CN106396047A - Production process for polymeric aluminum water-purifying agent - Google Patents
Production process for polymeric aluminum water-purifying agent Download PDFInfo
- Publication number
- CN106396047A CN106396047A CN201610436504.7A CN201610436504A CN106396047A CN 106396047 A CN106396047 A CN 106396047A CN 201610436504 A CN201610436504 A CN 201610436504A CN 106396047 A CN106396047 A CN 106396047A
- Authority
- CN
- China
- Prior art keywords
- aluminum
- water
- water purification
- purification agent
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a production process for a polymeric aluminum water-purifying agent. Raw materials for production of the polymeric aluminum water-purifying agent are composed of an aluminum chloride block, bauxite, hydrochloric acid and sodium hydroxide. With the production process, the quality of water purified by the polymeric aluminum water-purifying agent is superior to the quality of water purified by an aluminum sulfate flocculating agent, and water purification cost is reduced by about 25%. The polymeric aluminum water-purifying agent is applicable in a wide pH value range; the polymeric aluminum water-purifying agent has low corrosivity, good operation conditions and better dissolvability compared with aluminum sulfate.
Description
Technical field
The invention belongs to the production technology of water purification agent is and in particular to a kind of production technology of polyaluminium chloride water purification agent.
Background technology
Aluminum, ferrum macromolecule inorganic polymer water purification agent be from the seventies to the nineties research and development get up new
Chemical industry, serves great role for improving people's quality of life and Environment control.Water purification agent kind is a lot, and production technology is each
Differ.Aluminium polychlorid is a kind of water-purifying material, and inorganic polymer coagulant is called poly-aluminium for short again, and english abbreviation is
PAC, the molecular weight being produced due to the bridging action of hydroxide ion and the polymerization of multivalent anions is larger, electric charge is higher
Inorganic polymer water treatment agent.Morphologically solid and two kinds of liquid can be divided into again.Solid is divided into by color is different again
Sepia, ecru, golden yellow and white, liquid can be rendered as water white transparency, slightly yellow, light yellow to yellowish-brown.Different
The aluminium polychlorid of color also has larger difference in application and production technology.The synthetic method of aluminium polychlorid has a lot
Kind, according to the difference of raw material, metallic aluminium method, active aluminium hydroxide method, aluminium sesquioxide method, Alchlor process etc. can be divided into.
Content of the invention
In order to make up the deficiencies in the prior art, the invention provides a kind of production technology of polyaluminium chloride water purification agent, this
The polyaluminium chloride water purification agent water purification quality of invention is high, effect is good, adaptation pH value width, and strong adaptability is of many uses, after purification
Water quality is better than sulphuric acid aluminium flocculating agent, and corrosivity are little, and processing salinity in water increases less, is conducive to ion-exchange treatment and high-purity system
Water.
The technical solution adopted in the present invention is as follows:
A kind of production technology of polyaluminium chloride water purification agent, the raw material producing polyaluminium chloride water purification agent is chlorination aluminium block, aluminum vanadium
Soil, hydrochloric acid, sodium hydroxide, concretely comprise the following steps:
(1)Chlorination aluminium block is pulverized, grinding and sieving obtains chlorination aluminium powder, and is ground into powder with aluminum vanadine, stand-by;
(2)Pressure be 0.4~0.6Mpa reactor in add(1)In obtain chlorination aluminium powder, aluminum vanadine powder, add
Water, is heated to 90~100 DEG C;
(3)It is cooled to 20~30 DEG C, precipitation to be crystallized, obtain crystal aluminum chloride;
(4)Collection step(3)In the crystal aluminum chloride that obtains, continue to put in reactor, add hydrochloric acid and sodium hydroxide, then plus
Enter water, carry out ripening polymerization;
(5)It is cooled to 20~30 DEG C, obtain recrystallization aluminum chloride;
(6)By step(5)In obtained recrystallization aluminum chloride through solidification be dried, obtain polyaluminium chloride water purification agent.
Further, step(1)Middle grinding and sieving is 50~100 mesh sieves.
Further, step(4)In polymerization temperature be 150~300 DEG C.
The application process of the present invention:A kind of polyaluminium chloride water purification agent can be used for processing domestic water, industrial wastewater, city
Sewage etc., adds the waste water of water purification agent of the present invention, adjusts pH8-10, after stirring reaction 15-30min, COD in waste water at normal temperatures
Clearance up to more than 95%, meet discharging standards.
The present invention has following beneficial effect:
(1)Water quality after purification is better than sulphuric acid aluminium flocculating agent, and water purification cost is low by 25% about by comparison;
(2)The scope going for PH is wide;
(3)Corrosivity are little, and operating condition is good, and dissolubility is better than aluminum sulfate;
(4)Processing salinity in water increases less, is conducive to ion-exchange treatment and high-purity controlling the water circulation.
Specific embodiment
With reference to specific embodiment, the present invention is described further:
Embodiment 1
Configure polyaluminium chloride water purification agent according to following parts by weight:90 parts of chlorination aluminium block, 50 parts of aluminum vanadine, 20 parts of hydrochloric acid, hydrogen
20 parts of sodium oxide.
