CN106380827A - Gel red rubber for stroke bat - Google Patents

Gel red rubber for stroke bat Download PDF

Info

Publication number
CN106380827A
CN106380827A CN201610842844.XA CN201610842844A CN106380827A CN 106380827 A CN106380827 A CN 106380827A CN 201610842844 A CN201610842844 A CN 201610842844A CN 106380827 A CN106380827 A CN 106380827A
Authority
CN
China
Prior art keywords
striking plate
gel
plate
bat
glue
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610842844.XA
Other languages
Chinese (zh)
Inventor
洪硕宏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bonny Composite Tech Tongxiang Co Ltd
Original Assignee
Bonny Composite Tech Tongxiang Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bonny Composite Tech Tongxiang Co Ltd filed Critical Bonny Composite Tech Tongxiang Co Ltd
Priority to CN201610842844.XA priority Critical patent/CN106380827A/en
Publication of CN106380827A publication Critical patent/CN106380827A/en
Pending legal-status Critical Current

Abstract

The invention relates to the technical field of sports goods manufacturing, in particular to gel red rubber for a stroke bat. The gel red rubber is a solid compound which comprises components of PC-12PART-A, PC-12PART-B, 920 DU 4C, LOT#A. The Gel red rubber for the stroke bat, which is provided by the invention, is a viscous solid of multiple mixed and cured chemicals, and has the characteristics of being super high in elasticity, good in sag resistance, stable in chemical substance, good in recover property and the like. When the Gel red rubber material is applied to a hockey ball stroke bat, the recover property of the hockey ball stroke bat can be improved, and meanwhile the service life of the hockey ball stroke bat can be effectively ensured.

