CN106494074A - A kind of preparation method of screen printing plate - Google Patents
A kind of preparation method of screen printing plate Download PDFInfo
- Publication number
- CN106494074A CN106494074A CN201610883794.XA CN201610883794A CN106494074A CN 106494074 A CN106494074 A CN 106494074A CN 201610883794 A CN201610883794 A CN 201610883794A CN 106494074 A CN106494074 A CN 106494074A
- Authority
- CN
- China
- Prior art keywords
- silk screen
- screen
- conductive coating
- elastic support
- printing plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of preparation method of screen printing plate, comprises the following steps:1) the composite filament half tone for preparing is provided, and the composite filament half tone includes that silk screen and elastic support, the silk screen are located in the region that empties in the middle of the elastic support;2) in the upper equably applying conductive glue of the silk screen, so as to form conductive coating on the silk screen;3) wall building process is carried out to the conductive coating, that is, is utilized and conductive coating described in the incompatible sheet material concora crush of the conductive glue;4) combined with plating and/or electroforming process using photographing imaging technology, non-graphic region electroforming on the conductive coating is electroplate with layer of metal layer, graphics field is located in the metal level, so as to the screen printing plate is obtained.The present invention is more excellent because of the surface smoothness and flatness of conductive coating, thus on conductive coating, the same surface smoothness of the metal level of plating and flatness are more excellent, are beneficial to then follow-up printing effect.
Description
Technical field
A kind of the present invention relates to serigraphy field, more particularly to preparation method of screen printing plate.
Background technology
The preparation method principle of composite filament half tone is substantially:First, by stainless steel wire screen cloth according to size and angle demand,
Cutting is in blocks;Then stainless steel wire mesh sheet is compounded in polyester screen cloth;Mesh sheet after again will be compound is bonded in shape above screen frame
Into half tone, except screen frame outside, wire side is collectively constituted by polyester screen cloth and stainless steel wire screen cloth.And composite filament half tone, greatly reduce
The usage amount of stainless steel wire screen cloth, edge increased high resiliency polyester net, reduce the cost of half tone and improve printing
Life-span, it has also become the main flow of stainless steel wire half tone in the market.For the preparation method of composite filament half tone, often in the market
Seen is that hot pressing mode is combined, such as number of patent application:200810040592.4, patent name:A kind of hot manufacturing screen printing
The method of the compound version of brush, its process characteristic are as follows:
1), polyester webs Bradley is raised to after some tension and is fixed on screen frame;
2), according to the size of stainless steel wire screen cloth to be composite, " returning " type hot-melt film of cutting suitable dimension;
3), hot-melt film is placed in the centre of polyester half tone;
4), stainless steel wire mesh sheet is placed in the middle of polyester half tone, and wire cloth interface is located on hot-melt film;
5), a PET protection chip base is put on wire cloth;
6), pressed by blancher;
7), remove in compound boundary by the way of blanching or knife are cut, the polyester screen cloth on steel wire cloth cover;
8) by top frame device, screen frame is fixed on below composite steel wire screen cloth to reach needs the wire cloth after, will be compound
The tension force that asks;
9), in screen frame with gluing on screen cloth contact surface;
10) curing agent is applied on gluing, or is air-dried;
11), composite filament half tone completes.
Its technique is suffered from the drawback that:
Polyester screen cloth on wire rope net surface is removed after wire cloth is compound with polyester screen cloth, causing compound interface to go out has one
Obvious polyester screen cloth gradient, and polyester grenadine is thicker, polyester screen cloth gradient is higher, thus results in stainless steel wire screen cloth and polyester
At screen cloth compound interface, thickness evenness is poor, compound interface positive and negative poor flatness.
Additionally, it is also well known that half tone obtained in said method is primary half tone, also do not possess certain pattern specific, also
Cannot be used for printing, the figuratum screen printing plate of the tool that above-mentioned half tone is processed further and is formed need to also be stainless
The electroplated conductive layer with specific pattern is set on steel wire, however the screen printing plate also exist in preparation process following scarce
Point:
Stainless steel cloth is formed by warp one by one, parallel braiding, and silk thread is the filament of cylinder, from microcosmic
See, the surface of silk screen is the state that waveform rises and falls, thus the fineness and flatness on silk screen surface are poor, and silk screen surface is in electricity
After plating conductive layer, the surface of conductive layer remains the state of waveform fluctuating, thus the surface of conductive layer occurs surface in the same manner
The poor phenomenon of fineness and flatness, affects follow-up printing effect then.
Content of the invention
In order to solve above-mentioned technical problem, it is an object of the invention to a kind of preparation method of screen printing plate, so as to gram
The deficiencies in the prior art are taken.
