CN106432773A - PET fragile film and manufacturing method thereof - Google Patents
PET fragile film and manufacturing method thereof Download PDFInfo
- Publication number
- CN106432773A CN106432773A CN201610847512.0A CN201610847512A CN106432773A CN 106432773 A CN106432773 A CN 106432773A CN 201610847512 A CN201610847512 A CN 201610847512A CN 106432773 A CN106432773 A CN 106432773A
- Authority
- CN
- China
- Prior art keywords
- pet
- rupture diaphragm
- finished product
- fragile
- polyester liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a PET fragile film and a manufacturing method thereof. The PET fragile film comprises a PET fragile substrate layer and an outer layer of a release layer; the outer layer of the release layer coats the PET fragile substrate layer. The manufacturing method includes the following steps: 1) preparing materials, wherein a release film with a flat silicon-coated surface is selected as the PET fragile substrate layer; 2) filtering, wherein the polyester liquid is filtered to remove particulate impurities in the polyester liquid; 3) coating, wherein the release film is subjected to unwinding, and the polyester liquid is coated on the surface of the release film by a coating machine to obtain a PET fragile film semi-finished product; 4) drying, wherein the PET fragile film semi-finished product is dried in an oven; 5) rewinding, wherein the PET fragile film semi-finished product obtained in step 4) is subjected to rewinding to obtain the PET fragile film finished product. The PET fragile film has high transparency, corrosion resistance and thickness stability, and is not prone to deformation.
Description
Technical field
The present invention relates to polyester film preparation technology field is and in particular to a kind of PET rupture diaphragm and its manufacture method.
Background technology
Polyethylene terephthalate, abbreviation PET, it is high polymer, be dehydrated by ethylene glycol terephthalate
Condensation reaction.PET is milky or light yellow, highly crystalline polymer, and surface smooths glossy.Electrical insulating property is excellent
Good, or even under high-temperature high-frequency, its electrical property is still preferable.In addition there is good mechanical property, impact strength is other films
3~5 times, folding resistance is good.Oil resistant, resistance to fatty, resistance to diluted acid, diluted alkaline, resistance to most of solvents.P ET has excellent resistance to high and low
Warm nature energy, can in 120 DEG C of temperature ranges Long-Time Service, short-period used is resistant to 150 DEG C of high temperature, is resistant to -70 DEG C of low temperature, and high,
To its mechanical impact very little during low temperature.Nontoxic, tasteless, wholesomeness is good, can be directly used for packaging for foodstuff.So being directed to
The improvement of the properties such as the transparency of PET rupture diaphragm, tolerance level, is the research direction that people pay attention to.
Content of the invention
For the deficiencies in the prior art, it is an object of the invention to provide a kind of PET rupture diaphragm, this PET rupture diaphragm is transparent
Degree is high, corrosion-resistant, and thickness is stablized it is not easy to deform upon.
For achieving the above object, the present invention adopts the following technical scheme that:A kind of PET rupture diaphragm, described PET rupture diaphragm includes
PET fragile base material layer and release layer outer layer;Described release layer external sheath PET fragile base material layer.
A kind of preferred scheme as the present invention:The thickness of described PET fragile base material layer is 0.025~0.188mm.
A kind of preferred scheme as the present invention:The thickness of described release layer outer layer is 0.0006~0.0012mm.
Further object is that providing a kind of manufacture method of PET rupture diaphragm, the method technique simplifies, and manufactures
Efficiency high, the frangible film thickness of finished product PET is stable, and transparency is high, corrosion-resistant.
For achieving the above object, the present invention adopts the following technical scheme that:
The manufacture method of above-mentioned PET rupture diaphragm, comprises the following steps:
1) get the raw materials ready:Choose and apply the smooth mould release membrance of silicon face as PET fragile base material layer;
2) filter:Polyester liquid is filtered, is removed granule foreign therein;
3) it is coated with:Unreel mould release membrance, by coating machine by polyester liquid spreading on the surface of mould release membrance, obtain PET frangible
Film semi-finished product;
4) dry:PET rupture diaphragm semi-finished product are put in baking box and dries;Described baking box is divided into three sections, described PET rupture diaphragm
Semi-finished product sequentially pass through every section of baking box;The first paragraph temperature of wherein baking box is 80~90 DEG C;Second segment temperature is 100~120
℃;3rd section of temperature is 110~120 DEG C;
5) wind:To step 4 under conditions of winding tension is 40~50N) the PE T rupture diaphragm semi-finished product that obtain carry out
Winding, obtains PET rupture diaphragm finished product.
