CN106438789A - Ceramic brake pad - Google Patents
Ceramic brake pad Download PDFInfo
- Publication number
- CN106438789A CN106438789A CN201610917394.6A CN201610917394A CN106438789A CN 106438789 A CN106438789 A CN 106438789A CN 201610917394 A CN201610917394 A CN 201610917394A CN 106438789 A CN106438789 A CN 106438789A
- Authority
- CN
- China
- Prior art keywords
- fiber
- powder
- ceramic
- pottery
- brake pad
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a ceramic brake pad, and belongs to the technical field of automobile brake. The ceramic brake pad is prepared from the following components: 1-5 kg of acrylonitrile butadiene rubber powder, 5-10 kg of noise reduction powder, 6-10 kg of resin, 3-8 kg of whiskers, 3-8 kg of brass fiber, 1-4 kg of short fiber, 1-5 kg of frictional powder, 1-4 kg of long fiber, 8-16 kg of ceramic fiber, 3-8 kg of high-temperature barium, 4-9 kg of crystalline flake graphite(-195), 0.5-3 kg of iron, 2-6 kg of petroleum coke, 8-13 kg of ceramic additives, 8-13 kg of wear-resisting powder, 0.5-3 kg of aramid fiber, 1-4 kg of wood fiber, 2-6 kg of ceramic toughening agents, 1-4 kg of antimony sulfide, and 3-8 kg of stabilizers. The ceramic brake pad has the characteristics that a friction disk is not damaged, no brake noise is generated, the temperature resistance is high, the service life is long, and stable braking is realized.
Description
Technical field
The present invention relates to a kind of ceramic brake, belong to automobile brake technical field.
Background technology
Brake system of car is the critical system of impact vehicle safety, and the stability of brakes and reliability are then straight
Connect to be determined by the combination property of brake block.The brake block using on automobile at present is mainly semipermanent mold brake block, but this product
The major defect of product is:(1)Density is big, hardness is high, thus easily damages frictional disk, and easily produces chatter and braking
Noise;(2)Pyroconductivity is higher, easily makes brakes produce vapour lock in high temperature, may result in friction lamella and steel plate to disengage, makes
Become peril;(3)Steel fibre easily makes the wearability of product decline after easily corrosion, and corrosion, intensity and toughness fall
Low.Thus develop a kind of stability and the higher brake block of reliability has become the task of top priority.
Content of the invention
The present invention will provide a kind of ceramic brake, effectively solve the problems referred to above.
For achieving the above object, the technical scheme that the present invention takes is:
A kind of ceramic brake, is prepared from the following components:Butadiene acrylonitrile rubber powder 1~5kg, noise reduction powder 5~10kg, resin 6~
10kg, whisker 3~8kg, brass fiber 3~8kg, chopped fiber 1~4kg, Frication powder 1~5kg, long fibre 1~4kg, pottery is fine
Dimension 8~16kg, high temperature barium 3~8kg, crystalline flake graphite(-195)4~9kg, ferrum 0.5~3kg, oil coke 2~6kg, pottery adds
Plus agent 8~13kg, abrasion-resistant powder 8~13kg, aramid fiber 0.5~3kg, the wood fiber 1~4kg, pottery increasing grinding agent 2~6kg, antimony trisulfide 1
~4kg, stabilizer 3~8kg.
Further, its component presses following weight composition:Butadiene acrylonitrile rubber powder 3kg, noise reduction powder 7kg, resin 8kg, whisker 6kg,
Brass fiber 5kg, chopped fiber 2kg, Frication powder 3 kg, long fibre 2kg, ceramic fibre 11kg, high temperature barium 5kg, crystalline flake graphite(-
195)6kg, ferrum 1.5kg, oil coke 4kg, ceramic additive 10kg, abrasion-resistant powder 10kg, aramid fiber 1.5kg, wood fiber 2kg, pottery
Porcelain increases grinding agent 4kg, antimony trisulfide 2kg, stabilizer 5kg.
The invention has the advantages that:
The brake block of gained of the present invention have do not injure that frictional disk, brakeless noise, temperature tolerance be good, long service life, braking are relaxed
Suitable the features such as, and cost performance is high, low cost.
