CN106497379A - A kind of aqueous one-component fireproof coating and preparation method thereof - Google Patents

A kind of aqueous one-component fireproof coating and preparation method thereof Download PDF

Info

Publication number
CN106497379A
CN106497379A CN201611049279.8A CN201611049279A CN106497379A CN 106497379 A CN106497379 A CN 106497379A CN 201611049279 A CN201611049279 A CN 201611049279A CN 106497379 A CN106497379 A CN 106497379A
Authority
CN
China
Prior art keywords
parts
epoxy resin
standby
raw material
aqueous
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611049279.8A
Other languages
Chinese (zh)
Inventor
王顺峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Huanyu Textile Technology Co Ltd
Original Assignee
Jiangsu Huanyu Textile Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Huanyu Textile Technology Co Ltd filed Critical Jiangsu Huanyu Textile Technology Co Ltd
Priority to CN201611049279.8A priority Critical patent/CN106497379A/en
Publication of CN106497379A publication Critical patent/CN106497379A/en
Pending legal-status Critical Current

Abstract

The present invention discloses a kind of aqueous one-component fireproof coating and preparation method thereof, it is characterised in that：It is made up of following raw material：Epoxy resin, methyl trichlorosilane, polyaminoester emulsion, ATO dispersion liquids, acrylic modified epoxy resin, amino resins, glycol ether, two methylene level diisocyanate of durol, triethylamine, sodium bicarbonate, non-ionic associative type polyurethane, benzimidazole methyl carbamate, polydimethylsiloxane, deionized water, water；The aqueous one-component fireproof coating and preparation method thereof water resistance is high, effect of heat insulation and light transmission are high.

