CN106393892B - Thermoplastics type's health elastic material and its processing method - Google Patents

Thermoplastics type's health elastic material and its processing method Download PDF

Info

Publication number
CN106393892B
CN106393892B CN201610742374.XA CN201610742374A CN106393892B CN 106393892 B CN106393892 B CN 106393892B CN 201610742374 A CN201610742374 A CN 201610742374A CN 106393892 B CN106393892 B CN 106393892B
Authority
CN
China
Prior art keywords
layer
parts
elastic material
far infrared
thermoplastics type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610742374.XA
Other languages
Chinese (zh)
Other versions
CN106393892A (en
Inventor
傅陆军
杨顺国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hangzhou Kaiyue New Material Co Ltd
Original Assignee
Hangzhou Kaiyue New Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hangzhou Kaiyue New Material Co Ltd filed Critical Hangzhou Kaiyue New Material Co Ltd
Priority to CN201610742374.XA priority Critical patent/CN106393892B/en
Publication of CN106393892A publication Critical patent/CN106393892A/en
Application granted granted Critical
Publication of CN106393892B publication Critical patent/CN106393892B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to a kind of thermoplastics type's health elastic material and its processing methods, the elastic material by five layer by layer structure constitute, first layer is to reinforce setting layer, the second layer is anion adhesive layer, third layer is far infrared transmission layer, 4th layer is anion adhesive layer, and layer 5 is to reinforce setting layer, and the reinforcement setting layer is the warp-knit scrim layer of terylene suede；The anion adhesive layer is formed by the Raw material processing of following parts by weight：40 parts of TPU20,10 15 parts of diatom ooze, 12 20 parts of carbon fiber powder, 35 parts of 58 parts of PETG, EVA, 10 parts of PET5,30 50 parts of latex, 37 parts of negative ion powder, 35 parts of far-infared ceramic powder, 58 parts of magnetic ordered mesoporous carbon.Thermoplastics type's health elastic material of the present invention, have 5 layers of structure, wherein intermediate far infrared transmission layer is healthy basal layer, the heat emission of body temperature goes out the far infrared wave of the 4um 14um beneficial to human body between acceptable 25 DEG C 37 DEG C of human body, this far infrared wave can pass through human foot bottom acupuncture point, moisture in activating human body, boosts metabolism, and increases cell viability.