As a kind of preferred scheme of the present invention, step 3) in, the tension force that described mould release membrance unreels is 30~40N.
As a kind of preferred scheme of the present invention, step 3) in, the pressure by coater head during polyester liquid spreading is
50~60N.
As a kind of preferred scheme of the present invention, step 3) in, the coating weight of described polyester liquid is 4~12g/m2.
The beneficial effects of the present invention is:
1st, the present invention, by the improvement to manufacturing condition and parameter, makes the frangible film thickness of finished product PET stable, transparency is high,
Corrosion-resistant, and pass through three sections of drying courses, make the fastness of PET rupture diaphragm high, release layer upper strata and release layer lower floor are not easy to take off
Fall, PET rupture diaphragm is applicable to multiple fields;
2nd, PET rupture diaphragm manufacturing approach craft of the present invention simplifies, and manufacture efficiency is high.
Brief description:
Fig. 1 is the structural representation of PET rupture diaphragm of the present invention;
Wherein, 1, PET fragile base material layer;2nd, release layer outer layer.
Specific embodiment
Below, in conjunction with specific embodiment, the present invention is described further:
A kind of PET rupture diaphragm, including PET fragile base material layer 1 and release layer outer layer 2;Described release layer outer layer 2 coats PET
Fragile base material layer 1.Wherein, release layer outer layer 2, as protection PET fragile base material layer 1, plays antiseized effect it is adaptable to etch
Technique, corrosion resistant erosion degree is strong.
A kind of manufacture method of PET rupture diaphragm, comprises the following steps:
1) get the raw materials ready:Choose and apply the smooth mould release membrance of silicon face as PET fragile base material layer;
The thickness of described PET fragile base material layer is 0.025~0.188mm;
2) filter:Polyester liquid is filtered, is removed granule foreign therein;
3) it is coated with:Unreel mould release membrance;By coating machine by polyester liquid spreading in the surface of mould release membrance, polyester liquid spreading
When coater head pressure be 50~60N, the coating weight of the polyester liquid of described coating is 4~12g/m2, obtain PET rupture diaphragm
Semi-finished product;
4) dry:PET rupture diaphragm semi-finished product are put in baking box and dries;Described baking box is divided into three sections, described PET rupture diaphragm
Semi-finished product sequentially pass through every section of baking box;The first paragraph temperature of wherein baking box is 80~90 DEG C;Second segment temperature is 100~120
℃;3rd section of temperature is 110~120 DEG C;
The coating of polyester liquid forms release layer outer layer, and the thickness of release layer outer layer is 0.0006~0.0012mm;
5) wind:To step 4 under conditions of winding tension is 40~50N) the PE T rupture diaphragm semi-finished product that obtain carry out
Winding, obtains PET rupture diaphragm finished product.
Specific embodiment:
Embodiment 1
A kind of manufacture method of PET rupture diaphragm, comprises the following steps:
1) get the raw materials ready:Choose and apply the smooth mould release membrance of silicon face as PET fragile base material layer;The thickness of described PET fragile base material layer
Spend for 0.03mm;
2) filter:Polyester liquid is filtered, is removed granule foreign therein;
3) it is coated with:Unreel mould release membrance;By coating machine by polyester liquid spreading in the surface of mould release membrance, polyester liquid spreading
When coater head pressure be 50N, the coating weight of the polyester liquid of described coating is 4g/m2, obtain PET rupture diaphragm semi-finished product;
4) dry:PET rupture diaphragm semi-finished product are put in baking box and dries;Described baking oven is divided into three sections, described PET rupture diaphragm
Semi-finished product sequentially pass through every section of baking box;The first paragraph temperature of wherein baking box is 80 DEG C;Second segment temperature is 100 DEG C;3rd section
Temperature is 120 DEG C;
The coating of polyester liquid forms release layer outer layer, and the thickness of release layer outer layer is 0.0006mm;
5) wind:To step 4 under conditions of winding tension is for 40N) the PET rupture diaphragm semi-finished product that obtain wind,
Obtain PET rupture diaphragm finished product.
The thickness of the PET rupture diaphragm being obtained by embodiment 1 is:0.031mm, surface tension:38mN/m, light transmittance is
98.7%.
