CN106511106B - A kind of nano-titanium dioxide/nano zinc oxide composite powder material - Google Patents
A kind of nano-titanium dioxide/nano zinc oxide composite powder material Download PDFInfo
- Publication number
- CN106511106B CN106511106B CN201610929105.4A CN201610929105A CN106511106B CN 106511106 B CN106511106 B CN 106511106B CN 201610929105 A CN201610929105 A CN 201610929105A CN 106511106 B CN106511106 B CN 106511106B
- Authority
- CN
- China
- Prior art keywords
- nano
- titanium dioxide
- powder material
- composite powder
- zinc oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention belongs to technical field of nano material, and in particular to a kind of nano-titanium dioxide/nano zinc oxide composite powder material is made by following steps: 1) zinc acetate and butyl titanate being dissolved in dehydrated alcohol, stirred evenly, and mixed solution is made;2) water bath method will be carried out in mixed solution obtained, is then put in baking oven and is dried, places into and carries out high-temperature roasting in Muffle furnace, and composite granule is made;3) by composite granule obtained and stearic acid, carboxymethyl cellulose, hexamethylene mixing and ball milling, nano-titanium dioxide/nano zinc oxide composite powder material is obtained.After the present invention organically combines nano zine oxide and nano-titanium dioxide, the UVA and UVB in solar ultraviolet can be effectively shielded.
Description
Technical field
The invention belongs to technical field of nano material, and in particular to a kind of nano-titanium dioxide/nano zinc oxide compound powder
Body material.
Background technique
The ultraviolet light that solar radiation comes out can be divided by its wavelength: wavelength is the long wave ultraviolet of 320~400nm
UVA, the short wave ultraviolet UVC that the ultraviolet B radiation UVB and wavelength that wavelength is 290~320nm are 200~290nm.Research knot
Fruit shows: although the UVA for accounting for solar ultraviolet 91% will not cause fierce reaction as UVB, penetration is strong, 35~
50% can reach corium, keep the fibr tissue of intradermal injured, lead to shouting pain, cutis laxa and tanned, be to cause skin photoage
And one of the main reason for cutaneum carcinoma.UVC due to being absorbed substantially in atmosphere outer layer.
Nano zine oxide and nano-titanium dioxide are two kinds of important and widely used inorganic UV sun-screening agents, but its is right
The screening ability of UVA and UVB be it is discrepant, nano-titanium dioxide obstruct UVB effect it is very good, but to the shielding of UVA imitate
Fruit is not good enough;Nano zine oxide is undesirable to the shield effectiveness of UVB, but it obstructs UVA effect and is better than nano-titanium dioxide.
In order to effectively obstruct UVA and UVB, reaches overall protected purpose, need thus comprehensive in sunscreen cosmetic
Close the characteristic for utilizing nano zine oxide and nano-titanium dioxide.Therefore, it develops one kind and has both nano-titanium dioxide and nano oxidized
The composite powder material of zinc advantage is research hotspot.
Summary of the invention
The purpose of the present invention is to provide a kind of nano-titanium dioxide/nano zinc oxide composite powder materials.
In order to achieve the object of the present invention, The technical solution adopted by the invention is as follows:
A kind of nano-titanium dioxide/nano zinc oxide composite powder material, the composite powder material are made by following steps:
Step 1): zinc acetate and butyl titanate are dissolved in dehydrated alcohol, are stirred evenly, and mixed solution is made;
Step 2: will carry out water bath method, be then put in baking oven and be dried in mixed solution made from step 1), then
It is put into Muffle furnace and carries out high-temperature roasting, composite granule is made;
Step 3): by composite granule made from step 2 and stearic acid, carboxymethyl cellulose, hexamethylene mixing and ball milling, i.e.,
Nano-titanium dioxide/nano zinc oxide composite powder material is made;
Wherein, the mass volume ratio of the composite granule and stearic acid, carboxymethyl cellulose, cyclohexane is 1g:(0.5
~0.8) g:(0.05~0.1) g:(5~10) mL.
Preferably, in step 1), the mass ratio of the material of the zinc acetate and butyl titanate is 1:(1~3), the vinegar
The mass volume ratio 1g:10mL of sour zinc and dehydrated alcohol.
Preferably, in step 2, the high-temperature roasting condition are as follows: under excess oxygen, be warming up to 500 DEG C with 5 DEG C/min
Roasting 1~3 hour.
Preferably, in step 3), Ball-milling Time is 1~3 hour.
