CN106545708A - A kind of oil storage tank Antishocking metal hose and preparation method thereof - Google Patents
A kind of oil storage tank Antishocking metal hose and preparation method thereof Download PDFInfo
- Publication number
- CN106545708A CN106545708A CN201610959884.2A CN201610959884A CN106545708A CN 106545708 A CN106545708 A CN 106545708A CN 201610959884 A CN201610959884 A CN 201610959884A CN 106545708 A CN106545708 A CN 106545708A
- Authority
- CN
- China
- Prior art keywords
- metal
- parts
- bellowss
- metal hose
- storage tank
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of oil storage tank Antishocking metal hose and preparation method thereof, the metal hose includes the jointing at dictyosome part and its two ends, and the dictyosome includes metal bellowss, adapter, ring, wire sets；Wherein metal bellowss are made up of following components proportioning by weight：16～38 parts of ferrum, 12～26 parts of nickel, 2～7 parts of pyrite, 5～12 parts of zinc, 2～8 parts of titanium, 1～4 part of Graphene, 2～5 parts of magnesium sulfate, 1～4 part of carborundum.(1) metal hose of the present invention is not affected using length by flexible pipe, can reach compensation displacement, damping, the purpose for abating the noise；(2) the metal hose of the present invention frequency of vibration of itself is different from the frequency of earthquake, thus will not produce resonance, it is to avoid the generation of destruction.
Description
Technical field
The invention belongs to metal material field, it is related to a kind of metallic conduit, more particularly to a kind of oil storage tank antidetonation metal is soft
Pipe and preparation method thereof.
Background technology
Corrugated flexible metal tube is a kind of flexible duct of high-quality in modern industry pipeline, with good flexibility, is resisted
Many characteristics such as fatigability and pressure-bearing are high, temperature tolerance is good, corrosion-resistant, sealing is strong, than other flexible pipes, (rubber hose, plastics are soft
Pipe) life-span it is much higher.It is widely used in Aeronautics and Astronautics, oil, chemical industry, iron and steel, electric power, papermaking, building, rubber, weaving
In the industry such as printing and dyeing, medicine, food, transportation.With the development, soft to high-quality, high-performance corrugated metal of modern industry
The demand of pipe can be increasing.
The connection of tank advance outlet conduit generally should be using flexible or elastic connection.Earthquake intensity more than or equal to 7 grades,
In the case that geology is soft and when caliber is more than or equal to 150mm, oil storage tank antidetonation metal hose can be set.In oil storage tank
Import and export and corrugated flexible metal tube is added on pipeline, with the broken ring of the earthquake for mitigating oil storage tank, and for compensating under the ground of oil storage tank
Heavy, installation deviation when expanding with heat and contract with cold and constructing of pipeline etc..
Corrugated tube is through high accuracy plastic working molding by the very thin seamless or longitudinal seam stainless steel tube of tube wall.Ripple
The elasticity of metal hose determines which has good flexibility and fatigue resistance, make it be easy to absorb various motion deformations and
Cyclic loading, the ability for especially having compensation big displacement in pipe-line system.
The net of ripple outer tube layer is formed by certain parameter braiding by stainless steel silk or steel wire, is corrugated flexible metal tube
Pressure parts in pressure pipeline, while play a protective role to corrugated tube, according to the pressure size in pipeline and
Application places, may be selected one or more layers rustless steel steel wire or steel band and are woven.
The material that corrugated flexible metal tube major part is made in prior art is austenitic stainless steel, hereby it is ensured that flexible pipe
With good temperature tolerance and corrosion resistance, the operating temperature range of flexible pipe is extremely wide, generally subzero 196 DEG C～425 DEG C, by pipe
The rustless steel trade mark that the corrosion Sexual behavior mode of road institute pumped (conveying) medium is suitable for, it is ensured that the corrosion resistance of metal hose.Additionally, managing for compensation
Road displacement, installation deviation, foundation settlement and absorption vibration and reduction noise etc., preferably from annular corrugated metal hose；To pressure
Power is higher but the occasion that is infrequently subjected to displacement and vibrates, preferably from helical corrugation metal hose.But in above-mentioned prior art
If metal hose using length it is longer will produce unstability, increase flow resistance and increase mechanical damage and vibration the problems such as；If
Metal hose is too short, may not reach compensation displacement, damping, the purpose such as abate the noise, and can also cause bending stress excessive, shadow
Ring the life-span.
The content of the invention
The purpose of the present invention is：In order to overcome the defect of prior art, obtain, can
Compensation displacement, damping, the metal hose of purpose for abating the noise are reached, the invention provides a kind of oil storage tank Antishocking metal hose
And preparation method thereof.
