CN106398095A - Magnetron sputtering plastic target film - Google Patents
Magnetron sputtering plastic target film Download PDFInfo
- Publication number
- CN106398095A CN106398095A CN201610789451.7A CN201610789451A CN106398095A CN 106398095 A CN106398095 A CN 106398095A CN 201610789451 A CN201610789451 A CN 201610789451A CN 106398095 A CN106398095 A CN 106398095A
- Authority
- CN
- China
- Prior art keywords
- parts
- magnetron sputtering
- target film
- film according
- plastics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a magnetron sputtering plastic target film. The magnetron sputtering plastic target film is prepared from the following raw materials in parts by weight: 100 to 150 parts of ABS plastic, 10 to 30 parts of a coupling agent, 10 to 20 parts of a compatilizer, 1 to 5 parts of a lubricant, 10 to 20 parts of an antioxidant, 20 to 50 parts of a plasticizer and 10 to 20 parts of a conductive additive.
Description
Technical field
The present invention relates to Material Field, specifically, the present invention relates to a kind of magnetron sputtering plastics target film.
Background technology
Magnetron sputtering plastics target film has special requirement for electric conductivity, and the therefore research for its target is always this
The focus in field.
Content of the invention
It is an object of the invention to provide a kind of magnetron sputtering plastics target film.
In order to realize the purpose of the present invention, the present invention provides a kind of magnetron sputtering plastics target film, by following weight portion
Raw material is made：ABS plastic 100-150 part, coupling agent 10-30 part, compatilizer 10-20 part, lubricant 1-5 part, antioxidant 10-
20 parts, plasticizer 20-50 part and conductive auxiliary agent 10-20 part.
Preferably, magnetron sputtering plastics target film of the present invention is prepared by the raw materials in：ABS plastic
120 parts, 20 parts of coupling agent, 15 parts of compatilizer, 3 parts of lubricant, 15 parts of antioxidant, 30 parts of plasticizer and 15 parts of conductive auxiliary agent.
It is highly preferred that described coupling agent is Silane coupling agent KH550.
It is highly preferred that described compatilizer is acrylonitrile-butadiene-styrene (ABS) grafted maleic anhydride.
It is highly preferred that described lubricant is liquid paraffin.
It is highly preferred that described antioxidant is N, N- diphenyl is to aniline.
It is highly preferred that described plasticizer is Methyl Benzene-o-dicarboxylate.
It is highly preferred that described conductive auxiliary agent is：
Magnetron sputtering plastics target film of the present invention is worth large-scale promotion to use.
Specific embodiment
Below by way of the description of specific embodiment, the invention will be further described, but this is not the limit to the present invention
System, according to the basic thought of the present invention, various modifications may be made or improves for those skilled in the art, but without departing from this
The basic thought of invention, all within the scope of the present invention.
Embodiment 1
Weigh 120 kilograms of ABS plastic, 20 kilograms of coupling agent, 15 kilograms of compatilizer, 3 kilograms of lubricant, antioxidant 15,000
Gram, 30 kilograms of plasticizer and 15 kilograms of conductive auxiliary agent, described coupling agent is Silane coupling agent KH550.Described compatilizer is propylene
Nitrile-butadiene-styrene grafted maleic anhydride.Described lubricant is liquid paraffin.Described antioxidant is N, N- diphenyl pair
Aniline.Described plasticizer is Methyl Benzene-o-dicarboxylate.Described conductive auxiliary agent is：
Above-mentioned substance is heated to 80 DEG C, adds homogenizer, stirred 10 minutes with 1000 revs/min, then discharging
It is the processing temperature of double screw extruder in 40 double screw extruder to adding draw ratio (L/D)：One 170 DEG C of area's temperature, two
Area's temperature is 180 DEG C, and three area's temperature are 190 DEG C, and four area's temperature are 205 DEG C, and five area's temperature are 215 DEG C, and six area's temperature are 225
DEG C, seven area's temperature are 235 DEG C, and eight area's temperature are 240 DEG C, and engine speed is 350 turns/min；Cooling check rod, wind after extrusion
Dry pelletizing, obtains final product.
Embodiment 2
Prepare sample 2 according to the same manner as in Example 1, difference is not use conductive auxiliary agent：
Experimental example
Carry out test surfaces resistivity by IEC60093 requirement, result is as follows：The surface resistivity of the sample of embodiment 1
(Ω) it is 1.8 × 105, the surface resistivity (Ω) of the sample of embodiment 2 is 8.3 × 107It can be seen that, add conductive auxiliary agent
Afterwards, to significantly increasing, the result of embodiment 1 is compared electric conductivity with the result of embodiment 2, and difference has statistical significance (P
<0.05).
Claims (8)
1. a kind of magnetron sputtering plastics target film is it is characterised in that be prepared by the raw materials in：ABS plastic 100-150
Part, coupling agent 10-30 part, compatilizer 10-20 part, lubricant 1-5 part, antioxidant 10-20 part, plasticizer 20-50 part and lead
Electric auxiliary agent 10-20 part.
2. magnetron sputtering plastics target film according to claim 1 is it is characterised in that raw material system by following weight portion
Become：120 parts of ABS plastic, 20 parts of coupling agent, 15 parts of compatilizer, 3 parts of lubricant, 15 parts of antioxidant, 30 parts of plasticizer and conduction
15 parts of auxiliary agent.
3. magnetron sputtering plastics target film according to claim 1 and 2 is it is characterised in that described coupling agent is even for silane
Connection agent KH550.
4. magnetron sputtering plastics target film according to claim 1 and 2 it is characterised in that described compatilizer be acrylonitrile-
Butadiene-styrene grafted maleic anhydride.
5. magnetron sputtering plastics target film according to claim 1 and 2 is it is characterised in that described lubricant is liquid stone
Wax.
6. magnetron sputtering plastics target film according to claim 1 and 2 is it is characterised in that described antioxidant is N, N-
Diphenyl is to aniline.
7. magnetron sputtering plastics target film according to claim 1 and 2 is it is characterised in that described plasticizer is adjacent benzene two
Methyl formate.
8. magnetron sputtering plastics target film according to claim 1 and 2 is it is characterised in that described conductive auxiliary agent is：