CN106398842A - Non-toxic efficient rust-proof oil - Google Patents
Non-toxic efficient rust-proof oil Download PDFInfo
- Publication number
- CN106398842A CN106398842A CN201610805649.XA CN201610805649A CN106398842A CN 106398842 A CN106398842 A CN 106398842A CN 201610805649 A CN201610805649 A CN 201610805649A CN 106398842 A CN106398842 A CN 106398842A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil
- antioxidant
- polyacrylate
- paraffin wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses non-toxic efficient rust-proof oil which is prepared from the components of, by weight, 10-20 parts of castor oil, 3-8 parts of lanolin magnesium soap, 10-15 parts of paraffin wax, 1-5 parts of antioxidant, 8-15 parts of oil soluble gas phase corrosion inhibitor, 4-10 parts of sodium molybdate, 10-15 parts of film-forming agent, 8-12 parts of lauric acid, 5-15 parts of nanosilicon dioxide, 10-20 parts of petroleum sodium sulfonate, 1-4 parts of polyacrylate and 5-10 parts of rosin-polythylene oxide ester. According to the non-toxic efficient rust-proof oil, the preparation technology is simple, the preparation process is environmental-friendly and free of pollution, the rust-proof effect of the prepared rust-proof oil is good, the rust-proof period is long, and no pollution is caused to the environment; besides, the surface of a workpiece can be prevented from being scratched, and the workpiece quality is guaranteed.
Description
Technical field
The present invention relates to antirust oil preparing technical field, specially a kind of non-toxic efficient antirust oil.
Background technology
Corrosion is to make one of principal mode of securing member destruction, and automobile, motorcycle and various vehicle, machinery can be caused
Very big loss.According to statistics, every year because the direct economic loss caused by metal erosion accounts for the 2% of total value of production in national economy
~4%;For avoiding corrosion, reducing loss, people employ various methods, protect metal to fasten with anti-corrosive grease
Part, is one of modal means of defence at present;However, current antirust oil effect inconspicuous.
Content of the invention
It is an object of the invention to provide a kind of non-toxic efficient antirust oil, with asking of solving to propose in above-mentioned background technology
Topic.
For achieving the above object, the present invention provides following technical scheme:A kind of non-toxic efficient antirust oil, its component is by weight
Number includes Oleum Ricini 10-20 part, lanolin magnesium soap 3-8 part, paraffin wax 10-15 part, antioxidant 1-5 part, oil-soluble gas phase
Corrosion inhibiter 8-15 part, sodium molybdate 4-10 part, film former 10-15 part, lauric acid 8-12 part, nano silicon 5-15 part, oil
Sodium sulfonate 10-20 part, polyacrylate 1-4 part, polyoxylethylene abietate 5-10 part.
Preferably, preferred composition proportion is:15 parts of Oleum Ricini, 5 parts of lanolin magnesium soap, 12 parts of paraffin wax, antioxidant 3
Part, 12 parts of oil-soluble vapour phase inhibitor, 7 parts of sodium molybdate, 12 parts of film former, 10 parts of lauric acid, 10 parts of nano silicon, oil
15 parts of sodium sulfonate, 2 parts of polyacrylate, 7 parts of polyoxylethylene abietate.
Preferably, its preparation technology comprises the following steps:
A, by Oleum Ricini, lanolin magnesium soap, paraffin wax, antioxidant, oil-soluble vapour phase inhibitor mixing after add blender in
Carry out stirring at low speed, blender rotating speed is 500 revs/min, mixing time is 20min, obtains mixture A;
B, in mixture A add sodium molybdate, film former, lauric acid, nano silicon, petroleum sodium sulfonate, polyacrylate,
Polyoxylethylene abietate, adds reaction kettle for reaction after mixing, reactor heating-up temperature is 100 DEG C, and heat time heating time is
30min, obtains mixture B;
C, by mixture B using stirring by the way of be cooled to room temperature, afterwards stand 2h, that is, obtain antirust oil.
Compared with prior art, the invention has the beneficial effects as follows:Preparation process is simple of the present invention, preparation process environmental protection is no dirty
Dye, prepared antirust oil favorable rust preventing effect, the antirust cycle is long, environmentally safe;In addition it is possible to prevent surface of the work from drawing
Wound is it is ensured that workpiece quality.
Specific embodiment
Below the embodiment it is clear that described is clearly and completely described to the technical scheme in the embodiment of the present invention
It is only a part of embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, the common skill in this area
The every other embodiment that art personnel are obtained under the premise of not making creative work, broadly falls into the model of present invention protection
Enclose.