Technical scheme：A kind of oil storage tank Antishocking metal hose, the metal hose include the company at dictyosome part and its two ends
Joint, the dictyosome include metal bellowss, adapter, ring, wire sets；Wherein metal bellowss by following components by weight
Number proportioning is made：16～38 parts of ferrum, 12～26 parts of nickel, 2～7 parts of pyrite, 5～12 parts of zinc, 2～8 parts of titanium, Graphene 1～4
Part, 2～5 parts of magnesium sulfate, 1～4 part of carborundum.
Preferably, the metal hose includes the jointing at dictyosome part and its two ends, and the dictyosome includes metal wave
Stricture of vagina pipe, adapter, ring, wire sets；Wherein metal bellowss are made up of following components proportioning by weight：32 parts of ferrum, nickel 21
Part, 5 parts of pyrite, 9 parts of zinc, 6 parts of titanium, 3 parts of Graphene, 4 parts of magnesium sulfate, 3 parts of carborundum.
A kind of preparation method of oil storage tank Antishocking metal hose, metal hose are welded by dictyosome part and two ends jointing
Form, dictyosome is welded by metal bellowss, adapter, ring, wire sets；The preparation process of the metal bellowss is as follows：
(1) prepared by matrix：By in ferrum and nickel input metal smelter, melt under the conditions of temperature is for 1660～2400 DEG C, so
Put into zinc and pyrite afterwards thereto, to after melting is mixed completely, cool the temperature to 1560 DEG C, be incubated 2～5 hours, obtain matrix；
(2) prepared by additive：By Graphene, magnesium sulfate and carborundum mix after grind into powder, grinding particle diameter be 50～
120 mesh, titanium is melted under the conditions of 1660～1700 DEG C, is added thereto to mixed-powder after melting completely, to after mixing completely
1220～1380 DEG C are cooled to, additive is prepared；
(3) prepared by crude green body：In the metal smelter described in additive input step (1) that step (2) is obtained, and by stove
Temperature rises to 2230～2560 DEG C, is incubated 5～15 minutes；Jing moulds are processed into the straight tube that specification is 19.8 × 0.8mm, along straight tube
The full helical corrugation of outer wall spinning 4, spiral 1.6～2.5mm of groove depth, spiral 6.4～7.5mm of separation, 20～35 ° of helical angle,
Again by straight tube undergauge section one 7～11mm of transition arc of spinning, transition arc is obtained thick to 14.6～14.78mm of tube end diameter
Base metal bellowss；
(4) mechanical grinding：The crude green body metal bellowss that step (3) is obtained process burr using mechanical frosted, to surface
It is smooth；
(5) mechanical performance sizing：Industrial lubricants, juxtaposition are poured into into the metal bellowss Jing after step (4) process
Freezing processing is carried out 1～3 hour at -10～-20 DEG C；
(6) clean：The metal bellowss after step (5) freezing processing are taken out, the industrial lubricants circulation in collecting pipe makes
With cleaning metal bellowss with the aqueous hydrochloric acid solution that mass concentration is 1～5%, can be prepared by after being dried.
Preferably, in step (1) prepared by matrix：Ferrum and nickel are put in metal smelter, under the conditions of temperature is 2250 DEG C
Melting, then puts into zinc and pyrite thereto, to after melting is mixed completely, cools the temperature to 1560 DEG C, be incubated 4 hours, obtain
Matrix.
Preferably, in step (2) prepared by additive：Grind into powder after Graphene, magnesium sulfate and carborundum are mixed, powder
Abrasive particle footpath is 100 mesh, and titanium melt under the conditions of 1680 DEG C, is added thereto to mixed-powder completely, to mixing completely after melting
After be cooled to 1330 DEG C, prepare additive.
Preferably, in step (3) prepared by crude green body：The metal described in additive input step (1) that step (2) is obtained melts
In stove, and in-furnace temperature is risen to into 2480 DEG C, be incubated 12 minutes；Jing moulds are processed into the straight tube that specification is 19.8 × 0.8mm, edge
The full helical corrugation of straight tube outer wall spinning 4, spiral groove depth 2.2mm, spiral separation 6.9mm, 20～35 ° of helical angle, then will be straight
Pipe undergauge section one transition arc 9mm of spinning, transition arc are obtained crude green body metal bellowss to tube end diameter 14.72mm.
Preferably, mechanical performance sizing in step (5)：Industry is poured into into the metal bellowss Jing after step (4) process
Lubricant, carries out freezing processing 2 hours at being placed in -16 DEG C.