Description

Thermoplastics type's health elastic material and its processing method
Technical field
The present invention relates to a kind of thermoplastics type's health elastic material and its processing methods.
Background technology
Thermoplastics type's health elastic material is a kind of main attendant of a stage actor's head material of footwear, original traditional main heel toe cap it is hard, very, Basic demand, but existing product hardness, intensity and anti-impact force can only be met on bullet, system is still much not achieved in the performances such as anti-puncture The requirement of shoes standard, and its density is higher, material is heavier, it is expensive, and easy to produce the main attendant of a stage actor in the case where disliking strong low temperature environment Head rupture.These aspects are all with the improve that consumer's various aspects are realized, and the physical property of product requires and the property changed requires to be required for more It is further to be promoted, while being also required in terms of environment protection health to reach the requirement of consumer, thermoplastics type's health elastic material is exactly It develops in this context.
Invention content
In view of the deficiencies of the prior art, bent the purpose of the present invention is to provide a kind of quality and bullet, soft, tough, very characteristic Height, thermoplastics type's health elastic material of puncture-resistant are scratched, which also adds antibacterial, promotes cycle, generates anion and other effects, Adhesion strength is strong, is not easily broken, good permeability, is unlikely to deform after sizing and reusable, fits naturally after shoes molding, wears It is comfortable dry and comfortable, while keeping shoes the lines flow smoothly and overall beautiful.
The technical solution adopted by the present invention to solve the technical problems is：
Thermoplastics type's health elastic material,
The elastic material by five layer by layer structure constitute, first layer be reinforce setting layer, the second layer be anion adhesive layer, Third layer is far infrared transmission layer, and the 4th layer is anion adhesive layer, and layer 5 is to reinforce setting layer,
The reinforcement setting layer is the warp-knit scrim layer of terylene suede；
The anion adhesive layer is formed by the Raw material processing of following parts by weight：
20-40 parts of TPU, 10-15 parts of diatom ooze, 12-20 parts of carbon fiber powder, 3-5 parts of 5-8 parts of PETG, EVA, PET 5- 10 parts, 30-50 parts of latex, 3-7 parts of negative ion powder, 3-5 parts of far-infared ceramic powder, magnetic ordered mesoporous carbon 5-8 parts；
The far infrared transmission layer is by 40-60 parts by weight latex, 30-50 parts by weight PETPU and 5-20 parts by weight far infrareds Ceramic powder is mixed and processed.
Preferably, the anion adhesive layer is formed by the Raw material processing of following parts by weight：TPU30 parts, 12 parts of diatom ooze, 15 parts of carbon fiber powder, 6 parts of PETG, EVA4 parts, 6 parts of PET, 40 parts of latex, 5 parts of negative ion powder, 4 parts of far-infared ceramic powder, magnetic 6 parts of ordered mesoporous carbon of property.
Magnetism ordered mesoporous carbon of the present invention has huge specific surface area and abundant three dimensional pore structures, high Specific surface area is conducive to the adsorption storage of Carbon fiber powder and diatom ooze；Regular orderly open duct, size adjustable aperture be Anion generation provides path, is conducive to anion slowly lasting generation for a long time, improves thermoplastics type's health elastic material Using effect extends its service life.
Preferably, the far infrared transmission layer is made pottery by 50 parts by weight latexes, 40 parts by weight PETPU and 10 parts by weight far infrareds Porcelain powder is mixed and processed.
A kind of processing method of thermoplastics type's health elastic material, the process steps are as follows：
(1) the anion adhesive layer of formula ratio, which processes raw material, is sufficiently mixed, and experience iron determines after free from admixture after heavy metal free It is granulated milling, is melted under the conditions of 150-175 DEG C and uniformly mixing squeezes out, obtain the second layer and the 4th layer material；
(2) the far infrared transmission layer of formula ratio, which processes raw material, is sufficiently mixed, and experience iron determines after free from admixture after heavy metal free It is granulated milling, is melted under the conditions of 150-175 DEG C and uniformly mixing squeezes out, obtain third layer material；
(3) first and the reinforcement sizing layer material of layer 5 upper machine enters preparations in advance, when second and third and four layer materials are crowded When going out by high temperature fusion on the second layer and the 4th layer, thermoplastics type's health elastic material of 5 layers of structure is obtained using cooling.
The beneficial effects of the invention are as follows：
(1) thermoplastics type's health elastic material of the invention has 5 layers of structure, wherein intermediate far infrared transmission layer is healthy base Plinth layer, between acceptable 25 DEG C -37 DEG C of human body the heat emission of body temperature go out the far infrared wave of the 4um-14um beneficial to human body, it is this Far infrared wave can be by human foot bottom acupuncture point, and the moisture in activating human body boosts metabolism, and increases cell viability.
(2) far infrared transmission layer provides negative oxygen ion for anion adhesive layer simultaneously and generates support, and anion layer is remote red Lasting offer anion generates under the support of outer emission layer, and product can generate 3500-5000/ cubic metres of anionic particle, Keep shoes lumen dry and comfortable ventilative, while anion provides restraining and sterilizing bacteria effect, to candida albicans, staphylococcus aureus, large intestine bar Bacterium, other fungal molds have bactericidal bacteriostasis.
(3) reinforce setting layer and provide support for product is stiffening, the hardness of reinforcing product, deflects deflection.
Specific implementation mode
Below by specific embodiment, technical scheme of the present invention will be further explained in detail.
Embodiment 1：
Thermoplastics type's health elastic material,
The elastic material by five layer by layer structure constitute, first layer be reinforce setting layer, the second layer be anion adhesive layer, Third layer is far infrared transmission layer, and the 4th layer is anion adhesive layer, and layer 5 is to reinforce setting layer,
The reinforcement setting layer is the warp-knit scrim layer of terylene suede；
The anion adhesive layer is formed by the Raw material processing of following parts by weight：