Description

A kind of aqueous one-component fireproof coating and preparation method thereof
Technical field
The present invention relates to a kind of aqueous one-component fireproof coating and preparation method thereof.
Background technology
Glass and glass, because of attractive in appearance and performance needs, need to coat coating thereon, but existing glass coating There is a problem that as follows：1st, existing glass coating is dual-component coating, needs to allocate on the spot, after deployed, it is necessary to Just use in very short time（In several hours）, will otherwise fail, not only using inconvenience, and easily cause the wave of material Take；2nd, the glass coating that sells currently on the market mostly is oil paint, and its film forming matter is essentially from petroleum chemicals, and its solvent Also adopt organic solvent more, usually contain the noxious substances such as formaldehyde, free TDI and dimethylbenzene, these materials are given birth in glass coating Constantly come out during product process and use, not only cause environmental pollution, and damage health；3rd, to water, ethanol Poor performance is tolerated Deng common liquid, wearability is poor.
Content of the invention
The technical problem to be solved in the present invention is to provide that a kind of water resistance is high, the water that good heat-insulation effect and light transmission are high Property one-component glass coating.
For solving the above problems, the present invention is adopted the following technical scheme that：
A kind of aqueous one-component fireproof coating and preparation method thereof, is made up of following raw material：Epoxy resin, methyl trichlorosilane, Polyaminoester emulsion, ATO dispersion liquids, acrylic modified epoxy resin, amino resins, glycol ether, two methylene level two of durol Isocyanates, triethylamine, sodium bicarbonate, non-ionic associative type polyurethane, benzimidazole methyl carbamate, polydimethylsiloxanes Alkane, deionized water, water；The raw material is made up of following parts by weight proportioning：Epoxy resin 10-18 parts, methyl trichlorosilane 12- 20 parts, polyaminoester emulsion 14-20 parts, ATO dispersion liquid 8-16 parts, acrylic modified epoxy resin 8-14 parts, amino resins 14-18 Part, glycol ether 14-18 parts, two methylene level diisocyanate 10-16 parts of durol, triethylamine 6-10 parts, sodium bicarbonate 10- 16 parts, non-ionic associative type polyurethane 5-10 parts, benzimidazole methyl carbamate 4-8 parts, polydimethylsiloxane 12-16 Part, deionized water 10-20 parts, water 12-20 parts.
Further, the raw material is made up of following optimum parts by weight proportioning：14 parts of epoxy resin, methyl trichlorosilane 16 parts, 17 parts of polyaminoester emulsion, 12 parts of ATO dispersion liquids, 11 parts of acrylic modified epoxy resin, 16 parts of amino resins, dihydroxylic alcohols 16 parts of ether, two 13 parts of methylene level diisocyanate of durol, 8 parts of triethylamine, 13 parts of sodium bicarbonate, the poly- ammonia of non-ionic associative type 7.5 parts of ester, 6 parts of benzimidazole methyl carbamate, 14 parts of polydimethylsiloxane, 15 parts of deionized water, 16 parts of water.
The invention solves the problems that another technical problem be to provide a kind of aqueous one-component fireproof coating and its preparation side Method, comprises the following steps：
1）By epoxy resin 10-18 parts, methyl trichlorosilane 12-20 parts, the mixing of deionized water 10-20 parts, it is put into sand milling, divides Dissipate, stir in multiple purpose aeroplane, under the conditions of rotating speed is 2800rmp, disperses 15min at a high speed, standby；
2) polyaminoester emulsion 14-20 parts are added on the magnetic force heating stirrer with magneton, are 500r/min bars in rotating speed It is stirred continuously under part, continues 5min, standby；
3）To step 2）In again plus ATO dispersion liquid 8-16 parts, add water 12-20 parts, mixing speed to be adjusted to 1200r/min, continue 40min, standby；
4）Glycol ether 14-18 parts and the dehydration of two methylene level diisocyanate 10-16 parts of durol are added in four-hole boiling flask, Nitrogen protection is passed through, after 20min, triethylamine 6-10 parts is added, temperature is down to 30 DEG C, standby；
5）Sodium bicarbonate 10-16 parts are added to step 4）Raw material in, adjust pH value, stir, standby；
6）Will acrylic modified epoxy resin 8-14 parts add high-speed dispersing kettle in, add polydimethylsiloxane 12-16 parts, Non-ionic associative type polyurethane 5-10 parts, benzimidazole methyl carbamate 4-8 parts, stir, standby；
7）By step 6）Middle raw material sends into grinding machine for grinding to fineness≤12 μm, adds amino resins 14-18 parts, and stirring is Even, standby；
8）By step 1）, step 3）With step 5）In raw material be added to step 7）In, stir, be cooled to room temperature, you can Obtain a kind of aqueous one-component glass coating.
