CN106554195A - A kind of high-quality translucent white porcelain plate and its manufacturing process - Google Patents
A kind of high-quality translucent white porcelain plate and its manufacturing process Download PDFInfo
- Publication number
- CN106554195A CN106554195A CN201510635368.XA CN201510635368A CN106554195A CN 106554195 A CN106554195 A CN 106554195A CN 201510635368 A CN201510635368 A CN 201510635368A CN 106554195 A CN106554195 A CN 106554195A
- Authority
- CN
- China
- Prior art keywords
- mud
- translucent white
- white porcelain
- manufacturing process
- porcelain plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of high-quality translucent white porcelain plate and its manufacturing process, the pug of high-quality translucent white porcelain plate chemical constituent by weight percentage is：SiO2-66%、Al2O3-21.63%、Fe2O3-0.47%、CaO-0.61%、MgO-0.37、K2O-2.94%、Na2O-1.6%、Li-5.47%；The manufacturing process of the high-quality translucent white porcelain plate is completed by following steps：A, mud refining；B, compacting mud plate base, c, loading drying；D, corase grind；E, fine grinding；F, setting glazing；G, burn till.The high-quality translucent white porcelain plate made using the technique of the present invention can evade cracking, modification, the defect for warping, and drastically increase yield rate.
Description
Technical field
The invention belongs to ceramic fabricating technology field, specifically can be used as a kind of new support of painting and calligraphy（Underglaze colour drawing is write）And the manufacturing process of decorative ceramic plate.
Background technology
Although ceramic board has many superior characteristics, such as mechanical behavior under high temperature, chemical resistance of concrete performance, electrical insulating property, higher hardness and wearability, can be stable for a long time cultural bearing carrying agent etc..But the sheet material manufacture of the ceramic material of high-quality due to its structures shape, cracking is susceptible in production process, cause plastic deformation, defect is produced easily, there is crackle, and be easy to cause the stress concentration of height, thus numerous Production of Ceramics persons dare not be related to, therefore the manufacture method for improving ceramic board is the problem of ceramic boundary concern for a long time, conventional porcelain plate make adopted material and method and during can cause a series of defect, the porcelain plate with the defect for as cultural carrying agent have in all senses be worth.
The content of the invention
The present invention is directed to the problems referred to above, there is provided a kind of high-quality translucent white porcelain plate and its manufacturing process.
To solve the above problems, this is realized by following technological means using new：A kind of high-quality translucent white porcelain plate, the pug of high-quality translucent white porcelain plate chemical constituent by weight percentage is：SiO2-66%、Al2O3-21.63%、Fe2O3-0.47%、CaO-0.61%、MgO-0.37、K2O-2.94%、Na2O-1.6%、Li-5.47%.
The manufacturing process of the high-quality translucent white porcelain plate is carried out as follows：
The ratio of pug and water according to weight than 7 to 3 is mixed to prepare mud by a, mud refining, after being drained dehydration, standard mud bar is refined and refined into using vacuum deairing machine standby；
The mud bar roller press refined through vacuum is compressed into flake, is rolled into repeatedly mud plate base desired thickness by b, compacting mud plate base；
C, loading drying, load the mud plate base after compacting using the prefabricated blanket of absorbent material.Repeated multiple times loading is simultaneously fastened so that mud plate accelerates drying；
D, corase grind, to after compacting, semiarid mud plate base carries out polishing and reaches predetermined thickness；
E, fine grinding, carry out polishing to more dry mud plate base again and allow which more accurately to reach accurately thickness；
F, setting glazing, moulded pottery not yet put in a kiln to bake kiln-firing to 500 degree, are processed required smoothness again, carry out glazing after cooling；
G, burn till, kiln-firing is to 1330 degree of porcelain temperature again.
Preferably, the firing time of step f be set to 3 hours.
Preferably, the firing time of step g be set to 6 hours.
