CN106554188A - A kind of metope anticorrosion construction material - Google Patents
A kind of metope anticorrosion construction material Download PDFInfo
- Publication number
- CN106554188A CN106554188A CN201611055370.0A CN201611055370A CN106554188A CN 106554188 A CN106554188 A CN 106554188A CN 201611055370 A CN201611055370 A CN 201611055370A CN 106554188 A CN106554188 A CN 106554188A
- Authority
- CN
- China
- Prior art keywords
- parts
- metope
- construction material
- anticorrosion construction
- material according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of metope anticorrosion construction material, which is composed of the following components by weight：20 40 parts of kieselguhr, 20 40 parts of Kaolin, 20 40 parts of flyash, 10 15 parts of polrvinyl chloride, 5 15 parts of triethylamine, 8 15 parts of wood fibre, 15 parts of Calcium Carbonate, 26 parts of iron sesquioxide, 30 50 parts of acrylate, 20 30 parts of phenolic resin, 10 15 parts of polyvinyl alcohol, 7 19 parts of dimethyl ester, 30 50 parts of quick lime, 22 39 parts of zirconium dioxide, 10 20 parts of xanthan gum, 5 11 parts of foam plasticss, 27 parts of carbon cellulose, 13 parts of magnesium oxide, 0.5 2 parts of dispersant, 1.5 3.5 parts of water reducer, 0.1 3 parts of stabilizer, 0.1 0.5 parts of defoamer.The construction material of the present invention improves the corrosion resistance of metope well.
Description
Technical field
The present invention relates to a kind of construction material, specially a kind of metope anticorrosion construction material.
Background technology
Building anti-corrosion corrosion material is a critical function of building products, is to be related to the use value of building, use
Condition and sanitary condition, have influence on production activity, the quality of worklife of people, to ensureing that construction quality has important ground
Position.With the continuous improvement of social life condition, people increasingly pay attention to the quality of life of oneself, require in anticorrosion condition
Constantly increase.In recent years, quickly grow along with the development of social science and technology, novel anticorrosion product and its engineer applied technology,
And towards being developed from multilamellar to monolayer, from heat construction to the direction of cold construction.In the face of continuous progressive and renewal, the palm of science and technology
The preparation of construction and quality problems for holding anticorrosion engineering is particularly important, and the development to later architectural engineering has great meaning
Justice.
Building anti-corrosion erosion is prevents water from being adopted from construction material and on construction to the infiltration at some positions of building
The measure for taking.Using in roofing, hypogee, the under ground portion of building and the etch-proof interior room of need and water storage structure more than anticorrosion
Build thing etc..The measure taken by which and the difference of means, are divided into material antiseptic erosion and construction anticorrosion loses two big class.Main application neck
Domain includes roofing, underground, exterior wall and the interior of building construction；The municipal works such as urban road bridges and the underground space；It is public at a high speed
The bridge of road and high-speed railway, tunnel；The traffic engineering such as underground railway；Flume, reservoir, dam body, natural flow station and Shui Chu
Hydraulic engineerings such as reason, etc..With the progress and the development of Building technology of society, the application of building anti-corrosion corrosion material can also be to more
Multi-field extension.
The content of the invention
It is an object of the invention to provide a kind of metope anticorrosion construction material.
The purpose of the present invention can be achieved through the following technical solutions：
A kind of metope anticorrosion construction material, which is composed of the following components by weight：Kieselguhr 20-40 parts, kaolinite
Native 20-40 parts, flyash 20-40 parts, polrvinyl chloride 10-15 parts, triethylamine 5-15 parts, wood fibre 8-15 parts, Calcium Carbonate 1-5
Part, iron sesquioxide 2-6 parts, acrylate 30-50 parts, phenolic resin 20-30 parts, polyvinyl alcohol 10-15 parts, dimethyl ester
7-19 parts, quick lime 30-50 parts, zirconium dioxide 22-39 parts, xanthan gum 10-20 parts, foam plasticss 5-11 parts, carbon cellulose 2-7
Part, magnesium oxide 1-3 parts, dispersant 0.5-2 parts, water reducer 1.5-3.5 parts, stabilizer 0.1-3 parts, defoamer 0.1-0.5 parts.
Further, which is composed of the following components by weight：30 parts of kieselguhr, 30 parts of Kaolin, 30 parts of flyash,
12 parts of polrvinyl chloride, 10 parts of triethylamine, 10 parts of wood fibre, 2 parts of Calcium Carbonate, 4 parts of iron sesquioxide, 40 parts of acrylate, phenol
25 parts of urea formaldehyde, 12 parts of polyvinyl alcohol, 10 parts of dimethyl ester, 35 parts of quick lime, 30 parts of zirconium dioxide, 15 parts of xanthan gum, bubble
5 parts of foam plastics, 5 parts of carbon cellulose, 2 parts of magnesium oxide, 1 part of dispersant, 2 parts of water reducer, 2 parts of stabilizer, 0.3 part of defoamer.
Further, the dispersant is poly-hydroxy acid salt or polyacrylic acid sodium salt.
Further, the water reducer is melamine based water reducer.
Further, the stabilizer is barium stearate.
Further, the defoamer is silicon ether Copolymer.