Beneficial effects of the present invention are：Need not allocate on the spot during the aqueous one-component glass coating use, and possess Longer working life, it is to avoid the problems such as what conventional two-component coating easily occurred cause wastes, working life is short；This glass coating fills After dividing solidification, adhesive force is strong, intensity is big, tolerate excellent performance to common liquids such as water, ethanol, and exterior water moistens smooth, fire line Can be stable, light transmittance is high and effect of heat insulation is obvious.
Specific embodiment
Embodiment 1
A kind of aqueous one-component fireproof coating and preparation method thereof, is made up of following raw material：Epoxy resin, methyl trichlorosilane, Polyaminoester emulsion, ATO dispersion liquids, acrylic modified epoxy resin, amino resins, glycol ether, two methylene level two of durol Isocyanates, triethylamine, sodium bicarbonate, non-ionic associative type polyurethane, benzimidazole methyl carbamate, polydimethylsiloxanes Alkane, deionized water, water；The raw material is made up of following parts by weight proportioning：Epoxy resin 10-18 parts, methyl trichlorosilane 12- 20 parts, polyaminoester emulsion 14-20 parts, ATO dispersion liquid 8-16 parts, acrylic modified epoxy resin 8-14 parts, amino resins 14-18 Part, glycol ether 14-18 parts, two methylene level diisocyanate 10-16 parts of durol, triethylamine 6-10 parts, sodium bicarbonate 10- 16 parts, non-ionic associative type polyurethane 5-10 parts, benzimidazole methyl carbamate 4-8 parts, polydimethylsiloxane 12-16 Part, deionized water 10-20 parts, water 12-20 parts.
A kind of aqueous one-component fireproof coating and preparation method thereof, comprises the following steps：
1）By 10 parts of epoxy resin, 12 parts of methyl trichlorosilane, the mixing of 10 parts of deionized water, be put into sand milling, disperse, stir multiplex In machine, under the conditions of rotating speed is 2800rmp, disperse 15min at a high speed, standby；
2) by 14 parts of magnetic force heating stirrers being added to magneton of polyaminoester emulsion, under the conditions of rotating speed is 500r/min It is stirred continuously, continues 5min, standby；
3）To step 2）In again plus 8 parts of ATO dispersion liquids, add 12 parts of water, mixing speed is adjusted to 1200r/min, continues 40min, Standby；
4）The 10 parts of dehydrations of 14 parts of glycol ether and two methylene level diisocyanate of durol are added in four-hole boiling flask, nitrogen is passed through Gas shielded, adds 6 parts of triethylamine after 20min, and temperature is down to 30 DEG C, standby；
5）By sodium bicarbonate, 10 parts are added to step 4）Raw material in, adjust pH value, stir, standby；
6）By acrylic modified epoxy resin, 8 parts add in high-speed dispersing kettle, add 12 parts of polydimethylsiloxane, nonionic 5 parts of association type polyurethane, 4 parts of benzimidazole methyl carbamate, stir, standby；
7）By step 6）Middle raw material sends into grinding machine for grinding to fineness≤12 μm, adds 14 parts of amino resins, stirs, Standby；
8）By step 1）, step 3）With step 5）In raw material be added to step 7）In, stir, be cooled to room temperature, you can Obtain a kind of aqueous one-component glass coating.
Embodiment 2
A kind of aqueous one-component fireproof coating and preparation method thereof, is made up of following raw material：Epoxy resin, methyl trichlorosilane, Polyaminoester emulsion, ATO dispersion liquids, acrylic modified epoxy resin, amino resins, glycol ether, two methylene level two of durol Isocyanates, triethylamine, sodium bicarbonate, non-ionic associative type polyurethane, benzimidazole methyl carbamate, polydimethylsiloxanes Alkane, deionized water, water；The raw material is made up of following parts by weight proportioning：Epoxy resin 10-18 parts, methyl trichlorosilane 12- 20 parts, polyaminoester emulsion 14-20 parts, ATO dispersion liquid 8-16 parts, acrylic modified epoxy resin 8-14 parts, amino resins 14-18 Part, glycol ether 14-18 parts, two methylene level diisocyanate 10-16 parts of durol, triethylamine 6-10 parts, sodium bicarbonate 10- 16 parts, non-ionic associative type polyurethane 5-10 parts, benzimidazole methyl carbamate 4-8 parts, polydimethylsiloxane 12-16 Part, deionized water 10-20 parts, water 12-20 parts.
A kind of aqueous one-component fireproof coating and preparation method thereof, comprises the following steps：
1）By 14 parts of epoxy resin, 16 parts of methyl trichlorosilane, the mixing of 15 parts of deionized water, be put into sand milling, disperse, stir multiplex In machine, under the conditions of rotating speed is 2800rmp, disperse 15min at a high speed, standby；
2) by 17 parts of magnetic force heating stirrers being added to magneton of polyaminoester emulsion, under the conditions of rotating speed is 500r/min It is stirred continuously, continues 5min, standby；
3）To step 2）In again plus 12 parts of ATO dispersion liquids, add 16 parts of water, mixing speed is adjusted to 1200r/min, continues 40min, Standby；