It is an advantage of the current invention that：Porcelain plate is made using the method for the present invention and can evade cracking, modification, the defect for warping, the yield rate of porcelain plate firing is greatly improved.If making porcelain plate using former method, the porcelain plate worked it out is understood the big quantity cracking of large area, modification, is warped, and brings no small loss to Producer.
Description of the drawings
Without accompanying drawing.
Specific embodiment
The present invention is described in further detail with reference to embodiment.
A kind of high-quality translucent white porcelain plate, the pug of high-quality translucent white porcelain plate chemical constituent by weight percentage is：SiO2-66%、Al2O3-21.63%、Fe2O3-0.47%、CaO-0.61%、MgO-0.37、K2O-2.94%、Na2O-1.6%、Li-5.47%.
Its manufacturing process is carried out as follows：
The ratio of pug and water according to weight than 7 to 3 is mixed to prepare mud by a, mud refining, using appropriate dewatering, after being drained dehydration, is refined using vacuum deairing machine, is refined into standard mud bar standby；
The mud bar roller press refined through vacuum is compressed into flake, is rolled into repeatedly mud plate base desired thickness by b, compacting mud plate base；
C, loading drying, load the mud plate base after compacting using the prefabricated blanket of absorbent material.Repeated multiple times loading is simultaneously fastened so that mud plate accelerates drying；
D, corase grind, to after compacting, semiarid mud plate base carries out polishing and reaches predetermined thickness；
E, fine grinding, carry out polishing to more dry mud plate base again and allow which more accurately to reach accurately thickness；
F, setting glazing, moulded pottery not yet put in a kiln to bake kiln-firing to 500 degree, the firing time is 3 hours, and the smoothness needed for being worked into after its cooling again, the mud plate for completing postforming apply clear frit；
G, burn till, will apply the mud plate of clear frit again kiln-firing to 1330 degree of porcelain temperature, the procedure firing time is 6 hours, and finished product high-quality translucent white porcelain plate is obtained after its cooling.
Presently preferred embodiments of the present invention is the foregoing is only, not to limit the present invention, all any modification, equivalent and improvement made within the spirit and principles in the present invention etc., be should be included within the scope of the present invention.
Claims (4)
1. a kind of high-quality translucent white porcelain plate, the pug of high-quality translucent white porcelain plate chemical constituent by weight percentage is：SiO2-66%、Al2O3-21.63%、Fe2O3-0.47%、CaO-0.61%、MgO-0.37、K2O-2.94%、Na2O-1.6%、Li-5.47%.
2. the manufacturing process of a kind of high-quality translucent white porcelain plate according to described by claim 1, its manufacturing process are carried out as follows：
The ratio of pug and water according to weight than 7 to 3 is mixed to prepare mud by a, mud refining, after being drained dehydration, standard mud bar is refined and refined into using vacuum deairing machine standby；
The mud bar roller press refined through vacuum is compressed into flake, is rolled into repeatedly mud plate base desired thickness by b, compacting mud plate base；
C, loading drying, load the mud plate base after compacting using the prefabricated blanket of absorbent material；
Repeated multiple times loading is simultaneously fastened so that mud plate accelerates drying；
D, corase grind, to after compacting, semiarid mud plate base carries out polishing and reaches predetermined thickness；
E, fine grinding, carry out polishing to more dry mud plate base again and allow which more accurately to reach accurately thickness；
F, setting glazing, moulded pottery not yet put in a kiln to bake kiln-firing to 500 degree, reprocessing after cooling carries out glazing to required smoothness；
G, burn till, kiln-firing is to 1330 degree of porcelain temperature again.
3. the manufacturing process of a kind of high-quality translucent white porcelain plate according to described by claim 2, it is characterised in that：The time that step f is fired is 3 hours.
4. the manufacturing process of a kind of high-quality translucent white porcelain plate according to described by claim 2, it is characterised in that：The time that step g is fired is 6 hours.