Preferably, cleaning in step (6)：Take out the metal bellowss after step (5) freezing processing, the industry in collecting pipe
Lubricant is recycled, and metal bellowss are cleaned with the aqueous hydrochloric acid solution that mass concentration is 3.5%, be can be prepared by after being dried.
Beneficial effect：(1) metal hose of the present invention is not affected using length by flexible pipe, can reach compensation position
Shifting, damping, the purpose for abating the noise；(2) the metal hose of the present invention frequency of vibration of itself is different from the frequency of earthquake, because
Without producing resonance, it is to avoid the generation of destruction.
Specific embodiment
Embodiment 1
A kind of oil storage tank Antishocking metal hose, the metal hose include the jointing at dictyosome part and its two ends, institute
Stating dictyosome includes metal bellowss, adapter, ring, wire sets；Wherein metal bellowss are by following components proportioning by weight
Make：16 parts of ferrum, 12 parts of nickel, 2 parts of pyrite, 5 parts of zinc, 2 parts of titanium, 1 part of Graphene, 2 parts of magnesium sulfate, 1 part of carborundum.
A kind of preparation method of oil storage tank Antishocking metal hose, metal hose are welded by dictyosome part and two ends jointing
Form, dictyosome is welded by metal bellowss, adapter, ring, wire sets；The preparation process of the metal bellowss is as follows：
(1) prepared by matrix：By in ferrum and nickel input metal smelter, melt under the conditions of temperature is for 1660 DEG C, then to which
Middle input zinc and pyrite, to after melting is mixed completely, cool the temperature to 1560 DEG C, are incubated 2 hours, obtain matrix；
(2) prepared by additive：Grind into powder after Graphene, magnesium sulfate and carborundum are mixed, grinding particle diameter are 50 mesh,
Titanium is melted under the conditions of 1660 DEG C, after melting completely, mixed-powder is added thereto to, and 1220 DEG C is cooled to after mixing completely,
Prepare additive；
(3) prepared by crude green body：In the metal smelter described in additive input step (1) that step (2) is obtained, and by stove
Temperature rises to 2230 DEG C, is incubated 5 minutes；Jing moulds are processed into the straight tube that specification is 19.8 × 0.8mm, along straight tube outer wall spinning 4
The full helical corrugation of bar, spiral groove depth 1.6mm, spiral separation 6.4mm, 20 ° of helical angle, then by straight tube undergauge section one mistake of spinning
Circular arc 7mm is crossed, transition arc is obtained crude green body metal bellowss to tube end diameter 14.6mm；
(4) mechanical grinding：The crude green body metal bellowss that step (3) is obtained process burr using mechanical frosted, to surface
It is smooth；
(5) mechanical performance sizing：Industrial lubricants, juxtaposition are poured into into the metal bellowss Jing after step (4) process
Freezing processing is carried out at -10 DEG C 1 hour；
(6) clean：The metal bellowss after step (5) freezing processing are taken out, the industrial lubricants circulation in collecting pipe makes
With cleaning metal bellowss with the aqueous hydrochloric acid solution that mass concentration is 1%, can be prepared by after being dried.
Embodiment 2
A kind of oil storage tank Antishocking metal hose, the metal hose include the jointing at dictyosome part and its two ends, institute
Stating dictyosome includes metal bellowss, adapter, ring, wire sets；Wherein metal bellowss are by following components proportioning by weight
Make：32 parts of ferrum, 21 parts of nickel, 5 parts of pyrite, 9 parts of zinc, 6 parts of titanium, 3 parts of Graphene, 4 parts of magnesium sulfate, 3 parts of carborundum.
