CN106554190A - A kind of preparation method of type gate coreboard - Google Patents
A kind of preparation method of type gate coreboard Download PDFInfo
- Publication number
- CN106554190A CN106554190A CN201510630835.XA CN201510630835A CN106554190A CN 106554190 A CN106554190 A CN 106554190A CN 201510630835 A CN201510630835 A CN 201510630835A CN 106554190 A CN106554190 A CN 106554190A
- Authority
- CN
- China
- Prior art keywords
- proportion
- weighed
- stirring
- solution
- coreboard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of type gate coreboard, body step is as follows：Required magnesium sulfate is weighed in proportion in container, is added appropriate water, is heated to 52 DEG C of stirring and dissolvings；Required magnesia powder and silicon powder are weighed in proportion, and the nano titanium oxide and polypropylene fibre of additional proportion amount take trehalose and foam in proportion in another container, add remaining water, stirring；Step 4 solution is all poured in step 3 solution, is stirred and is poured mould into, scrape flat surface, natural air drying；After to be dried, take out, the block board after sanding is polished using polishing machine, the surface spraying of door panel is painted using spray gun in paint spray booth；Packaging shaping.Beneficial effects of the present invention：Dispensing is few, prepare it is simple, obtained finished product light weight, do not fire, non-toxic and non-radioactive, to human body and environmentally friendly, bend resistance ability is strong, and sound-insulating and heat-insulating effect is good；Its stable production process, environmental protection, it is easy to industrialized production and with low cost.
Description
Technical field
The present invention relates to a kind of door panel production technology, more particularly to a kind of preparation method of type gate coreboard.
Background technology
Timber is common in our daily life, door panel is the important composition part of timber, therefore the fine or not and whether attractive in appearance direct relation of door panel the fine or not and whether attractive in appearance of timber, but, using existing door panel, not only quality is not fine, be cannot withstand natural calamities, and will be damaged using after a period of time, short life, and appearance is coarse, unsightly.
The content of the invention
It is an object of the invention to the above-mentioned deficiency in the presence of overcoming prior art, there is provided a kind of preparation method of type gate coreboard.
In order to realize foregoing invention purpose, the invention provides technical scheme below：
A kind of preparation method of type gate coreboard, body step are as follows：
Step one, required magnesium sulfate is weighed in proportion in container, add appropriate water, be heated to 50-60 DEG C of stirring and dissolving；
Step 2, required magnesia powder and silicon powder are weighed in proportion, be sufficiently mixed in a reservoir stand-by；
Step 3, after the magnesium sulfate dissolving completely in step one, the nano titanium oxide and polypropylene fibre of additional proportion amount are stirred and are cooled to room temperature；
Step 4, trehalose and foam are taken in proportion in another container, add remaining water, stirring；
Step 5, step 4 solution is all poured in step 3 solution, stir and pour mould into, scrape flat surface, natural air drying；
Step 6：After to be dried, take out, the block board after sanding is polished using polishing machine, the surface spraying of door panel is painted using spray gun in paint spray booth；
Step 7：Packaging shaping.
Compared with prior art, beneficial effects of the present invention：Dispensing is few, prepare it is simple, obtained finished product light weight, do not fire, non-toxic and non-radioactive, to human body and environmentally friendly, bend resistance ability is strong, and sound-insulating and heat-insulating effect is good；Its stable production process, environmental protection, it is easy to industrialized production and with low cost.
Specific embodiment
With reference to test example and specific embodiment, the present invention is described in further detail.But this scope for being interpreted as above-mentioned theme of the invention should not be only limitted to below example, all technologies realized based on present invention belong to the scope of the present invention.
Embodiment 1：
A kind of preparation method of type gate coreboard, body step are as follows：
Step one, required magnesium sulfate is weighed in proportion in container, add appropriate water, be heated to 52 DEG C of stirring and dissolvings；
Step 2, required magnesia powder and silicon powder are weighed in proportion, be sufficiently mixed in a reservoir stand-by；
Step 3, after the magnesium sulfate dissolving completely in step one, the nano titanium oxide and polypropylene fibre of additional proportion amount are stirred and are cooled to room temperature；
Step 4, trehalose and foam are taken in proportion in another container, add remaining water, stirring；
Step 5, step 4 solution is all poured in step 3 solution, stir and pour mould into, scrape flat surface, natural air drying；
Step 6：After to be dried, take out, the block board after sanding is polished using polishing machine, the surface spraying of door panel is painted using spray gun in paint spray booth；
Step 7：Packaging shaping.
Claims (1)
1. a kind of preparation method of type gate coreboard, it is characterised in that body step is as follows：
Step one, required magnesium sulfate is weighed in proportion in container, add appropriate water, be heated to 50-60 DEG C of stirring and dissolving；
Step 2, required magnesia powder and silicon powder are weighed in proportion, be sufficiently mixed in a reservoir stand-by；
Step 3, after the magnesium sulfate dissolving completely in step one, the nano titanium oxide and polypropylene fibre of additional proportion amount are stirred and are cooled to room temperature；
Step 4, trehalose and foam are taken in proportion in another container, add remaining water, stirring；
Step 5, step 4 solution is all poured in step 3 solution, stir and pour mould into, scrape flat surface, natural air drying；
Step 6：After to be dried, take out, the block board after sanding is polished using polishing machine, the surface spraying of door panel is painted using spray gun in paint spray booth；
Step 7：Packaging shaping.