard, and filoplume is more, and convergence is good, but wetting-out rate is partially slow.And it is unsaturated poly-
Ester resin emulsion plays a leading role on wetting-out rate, and epoxy resin latex convergence is very good, also, unsaturated polyester resin
The number-average molecular weight of lotion need to be greater than the number-average molecular weight of epoxy resin latex, the number-average molecular weight of Emulsion of UPR
It is 500~1000, preferably 800~1000, more preferable 850~1000;The number-average molecular weight of epoxy resin latex is 300~800,
It is preferred that 400~800.The present invention can guarantee that glass fibre possesses good convergence and impregnability using such combine, and draw
It extrudes in product and is uniformly dispersed, filoplume is few, is impregnated with fastly, product surface is smooth, also improves the mechanical strength of pultrusion product.
The present invention is used as pH adjusting agent using acid, and one of acetic acid, citric acid, hydrochloric acid and formic acid or more can be selected
Kind, mainly play a part of to adjust size pH value.The solid masses of pH adjusting agent account for size solid gross mass 0.5~
5%, preferably 1~4%.
The hydrolysis with dispersion of coupling agent need under certain pH environment in size, require to meet dispersion, this hair
Bright size need to control as slant acidity environment, and pH value is 2~7, preferably 3~6.Size provided by the invention makes glass
Glass fiber has good convergence and impregnability, is very suitable to the pultrusion molding process of glass fiber reinforced composite product, and
Composite article obtained, especially umbrella frame have excellent mechanical performance.Further, which is particularly suitable for alkali-free
The enhancing of glass fibre, composite article obtained can satisfy the demand of high-end customer.Therefore, the present invention also provides above-mentioned leachings
Moisten purposes of the agent on the pultrusion molding process of the enhanced umbrella frame of alkali-free glass fibre.
If it should be noted that instant component lotion or solution form, the solid masses of the component is after drying
The quality of remainder is the component of liquid or gas for solute, such as when pH adjusting agent is formic acid solution, solid masses
Then in nail acid solution solute formic acid quality.
Water in the present invention primarily serves the effect of each component in dispersion size, and the solid masses of size accounts for size
The 4~12% of gross mass, residual mass are then water, preferably deionized water.
Compared with prior art, the present invention its advantages are embodied in:
First, the application introduces film forming agent and suitable coupling agent, lubricant and pH adjusting agent of high-content etc.
Component effectively improves the wetting-out rate of glass fibre, more conducively reinforcing glass fiber pultrusion molding process.
Second, size provided by the invention use the compounded combination of polyester resin emulsion and epoxy resin latex as at
Film, it is ensured that glass fibre possesses good convergence and impregnability, is uniformly dispersed in pultrusion product, and filoplume is few, is impregnated with
Fastly, product surface is smooth, also improves the mechanical strength of pultrusion product.
Third, size provided by the invention have selected suitable component and proportion, and coating effect is good, not only guarantees glass
Quick impregnability of the fiber in pultrusion molding process, and guarantee the excellent compatibility of glass fibre and matrix resin, make compound
Material has excellent mechanical performance.
The beneficial effect of the selection of size each component and its content of the invention will provide specific experiment by embodiment
Data are illustrated.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with the embodiment of the present invention
Technical scheme in the embodiment of the invention is clearly and completely described, it is clear that described embodiment is the present invention one
Divide embodiment, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not making
Every other embodiment obtained, shall fall within the protection scope of the present invention under the premise of creative work.It should be noted that
In the case where not conflicting, the features in the embodiments and the embodiments of the present application can mutual any combination.
Embodiment
In the embodiment of the present invention, the content of water accounts for the 94% of size gross mass, and it is solid that table 1 shows each component in size
The percent value of size solid gross mass shared by weight, the corresponding numerical value of each component are mass percent/%.Wherein, even
Join agent and uses γ-methacryloxypropyl trimethoxy silane (the production trade mark is A-174), gamma-aminopropyl-triethoxy
Silane (the production trade mark is A-1100), γ-(2,3- glycidoxy) propyl trimethoxy silicane (A-187) and vinyl three
One of ('beta '-methoxy ethyoxyl) silane (A-172) is a variety of;Lubricant uses PEG1000;Film forming agent A uses unsaturated
Polyester resin emulsion (the production trade mark is Neoxil 954);Film forming agent B uses epoxy resin latex (the production trade mark is BH-620);
PH adjusting agent uses acetic acid.