To achieve these goals, technical scheme is as follows:A kind of preparation method of screen printing plate, including with
Lower step:1) the composite filament half tone for preparing is provided, and the composite filament half tone includes silk screen and elastic support,
The silk screen is located in the region that empties in the middle of the elastic support, the connection of the silk screen and elastic support
There is an overlapping seam at place;
2) equably applying conductive glue on the silk screen, so that form conductive coating, wherein, institute on the silk screen
The surface for stating conductive coating is at least above the upper surface of the silk screen;
3) wall building process is carried out to the conductive coating, that is, utilize with described in the incompatible sheet material concora crush of the conductive glue
Conductive coating is so that the conductive coating surface obtains the surface smoothness and flatness of sets requirement, wherein, described
Material has the surface smoothness and flatness of sets requirement;
4) combined with plating and/or electroforming process using photographing imaging technology, the non-graphic area on the conductive coating
Domain electroforming or plating layer of metal layer, graphics field are located in the metal level, so as to the screen printing plate is obtained.
One of preferred version as the present invention, the sheet material at least adopts resin based sheet, glass sheet, stainless steel
Any one in sheet material.But, the sheet material is not limited to this resin based sheet, glass sheet, stainless steel sheet material, can also be
Other sheet materials with good surface smoothness and flatness.
Further, the one side that the sheet material is contacted with the conductive coating is coated with silicone oil.
One of preferred version as the present invention, the silk screen are compiled by the warp and parallel of terylene/nylon/stainless steel
Knit and form;And/or, the hole that the silk screen is molded on the thin plate by thin plate and through overetch and/or electrolysis and/electroforming process
Shape structure composition;Preferably, the etch process adopts laser-induced thermal etching.
One of preferred version as the present invention, the elastic support adopt terylene grenadine.As the preferred of the present invention
One of scheme, the metal level are copper metal layer or nickel metal layer.One of preferred version as the present invention, the metal thickness
Spend for 0.01-10mm.One of preferred version as the present invention, the preparation method of the composite filament half tone is comprised the following steps:
A1) elastic support is stretched to after some tension to be fixed on the first screen frame and forms elastic half tone;A2) silk screen is passed through
Glue is bonded in the zone line of the elastic support, and the zone line that the elastic support is overlapped with the silk screen
Cut off;A3) component of the silk screen being combined and elastic support is positioned in top frame device, the second screen frame for treating bonding is existed
Jack-up is faced upwards under the elastic support of the component in the presence of the top frame device, till reaching demand tension force,
The elastic support framework of first screen frame beyond is subsequently cut off, so as to the composite filament half tone is obtained;
A4) detection, cleaning, standby, subsequently, carries out microetch and processes so as to obtaining smooth silk screen surface, and deoil
Process and dry.
One of preferred version as the present invention, 4) above-mentioned steps specifically include:B1) in the upper surface of the conductive coating
The region of metal cladding is not required at coating photoresists, and laser explosure graphics field and non-graphic region in uniform way, so that
Solidify at exposure, wash away unexposed photoresists;
B2) the electroplated metal layer in addition to exposure area on the conductive coating, wherein, photoresists after exposure curing
Height need to be higher than the metal level height;B3 the photoresists after exposure curing) are washed away, partially electronically conductive glue is subsequently washed away again
Water, and retain the conductive glue being in close contact with the metal level.Compared with prior art,
Advantages of the present invention at least that:
The present invention equably applying conductive glue on silk screen, so that form conductive coating, wherein, institute on the silk screen
The surface for stating conductive coating is at least above the upper surface of the silk screen;Wall building process is carried out to the conductive coating, that is, utilize with
Conductive coating described in the incompatible sheet material concora crush of the conductive glue is so that the conductive coating surface obtains preferably table
Face fineness and flatness.Because the surface smoothness and flatness of conductive coating more excellent, thus on conductive coating electroplate gold
The same surface smoothness of category layer and flatness are more excellent, are beneficial to then follow-up printing effect, improve the quality of product printing.
Description of the drawings
In order to be illustrated more clearly that present configuration feature and technical essential, right with reference to the accompanying drawings and detailed description
The present invention is described in detail.
Fig. 1-4 is the schematic diagram of each step of the preparation method of the composite filament half tone disclosed in the embodiment of the present invention;
Fig. 5-11 is that the schematic diagram of each step of the preparation method of the screen printing plate disclosed in the embodiment of the present invention (is not wrapped
Include each step of the preparation method of composite filament half tone).
Specific embodiment
Accompanying drawing in below in conjunction with the present embodiment, to embodiment in technical scheme carry out specifically, clearly and completely retouch
State.