The present invention provides a kind of technical scheme:A kind of non-toxic efficient antirust oil, its component includes Oleum Ricini by weight
10-20 part, lanolin magnesium soap 3-8 part, paraffin wax 10-15 part, antioxidant 1-5 part, oil-soluble vapour phase inhibitor 8-15 part, molybdenum
Sour sodium 4-10 part, film former 10-15 part, lauric acid 8-12 part, nano silicon 5-15 part, petroleum sodium sulfonate 10-20 part, poly-
Acrylate 1-4 part, polyoxylethylene abietate 5-10 part.
Embodiment one:
Using composition proportion be:10 parts of Oleum Ricini, 3 parts of lanolin magnesium soap, 10 parts of paraffin wax, 1 part of antioxidant, oil-soluble gas
8 parts of phase corrosion inhibitor, 4 parts of sodium molybdate, 10 parts of film former, 8 parts of lauric acid, 5 parts of nano silicon, 10 parts of petroleum sodium sulfonate, poly-
1 part of acrylate, 5 parts of polyoxylethylene abietate.
The preparation technology of the present embodiment comprises the following steps:
A, by Oleum Ricini, lanolin magnesium soap, paraffin wax, antioxidant, oil-soluble vapour phase inhibitor mixing after add blender in
Carry out stirring at low speed, blender rotating speed is 500 revs/min, mixing time is 20min, obtains mixture A;
B, in mixture A add sodium molybdate, film former, lauric acid, nano silicon, petroleum sodium sulfonate, polyacrylate,
Polyoxylethylene abietate, adds reaction kettle for reaction after mixing, reactor heating-up temperature is 100 DEG C, and heat time heating time is
30min, obtains mixture B;
C, by mixture B using stirring by the way of be cooled to room temperature, afterwards stand 2h, that is, obtain antirust oil.
Embodiment two:
Using composition proportion be:20 parts of Oleum Ricini, 8 parts of lanolin magnesium soap, 15 parts of paraffin wax, 5 parts of antioxidant, oil-soluble gas
15 parts of phase corrosion inhibitor, 10 parts of sodium molybdate, 15 parts of film former, 12 parts of lauric acid, 15 parts of nano silicon, petroleum sodium sulfonate 20
Part, 4 parts of polyacrylate, 10 parts of polyoxylethylene abietate.
The preparation technology of the present embodiment comprises the following steps:
A, by Oleum Ricini, lanolin magnesium soap, paraffin wax, antioxidant, oil-soluble vapour phase inhibitor mixing after add blender in
Carry out stirring at low speed, blender rotating speed is 500 revs/min, mixing time is 20min, obtains mixture A;
B, in mixture A add sodium molybdate, film former, lauric acid, nano silicon, petroleum sodium sulfonate, polyacrylate,
Polyoxylethylene abietate, adds reaction kettle for reaction after mixing, reactor heating-up temperature is 100 DEG C, and heat time heating time is
30min, obtains mixture B;
C, by mixture B using stirring by the way of be cooled to room temperature, afterwards stand 2h, that is, obtain antirust oil.
Embodiment three:
Using composition proportion be:12 parts of Oleum Ricini, 4 parts of lanolin magnesium soap, 11 parts of paraffin wax, 2 parts of antioxidant, oil-soluble gas
9 parts of phase corrosion inhibitor, 5 parts of sodium molybdate, 11 parts of film former, 9 parts of lauric acid, 6 parts of nano silicon, 12 parts of petroleum sodium sulfonate, poly-
2 parts of acrylate, 6 parts of polyoxylethylene abietate.
The preparation technology of the present embodiment comprises the following steps:
A, by Oleum Ricini, lanolin magnesium soap, paraffin wax, antioxidant, oil-soluble vapour phase inhibitor mixing after add blender in
Carry out stirring at low speed, blender rotating speed is 500 revs/min, mixing time is 20min, obtains mixture A;
B, in mixture A add sodium molybdate, film former, lauric acid, nano silicon, petroleum sodium sulfonate, polyacrylate,
Polyoxylethylene abietate, adds reaction kettle for reaction after mixing, reactor heating-up temperature is 100 DEG C, and heat time heating time is
30min, obtains mixture B;
C, by mixture B using stirring by the way of be cooled to room temperature, afterwards stand 2h, that is, obtain antirust oil.
Example IV:
Using composition proportion be:18 parts of Oleum Ricini, 7 parts of lanolin magnesium soap, 14 parts of paraffin wax, 4 parts of antioxidant, oil-soluble gas
14 parts of phase corrosion inhibitor, 9 parts of sodium molybdate, 14 parts of film former, 11 parts of lauric acid, 14 parts of nano silicon, 18 parts of petroleum sodium sulfonate,
3 parts of polyacrylate, 9 parts of polyoxylethylene abietate.