Compared with prior art, the advantageous effects of technical solution of the present invention are:
1, nano zine oxide of the invention/nano-titanium dioxide composite powder material can effectively shield after organically combining
Cover the UVA and UVB in solar ultraviolet.
2, nano zine oxide of the invention/nano-titanium dioxide composite powder material, through stearic acid, carboxymethyl cellulose
Ball-milling reaction, changes the surface nature of composite powder material, and nano zine oxide/nano-titanium dioxide composite powder material has
Preferably dispersion performance.
3, raw material of the invention is easy to get, at low cost, and reaction is easy to control.
Specific embodiment
The present invention will be further described combined with specific embodiments below.
A kind of nano-titanium dioxide/nano zinc oxide composite powder material, the composite powder material are made by following steps:
Step 1): zinc acetate and butyl titanate are dissolved in dehydrated alcohol, are stirred evenly, and mixed solution is made;
Step 2: will carry out water bath method, be then put in baking oven and be dried in mixed solution made from step 1), then
It is put into Muffle furnace and carries out high-temperature roasting, composite granule is made;
Step 3): by composite granule made from step 2 and stearic acid, carboxymethyl cellulose, hexamethylene mixing and ball milling, i.e.,
Nano-titanium dioxide/nano zinc oxide composite powder material is made.
Embodiment 1
1) it weighs 18.35g zinc acetate and 34.03g butyl titanate is dissolved in 183.5mL dehydrated alcohol, stir evenly, be made
Mixed solution.
2) by mixed solution at 80 DEG C water bath method, be then put in baking oven and be dried, place into Muffle furnace,
Under excess oxygen, 500 DEG C are warming up to 5 DEG C/min and is roasted 2 hours, composite granule is made.
3) 5g composite granule and 3g stearic acid, 0.04g carboxymethyl cellulose, 40mL cyclohexane mixing and ball milling 2 hours are weighed,
?.
Embodiment 2
1) it weighs 18.35g zinc acetate and 34.03g butyl titanate is dissolved in 183.5mL dehydrated alcohol, stir evenly, be made
Mixed solution.
2) by mixed solution at 65 DEG C water bath method, be then put in baking oven and be dried, place into Muffle furnace,
Under excess oxygen, 500 DEG C are warming up to 5 DEG C/min and is roasted 1 hour, composite granule is made.
3) it weighs 5g composite granule and 2.5g stearic acid, 0.25g carboxymethyl cellulose, 25mL cyclohexane mixing and ball milling 1 is small
When.
Embodiment 3
1) it weighs 18.35g zinc acetate and 34.03g butyl titanate is dissolved in 183.5mL dehydrated alcohol, stir evenly, be made
Mixed solution.
2) by mixed solution at 95 DEG C water bath method, be then put in baking oven and be dried, place into Muffle furnace,
Under excess oxygen, 500 DEG C are warming up to 5 DEG C/min and is roasted 3 hours, composite granule is made.
3) 5g composite granule and 4g stearic acid, 0.5g carboxymethyl cellulose, 50mL cyclohexane mixing and ball milling 3 hours are weighed,
?.
Embodiment 4
Nano-titanium dioxide made from step 1~3/nano zinc oxide composite powder material is subjected to average grain diameter and light transmission
The test of rate.Wherein, T308 indicates the transmitance at 308nm, and reflection is screening ability of the composite granule to UVB, T308
Be worth it is smaller, illustrate shield UVB ability it is better;T360 indicates the transmitance at 360nm, and reflection is composite granule to UVA
Screening ability, T360 value is smaller, illustrates that shielding UVA ability is better.Test result shows that the average grain diameter of composite granule exists
100nm, T308 value are that 0, T360 value is not more than 2.Nano-titanium dioxide made from the method for the present invention-zinc oxide composite powder material
Average particle size is small, strong to the absorbability of UVA and UVB.
Claims (1)
1. a kind of nano-titanium dioxide/nano zinc oxide composite powder material, it is characterised in that: the composite powder material is by as follows
Step is made:
1) it weighs 18.35g zinc acetate and 34.03g butyl titanate is dissolved in 183.5mL dehydrated alcohol, stir evenly, mixing is made
Solution;
2) by mixed solution at 65 DEG C water bath method, be then put in baking oven and be dried, place into Muffle furnace, oxygen-enriched
Under the conditions of, 500 DEG C are warming up to 5 DEG C/min and is roasted 1 hour, and composite granule is made;
3) 5g composite granule and 2.5g stearic acid, 0.25g carboxymethyl cellulose, 25mL cyclohexane mixing and ball milling 1 hour are weighed, i.e.,
It can.