4）The 13 parts of dehydrations of 16 parts of glycol ether and two methylene level diisocyanate of durol are added in four-hole boiling flask, nitrogen is passed through Gas shielded, adds 8 parts of triethylamine after 20min, and temperature is down to 30 DEG C, standby；
5）By sodium bicarbonate, 13 parts are added to step 4）Raw material in, adjust pH value, stir, standby；
6）11 parts of acrylic modified epoxy resin is added in high-speed dispersing kettles, add 14 parts of polydimethylsiloxane, non-from 7.5 parts of sub- association type polyurethane, 6 parts of benzimidazole methyl carbamate, stir, standby；
7）By step 6）Middle raw material sends into grinding machine for grinding to fineness≤12 μm, adds 16 parts of amino resins, stirs, Standby；
8）By step 1）, step 3）With step 5）In raw material be added to step 7）In, stir, be cooled to room temperature, you can Obtain a kind of aqueous one-component glass coating.
Embodiment 3
A kind of aqueous one-component fireproof coating and preparation method thereof, is made up of following raw material：Epoxy resin, methyl trichlorosilane, Polyaminoester emulsion, ATO dispersion liquids, acrylic modified epoxy resin, amino resins, glycol ether, two methylene level two of durol Isocyanates, triethylamine, sodium bicarbonate, non-ionic associative type polyurethane, benzimidazole methyl carbamate, polydimethylsiloxanes Alkane, deionized water, water；The raw material is made up of following parts by weight proportioning：Epoxy resin 10-18 parts, methyl trichlorosilane 12- 20 parts, polyaminoester emulsion 14-20 parts, ATO dispersion liquid 8-16 parts, acrylic modified epoxy resin 8-14 parts, amino resins 14-18 Part, glycol ether 14-18 parts, two methylene level diisocyanate 10-16 parts of durol, triethylamine 6-10 parts, sodium bicarbonate 10- 16 parts, non-ionic associative type polyurethane 5-10 parts, benzimidazole methyl carbamate 4-8 parts, polydimethylsiloxane 12-16 Part, deionized water 10-20 parts, water 12-20 parts.
A kind of aqueous one-component fireproof coating and preparation method thereof, comprises the following steps：
1）By 18 parts of epoxy resin, 20 parts of methyl trichlorosilane, the mixing of 20 parts of deionized water, be put into sand milling, disperse, stir multiplex In machine, under the conditions of rotating speed is 2800rmp, disperse 15min at a high speed, standby；
2) by 20 parts of magnetic force heating stirrers being added to magneton of polyaminoester emulsion, under the conditions of rotating speed is 500r/min It is stirred continuously, continues 5min, standby；
3）To step 2）In again plus ATO dispersion liquid 8-16 parts, add 20 parts of water, mixing speed is adjusted to 1200r/min, continues 40min, standby；
4）The 16 parts of dehydrations of 18 parts of glycol ether and two methylene level diisocyanate of durol are added in four-hole boiling flask, nitrogen is passed through Gas shielded, adds 10 parts of triethylamine after 20min, and temperature is down to 30 DEG C, standby；
5）By sodium bicarbonate, 16 parts are added to step 4）Raw material in, adjust pH value, stir, standby；
6）14 parts of acrylic modified epoxy resin is added in high-speed dispersing kettles, add 16 parts of polydimethylsiloxane, non-from 10 parts of sub- association type polyurethane, 8 parts of benzimidazole methyl carbamate, stir, standby；
7）By step 6）Middle raw material sends into grinding machine for grinding to fineness≤12 μm, adds 18 parts of amino resins, stirs, Standby；
8）By step 1）, step 3）With step 5）In raw material be added to step 7）In, stir, be cooled to room temperature, you can Obtain a kind of aqueous one-component glass coating.
Experimental example
Choose embodiment 1）, embodiment 2）With embodiment 3）In sample and simple glass coating, be divided into four groups, observe each group glass Impact of the glass coating to glass.
Comparing result see the table below：
Project group Light transmittance Adhesive force Hardness Water-fast natural law
Simple glass coating 79.8% 2 grades HB 3 days
Embodiment 1 90.2% 1 grade H 10 days
Embodiment 2 92.6% 1 grade 2H 13 days
Embodiment 3 91.4% 1 grade H 10 days
As can be seen here, embodiment 2）In aqueous one-component glass coating effect preferably, optimal implementation result can be reached.
Beneficial effects of the present invention are：Need not allocate on the spot during the aqueous one-component glass coating use, and possess Longer working life, it is to avoid the problems such as what conventional two-component coating easily occurred cause wastes, working life is short；This glass coating fills After dividing solidification, adhesive force is strong, intensity is big, tolerate excellent performance to common liquids such as water, ethanol, and exterior water moistens smooth, fire line Can be stable, light transmittance is high and effect of heat insulation is obvious.
The above, the only specific embodiment of the present invention, but protection scope of the present invention is not limited thereto, any The change or replacement that expects without creative work, should all cover within the scope of the present invention.