Specific embodiment
With reference to specific embodiment, technical scheme is described in detail:
Embodiment one
A kind of ceramic brake, is made up of following components:Butadiene acrylonitrile rubber powder 1~5kg, noise reduction powder 5~10kg, resin 6~10kg,
Whisker 3~8kg, brass fiber 3~8kg, chopped fiber 1~4kg, Frication powder 1~5kg, long fibre 1~4kg, ceramic fibre 8~
16kg, high temperature barium 3~8kg, crystalline flake graphite(-195)4~9kg, ferrum 0.5~3kg, oil coke 2~6kg, ceramic additive 8
~13kg, abrasion-resistant powder 8~13kg, aramid fiber 0.5~3kg, the wood fiber 1~4kg, pottery increases grinding agent 2~6kg, antimony trisulfide 1~4kg,
Stabilizer 3~8kg.
During making, weigh by above-mentioned recipe requirements, material is ground to form fine particle, be then fed into batch mixing in batch mixer;
Ready steel back and dispensing hot pressing die are 160 DEG C in temperature, under conditions of pressure is 115MPa, the time is 10min
Hot-forming, by above-mentioned hot-forming after product put in temperature control drying oven, carry out heat treatment;Through spraying, finishing etc. after
Can use.
Embodiment two
A kind of ceramic brake, is made up of following components:Butadiene acrylonitrile rubber powder 3kg, noise reduction powder 7kg, resin 8kg, whisker 6kg, pyrite
Fiber 5kg, chopped fiber 2kg, Frication powder 3 kg, long fibre 2kg, ceramic fibre 11kg, high temperature barium 5kg, crystalline flake graphite(-195)
6kg, ferrum 1.5kg, oil coke 4kg, ceramic additive 10kg, abrasion-resistant powder 10kg, aramid fiber 1.5kg, wood fiber 2kg, pottery increases
Grinding agent 4kg, antimony trisulfide 2kg, stabilizer 5kg.
During making, weigh by above-mentioned recipe requirements, material is ground to form fine particle, be then fed into batch mixing in batch mixer;
Ready steel back and dispensing hot pressing die are 160 DEG C in temperature, under conditions of pressure is 115MPa, the time is 10min
Hot-forming, by above-mentioned hot-forming after product put in temperature control drying oven, carry out heat treatment;Through spraying, finishing etc. after
Can use.
Above-described embodiment only implementation process to illustrate the invention it is noted that ordinary skill for the art
For personnel, under the premise without departing from the principles of the invention, some improvement can also be made, these improvement also should be regarded as the present invention
Protection domain.
Claims (2)
1. a kind of ceramic brake, is prepared from the following components:Butadiene acrylonitrile rubber powder 1~5kg, noise reduction powder 5~10kg, resin 6~
10kg, whisker 3~8kg, brass fiber 3~8kg, chopped fiber 1~4kg, Frication powder 1~5kg, long fibre 1~4kg, pottery is fine
Dimension 8~16kg, high temperature barium 3~8kg, crystalline flake graphite(-195)4~9kg, ferrum 0.5~3kg, oil coke 2~6kg, pottery adds
Plus agent 8~13kg, abrasion-resistant powder 8~13kg, aramid fiber 0.5~3kg, the wood fiber 1~4kg, pottery increasing grinding agent 2~6kg, antimony trisulfide 1
~4kg, stabilizer 3~8kg.
2. a kind of ceramic brake according to claim 1 is it is characterised in that its component presses following weight composition:Butadiene acrylonitrile rubber
Powder 3kg, noise reduction powder 7kg, resin 8kg, whisker 6kg, brass fiber 5kg, chopped fiber 2kg, Frication powder 3 kg, long fibre 2kg, pottery
Porcelain fiber 11kg, high temperature barium 5kg, crystalline flake graphite(-195)6kg, ferrum 1.5kg, oil coke 4kg, ceramic additive 10kg, resistance to
Pulverizing 10kg, aramid fiber 1.5kg, wood fiber 2kg, pottery increases grinding agent 4kg, antimony trisulfide 2kg, stabilizer 5kg.