1 size specific embodiment list of table
Wherein, embodiment 1, it is that the coupling agent of A-174 and A-1100 is compounded that the coupling agent of embodiment 4, which selects the trade mark,
The solid content that the solid content of A-174 is 7%, A-1100 in embodiment 1 is 2%;In embodiment 4, the solid of A-174 contains
The solid content that amount is 8%, A-1100 is 3%.It is the coupling agent of A-174 that coupling agent, which selects the trade mark, in the remaining embodiments.
Test case
Above-described embodiment is applied to the production of glass fibre, and by corresponding glass fiber applications in pultrusion molding process
In, such as the pultrusion molding process of umbrella frame, and to its processing performance and finally obtained fiber glass reinforcement into
Row performance test.As a result as follows:
2 different glass fibre property test result of table
From above-mentioned test case it will be seen that using glass fibre performance made from size provided by the invention compared with
It is good, be embodied in mechanical performance (bending strength) and pultrusion molding process performance (filoplume amount, yarn be soft or hard, penetration period, with
The associativity of resin) aspect:
In terms of reinforcing material measuring mechanical property, the average bending strength of 1~embodiment of embodiment 8 is 1861.6MPa.
In terms of pultrusion molding process performance test, the average filoplume amount of glass fibre is 20mg/kg, and average penetration period is 14.8
Second, the convergence of glass fibre is preferable, and yarn is softer, and wetting-out rate is fast, good with the compatibility of resin.
It is further known that using the embodiment 1 and 4 comprehensive performance of embodiment of Compositional type coupling agent in Examples 1 to 8
It is more excellent, and embodiment 8 and resin-bound are slightly worse, it may be possible to since film former content is very few, first and last, Examples 1 to 8
The associativity of glass fibre and resin is preferable, no Bai Si or contains only a small amount of white silk.
In conclusion the present invention have it is following the utility model has the advantages that
First, the application introduces film forming agent and suitable coupling agent, lubricant and pH adjusting agent of high-content etc.
Component effectively improves the wetting-out rate of glass fibre, more conducively reinforcing glass fiber pultrusion molding process.
Second, size provided by the invention use the compounded combination of polyester resin emulsion and epoxy resin latex as at
Film, it is ensured that glass fibre possesses good convergence and impregnability, is uniformly dispersed in pultrusion product, and filoplume is few, is impregnated with
Fastly, product surface is smooth, also improves the mechanical strength of pultrusion product.
Third, size provided by the invention have selected suitable component and proportion, and coating effect is good, not only guarantees glass
Quick impregnability of the fiber in pultrusion molding process, and guarantee the excellent compatibility of glass fibre and matrix resin, make compound
Material has excellent mechanical performance.
Finally, it should be noted that herein, the terms "include", "comprise" or its any other variant are intended to non-
It is exclusive to include, so that the process, method, article or equipment comprising a series of elements not only includes those elements,
It but also including other elements that are not explicitly listed, or further include solid by this process, method, article or equipment
Some elements.In the absence of more restrictions, the element limited by sentence " including one ... ", it is not excluded that including institute
State in the process, method, article or equipment of element that there is also other identical elements.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations.Although with reference to the foregoing embodiments
Invention is explained in detail, those skilled in the art should understand that: it still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features;And these modification or
Replacement, the spirit and scope for technical solution of various embodiments of the present invention that it does not separate the essence of the corresponding technical solution.