A kind of preparation method of oil storage tank Antishocking metal hose, metal hose are welded by dictyosome part and two ends jointing
Form, dictyosome is welded by metal bellowss, adapter, ring, wire sets；The preparation process of the metal bellowss is as follows：
(1) prepared by matrix：By in ferrum and nickel input metal smelter, melt under the conditions of temperature is for 2250 DEG C, then to which
Middle input zinc and pyrite, to after melting is mixed completely, cool the temperature to 1560 DEG C, are incubated 4 hours, obtain matrix；
(2) prepared by additive：Grind into powder after Graphene, magnesium sulfate and carborundum are mixed, grinding particle diameter are 100
Mesh, titanium is melted under the conditions of 1680 DEG C, is added thereto to mixed-powder after melting completely, to after mixing completely is cooled to 1330
DEG C, prepare additive；
(3) prepared by crude green body：In the metal smelter described in additive input step (1) that step (2) is obtained, and by stove
Temperature rises to 2480 DEG C, is incubated 12 minutes；Jing moulds are processed into the straight tube that specification is 19.8 × 0.8mm, along straight tube outer wall spinning 4
The full helical corrugation of bar, spiral groove depth 2.2mm, spiral separation 6.9mm, 20～35 ° of helical angle, then by straight tube undergauge section spinning one
Individual transition arc 9mm, transition arc are obtained crude green body metal bellowss to tube end diameter 14.72mm；
(4) mechanical grinding：The crude green body metal bellowss that step (3) is obtained process burr using mechanical frosted, to surface
It is smooth；
(5) mechanical performance sizing：Industrial lubricants, juxtaposition are poured into into the metal bellowss Jing after step (4) process
Freezing processing is carried out at -16 DEG C 2 hours；
(6) clean：The metal bellowss after step (5) freezing processing are taken out, the industrial lubricants circulation in collecting pipe makes
With cleaning metal bellowss with the aqueous hydrochloric acid solution that mass concentration is 3.5%, can be prepared by after being dried.
Embodiment 3
A kind of oil storage tank Antishocking metal hose, the metal hose include the jointing at dictyosome part and its two ends, institute
Stating dictyosome includes metal bellowss, adapter, ring, wire sets；Wherein metal bellowss are by following components proportioning by weight
Make：38 parts of ferrum, 26 parts of nickel, 7 parts of pyrite, 12 parts of zinc, 8 parts of titanium, 4 parts of Graphene, 5 parts of magnesium sulfate, 4 parts of carborundum.
A kind of preparation method of oil storage tank Antishocking metal hose, metal hose are welded by dictyosome part and two ends jointing
Form, dictyosome is welded by metal bellowss, adapter, ring, wire sets；The preparation process of the metal bellowss is as follows：
(1) prepared by matrix：By in ferrum and nickel input metal smelter, melt under the conditions of temperature is for 2400 DEG C, then to which
Middle input zinc and pyrite, to after melting is mixed completely, cool the temperature to 1560 DEG C, are incubated 5 hours, obtain matrix；
(2) prepared by additive：Grind into powder after Graphene, magnesium sulfate and carborundum are mixed, grinding particle diameter are 120
Mesh, titanium is melted under the conditions of 1700 DEG C, is added thereto to mixed-powder after melting completely, to after mixing completely is cooled to 1380
DEG C, prepare additive；
(3) prepared by crude green body：In the metal smelter described in additive input step (1) that step (2) is obtained, and by stove
Temperature rises to 2560 DEG C, is incubated 15 minutes；Jing moulds are processed into the straight tube that specification is 19.8 × 0.8mm, along straight tube outer wall spinning 4
The full helical corrugation of bar, spiral groove depth 2.5mm, spiral separation 7.5mm, 35 ° of helical angle, then by straight tube undergauge section one mistake of spinning
Circular arc 11mm is crossed, transition arc is obtained crude green body metal bellowss to tube end diameter 14.78mm；
(4) mechanical grinding：The crude green body metal bellowss that step (3) is obtained process burr using mechanical frosted, to surface
It is smooth；
(5) mechanical performance sizing：Industrial lubricants, juxtaposition are poured into into the metal bellowss Jing after step (4) process
Freezing processing is carried out at -20 DEG C 3 hours；
(6) clean：The metal bellowss after step (5) freezing processing are taken out, the industrial lubricants circulation in collecting pipe makes
With cleaning metal bellowss with the aqueous hydrochloric acid solution that mass concentration is 5%, can be prepared by after being dried.
The oil storage tank Antishocking metal hose that embodiment 1～3 is prepared is detected, it is as a result as shown in the table：
Claims (8)
1. a kind of oil storage tank Antishocking metal hose, it is characterised in that the metal hose includes the company at dictyosome part and its two ends
Joint, the dictyosome include metal bellowss, adapter, ring, wire sets；Wherein metal bellowss by following components by weight
Number proportioning is made：16～38 parts of ferrum, 12～26 parts of nickel, 2～7 parts of pyrite, 5～12 parts of zinc, 2～8 parts of titanium, Graphene 1～4
Part, 2～5 parts of magnesium sulfate, 1～4 part of carborundum.
2. a kind of oil storage tank Antishocking metal hose according to claim 1, it is characterised in that the metal hose includes net
Body portion and its jointing at two ends, the dictyosome include metal bellowss, adapter, ring, wire sets；Wherein wavy metal
Pipe is made up of following components proportioning by weight：32 parts of ferrum, 21 parts of nickel, 5 parts of pyrite, 9 parts of zinc, 6 parts of titanium, 3 parts of Graphene, sulfur
4 parts of sour magnesium, 3 parts of carborundum.
