CN106497240A - High blotting calorimetric distillation coating - Google Patents
High blotting calorimetric distillation coating Download PDFInfo
- Publication number
- CN106497240A CN106497240A CN201610893642.8A CN201610893642A CN106497240A CN 106497240 A CN106497240 A CN 106497240A CN 201610893642 A CN201610893642 A CN 201610893642A CN 106497240 A CN106497240 A CN 106497240A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- isopropanol
- poly
- calorimetric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The coating the invention discloses a kind of high blotting calorimetric distils, is grouped into by each group of following parts by weight:30 50 parts of carboxymethylcellulose calcium, 10 15 parts of polyacrylamide, 39 parts of Arabic gum, 46 parts of aluminum oxide, 46 parts of styrene ethylacrylate copolymer, 26 parts of N methyl pyrrolidones, 0.1 3 parts of isopropanol, 0.5 6 parts of diethylene glycol (DEG), 13 parts of poly- citric acid, 0.5 2 parts of carbon black, balance of deionized water.Using the high blotting calorimetric distillation coating made by preparation method of the invention, blotting amount is high, and pattern color is vivid.
Description
Technical field
The present invention relates to heat sublimation technical field, and in particular to a kind of high blotting calorimetric distillation coating.
Background technology
Coating on stock surface is used for the pattern for receiving transfer, and current heat sublimation coating blotting amount is poor, causes
Pattern color is not distinct, and the working time extends, and operating efficiency is low, and defect rate is improved.
Content of the invention
Goal of the invention:The invention aims to making up the deficiency of existing investigative technique, there is provided a kind of high blotting amount
Heat sublimation coating.
Technical scheme:A kind of high blotting calorimetric distillation coating, is grouped into by each group of following parts by weight:Carboxymethyl cellulose
Plain 30-50 parts, polyacrylamide 10-15 parts, Arabic gum 3-9 parts, aluminum oxide 4-6 parts, Styrene And Chloroalkyl Acrylates methacrylate copolymers
4-6 parts, 1-METHYLPYRROLIDONE 2-6 parts, isopropanol 0.1-3 parts, diethylene glycol (DEG) 0.5-6 parts, poly- citric acid 1-3 parts, carbon black 0.5-2
Part, balance of deionized water.
Preferably, high blotting calorimetric distillation coating is grouped into by each group of following parts by weight:Carboxymethylcellulose calcium 40
Part, 12 parts of polyacrylamide, 6 parts of Arabic gum, 5 parts of aluminum oxide, 5 parts of Styrene And Chloroalkyl Acrylates methacrylate copolymers, N- methylpyrroles
4 parts of alkanone, 1.5 parts of isopropanol, 3 parts of diethylene glycol (DEG), 2 parts of poly- citric acid, 1 part of carbon black, surplus add deionized water to 100 parts.
The preparation method of coating the invention also discloses a kind of high blotting calorimetric distils, comprises the following steps:
A. Arabic gum is ground to gummi arabicum pulveratum;
B. gummi arabicum pulveratum, carboxymethylcellulose calcium, polyacrylamide, aluminum oxide are sequentially added in reactor, 180 DEG C anti-
Answer 2 hours;
C. Styrene And Chloroalkyl Acrylates methacrylate copolymers, 1-METHYLPYRROLIDONE, isopropanol, the poly- citric acid of diethylene glycol (DEG), charcoal are added
Black, open stirring, be warmed up to 270 DEG C, keep 1-2 hours, after every 30min sampling once check acid number, qualified after by pressure
Power discharges, you can.
Beneficial effect:Using the high blotting calorimetric distillation coating made by preparation method of the invention, blotting amount is high, pattern
It is in bright colors.
Specific embodiment:
Embodiment 1:
A kind of high blotting calorimetric distillation coating, is grouped into by each group of following parts by weight:30 parts of carboxymethylcellulose calcium, gathers
10 parts of acrylamide, 3 parts of Arabic gum, 4 parts of aluminum oxide, 4 parts of Styrene And Chloroalkyl Acrylates methacrylate copolymers, 1-METHYLPYRROLIDONE 2
Part, 0.1 part of isopropanol, 0.5 part of diethylene glycol (DEG), 1 part of poly- citric acid, 0.5 part of carbon black, balance of deionized water.
A kind of preparation method of high blotting calorimetric distillation coating, comprises the following steps:
A. Arabic gum is ground to gummi arabicum pulveratum;
B. gummi arabicum pulveratum, carboxymethylcellulose calcium, polyacrylamide, aluminum oxide are sequentially added in reactor, 180 DEG C anti-
Answer 2 hours;
C. Styrene And Chloroalkyl Acrylates methacrylate copolymers, 1-METHYLPYRROLIDONE, isopropanol, the poly- citric acid of diethylene glycol (DEG), charcoal are added
Black, open stirring, be warmed up to 270 DEG C, keep 1-2 hours, after every 30min sampling once check acid number, qualified after by pressure
Power discharges, you can.
