CN106585053A - Production technology for rubber running track coiled material - Google Patents
Production technology for rubber running track coiled material Download PDFInfo
- Publication number
- CN106585053A CN106585053A CN201611089254.0A CN201611089254A CN106585053A CN 106585053 A CN106585053 A CN 106585053A CN 201611089254 A CN201611089254 A CN 201611089254A CN 106585053 A CN106585053 A CN 106585053A
- Authority
- CN
- China
- Prior art keywords
- coiled material
- rubber
- running track
- production technology
- track coiled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production technology for a rubber running track coiled material. The production technology for the rubber running track coiled material includes the following steps that fiberglass mesh fabric or glass fiber cloth is pressed onto the bottom face of a rubber coiled material, so that a running track base material is obtained; the running track base material is vulcanized; and the vulcanized running track base material is subjected to edge cutting and trimming, and accordingly the rubber running track coiled material is obtained. The production technology for the rubber running track coiled material has the beneficial effects that the fiberglass mesh fabric or the glass fiber cloth is pressed onto the bottom face of the rubber coiled material, the thickness of the fiberglass mesh fabric or the glass fiber cloth is controlled to be 0.5-2mm, and therefore the performance of an original rubber running track coiled material cannot be affected; and moreover, the fiberglass mesh fabric or the glass fiber cloth has good alkali resistance, flexibility and tensile resistance, mildew proofing and insect prevention can be achieved, the flexibility of a running track is improved due to arrangement of the fiberglass mesh fabric, the phenomenon of cracking of the running track can be effectively prevented, and the service life of the running track is prolonged.
Description
Technical field
The present invention relates to a kind of runway, and in particular to a kind of production technology of rubber track coiled material.
Background technology
Due to rubber place, rubber track comprcssive strength height, good flatness, stable physical property, hardness elasticity it is appropriate etc.
Characteristic.At present, it is widely used in many places such as school, gymnasium, but its cost is higher than general runway, therefore reduce
Expense when rubber track is mated formation, extending its use time becomes the importance studied when runway is mated formation.
Prevent runway cracking in use and the problems such as delamination, be the effective way for extending runway service life
Footpath, but there are several factors to cause cracking and the delamination of runway during construction and runway use, such as：In work progress
In if workmen is non-professional runway setter, temperature control during construction is bad, and the proportioning of material, catalyst are matched somebody with somebody
When binding agent improper use etc., can all cause cracking and the delamination of runway.
The A of Chinese patent CN 103276653 disclose a kind of installation method of prefabrication type self-adhesion running track coiled material, the prefabrication type
Self-adhesion running track coiled material includes anti-skid wearable surface layer compound successively from top to bottom, cushion, self-adhesive layer and separator paper layer, in the race
The both sides of road coiled material are provided with mutual corresponding overlap joint groove.The mounting process of the prefabrication type self-adhesion running track coiled material is：(1) according to routine
Technique carries out runway foundation construction；(2) separator paper layer below the self-adhesive layer of running track coiled material is thrown off, using gluing that self-adhesive layer has
Attached power is by itself and base surface secure bond；(3) the overlap joint groove between the several adjacent coil edge in the middle part of runway section is mutual
Overlap joint, and bondd with binding agent, then it is connected with each other with screw；(4) the most left and rightmost overlap joint groove Z-shaped in runway section
Metal sealed edges and screw fix with surface of base.This is that running track coiled material cracking is reduced by the method for running track coiled material installation
Delamination, extends the service life of runway, but undeclared how to improve it by the improvement to running track coiled material itself and use
Life-span.
The content of the invention
It is an object of the invention to provide a kind of pliability is by force and with the production of mould proof, insect prevention function rubber track coiled material
Technique.
A kind of production technology of rubber track coiled material, comprises the following steps：
(1) fiberglass gridding cloth or glass fabric are pressed into the bottom surface of rubber coiled material, runway base material is obtained；Glass fibers
Dimension grid cloth is that, with fiberglass woven fabric as base material, the anti-emulsion of Jing macromolecules soaks coating.With good alkali resistance, flexible
Property and longitude and latitude have functions that anti-mildew, insect prevention to height stretching resistance；Glass fabric has resistance to chemical attack, resistance to
The effect of strong acid, highly basic, and with good mechanical property.
(2) vulcanizing treatment is carried out to runway base material；
(3) the runway base material after sulfuration is carried out into trimming rest and reorganization, obtains described rubber track coiled material.