20 parts of TPU, 10 parts of diatom ooze, 12 parts of carbon fiber powder, 3 parts of 5 parts of PETG, EVA, 5 parts of PET, 30 parts of latex are born 3 parts of ion powder, 3 parts of far-infared ceramic powder, 5 parts of magnetic ordered mesoporous carbon；
The far infrared transmission layer is mixed by 40 parts by weight latexes, 30 parts by weight PETPU and 5 parts by weight far-infared ceramic powders It is process.
The processing method of thermoplastics type's health elastic material, the process steps are as follows：
(1) the anion adhesive layer of formula ratio, which processes raw material, is sufficiently mixed, and experience iron determines after free from admixture after heavy metal free It is granulated milling, is melted under the conditions of 150- DEG C and uniformly mixing squeezes out, obtain the second layer and the 4th layer material；
(2) the far infrared transmission layer of formula ratio, which processes raw material, is sufficiently mixed, and experience iron determines after free from admixture after heavy metal free It is granulated milling, is melted under the conditions of 150 DEG C and uniformly mixing squeezes out, obtain third layer material；
(3) first and the reinforcement sizing layer material of layer 5 upper machine enters preparations in advance, when second and third and four layer materials are crowded When going out by high temperature fusion on the second layer and the 4th layer, thermoplastics type's health elastic material of 5 layers of structure is obtained using cooling.
Embodiment 2
Thermoplastics type's health elastic material,
The elastic material by five layer by layer structure constitute, first layer be reinforce setting layer, the second layer be anion adhesive layer, Third layer is far infrared transmission layer, and the 4th layer is anion adhesive layer, and layer 5 is to reinforce setting layer,
The reinforcement setting layer is the warp-knit scrim layer of terylene suede；
The anion adhesive layer is formed by the Raw material processing of following parts by weight：
TPU40 parts, 15 parts of diatom ooze, 20 parts of carbon fiber powder, 5 parts of 8 parts of PETG, EVA, 10 parts of PET, 50 parts of latex, bear 7 parts of ion powder, 5 parts of far-infared ceramic powder, 8 parts of magnetic ordered mesoporous carbon；
The far infrared transmission layer is mixed by 60 parts by weight latexes, 50 parts by weight PETPU and 20 parts by weight far-infared ceramic powders Conjunction is process.
The processing method of thermoplastics type's health elastic material, the process steps are as follows：
(1) the anion adhesive layer of formula ratio, which processes raw material, is sufficiently mixed, and experience iron determines after free from admixture after heavy metal free It is granulated milling, is melted under the conditions of 175 DEG C and uniformly mixing squeezes out, obtain the second layer and the 4th layer material；
(2) the far infrared transmission layer of formula ratio, which processes raw material, is sufficiently mixed, and experience iron determines after free from admixture after heavy metal free It is granulated milling, is melted under the conditions of 175 DEG C and uniformly mixing squeezes out, obtain third layer material；
(3) first and the reinforcement sizing layer material of layer 5 upper machine enters preparations in advance, when second and third and four layer materials are crowded When going out by high temperature fusion on the second layer and the 4th layer, thermoplastics type's health elastic material of 5 layers of structure is obtained using cooling.
Embodiment 3
Thermoplastics type's health elastic material,
The elastic material by five layer by layer structure constitute, first layer be reinforce setting layer, the second layer be anion adhesive layer, Third layer is far infrared transmission layer, and the 4th layer is anion adhesive layer, and layer 5 is to reinforce setting layer,
The reinforcement setting layer is the warp-knit scrim layer of terylene suede；
TPU30 parts, 12 parts of diatom ooze, 15 parts of carbon fiber powder, 4 parts of 6 parts of PETG, EVA, 6 parts of PET, 40 parts of latex, bear 5 parts of ion powder, 4 parts of far-infared ceramic powder, 6 parts of magnetic ordered mesoporous carbon；
The far infrared transmission layer is mixed by 50 parts by weight latexes, 40 parts by weight PETPU and 10 parts by weight far-infared ceramic powders Conjunction is process.
The processing method of thermoplastics type's health elastic material, the process steps are as follows：
(1) the anion adhesive layer of formula ratio, which processes raw material, is sufficiently mixed, and experience iron determines after free from admixture after heavy metal free It is granulated milling, is melted under the conditions of 165 DEG C and uniformly mixing squeezes out, obtain the second layer and the 4th layer material；
(2) the far infrared transmission layer of formula ratio, which processes raw material, is sufficiently mixed, and experience iron determines after free from admixture after heavy metal free It is granulated milling, is melted under the conditions of 165 DEG C and uniformly mixing squeezes out, obtain third layer material；
(3) first and the reinforcement sizing layer material of layer 5 upper machine enters preparations in advance, when second and third and four layer materials are crowded When going out by high temperature fusion on the second layer and the 4th layer, thermoplastics type's health elastic material of 5 layers of structure is obtained using cooling.
Thermoplastics type's health elastic material that 1-3 processing of the embodiment of the present invention obtains has following excellent performance：
(1) thermoplastics type's health elastic material of the invention has 5 layers of structure, wherein intermediate far infrared transmission layer is healthy base Plinth layer, between acceptable 25 DEG C -37 DEG C of human body the heat emission of body temperature go out the far infrared wave of the 4um-14um beneficial to human body, it is this Far infrared wave can be by human foot bottom acupuncture point, and the moisture in activating human body boosts metabolism, and increases cell viability.
(2) far infrared transmission layer provides negative oxygen ion for anion adhesive layer simultaneously and generates support, and anion layer is remote red Lasting offer anion generates under the support of outer emission layer, and product can generate 3500-5000/ cubic metres of anionic particle, Keep shoes lumen dry and comfortable ventilative, while anion provides restraining and sterilizing bacteria effect, to candida albicans, staphylococcus aureus, large intestine bar Bacterium, other fungal molds have bactericidal bacteriostasis.
(3) reinforce setting layer and provide support for product is stiffening, the hardness of reinforcing product, deflects deflection.
Above-mentioned embodiment is only a preferred solution of the present invention, not the present invention is made in any form Limitation, on the premise of not exceeding the technical scheme recorded in the claims also other variations and modifications.