Embodiment 2
A kind of manufacture method of PET rupture diaphragm, comprises the following steps:
1) get the raw materials ready:Choose and apply the smooth mould release membrance of silicon face as PET fragile base material layer;The thickness of described PET fragile base material layer
Spend for 0.1mm;
2) filter:Polyester liquid is filtered, is removed granule foreign therein;
3) it is coated with:Unreel mould release membrance;By coating machine by polyester liquid spreading in the surface of mould release membrance, polyester liquid spreading
When coater head pressure be 55N, the coating weight of the polyester liquid of described coating is 8g/m2, obtain PET rupture diaphragm semi-finished product;
4) dry:PET rupture diaphragm semi-finished product are put in baking box and dries;Described baking box is divided into three sections, described PET rupture diaphragm
Semi-finished product sequentially pass through every section of baking box;The first paragraph temperature of wherein baking box is 85 DEG C;Second segment temperature is 110 DEG C;3rd section
Temperature is 120 DEG C;
The coating of polyester liquid forms release layer outer layer, and the thickness of release layer outer layer is 0.0008mm;
5) wind:To step 4 under conditions of winding tension is for 45N) the PET rupture diaphragm semi-finished product that obtain wind,
Obtain PET rupture diaphragm finished product.
The thickness of the PET rupture diaphragm being obtained by embodiment 2 is:0.1015mm, surface tension:45mN/m, light transmittance is
99.1%.
Embodiment 3
A kind of manufacture method of PET rupture diaphragm, comprises the following steps:
1) get the raw materials ready:Choose and apply the smooth mould release membrance of silicon face as PET fragile base material layer;
The thickness of described PET fragile base material layer is 0.18mm;
2) filter:Polyester liquid is filtered, is removed granule foreign therein;
3) it is coated with:Unreel mould release membrance;By coating machine by polyester liquid spreading in the surface of mould release membrance, polyester liquid spreading
When coater head pressure be 60N, the coating weight of the polyester liquid of described coating is 10g/m2, obtain PET rupture diaphragm semi-finished product;
4) dry:PET rupture diaphragm semi-finished product are put in baking box and dries;Described baking box is divided into three sections, described PET rupture diaphragm
Semi-finished product sequentially pass through every section of baking box;The first paragraph temperature of wherein baking box is 90 DEG C;Second segment temperature is 105 DEG C;3rd section
Temperature is 115 DEG C;
The coating of polyester liquid forms release layer outer layer, and the thickness of release layer outer layer is 0.0012mm;
5) wind:To step 4 under conditions of winding tension is for 50N) the PET rupture diaphragm semi-finished product that obtain wind,
Obtain PET rupture diaphragm finished product.
The thickness of the PET rupture diaphragm being obtained by embodiment 3 is:0.182mm, surface tension:59mN/m, light transmittance is
98.8%.
For a person skilled in the art, can technical scheme as described above and design, make other each
Plant corresponding change and deform, and all these changes and deforms the protection model that all should belong to the claims in the present invention
Within enclosing.
Claims (7)
1. a kind of PET rupture diaphragm it is characterised in that:Described PET rupture diaphragm includes PET fragile base material layer and release layer outer layer;Institute
State release layer external sheath PET fragile base material layer.
2. PET rupture diaphragm as claimed in claim 1 it is characterised in that:The thickness of described PET fragile base material layer be 0.025~
0.188mm.
3. PET rupture diaphragm as claimed in claim 1 it is characterised in that:The thickness of described release layer outer layer be 0.0006~
0.0012mm.
4. a kind of manufacture method of described PET rupture diaphragm as arbitrary in claim 1-3 is it is characterised in that comprise the following steps:
1) get the raw materials ready:Choose and apply the smooth mould release membrance of silicon face as PET fragile base material layer;
2) filter:Polyester liquid is filtered, is removed granule foreign therein;
3) it is coated with:Unreel mould release membrance, by coating machine by polyester liquid spreading on the surface of mould release membrance, obtain PET rupture diaphragm half
Finished product;
4) dry:PET rupture diaphragm semi-finished product are put in baking box and dries;Described baking box is divided into three sections, and described PET rupture diaphragm half becomes
Product sequentially pass through every section of baking box;The first paragraph temperature of wherein baking box is 80~90 DEG C;Second segment temperature is 100~120 DEG C;The
Three sections of temperature are 110~120 DEG C;
5) wind:To step 4 under conditions of winding tension is 40~50N) the PET rupture diaphragm semi-finished product that obtain wind,
Obtain PET rupture diaphragm finished product.
5. PET rupture diaphragm as claimed in claim 4 manufacture method it is characterised in that:Step 3) in, described mould release membrance unreels
Tension force be 30~40N.
6. PET rupture diaphragm as claimed in claim 4 manufacture method it is characterised in that:Step 3) in, by polyester liquid spreading
When coater head pressure be 50~60N.
7. PET rupture diaphragm as claimed in claim 4 manufacture method it is characterised in that:Step 3) in, described polyester liquid
Coating weight is 4~12g/m2.