Further, described rubber coiled material is made up of natural rubber, synthetic rubber, pigment, auxiliary agent and filler.Auxiliary agent is
Vulcanizing agent, accelerator, activator and antiscorching agent etc.；Filler is calcium powder or white carbon etc..
Further, in step (1), the thickness of the fiberglass gridding cloth or glass fabric is 0.5-2mm.At this
In control the thickness of fiberglass gridding cloth or glass fabric, it is to avoid its performance to original rubber track coiled material causes shadow
Ring.
Further, in step (1), fiberglass gridding cloth or glass fabric are pressed into rubber by two-roll calendar
On coiled material.
Further, in step (2), runway base material is carried out into vulcanizing treatment under conditions of temperature is for 100-200 DEG C.
Further, the time that runway base material carries out vulcanizing treatment is 30-40min.
Further, microtome carries out section finishing used in step (3).
Beneficial effects of the present invention are：The production technology of rubber track coiled material of the present invention, by fiberglass gridding
Cloth or glass fabric are pressed into the bottom surface of rubber coiled material, and control the thickness of fiberglass gridding cloth or glass fabric and be
0.5-2mm, because the thickness of fiberglass gridding cloth or glass fabric is than relatively thin, will not be to the property of original rubber track coiled material
Can impact, and fiberglass gridding cloth or glass fabric have good alkali resistance, pliability and longitude and latitude to high resistance
Pulling force, and the setting of energy anti-mildew, insect prevention, i.e. fiberglass gridding cloth increased the pliability of runway, can be effectively pre-
The cracking phenomenon of anti-runway, extends the service life of runway.
Specific embodiment
Embodiment one
A kind of production technology of rubber track coiled material, comprises the following steps：
(1) fiberglass gridding cloth or glass fabric are pressed into the bottom surface of rubber coiled material by two-roll calendar, are obtained
Runway base material；Rubber coiled material referred herein is made up of natural rubber, synthetic rubber, pigment, auxiliary agent and filler；The glass fibers
The thickness of dimension grid cloth or glass fabric is 0.5mm, and described fiberglass gridding cloth or the thickness of glass fabric will foot
It is enough thin, it is to avoid its performance to rubber track coiled material is impacted；
(2) runway base material is placed at a temperature of 200 DEG C carries out vulcanizing treatment 30min, is then cut using microtome
Side is rested and reorganized, and obtains described rubber track coiled material.
When described rubber track coiled material is installed, weather condition need to be checked：Outdoor temperature is below 5 DEG C and sleety weather
Shi Buneng constructs, when relative air humidity is more than 85%, construction of trying not；Check evenness of road surface degree：With level indicator or water
Flat thick stick chi measures the physical features of road bed, and physical features eminence is polished with polisher, is polished to and surrounding basic horizontal, right
Physical features lower is filled up so as to substantially with surrounding level, then carries out examination water, and according to the result of examination water road surface whether needs are seen
Fill up again or polish；Detection glue bonding performance：5-8 block running track coiled material sample blocks are selected, sample block is bonded in into road surface with glue
On, the adhesion strength of destructive testing, testing glue and runway is carried out after glue curing.At summer, glue curing two days
After carry out destructive testing, at winter, glue curing carries out destructive testing in seven days or so.
According to above-mentioned test result, after the adhesive property of glue is qualified, glue is applied to after foundation construction
On runway, after glue is applied and wiped, described rubber track coiled material is layered on the runway of spreading glue, then with nail to described
Rubber track coiled material be fixed.
Embodiment two
A kind of production technology of rubber track coiled material, comprises the following steps：
(1) fiberglass gridding cloth or glass fabric are pressed into the bottom surface of rubber coiled material by two-roll calendar, are obtained
Runway base material；Rubber coiled material referred herein is made up of natural rubber, synthetic rubber, pigment, auxiliary agent and filler；The glass fibers
The thickness of dimension grid cloth or glass fabric is 1mm, and described fiberglass gridding cloth or the thickness of glass fabric is enough
It is thin, it is to avoid its performance to rubber track coiled material is impacted；
(2) runway base material is placed at a temperature of 150 DEG C carries out vulcanizing treatment 35min, is then cut using microtome
Side is rested and reorganized, and obtains described rubber track coiled material.
