CN106583203A - Machining method of light-weight glass-effect metal composite steel plate - Google Patents
Machining method of light-weight glass-effect metal composite steel plate Download PDFInfo
- Publication number
- CN106583203A CN106583203A CN201610879905.XA CN201610879905A CN106583203A CN 106583203 A CN106583203 A CN 106583203A CN 201610879905 A CN201610879905 A CN 201610879905A CN 106583203 A CN106583203 A CN 106583203A
- Authority
- CN
- China
- Prior art keywords
- epoxy
- steel plate
- base material
- effect metal
- processing method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a machining method of a light-weight glass-effect metal composite steel plate. The machining method comprises the following steps of pretreating a galvanized plate base material; coating chemical coating fluid; coating epoxy primer and anti-corrosion back paint with a roller; coating epoxy intermediate coat with the roller; coating epoxy finishing coat with the roller; carrying out polishing treatment; and sticking an acrylic film or coating gloss oil. The machining method is simple in process; a common galvanized plate is adopted; the front surface of the base material is coated with the epoxy finishing coat with the roller, the epoxy finishing coat is subjected to precise and controllable polishing in a manner of not damaging the finishing coat, and the acrylic film is stuck or the gloss oil is coated, so that the appearance effect that the glossiness is close to that of mirror glass is achieved; and the steel plate is high in processing property and can be perforated and bent.
Description
Technical field
The present invention relates to steel plate processing technique field, more particularly to a kind of processing of foam glass effect metal clad steel plate
Method.
Background technology
Under consumption upgrading overall background, household appliances require more and more higher to improve competitiveness to product appearance.Household electrical appliances face
Sheet material matter also progressively develops into the various materials such as film coated plate, glass plate, ceramic wafer by initially single lacquered board.Although glass,
The panels such as ceramics can the performance of significant increase product appearance, but due to the essence of its material brittle, cause processing difficulties, cost compared with
Height, therefore only have on the expensive goods of part a small amount of application, and common film coated plate mature production technology, but opposing product outward appearance is old
It is old, it is impossible to meet the market demand.
Psychology of vision research shows that people are to the impression of material appearance essentially from the side such as color, skin texture, glossiness
Face.Glossiness is higher, and visual cognition is more intended to luxurious, wealth and rank.And glass, the ceramic phase advantage more maximum than paint is that it
Fine polishing can be passed through and obtain higher glossiness.
Finish polishing is in the long-term ripe application of the fields such as automobile, the reparation of furniture finish paint.Select applicable polishing material
Material and polishing agent, scratch or can recover as new after aging finish paint is polished.And conventional painted steel sheet and film coated plate are due to material
Consistency itself and surface roughness are limited, far below the glossiness of glass ceramic material.
The content of the invention
In order to overcome the above-mentioned deficiencies of the prior art, the invention provides a kind of foam glass effect metal clad steel plate
Processing method, can obtain the metal composite steel plate of the close two-way mirror glossiness of glossiness.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of processing method of foam glass effect metal clad steel plate, comprises the following steps:
Step one, adopt thickness and do base material for the galvanized sheet of 0.4 ~ 1mm, alkali cleaning process is carried out to base material, after alkali cleaning is processed
Base material carry out hot water scrub, then dry;
Step 2, to Jing step one process after base material paintingization masking liquid, then dry, formationization coating;
Step 3, in base material front roller coat epoxy primer, apply anti-corrosion back of the body paint in substrate backside, epoxy primer and the anti-corrosion back of the body are painted into
Row hot setting, water-filling cold treatment of going forward side by side, then air-dries;
Step 4, in base material front roller coat epoxy intermediate coat, hot setting is carried out to epoxy intermediate coat, water-filling cold treatment of going forward side by side,
Then air-dry;
Step 5, in base material front roller coat epoxy finish, hot setting is carried out to epoxy finish, water-filling cold treatment of going forward side by side, then
Air-dry;
Step 6, epoxy finish is processed by shot blasting, then pastes acrylic film or glazing oil.
As the improvement of above-mentioned technical proposal, in step 6, when being processed by shot blasting to epoxy finish, after first rough polishing
Essence is thrown, and rough polishing and essence are thrown using four polishing roll series connection polishings, and every polishing roll rear side is respectively arranged with photometer, according to photometer
Reading controls polished amount.
Used as the improvement of above-mentioned technical proposal, the formula of epoxy finish is consisted of by weight percentage:Epoxy resin 40%,
Calcium sulfate crystal whiskers 30%, filler 20%, pigment 4%, auxiliary agent 6%.
Used as the improvement of above-mentioned technical proposal, described filler is white carbon or titanium dioxide.
Used as the improvement of above-mentioned technical proposal, the particle diameter of the pigment is not more than 10 μm.
Used as the improvement of above-mentioned technical proposal, the thickness of epoxy finish is 30 μm.
It it is 10 μm as the thickness of the improvement of above-mentioned technical proposal, acrylic film or gloss oil.