The preparation technology of the present embodiment comprises the following steps:
A, by Oleum Ricini, lanolin magnesium soap, paraffin wax, antioxidant, oil-soluble vapour phase inhibitor mixing after add blender in
Carry out stirring at low speed, blender rotating speed is 500 revs/min, mixing time is 20min, obtains mixture A;
B, in mixture A add sodium molybdate, film former, lauric acid, nano silicon, petroleum sodium sulfonate, polyacrylate,
Polyoxylethylene abietate, adds reaction kettle for reaction after mixing, reactor heating-up temperature is 100 DEG C, and heat time heating time is
30min, obtains mixture B;
C, by mixture B using stirring by the way of be cooled to room temperature, afterwards stand 2h, that is, obtain antirust oil.
Embodiment five:
Using composition proportion be:15 parts of Oleum Ricini, 5 parts of lanolin magnesium soap, 12 parts of paraffin wax, 3 parts of antioxidant, oil-soluble gas
12 parts of phase corrosion inhibitor, 7 parts of sodium molybdate, 12 parts of film former, 10 parts of lauric acid, 10 parts of nano silicon, 15 parts of petroleum sodium sulfonate,
2 parts of polyacrylate, 7 parts of polyoxylethylene abietate.
The preparation technology of the present embodiment comprises the following steps:
A, by Oleum Ricini, lanolin magnesium soap, paraffin wax, antioxidant, oil-soluble vapour phase inhibitor mixing after add blender in
Carry out stirring at low speed, blender rotating speed is 500 revs/min, mixing time is 20min, obtains mixture A;
B, in mixture A add sodium molybdate, film former, lauric acid, nano silicon, petroleum sodium sulfonate, polyacrylate,
Polyoxylethylene abietate, adds reaction kettle for reaction after mixing, reactor heating-up temperature is 100 DEG C, and heat time heating time is
30min, obtains mixture B;
C, by mixture B using stirring by the way of be cooled to room temperature, afterwards stand 2h, that is, obtain antirust oil.
Preparation process is simple of the present invention, preparation process is environment friendly and pollution-free, prepared antirust oil favorable rust preventing effect, the antirust cycle
Long, environmentally safe;In addition it is possible to prevent surface of the work from scratching it is ensured that workpiece quality.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, permissible
Understand and can carry out multiple changes, modification, replacement to these embodiments without departing from the principles and spirit of the present invention
And modification, the scope of the present invention be defined by the appended.
Claims (3)
1. a kind of non-toxic efficient antirust oil it is characterised in that:Its component includes Oleum Ricini 10-20 part, lanoline by weight
Magnesium soap 3-8 part, paraffin wax 10-15 part, antioxidant 1-5 part, oil-soluble vapour phase inhibitor 8-15 part, sodium molybdate 4-10 part, one-tenth
Membrane 10-15 part, lauric acid 8-12 part, nano silicon 5-15 part, petroleum sodium sulfonate 10-20 part, polyacrylate 1-4
Part, polyoxylethylene abietate 5-10 part.
2. a kind of non-toxic efficient antirust oil according to claim 1 it is characterised in that:Preferably composition proportion is:Semen Ricini
15 parts of oil, 5 parts of lanolin magnesium soap, 12 parts of paraffin wax, 3 parts of antioxidant, 12 parts of oil-soluble vapour phase inhibitor, 7 parts of sodium molybdate, one-tenth
12 parts of membrane, 10 parts of lauric acid, 10 parts of nano silicon, 15 parts of petroleum sodium sulfonate, 2 parts of polyacrylate, rosin acid polyoxy
7 parts of vinyl acetate.
3. a kind of non-toxic efficient antirust oil according to claim 1 it is characterised in that:Its preparation technology includes following step
Suddenly:
A, by Oleum Ricini, lanolin magnesium soap, paraffin wax, antioxidant, oil-soluble vapour phase inhibitor mixing after add blender in
Carry out stirring at low speed, blender rotating speed is 500 revs/min, mixing time is 20min, obtains mixture A;
B, in mixture A add sodium molybdate, film former, lauric acid, nano silicon, petroleum sodium sulfonate, polyacrylate,
Polyoxylethylene abietate, adds reaction kettle for reaction after mixing, reactor heating-up temperature is 100 DEG C, and heat time heating time is
30min, obtains mixture B;
C, by mixture B using stirring by the way of be cooled to room temperature, afterwards stand 2h, that is, obtain antirust oil.