When described rubber track coiled material is installed, weather condition need to be checked：Outdoor temperature is below 5 DEG C and sleety weather
Shi Buneng constructs, when relative air humidity is more than 85%, construction of trying not；Check evenness of road surface degree：With level indicator or water
Flat thick stick chi measures the physical features of road bed, and physical features eminence is polished with polisher, is polished to and surrounding basic horizontal, right
Physical features lower is filled up so as to substantially with surrounding level, then carries out examination water, and according to the result of examination water road surface whether needs are seen
Fill up again or polish；Detection glue bonding performance：5-8 block running track coiled material sample blocks are selected, sample block is bonded in into road surface with glue
On, the adhesion strength of destructive testing, testing glue and runway is carried out after glue curing.At summer, glue curing two days
After carry out destructive testing, at winter, glue curing carries out destructive testing in seven days or so.
According to above-mentioned test result, after the adhesive property of glue is qualified, glue is applied to after foundation construction
On runway, after glue is applied and wiped, described rubber track coiled material is layered on the runway of spreading glue, then with nail to described
Rubber track coiled material be fixed.
Embodiment three
A kind of production technology of rubber track coiled material, comprises the following steps：
(1) fiberglass gridding cloth or glass fabric are pressed into the bottom surface of rubber coiled material by two-roll calendar, are obtained
Runway base material；Rubber coiled material referred herein is made up of natural rubber, synthetic rubber, pigment, auxiliary agent and filler；The glass fibers
The thickness of dimension grid cloth or glass fabric is 2mm, and described fiberglass gridding cloth or the thickness of glass fabric is enough
It is thin, it is to avoid its performance to rubber track coiled material is impacted；
(2) runway base material is placed at a temperature of 100 DEG C carries out vulcanizing treatment 40min, is then cut using microtome
Side is rested and reorganized, and obtains described rubber track coiled material.
When described rubber track coiled material is installed, weather condition need to be checked：Outdoor temperature is below 5 DEG C and sleety weather
Shi Buneng constructs, when relative air humidity is more than 85%, construction of trying not；Check evenness of road surface degree：With level indicator or water
Flat thick stick chi measures the physical features of road bed, and physical features eminence is polished with polisher, is polished to and surrounding basic horizontal, right
Physical features lower is filled up so as to substantially with surrounding level, then carries out examination water, and according to the result of examination water road surface whether needs are seen
Fill up again or polish；Detection glue bonding performance：5-8 block running track coiled material sample blocks are selected, sample block is bonded in into road surface with glue
On, the adhesion strength of destructive testing, testing glue and runway is carried out after glue curing.At summer, glue curing two days
After carry out destructive testing, at winter, glue curing carries out destructive testing in seven days or so.
According to above-mentioned test result, after the adhesive property of glue is qualified, glue is applied to after foundation construction
On runway, after glue is applied and wiped, described rubber track coiled material is layered on the runway of spreading glue, then with nail to described
Rubber track coiled material be fixed.
The present invention is not limited to above-mentioned preferred forms, and anyone can show that other are various under the enlightenment of the present invention
The product of form, however, make any change in its details, it is every with technical scheme identical or similar to the present application,
It is within the scope of the present invention.
Claims (7)
1. a kind of production technology of rubber track coiled material, it is characterised in that comprise the following steps：
(1) fiberglass gridding cloth or glass fabric are pressed into the bottom surface of rubber coiled material, runway base material is obtained；
(2) vulcanizing treatment is carried out to runway base material；
(3) the runway base material after sulfuration is carried out into trimming rest and reorganization, obtains described rubber track coiled material.
2. the production technology of rubber track coiled material according to claim 1, it is characterised in that described rubber coiled material is by natural
Rubber, synthetic rubber, pigment, auxiliary agent and filler composition.
3. the production technology of rubber track coiled material according to claim 1, it is characterised in that in step (1), the glass fibers
The thickness of dimension grid cloth or glass fabric is 0.5-2mm.
4. the production technology of rubber track coiled material according to claim 1, it is characterised in that in step (1), glass fiber mesh
Lattice cloth or glass fabric are pressed on rubber coiled material by two-roll calendar.
5. the production technology of rubber track coiled material according to claim 1, it is characterised in that in step (2), by runway base material
Vulcanizing treatment is carried out under conditions of temperature is for 100-200 DEG C.
6. the production technology of rubber track coiled material according to claim 4, it is characterised in that runway base material carries out vulcanizing treatment
Time be 30-40min.
7. the production technology of rubber track coiled material according to claim 1, it is characterised in that microtome used in step (3)
Carry out section finishing.