A kind of production technology of polyaluminium chloride water purification agent, comprises the following steps:
(1)Chlorination aluminium block is pulverized, crosses 100 mesh sieves after pulverizing and obtain chlorination aluminium powder, and be ground into powder with aluminum vanadine, stand-by;
(2)Add in pressure is for the reactor of 0.6Mpa(1)In obtain chlorination aluminium powder, aluminum vanadine powder, add water, plus
Heat is to 100 DEG C;
(3)It is cooled to 30 DEG C, precipitation to be crystallized, obtain crystal aluminum chloride;
(4)Collection step(3)In the crystal aluminum chloride that obtains, continue to put in reactor, add hydrochloric acid and sodium hydroxide, then plus
Enter water, carry out ripening polymerization, polymerization temperature is 170 DEG C;
(5)It is cooled to 30 DEG C, obtain recrystallization aluminum chloride;
(6)By step(5)In obtained recrystallization aluminum chloride through solidification be dried, obtain polyaluminium chloride water purification agent.
Embodiment 2
Configure polyaluminium chloride water purification agent according to following parts by weight:180 parts of chlorination aluminium block, 100 parts of aluminum vanadine, 30 parts of hydrochloric acid,
30 parts of sodium hydroxide.
A kind of production technology of polyaluminium chloride water purification agent, comprises the following steps:
(1)Chlorination aluminium block is pulverized, crosses 100 mesh sieves after pulverizing and obtain chlorination aluminium powder, and be ground into powder with aluminum vanadine, stand-by;
(2)Add in pressure is for the reactor of 0.6Mpa(1)In obtain chlorination aluminium powder, aluminum vanadine powder, add water, plus
Heat is to 100 DEG C;
(3)It is cooled to 30 DEG C, precipitation to be crystallized, obtain crystal aluminum chloride;
(4)Collection step(3)In the crystal aluminum chloride that obtains, continue to put in reactor, add hydrochloric acid and sodium hydroxide, then plus
Enter water, carry out ripening polymerization, polymerization temperature is 200 DEG C;
(5)It is cooled to 30 DEG C, obtain recrystallization aluminum chloride;
(6)By step(5)In obtained recrystallization aluminum chloride through solidification be dried, obtain polyaluminium chloride water purification agent.Implement
Example 3
Configure polyaluminium chloride water purification agent according to following parts by weight:100 parts of chlorination aluminium block, 70 parts of aluminum vanadine, 10 parts of hydrochloric acid, hydrogen
10 parts of sodium oxide.
A kind of production technology of polyaluminium chloride water purification agent, comprises the following steps:
(1)Chlorination aluminium block is pulverized, crosses 100 mesh sieves after pulverizing and obtain chlorination aluminium powder, and be ground into powder with aluminum vanadine, stand-by;
(2)Add in pressure is for the reactor of 0.6Mpa(1)In obtain chlorination aluminium powder, aluminum vanadine powder, add water, plus
Heat is to 100 DEG C;
(3)It is cooled to 30 DEG C, precipitation to be crystallized, obtain crystal aluminum chloride;
(4)Collection step(3)In the crystal aluminum chloride that obtains, continue to put in reactor, add hydrochloric acid and sodium hydroxide, then plus
Enter water, carry out ripening polymerization, polymerization temperature is 200 DEG C;
(5)It is cooled to 30 DEG C, obtain recrystallization aluminum chloride;
(6)By step(5)In obtained recrystallization aluminum chloride through solidification be dried, obtain polyaluminium chloride water purification agent.
Claims (3)
1. a kind of production technology of polyaluminium chloride water purification agent it is characterised in that:Produce polyaluminium chloride water purification agent raw material be
Chlorination aluminium block, aluminum vanadine, hydrochloric acid, sodium hydroxide, concretely comprise the following steps:
(1) chlorination aluminium block is pulverized, grinding and sieving obtains chlorination aluminium powder, and is ground into powder with aluminum vanadine, stand-by;
(2) pressure be 0.4~0.6Mpa reactor in add(1)In obtain chlorination aluminium powder, aluminum vanadine powder, add
Water, is heated to 90~100 DEG C;
(3) it is cooled to 20~30 DEG C, precipitation to be crystallized, obtain crystal aluminum chloride;
(4) collection step(3)In the crystal aluminum chloride that obtains, continue to put in reactor, add hydrochloric acid and sodium hydroxide, then plus
Enter water, carry out ripening polymerization;
(5) it is cooled to 20~30 DEG C, obtain recrystallization aluminum chloride;
(6) by step(5)In obtained recrystallization aluminum chloride through solidification be dried, obtain polyaluminium chloride water purification agent.
2. production technology according to claim 1 is it is characterised in that step(1)Middle grinding and sieving is 50~100 mesh
Sieve.
3. production technology according to claim 1 is it is characterised in that step(4)In polymerization temperature be 150~300 DEG C.