CN106587219A - Polyferric chloride water purifying agent and preparation method - Google Patents
Polyferric chloride water purifying agent and preparation method Download PDFInfo
- Publication number
- CN106587219A CN106587219A CN201710113535.3A CN201710113535A CN106587219A CN 106587219 A CN106587219 A CN 106587219A CN 201710113535 A CN201710113535 A CN 201710113535A CN 106587219 A CN106587219 A CN 106587219A
- Authority
- CN
- China
- Prior art keywords
- purifying agent
- preparation
- added
- acid solution
- poly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a polyferric chloride water purifying agent and a preparation method. Iron is added into a waste hydrochloric acid solution for a reaction, and the waste hydrochloric acid solution reaching the certain 1.5-1.6 molar ratio of [H+]/[Fe2+] is added into a reaction kettle through a metering tank; under the normal temperature, 2-5% of sulfuric acid, 3-6% of sodium silicate and 0.1-0.6% of borax are added during stirring, and a reaction is performed for 25-35 min; and when it is detected that the specific gravity of ferrous ions is 1.3: 10, a mixed material is placed into a storage tank to be subjected to ageing for 24 h, and then the product is obtained. According to the polyferric chloride water purifying agent and the preparation method, waste hydrochloric acid is adopted as a raw material and is made to be capable of cyclically utilized again, because the sulfuric acid, the sodium silicate and the borax are added, the water purifying effect is good, various pollution components in water can be effectively treated, the adsorbing capacity is high, and no secondary pollution is generated.
Description
Technical field
The invention belongs to field of sewage treatment, is related to the preparation that the industry sewages such as paper-making industry, dyeing industry administer water purification agent
Method.
Background technology
At present country's steel and iron industry, metal product industry in process of production, need to remove steel surface iron scale and make
Pickling is carried out with hydrochloric acid, a certain amount of waste hydrochloric acid liquor can be produced in acid cleaning process, the composition of spent carbonate hydrochloric acid solution mainly has;It is free
Acid, frerrous chloride and water.
The content of the invention
The purpose of the present invention is:For above-mentioned problem of environmental pollution, there is provided a kind of poly-ferric chloride purifying agent
Preparation method, can reduce the pollution that waste hydrochloric acid liquor is brought, environmental protection, energy saving.
The technical scheme is that:A kind of poly-ferric chloride purifying agent, it is characterised in that:By following percentage by weight
Component is constituted:Iron chloride is not more than 0.4%, silica 0.8-2.0%, sodium sulphate 1.6- not less than 38.0%, ferrous chloride
2.4%th, borax 0.1-0.3% and water, density is 1.2-1.3 grams per milliliters, and pH value is 1.0-2.0.2nd, a kind of poly-ferric chloride water purification
The preparation method of agent, it is characterised in that:Iron reaction will be added in abraum salt acid solution, reach [H+]/[Fe2+] mol ratios for 1.5-
1.6:1, Jing measuring tank is added in reactor, at normal temperatures, sulfuric acid, the sodium metasilicate of 3-6% and the 0.1- of 2-5% is added in stirring
0.6% borax, reacts 25-35 minutes, checks ferrous ion proportion to be in the solution 1.3:When 10, storage tank ageing 24 is put into
Hour, obtain final product this product.
Abraum salt acid solution of the present invention consists of the following composition and is according to parts by weight:230 parts of hydrogen chloride, 97.7 parts
Ferrous ion, 15.8 parts of iron ions, remaining be micro silica.
Abraum salt acid solution of the present invention is taken from carries out giving up after pickling except steel surface iron scale using hydrochloric acid
Hydrochloric acid solution.
The present invention is for the waste water in terms of purification printing and dyeing, plating, papermaking.
The invention has the beneficial effects as follows:The present invention is using waste hydrochloric acid as raw material so that waste hydrochloric acid can recirculate utilization, this
Invention is due to adding sulfuric acid, sodium metasilicate and borax so that purifying water effect is good, can to water in various pollutant components have
Effect process, absorption affinity is strong, will not produce secondary pollution.
Specific embodiment
Embodiment 1:
Iron reaction will be added in abraum salt acid solution, reach the abraum salt acid solution of certain [H+]/[Fe2+] mol ratios, Jing measuring tanks add
In entering reactor, at normal temperatures, 2% sulfuric acid, 3% sodium metasilicate and 0.1% borax is added in stirring, reacted 25 minutes, inspection
The proportion of ferrous ion is 1.3:When 1, it is put into storage tank and is aged 24 hours, obtains final product this product.
Embodiment 2:
Iron reaction will be added in abraum salt acid solution, reach the abraum salt acid solution of certain 1.5-1.6 [H+]/[Fe2+] mol ratio, Jing
Measuring tank is added in reactor, at normal temperatures, 5% sulfuric acid, 6% sodium metasilicate and 0.6% borax, reaction 35 is added in stirring
Minute, the proportion for checking ferrous ion is 1.3:When 1, it is put into storage tank and is aged 24 hours, obtains final product this product.
Embodiment 3:
Iron reaction will be added in abraum salt acid solution, reach the abraum salt acid solution of certain 1.5-1.6 [H+]/[Fe2+] mol ratio, Jing
Measuring tank is added in reactor, at normal temperatures, the borax of 3.2% sulfuric acid, 4.6% sodium metasilicate and 0.46 % is added in stirring,
Reaction 25-35 minutes, the proportion for checking ferrous ion is 1.3:When 1, it is put into storage tank and is aged 24 hours, obtains final product this product.
The waste water in terms of printing and dyeing, plating, papermaking after present invention purification can rear discharge up to standard.
Claims (5)
1. a kind of poly-ferric chloride purifying agent, it is characterised in that:Consist of the following components in percentage by weight:Iron chloride is not less than
38.0%th, frerrous chloride is not more than 0.4%, silica 0.8-2.0%, sodium sulphate 1.6-2.4%, borax 0.1-0.3% and water, close
Spend for 1.2-1.3 grams per milliliters, pH value is 1.0-2.0.
2. a kind of preparation method of poly-ferric chloride purifying agent as claimed in claim 1, it is characterised in that:By abraum salt acid solution
Middle addition iron reaction, reaches [H+]/[Fe2+] mol ratios for 1.5-1.6:1, Jing measuring tank is added in reactor, at normal temperatures,
The borax of the sulfuric acid, the sodium metasilicate of 3-6% and 0.1-0.6% of 2-5% is added in stirring, 25-35 minutes are reacted, ferrous ion is checked
Proportion in the solution is 1.3:When 10, it is put into storage tank and is aged 24 hours, obtains final product this product.
3. the preparation method of a kind of poly-ferric chloride purifying agent according to claim 2, it is characterised in that:Described abraum salt
Acid solution consists of the following composition and is according to parts by weight:230 parts of hydrogen chloride, 97.7 parts of ferrous ions, 15.8 parts of iron ions, its
It is remaining for micro silica.
4. the preparation method of a kind of poly-ferric chloride purifying agent according to claim 2, it is characterised in that:Described abraum salt
Acid solution is taken from carries out the abraum salt acid solution after pickling using hydrochloric acid except steel surface iron scale.
5. a kind of a kind of poly-ferric chloride purifying agent as claimed in claim 1, it is characterised in that:Print and dye for purification, electroplate,
Waste water in terms of papermaking.