Claims (3)

1. a kind of aqueous one-component fireproof coating and preparation method thereof, it is characterised in that：It is made up of following raw material：Epoxy resin, Methyl trichlorosilane, polyaminoester emulsion, ATO dispersion liquids, acrylic modified epoxy resin, amino resins, glycol ether, tetramethyl Two methylene level diisocyanate of benzene, triethylamine, sodium bicarbonate, non-ionic associative type polyurethane, benzimidazole methyl carbamate, Polydimethylsiloxane, deionized water, water；The raw material is made up of following parts by weight proportioning：Epoxy resin 10-18 parts, first Base trichlorosilane 12-20 part, polyaminoester emulsion 14-20 parts, ATO dispersion liquid 8-16 parts, acrylic modified epoxy resin 8-14 parts, Amino resins 14-18 parts, glycol ether 14-18 parts, two methylene level diisocyanate 10-16 parts of durol, triethylamine 6-10 Part, sodium bicarbonate 10-16 parts, non-ionic associative type polyurethane 5-10 parts, benzimidazole methyl carbamate 4-8 parts, poly- diformazan Radical siloxane 12-16 parts, deionized water 10-20 parts, water 12-20 parts.
2. aqueous one-component fireproof coating as claimed in claim 1 and preparation method thereof, it is characterised in that：The raw material by with Lower optimum parts by weight proportioning composition：14 parts of epoxy resin, 16 parts of methyl trichlorosilane, 17 parts of polyaminoester emulsion, ATO dispersion liquids 12 parts, 11 parts of acrylic modified epoxy resin, 16 parts of amino resins, 16 parts of glycol ether, two methylene level of durol, two isocyanide 13 parts of acid esters, 8 parts of triethylamine, 13 parts of sodium bicarbonate, 7.5 parts of non-ionic associative type polyurethane, benzimidazole methyl carbamate 6 Part, 14 parts of polydimethylsiloxane, 15 parts of deionized water, 16 parts of water.
3. a kind of aqueous one-component fireproof coating as claimed in claim 1 and preparation method thereof, it is characterised in that：Including following Step：
1）By epoxy resin 10-18 parts, methyl trichlorosilane 12-20 parts, the mixing of deionized water 10-20 parts, it is put into sand milling, divides Dissipate, stir in multiple purpose aeroplane, under the conditions of rotating speed is 2800rmp, disperses 15min at a high speed, standby；
2) polyaminoester emulsion 14-20 parts are added on the magnetic force heating stirrer with magneton, are 500r/min bars in rotating speed It is stirred continuously under part, continues 5min, standby；
3）To step 2）In again plus ATO dispersion liquid 8-16 parts, add water 12-20 parts, mixing speed to be adjusted to 1200r/min, continue 40min, standby；
4）Glycol ether 14-18 parts and the dehydration of two methylene level diisocyanate 10-16 parts of durol are added in four-hole boiling flask, Nitrogen protection is passed through, after 20min, triethylamine 6-10 parts is added, temperature is down to 30 DEG C, standby；
5）Sodium bicarbonate 10-16 parts are added to step 4）Raw material in, adjust pH value, stir, standby；
6）Will acrylic modified epoxy resin 8-14 parts add high-speed dispersing kettle in, add polydimethylsiloxane 12-16 parts, Non-ionic associative type polyurethane 5-10 parts, benzimidazole methyl carbamate 4-8 parts, stir, standby；
7）By step 6）Middle raw material sends into grinding machine for grinding to fineness≤12 μm, adds amino resins 14-18 parts, and stirring is Even, standby；
8）By step 1）, step 3）With step 5）In raw material be added to step 7）In, stir, be cooled to room temperature, you can Obtain a kind of aqueous one-component glass coating.
CN201611049279.8A 2016-11-25 2016-11-25 A kind of aqueous one-component fireproof coating and preparation method thereof Pending CN106497379A (en)