The embodiment of the invention discloses a kind of preparation method of screen printing plate, comprises the following steps:1) provide and prepare
Composite filament half tone, wherein, composite filament half tone includes silk screen 3 and elastic support 2, and silk screen 3 is located in the middle of elastic support 2
In the region that empties, there is an overlapping seam junction of silk screen 3 and elastic support 2;
Specifically, the preparation method of composite filament half tone is comprised the following steps:
A1) elastic support 2 is stretched to after some tension to be fixed on the first screen frame 1 and forms elastic half tone, such as Fig. 1 institutes
Show;
A2) silk screen 3 be bonded in the zone line of elastic support 2 by glue, and by elastic support 2 and silk screen 3
The zone line of overlapping cuts off, as shown in Figure 2;
A3) as shown in figure 3, the component of the silk screen 3 being combined and elastic support 2 is positioned in top frame device, will treat
Second screen frame 4 of bonding faces upwards jack-up in the presence of top frame device under the elastic support 2 of the component, until reaching
Till demand tension force, the elastic support 2 beyond the framework of the first screen frame 1 is subsequently cut off, so as to composite filament half tone is obtained (as schemed
Shown in 4);
A4) detection, cleaning, standby, subsequently, carries out microetch and processes so as to obtaining smooth silk screen surface, and deoil
Process and dry.
The preparation method of above-mentioned composite filament half tone has advantages below:
Silk screen 3 can be realized using mode of printing with 2 compound interface glue of elastic support.Compound interface after printing
Thickness is uniform, and good straightness degree;Silk screen 3 and 2 interface of elastic support are completely encapsulated in bonding glue, and positive and negative is without obvious ladder
Degree, greatly reduces.
2) as shown in figure 5, on silk screen 3 equably applying conductive glue, so as to form conductive coating 5 on silk screen 3, its
In, the surface of conductive coating 5 is at least above the upper surface of silk screen 3;
3) as shown in fig. 6, carrying out wall building process to conductive coating 5, that is, utilize and the incompatible sheet material of 5 material of conductive coating
Concora crush conductive coating 5 is so that 5 surface of conductive coating obtains the surface smoothness and flatness of sets requirement, wherein, sheet material
There is the surface smoothness and flatness of sets requirement;
4) combined with plating and/or electroforming process using photographing imaging technology, the non-graphic region electricity on conductive coating 5
Casting is electroplate with layer of metal layer 8, and graphics field is located in metal level 8, so as to screen printing plate is obtained;
Wherein, specifically, 4) above-mentioned steps comprise the following steps:
B1) as shown in fig. 7, being coated with photoresists 6, and laser explosure graphics field with being evenly distributed in the upper surface in conductive coating 5
With the region for being not required to metal cladding 8 at non-graphic region so that 7 solidify at exposure, as shown in figure 8, washing away unexposed
Photoresists 6;
B2) as shown in figure 9, electroplated metal layer 8 in addition to exposure area on conductive coating 5, wherein, after exposure curing
Photoresists (i.e. 7 at exposure) height need to be higher than metal level 8 height;This design, for preventing electroplated metal layer 8 from occurring not
Regular shape.
B3) as shown in Figure 10, wash away the photoresists after exposure curing 6, as shown in figure 11, subsequently wash away partially electronically conductive glue again
Water, and retain the conductive glue being in close contact with metal level 8.As the preferred of the present invention
One of scheme, sheet material is at least using any one in resin based sheet, glass sheet, stainless steel sheet material.But, piece
Material is not limited to this resin based sheet, glass sheet, stainless steel sheet material, can also be other and there is good surface smoothness
Sheet material with flatness.
Further, the one side that sheet material is contacted with conductive coating 5 is coated with silicone oil.
One of preferred version as the present invention, silk screen 3 are woven by the warp and parallel of terylene/nylon/stainless steel
Form, but be not limited to this;And/or, silk screen 3 is molded on thin plate by thin plate and through overetch and/or electrolysis and/electroforming process
Cavernous structure composition.Preferably, etch process adopts laser-induced thermal etching.
One of preferred version as the present invention, elastic support 2 adopt terylene grenadine, but are not limited to terylene grenadine,
It can also be the grenadine of other elastic materials.
One of preferred version as the present invention, metal level 8 are copper metal layer or nickel metal layer, but are not limited to copper metal
Layer or the electrodeposited coating of nickel metal layer, or other metal materials.