Claims (8)
1. a kind of glass fiber infiltration agent, which is characterized in that the size includes coupling agent, lubricant, film forming agent A, film forming
Agent B, pH adjusting agent and water, the coupling agent are the silane coupling agent containing vinyl, metacryloxy, amino or epoxy group
One of or it is a variety of, the film forming agent A is polyester resin emulsion, the film forming agent B is epoxy resin latex, wherein described
The solid masses of size accounts for the 4 ~ 12% of size gross mass;Also, it is total that the solid masses of each component accounts for the size solid
The percentage of quality is as follows:
Coupling agent 3 ~ 15%
Lubricant 1 ~ 10%
Film forming agent A 10 ~ 80%
Film forming agent B 10 ~ 80%
Film forming agent A+ film forming agent B 70 ~ 90%
PH adjusting agent 0.5 ~ 5%;
Also, the pH value control of the size is 2 ~ 7;
The film forming agent A is Emulsion of UPR, and number-average molecular weight is 500 ~ 1000;
The film forming agent B is epoxy resin latex, and number-average molecular weight is 300 ~ 800;
The number-average molecular weight of the Emulsion of UPR is greater than the number-average molecular weight of the epoxy resin latex.
2. glass fiber infiltration agent as described in claim 1, which is characterized in that the solid masses of each component accounts for the size
The percentage of solid gross mass is as follows:
Coupling agent 5 ~ 15%
Lubricant 1 ~ 8%
Film forming agent A 30 ~ 50%
Film forming agent B 30 ~ 50%
Film forming agent A+ film forming agent B 72 ~ 90%
PH adjusting agent 0.5 ~ 5%.
3. glass fiber infiltration agent as described in claim 1, which is characterized in that the solid masses of each component accounts for the size
The percentage of solid gross mass is as follows:
Coupling agent 5 ~ 13%
Lubricant 1 ~ 8%
Film forming agent A 30 ~ 50%
Film forming agent B 35 ~ 50%
Film forming agent A+ film forming agent B 75 ~ 90%
PH adjusting agent 1 ~ 4%.
4. glass fiber infiltration agent as described in claim 1, which is characterized in that the coupling agent includes γ-methacryl
Oxygroup propyl trimethoxy silicane and gamma-aminopropyl-triethoxy-silane, also, the γ-methacryloxypropyl three
The solid masses of methoxy silane accounts for the 6 ~ 8% of size solid gross mass, the solid of the gamma-aminopropyl-triethoxy-silane
Quality accounts for the 1 ~ 3% of size solid gross mass.
5. glass fiber infiltration agent as described in claim 1, which is characterized in that the coupling agent is γ-methacryloxypropyl
Base propyl trimethoxy silicane, gamma-aminopropyl-triethoxy-silane, γ-(2,3- glycidoxy) propyl trimethoxy silicane
With one of vinyl three ('beta '-methoxy ethyoxyl) silane or a variety of;The lubricant is PEG series lubricant agent;The pH value
Regulator is one of acetic acid, citric acid, hydrochloric acid and formic acid or a variety of.
6. glass fiber infiltration agent as described in claim 1, which is characterized in that the size by coupling agent, lubricant, at
Film, pH adjusting agent and water composition, and the film forming agent is the group of Emulsion of UPR and epoxy resin latex
Object is closed, the percentage that the solid masses of each component accounts for the size solid gross mass is as follows:
Coupling agent 3 ~ 15%
Lubricant 1 ~ 10%
Emulsion of UPR 30 ~ 50%
Epoxy resin latex 35 ~ 50%
Film forming agent 70 ~ 90%
PH adjusting agent 0.5 ~ 5%;
Also, the number-average molecular weight of the Emulsion of UPR is 500 ~ 1000, and the number of the epoxy resin latex is equal
Molecular weight is 300 ~ 800, and the pH value control of the size is 3 ~ 6.
7. the glass fiber infiltration agent as described in any one of claim 1 ~ 6, which is characterized in that the size is for increasing
The glass fiber infiltration agent of strong umbrella frame.
8. a kind of glass fiber infiltration agent as described in any one of claim 1 ~ 6 is in the enhanced Umbrella frame of alkali-free glass fibre
Purposes on the pultrusion molding process of frame.