Embodiment 2:
A kind of high blotting calorimetric distillation coating, is grouped into by each group of following parts by weight:50 parts of carboxymethylcellulose calcium, gathers
15 parts of acrylamide, 9 parts of Arabic gum, 6 parts of aluminum oxide, 6 parts of Styrene And Chloroalkyl Acrylates methacrylate copolymers, 1-METHYLPYRROLIDONE 6
Part, 3 parts of isopropanol, 6 parts of diethylene glycol (DEG), 3 parts of poly- citric acid, 2 parts of carbon black, balance of deionized water.
A kind of preparation method of high blotting calorimetric distillation coating, comprises the following steps:
A. Arabic gum is ground to gummi arabicum pulveratum;
B. gummi arabicum pulveratum, carboxymethylcellulose calcium, polyacrylamide, aluminum oxide are sequentially added in reactor, 180 DEG C anti-
Answer 2 hours;
C. Styrene And Chloroalkyl Acrylates methacrylate copolymers, 1-METHYLPYRROLIDONE, isopropanol, the poly- citric acid of diethylene glycol (DEG), charcoal are added
Black, open stirring, be warmed up to 270 DEG C, keep 1-2 hours, after every 30min sampling once check acid number, qualified after by pressure
Power discharges, you can.
Embodiment 3:
A kind of high blotting calorimetric distillation coating, is grouped into by each group of following parts by weight:35 parts of carboxymethylcellulose calcium, gathers
12 parts of acrylamide, 4 parts of Arabic gum, 5 parts of aluminum oxide, 6 parts of Styrene And Chloroalkyl Acrylates methacrylate copolymers, 1-METHYLPYRROLIDONE 6
Part, 3 parts of isopropanol, 6 parts of diethylene glycol (DEG), 3 parts of poly- citric acid, 2 parts of carbon black, balance of deionized water.
A kind of preparation method of high blotting calorimetric distillation coating, comprises the following steps:
A. Arabic gum is ground to gummi arabicum pulveratum;
B. gummi arabicum pulveratum, carboxymethylcellulose calcium, polyacrylamide, aluminum oxide are sequentially added in reactor, 180 DEG C anti-
Answer 2 hours;
C. Styrene And Chloroalkyl Acrylates methacrylate copolymers, 1-METHYLPYRROLIDONE, isopropanol, the poly- citric acid of diethylene glycol (DEG), charcoal are added
Black, open stirring, be warmed up to 270 DEG C, keep 1-2 hours, after every 30min sampling once check acid number, qualified after by pressure
Power discharges, you can.
Using the high blotting calorimetric distillation coating made by preparation method of the invention, blotting amount is high, and pattern color is vivid.
Claims (3)
1. a kind of high blotting calorimetric distils coating, it is characterised in that:It is grouped into by each group of following parts by weight:Carboxymethyl cellulose
Plain 30-50 parts, polyacrylamide 10-15 parts, Arabic gum 3-9 parts, aluminum oxide 4-6 parts, Styrene And Chloroalkyl Acrylates methacrylate copolymers
4-6 parts, 1-METHYLPYRROLIDONE 2-6 parts, isopropanol 0.1-3 parts, diethylene glycol (DEG) 0.5-6 parts, poly- citric acid 1-3 parts, carbon black 0.5-2
Part, balance of deionized water.
2. a kind of high blotting calorimetric distils coating, it is characterised in that:It is grouped into by each group of following parts by weight:Carboxymethyl cellulose
40 parts of element, 12 parts of polyacrylamide, 6 parts of Arabic gum, 5 parts of aluminum oxide, 5 parts of Styrene And Chloroalkyl Acrylates methacrylate copolymers, N- methyl
4 parts of pyrrolidones, 1.5 parts of isopropanol, 3 parts of diethylene glycol (DEG), 2 parts of poly- citric acid, 1 part of carbon black, surplus add deionized water to 100 parts.
3. a kind of high blotting calorimetric distils the preparation method of coating, it is characterised in that:Comprise the following steps:
A. Arabic gum is ground to gummi arabicum pulveratum;
B. gummi arabicum pulveratum, carboxymethylcellulose calcium, polyacrylamide, aluminum oxide are sequentially added in reactor, 180 DEG C of reactions 2
Hour;
C. Styrene And Chloroalkyl Acrylates methacrylate copolymers, 1-METHYLPYRROLIDONE, isopropanol, the poly- citric acid of diethylene glycol (DEG), carbon black are added,
Open stirring, be warmed up to 270 DEG C, keep 1-2 hours, after every 30min sampling once check acid number, qualified after gone out by pressure
Material, you can.