Beneficial effects of the present invention：The construction material of the present invention improves the corrosion resistance of metope well.
Specific embodiment
The present invention is described further with reference to embodiment.
Embodiment 1
A kind of metope anticorrosion construction material, which is composed of the following components by weight：20 parts of kieselguhr, Kaolin 20
Part, 20 parts of flyash, 10 parts of polrvinyl chloride, 5 parts of triethylamine, 8 parts of wood fibre, 1 part of Calcium Carbonate, 2 parts of iron sesquioxide, propylene
30 parts of acid esters, 20 parts of phenolic resin, 10 parts of polyvinyl alcohol, 7 parts of dimethyl ester, 30 parts of quick lime, 22 parts of zirconium dioxide, xanthan
10 parts of glue, 5 parts of foam plasticss, 2 parts of carbon cellulose, 1 part of magnesium oxide, 0.5 part of dispersant, 1.5 parts of water reducer, 0.1 part of stabilizer,
0.1 part of defoamer.
Embodiment 2
A kind of metope anticorrosion construction material, which is composed of the following components by weight：40 parts of kieselguhr, Kaolin 40
Part, 40 parts of flyash, 15 parts of polrvinyl chloride, 15 parts of triethylamine, 15 parts of wood fibre, 5 parts of Calcium Carbonate, 6 parts of iron sesquioxide, third
50 parts of olefin(e) acid ester, 30 parts of phenolic resin, 15 parts of polyvinyl alcohol, 19 parts of dimethyl ester, 50 parts of quick lime, 39 parts of zirconium dioxide,
20 parts of xanthan gum, 11 parts of foam plasticss, 7 parts of carbon cellulose, 3 parts of magnesium oxide, 2 parts of dispersant, 3.5 parts of water reducer, stabilizer 3
Part, 0.5 part of defoamer.
Embodiment 3
A kind of metope anticorrosion construction material, which is composed of the following components by weight：30 parts of kieselguhr, Kaolin 30
Part, 30 parts of flyash, 12 parts of polrvinyl chloride, 10 parts of triethylamine, 10 parts of wood fibre, 2 parts of Calcium Carbonate, 4 parts of iron sesquioxide, third
40 parts of olefin(e) acid ester, 25 parts of phenolic resin, 12 parts of polyvinyl alcohol, 10 parts of dimethyl ester, 35 parts of quick lime, 30 parts of zirconium dioxide,
15 parts of xanthan gum, 5 parts of foam plasticss, 5 parts of carbon cellulose, 2 parts of magnesium oxide, 1 part of dispersant, 2 parts of water reducer, 2 parts of stabilizer disappear
0.3 part of infusion.
Above content is only to present configuration example and explanation, affiliated those skilled in the art couple
Described instantiation is made various modifications or supplements or substituted using similar mode, as long as will not past this right
Scope defined in book is sought, the protection domain of invention all should be belonged to.
Claims (6)
1. a kind of metope anticorrosion construction material, it is characterised in which is composed of the following components by weight：Kieselguhr 20-
40 parts, Kaolin 20-40 parts, flyash 20-40 parts, polrvinyl chloride 10-15 parts, triethylamine 5-15 parts, wood fibre 8-15 parts,
Calcium Carbonate 1-5 part, iron sesquioxide 2-6 parts, acrylate 30-50 parts, phenolic resin 20-30 parts, polyvinyl alcohol 10-15 parts,
Dimethyl ester 7-19 parts, quick lime 30-50 parts, zirconium dioxide 22-39 parts, xanthan gum 10-20 parts, foam plasticss 5-11 parts,
Carbon cellulose 2-7 parts, magnesium oxide 1-3 parts, dispersant 0.5-2 parts, water reducer 1.5-3.5 parts, stabilizer 0.1-3 parts, defoamer
0.1-0.5 parts.
2. a kind of metope anticorrosion construction material according to claim 1, it is characterised in which is by with the following group by weight
It is grouped into：30 parts of kieselguhr, 30 parts of Kaolin, 30 parts of flyash, 12 parts of polrvinyl chloride, 10 parts of triethylamine, 10 parts of wood fibre,
2 parts of Calcium Carbonate, 4 parts of iron sesquioxide, 40 parts of acrylate, 25 parts of phenolic resin, 12 parts of polyvinyl alcohol, dimethyl ester 10
Part, 35 parts of quick lime, 30 parts of zirconium dioxide, 15 parts of xanthan gum, 5 parts of foam plasticss, 5 parts of carbon cellulose, 2 parts of magnesium oxide, dispersion
1 part of agent, 2 parts of water reducer, 2 parts of stabilizer, 0.3 part of defoamer.
3. a kind of metope anticorrosion construction material according to claim 1, it is characterised in that the dispersant is poly-hydroxy acid salt
Or polyacrylic acid sodium salt.
4. a kind of metope anticorrosion construction material according to claim 1, it is characterised in that the water reducer subtracts for melamine system
Water preparation.
5. a kind of metope anticorrosion construction material according to claim 1, it is characterised in that the stabilizer is stearic acid
Barium.
6. a kind of metope anticorrosion construction material according to claim 1, it is characterised in that the defoamer is silicon ether copolymerization
Class.