CN106566116A - A water pipe formula - Google Patents
A water pipe formula Download PDFInfo
- Publication number
- CN106566116A CN106566116A CN201610938036.3A CN201610938036A CN106566116A CN 106566116 A CN106566116 A CN 106566116A CN 201610938036 A CN201610938036 A CN 201610938036A CN 106566116 A CN106566116 A CN 106566116A
- Authority
- CN
- China
- Prior art keywords
- parts
- water pipe
- pipe formula
- lubricant
- foaming agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A water pipe formula is disclosed. The formula comprises, by weight, 80-150 parts of PVC resin, 2-6 parts of paraffin, 15-25 parts of a plasticizer, 7-18 parts of a stabilizing agent, 10-20 parts of a lubricant, 0.5-1 part of a coloring agent, 5-15 parts of a filler and 5-10 parts of a defoamer. A water pipe prepared according to the formula has advantages of high wear resistance, high hardness, and the like.
Description
Technical field
The present invention relates to a kind of water pipe formula, is applied to the production preparation field of water pipe.
Background technology
Water pipe is now requisite product in finishing, and the domestic water in family is all sent by water pipe,
The degree of safety of drinking water is just closely bound up with the safety of water pipe in family, as the development people of society are to construction material in family
Safety is increasingly valued, and especially the environmentally friendly Chengdu of water pipe determines the safe coefficient of drinking water.
Traditional water pipe is due to the limitation of technology at that time so that the water pipe hardness produced is inadequate and not wear-resisting, and Jing is normal
There is pipe burst, the contaminated situation of drinking water.
The content of the invention
For above-mentioned technical problem, the invention discloses a kind of strong water pipe formula of corrosion-resistant, hardness.
The invention discloses a kind of water pipe formula, by weight number scale, component is as follows：Polyvinyl chloride resin 80-150 parts, paraffin 2-
6 parts, plasticizer 15-25 parts, stabilizer 7-18 parts, lubricant 10-20 parts, coloring agent 0.5-1 parts, inserts 5-15 parts, foaming
Agent 5-10 parts.
Further preferably, described plasticizer is phthalic acid ester.
Further preferably, described lubricant is Tissuemat E.
Further preferably, described coloring agent is titanium dioxide.
Further preferably, described filling powder is Calcium Carbonate.
Further preferably, described foaming agent is ADC foaming agent.
Beneficial effects of the present invention：The wearability of water pipe, filling increased by the interaction of stabilizer and lubricant
Powder increased the hardness of water pipe so that obtained water pipe not cracky.
Specific embodiment
Embodiment 1：A kind of water pipe formula, counts by weight, and component is as follows：100 parts of polyvinyl chloride resin, 3 parts of paraffin, plasticising
20 parts of agent, 12 parts of stabilizer, 15 parts of lubricant, 0.6 part of coloring agent, 8 parts of inserts, 6 parts of foaming agent.
Embodiment two：A kind of water pipe formula, counts by weight, and component is as follows：120 parts of polyvinyl chloride resin, 4 parts of paraffin, plasticising
22 parts of agent, 15 parts of stabilizer, 13 parts of lubricant, 0.7 part of coloring agent, 10 parts of inserts, 7 parts of foaming agent.
The ultimate principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
It should be appreciated that the present invention is not restricted to the described embodiments, described in above-described embodiment and description is only the present invention to personnel
Preference, be not intended to limit the present invention, without departing from the spirit and scope of the present invention, the present invention also have it is various
Changes and improvements, these changes and improvements are both fallen within scope of the claimed invention.The claimed scope of the invention is by institute
Attached claims and its equivalent thereof.
Claims (6)
1. a kind of water pipe formula, by weight number scale, component is as follows：Polyvinyl chloride resin 80-150 parts, paraffin 2-6 parts, plasticizer 15-
25 parts, stabilizer 7-18 parts, lubricant 10-20 parts, coloring agent 0.5-1 parts, inserts 5-15 parts, foaming agent 5-10 parts.
2. according to a kind of water pipe formula described in claim 1, it is characterised in that：Described plasticizer is phthalic acid
Ester.
3. according to a kind of water pipe formula described in claim 1, it is characterised in that：Described lubricant is Tissuemat E.
4. according to a kind of water pipe formula described in claim 1, it is characterised in that：Described coloring agent is titanium dioxide.
5. according to a kind of water pipe formula described in claim 1, it is characterised in that：Described filling powder is Calcium Carbonate.
6. according to a kind of water pipe formula described in claim 1, it is characterised in that：Described foaming agent is ADC foaming agent.