Beneficial effects of the present invention have:
This processing method process is simple, using common galvanized sheet, in base material front roller coat epoxy finish, and enters to epoxy finish
The polishing of row controllable precise, does not damage finish paint, then pastes acrylic film or glazing oil, can obtain the close two-way mirror light of glossiness
The appearance of damp degree, processing performance is good, can perforate, bending.
Specific embodiment
A kind of processing method of foam glass effect metal clad steel plate of the present invention, comprises the following steps:
Step one, adopt thickness and do base material for the galvanized sheet of 0.4 ~ 1mm, alkali cleaning process is carried out to base material, after alkali cleaning is processed
Base material carry out hot water scrub, then dry;
Step 2, to Jing step one process after base material paintingization masking liquid, then dry, formationization coating;
Step 3, in base material front roller coat epoxy primer, apply anti-corrosion back of the body paint in substrate backside, epoxy primer and the anti-corrosion back of the body are painted into
Row hot setting, water-filling cold treatment of going forward side by side, then air-dries;
Step 4, in base material front roller coat epoxy intermediate coat, hot setting is carried out to epoxy intermediate coat, water-filling cold treatment of going forward side by side,
Then air-dry;
Step 5, in base material front roller coat epoxy finish, hot setting is carried out to epoxy finish, water-filling cold treatment of going forward side by side, then
Air-dry;
Step 6, epoxy finish is processed by shot blasting, then pastes acrylic film or glazing oil.
Further, in step 6, when being processed by shot blasting to epoxy finish, after first rough polishing essence throw, rough polishing and
Essence is thrown using four polishing roll series connection polishings, and every polishing roll rear side is respectively arranged with photometer, is thrown according to the control of photometer reading
Light quantity.
Specifically, the formula of epoxy finish is consisted of by weight percentage:Epoxy resin 40%, calcium sulfate crystal whiskers 30%, fill out
Material 20%, pigment 4%, auxiliary agent 6%.Wherein, auxiliary agent can have defoamer, firming agent, organosilicon to help levelling agent, macromolecule dispersing agent
And antioxidant, filler is white carbon or titanium dioxide, and the particle diameter of pigment is not more than 10 μm, and the thickness of epoxy finish is 30 μ
The thickness of m, acrylic film or gloss oil is 10 μm, can obtain the appearance of the close two-way mirror glossiness of glossiness, manufacturability
Can be good, can perforate, bending.
The above, simply better embodiment of the invention, but the present invention is not limited to above-described embodiment, as long as
It reaches the technique effect of the present invention with any same or similar means, should all belong to protection scope of the present invention.
Claims (7)
1. a kind of processing method of foam glass effect metal clad steel plate, it is characterised in that comprise the following steps:
Step one, adopt thickness and do base material for the galvanized sheet of 0.4 ~ 1mm, alkali cleaning process is carried out to base material, after alkali cleaning is processed
Base material carry out hot water scrub, then dry;
Step 2, to Jing step one process after base material paintingization masking liquid, then dry, formationization coating;
Step 3, in base material front roller coat epoxy primer, apply anti-corrosion back of the body paint in substrate backside, epoxy primer and the anti-corrosion back of the body are painted into
Row hot setting, water-filling cold treatment of going forward side by side, then air-dries;
Step 4, in base material front roller coat epoxy intermediate coat, hot setting is carried out to epoxy intermediate coat, water-filling cold treatment of going forward side by side,
Then air-dry;
Step 5, in base material front roller coat epoxy finish, hot setting is carried out to epoxy finish, water-filling cold treatment of going forward side by side, then
Air-dry;
Step 6, epoxy finish is processed by shot blasting, then pastes acrylic film or glazing oil.
2. the processing method of a kind of foam glass effect metal clad steel plate according to claim 1, it is characterised in that
In step 6, when being processed by shot blasting to epoxy finish, essence is thrown after first rough polishing, and rough polishing and essence are thrown and adopt four polishing roll strings
Connection polishing, every polishing roll rear side is respectively arranged with photometer, and according to photometer reading polished amount is controlled.
3. a kind of processing method of foam glass effect metal clad steel plate according to claim 1, it is characterised in that ring
The formula of oxygen finish paint is consisted of by weight percentage:Epoxy resin 40%, calcium sulfate crystal whiskers 30%, filler 20%, pigment 4%, auxiliary agent
6%。
4. a kind of processing method of foam glass effect metal clad steel plate according to claim 3, it is characterised in that institute
Filler is stated for white carbon or titanium dioxide.
5. a kind of processing method of foam glass effect metal clad steel plate according to claim 3, it is characterised in that institute
The particle diameter for stating pigment is not more than 10 μm.
6. a kind of processing method of foam glass effect metal clad steel plate according to claim 1, it is characterised in that ring
The thickness of oxygen finish paint is 30 μm.
7. the processing method of a kind of foam glass effect metal clad steel plate according to claim 1, it is characterised in that sub-
The thickness of gram force film or gloss oil is 10 μm.