One of preferred version as the present invention, 8 thickness of metal level are 0.01-10mm.By above technical scheme, this
Bright equably applying conductive glue on silk screen 3, so that form conductive coating 5, wherein, the surface of conductive coating 5 on silk screen 3
The upper surface of at least above silk screen 3;Then, wall building process is carried out to conductive coating 5, that is, is utilized not close with 5 material of conductive coating
The sheet material concora crush conductive coating 5 of sum is so that 5 surface of conductive coating obtains preferably surface smoothness and flatness.Because of conduction
The surface smoothness and flatness of coating 5 is more excellent, thus on conductive coating 5 electroplate 8 same surface smoothness of metal level and
Flatness is more excellent, is beneficial to then follow-up printing effect, improves the quality of product printing.
Above-mentioned specific embodiment, only technology design to illustrate the invention and architectural feature, it is therefore intended that allow and be familiar with this
The stakeholder of item technology can implement according to this, but above said content is not intended to limit protection scope of the present invention, every foundation
Any equivalence changes or modification that the Spirit Essence of the present invention is made, all should fall under the scope of the present invention.
Claims (9)
1. a kind of preparation method of screen printing plate, it is characterised in that comprise the following steps:
1) the composite filament half tone for preparing is provided, and the composite filament half tone includes silk screen and elastic support, the silk screen position
In the region that empties in the middle of the elastic support, there is an overlapping seam junction of the silk screen and elastic support;
2) equably applying conductive glue on the silk screen, so as to form conductive coating on the silk screen, wherein, described leads
The surface of electrocoat is at least above the upper surface of the silk screen;
3) wall building process is carried out to the conductive coating, that is, is utilized conductive with described in the incompatible sheet material concora crush of the conductive glue
Coating is so that the surface smoothness and flatness of conductive coating surface acquisition sets requirement, wherein, the sheet material has
There are the surface smoothness and flatness of sets requirement;
4) combined with plating and/or electroforming process using photographing imaging technology, the non-graphic region electricity on the conductive coating
Casting or plating layer of metal layer, graphics field are located in the metal level, so as to the screen printing plate is obtained.
2. the preparation method of a kind of screen printing plate according to claim 1, it is characterised in that the sheet material is at least adopted
Any one in resin based sheet, glass sheet, stainless steel sheet material.
3. the preparation method of a kind of screen printing plate according to claim 2, it is characterised in that the sheet material is led with described
The one side of electrocoat contact is coated with silicone oil.
4. the preparation method of a kind of screen printing plate according to claim 1, it is characterised in that the silk screen by terylene/
The warp of nylon/stainless steel and parallel braiding are formed;And/or, the silk screen is by thin plate and through overetch and/or electrolysis
The cavernous structure composition being molded on the thin plate with/electroforming process;Preferably, the etch process adopts laser-induced thermal etching.
5. the preparation method of a kind of screen printing plate according to claim 1, it is characterised in that the elastic support is adopted
Use terylene grenadine.
6. the preparation method of a kind of screen printing plate according to claim 1, it is characterised in that the metal level is copper gold
Category layer or nickel metal layer.
7. the preparation method of a kind of screen printing plate according to claim 1, it is characterised in that the metal layer thickness is
0.01-10mm.
8. the preparation method of a kind of screen printing plate according to any one of claim 1-7, it is characterised in that described multiple
The preparation method of plying half tone is comprised the following steps:
A1) elastic support is stretched to after some tension to be fixed on the first screen frame and forms elastic half tone;
A2) silk screen be bonded in the zone line of the elastic support by glue, and by the elastic support with
The zone line of the silk screen overlapping cuts off;
A3) component of the silk screen being combined and elastic support is positioned in top frame device, the second screen frame for treating bonding is existed
Jack-up is faced upwards under the elastic support of the component in the presence of the top frame device, till reaching demand tension force,
The elastic support framework of first screen frame beyond is subsequently cut off, so as to the composite filament half tone is obtained;
A4) detection, cleaning, standby, subsequently, carries out microetch and processes so as to obtaining smooth silk screen surface, and go oil processing
And dry.
9. a kind of preparation method of the screen printing plate according to any one of claim 1-7, it is characterised in that the step
Rapid 4) specifically include:
B1) photoresists, and laser explosure graphics field and non-graphic region are coated with being evenly distributed in the upper surface in the conductive coating
Place is not required to the region of metal cladding, so that solidifying at exposure, washes away unexposed photoresists;
B2) the electroplated metal layer in addition to exposure area on the conductive coating, wherein, the height of the photoresists after exposure curing
Degree need to be higher than the height of the metal level;
B3 the photoresists after exposure curing) are washed away, partially electronically conductive glue is subsequently washed away again, and is retained and is closely connect with the metal level
Tactile conductive glue.