3. the preparation method of a kind of oil storage tank Antishocking metal hose described in claim 1, it is characterised in that metal hose is by net
Body portion and two ends jointing are welded, and dictyosome is welded by metal bellowss, adapter, ring, wire sets；The gold
The preparation process of category corrugated tube is as follows：
(1) prepared by matrix：By in ferrum and nickel input metal smelter, melt under the conditions of temperature is for 1660～2400 DEG C, Ran Houxiang
Zinc and pyrite are wherein put into, to after melting is mixed completely, 1560 DEG C is cooled the temperature to, 2～5 hours are incubated, matrix is obtained；
(2) prepared by additive：Grind into powder after Graphene, magnesium sulfate and carborundum are mixed, grinding particle diameter are 50～120
Mesh, titanium is melted under the conditions of 1660～1700 DEG C, is added thereto to mixed-powder after melting completely, is lowered the temperature to after mixing completely
To 1220～1380 DEG C, additive is prepared；
(3) prepared by crude green body：In the metal smelter described in additive input step (1) that step (2) is obtained, and by in-furnace temperature
2230～2560 DEG C are risen to, 5～15 minutes are incubated；Jing moulds are processed into the straight tube that specification is 19.8 × 0.8mm, along straight tube outer wall
The full helical corrugation of spinning 4, spiral 1.6～2.5mm of groove depth, spiral 6.4～7.5mm of separation, 20～35 ° of helical angle, then will
Straight tube undergauge section one 7～11mm of transition arc of spinning, transition arc are obtained crude green body gold to 14.6～14.78mm of tube end diameter
Category corrugated tube；
(4) mechanical grinding：The crude green body metal bellowss that step (3) is obtained process burr using mechanical frosted, smooth to surface；
(5) mechanical performance sizing：Industrial lubricants are poured into into the metal bellowss Jing after step (4) process, -10 are placed in
Freezing processing is carried out at～-20 DEG C 1～3 hour；
(6) clean：The metal bellowss after step (5) freezing processing are taken out, the industrial lubricants in collecting pipe are recycled, used
Mass concentration is 1～5% aqueous hydrochloric acid solution cleaning metal bellowss, be can be prepared by after being dried.
4. a kind of preparation method of oil storage tank Antishocking metal hose according to claim 3, it is characterised in that step (1)
It is prepared by middle matrix：By ferrum and nickel input metal smelter in, temperature be 2250 DEG C under the conditions of melt, then thereto put into zinc and
Pyrite, to after melting is mixed completely, cools the temperature to 1560 DEG C, is incubated 4 hours, obtains matrix.
5. a kind of preparation method of oil storage tank Antishocking metal hose according to claim 3, it is characterised in that step (2)
It is prepared by middle additive：Grind into powder after Graphene, magnesium sulfate and carborundum are mixed, grinding particle diameter are 100 mesh, and titanium is existed
Melting under the conditions of 1680 DEG C, after melting completely, being added thereto to mixed-powder, 1330 DEG C are cooled to after mixing completely, preparation is obtained
Obtain additive.
6. a kind of preparation method of oil storage tank Antishocking metal hose according to claim 3, it is characterised in that step (3)
It is prepared by middle crude green body：In the metal smelter described in additive input step (1) that step (2) is obtained, and in-furnace temperature is risen to
2480 DEG C, it is incubated 12 minutes；Jing moulds are processed into the straight tube that specification is 19.8 × 0.8mm, along 4 full spirals of straight tube outer wall spinning
Ripple, spiral groove depth 2.2mm, spiral separation 6.9mm, 20～35 ° of helical angle, then by straight tube undergauge section one transition circle of spinning
Arc 9mm, transition arc are obtained crude green body metal bellowss to tube end diameter 14.72mm.
7. a kind of preparation method of oil storage tank Antishocking metal hose according to claim 3, it is characterised in that step (5)
Middle mechanical performance sizing：Industrial lubricants are poured into into the metal bellowss Jing after step (4) process, is placed in entering at -16 DEG C
Row freezing processing 2 hours.
8. a kind of preparation method of oil storage tank Antishocking metal hose according to claim 3, it is characterised in that step (6)
Middle cleaning：The metal bellowss after step (5) freezing processing are taken out, the industrial lubricants in collecting pipe are recycled, and use quality
Concentration is 3.5% aqueous hydrochloric acid solution cleaning metal bellowss, be can be prepared by after being dried.