Claims (2)

1. thermoplastics type's health elastic material, it is characterised in that：
The elastic material by five layer by layer structure constitute, first layer be reinforce setting layer, the second layer be anion adhesive layer, third Layer is far infrared transmission layer, and the 4th layer is anion adhesive layer, and layer 5 is to reinforce setting layer,
The reinforcement setting layer is the warp-knit scrim layer of terylene suede；
The anion adhesive layer is formed by the Raw material processing of following parts by weight：
20-40 parts of TPU, 10-15 parts of diatom ooze, 12-20 parts of carbon fiber powder, 3-5 parts of 5-8 parts of PETG, EVA, PET 5-10 Part, 30-50 parts of latex, 3-7 parts of negative ion powder, 3-5 parts of far-infared ceramic powder, magnetic ordered mesoporous carbon 5-8 parts；
The process steps of thermoplastics type's health elastic material are as follows：
（1）The anion adhesive layer of formula ratio, which processes raw material, to be sufficiently mixed, and experience iron is granulated milling after determining free from admixture, in 150- It is melted under the conditions of 175 DEG C and uniformly mixing squeezes out, obtain the second layer and the 4th layer material；
（2）Far infrared transmission layer, which processes raw material, to be sufficiently mixed, and experience iron is granulated milling after determining free from admixture, in 150-175 DEG C of item It is melted under part and uniformly mixing squeezes out, obtain third layer material；
（3）First and the reinforcement sizing layer material of layer 5 upper machine enters preparations in advance, when second and third and four layer materials extrusion By high temperature fusion on the second layer and the 4th layer, thermoplastics type's health elastic material of five-layer structure is obtained using cooling.
2. thermoplastics type's health elastic material according to claim 1, it is characterised in that：The anion adhesive layer is by following The Raw material processing of parts by weight forms：TPU30 parts, 12 parts of diatom ooze, 15 parts of carbon fiber powder, 4 parts of 6 parts of PETG, EVA, PET 6 Part, 40 parts of latex, 5 parts of negative ion powder, 4 parts of far-infared ceramic powder, 6 parts of magnetic ordered mesoporous carbon.
CN201610742374.XA 2016-08-28 2016-08-28 Thermoplastics type's health elastic material and its processing method Active CN106393892B (en)