Description

A kind of Gel redness glue for striking plate
Technical field
The present invention relates to sports goods manufacture technology field, especially a kind of Gel redness glue for striking plate.
Background technology
When using, when striking plate hits spheroid, striking plate needs to bear powerful moment traditional hockey batting ball Impulsive force and vibrations, striking plate reconstitution properties are poor, and striking plate is easily bent deformation or ruptures, hockey batting ball service life Short.
Content of the invention
The invention aims to solving the deficiency of above-mentioned technology and providing one kind can improve striking plate elastic force, make batting Plate is subject to the on-deformable Gel redness glue for striking plate after impulsive force.
In order to achieve the above object, a kind of Gel redness glue designed by the present invention, it is solid compounds, and its composition is: PC-12PART-A (polyurethane resin), PC-12PART-B (polyurethane spontaneous recovery agent), 920 DU 4C (foaming agent), LOT#A are (red Color pigment).The mixing quality ratio of wherein each component, polyurethane resin:Polyurethane spontaneous recovery agent:Foaming agent:Red pigment is 0.5-1.5:0.3-0.8:1.5-2.5:1.2-1.8.
The striking plate that a kind of application Gel redness glue produces, it includes filling plate and handle preform, in filling plate front patch One layer of Gel redness glue, the outer surface after filling plate and Gel redness glue laminating wraps up one layer of clad, is enclosed with clad Filling plate surface car has the consistent nylon wire of 3-5 stripe pitch or carat line, forms filler piece, filler piece and handle preform pair Connect, if wrapping up dried layer clad in filler piece outside and filler piece with the front of handle preform junction, reverse side.
Described clad is the carbon fiber yarn bed of material or is glass fiber layer.
The width of described Gel redness glue is 30mm, and length is 150mm, and thickness is 1mm.
This design application and hockey batting ball, can reach and make striking plate inside stuffing Coating combination good, can make again Product has good elastic force and reconstitution properties, can extensive utilization and athletic sports appliance articles for use.
As optimization, the epoxy resin foam material that described filling plate is 0.06 g/cm3 to 0.5g/cm3 using density Make.
It is provided with filler piece, striking plate outer layer covers different glass fiber yarn material or carbon inside common hockey batting ball Silvalin material, because after inserts and glass fiber yarn material or carbon fiber yarn material molding, striking plate face has hard force, when spheroid hits When hitting striking plate, batting plate face can bear strong impact power, and the hockey batting ball that same material is made does not have certain torsion, It may appear that striking plate ruptures and different degrees of damaging after striking plate is subject to a certain degree of shock.
Therefore, to provide a kind of Gel redness glue to be applied to hockey batting ball poor to solve striking plate reconstitution properties for the present invention And produce the fracture of striking plate plate face and inserts or silvalin material lamination, so that hockey batting ball is increased the service life.
Gel redness glue is that the one kind after multiple chemicals mixing solidifications has sticking solidfied material, has ultra-strong elasticity, resists Hammer good fluidity, the features such as chemical substance is stable, reconstitution properties are good.When Gel redness glue material is applied to hockey batting ball, increasing Plus while striking plate restoration, and its life-span being effectively guaranteed hockey batting ball.
Due to Gel redness glue be a kind of have Red viscous jelly springy, be applied to have on striking plate filler piece Superpower shock-absorbing power and bounce, after striking plate front is subject to impulsive force, can make striking plate play good recovery effect.
Because the red glue of Gel is that a kind of viscosity is preferable, in the specification application of design 1mm thickness and striking plate filler piece, energy Combine the Coating combination with carbon fiber yarn material for the striking plate filler piece very well, reduce striking plate internal clearance, be prevented effectively from inserts The problem of hole occurs.When striking plate stress, red glue material mass-energy makes striking plate have transient absorption impulsive force, but can and When restore, prevent striking plate to be subject to rupture after certain impulsive force.
A kind of manufacture method of above-mentioned striking plate, comprises the steps:
(1), utilize laser cutting machine by platy structure inserts cut into some pieces be used for make filling plate pre- templates;(2)、 In the environment of temperature is 100 DEG C -130 DEG C, to each piece of pre- template heating and dehumidification 2-3h;(3), pre- template is put into shaping die At a temperature of 125 DEG C -135 DEG C, moulding 10-15min forms the filling plate of striking plate;(4), will be moulding after filling plate surrounding Edge position burr removing and filling wrench portion and root machine break into TAPER shape;(5), will fill plate front patch last layer Gel red Coloring agent, then plate front and reverse side parcel last layer carbon fiber or glass fiber yarn material will be filled, the width of wherein Gel redness glue is 30mm, length is 150mm, and thickness is 1mm;(6), the 3-5 stripe pitch one on fare machine is got on the bus of the filling plate after yarn material will be wrapped The nylon wire causing or carat line, obtain hockey filler piece;(7), cover on handle pre-shaped fixture thickness be 0.035- The plastics membrane tube of 0.05mm and an end closure, vacuum tube is inserted at plastic foil tube opening end, by plastics membrane tube and handle pre-shaped fixture Between air extract out, make plastics membrane tube be adjacent to handle pre-shaped fixture;(8)If, in handle pre-shaped fixture outer wrap dried layer carbon Fiber or glass fiber yarn material, form the handle preform of striking plate;(9), by filler piece and handle preform to connecting, filling out If filling outside piece, filler piece and the front of handle preform connecting portion, reverse side superscribe dried layer carbon fiber or glass fiber yarn Material;(10), vacuum tube is removed, and extract handle pre-shaped fixture out, form striking plate preform;(11), by hockey preform Put in mould, at handle end opening, access wind-pressure tube, in mould, wind and heating are filled to striking plate preform, become Type temperature is 100-140 DEG C, and molding time is 50-70min, obtains striking plate young bird body;(12), by striking plate young bird body from shaping mould Take out in tool, burr of pruning, striking plate completes.
Gel redness glue is applied to hockey batting ball, when carrying out ice ground field hockey, improves the bounce-back of striking plate Power and the recovery effect after receiving strong impact power with moment, make striking plate not easy fracture, extend hockey batting ball Service life.
Beneficial effect obtained by the present invention is:1. reduce striking plate inner void;2. striking plate be subject to impulsive force when have There is bounce and have reconstitution properties, so that striking plate is unlikely to deform or rupture.3. long service life.
Brief description
Fig. 1 is the structural representation of the filling plate of the present invention;
Fig. 2 posts the schematic diagram of the filling plate of Gel redness glue for front of the present invention;
Fig. 3 is the structural representation of the handle preform of the present invention;
Fig. 4 is the filling schematic diagram that is connected with handle preform of plate of the present invention;
Fig. 5 is the schematic cross-section of the striking plate of the present invention.
Specific embodiment
The invention will be further described to combine accompanying drawing below by embodiment.
Embodiment 1:
A kind of Gel redness glue for striking plate of the present embodiment description, it is solid compounds, and its composition is:PC- 12PART-A, PC-12PART-B, 920 DU 4C, LOT#A, the mixed proportion of wherein each component is:PC-12PART-A、PC- 12PART-B, 920 DU 4C, LOT#A are 1:0.5:2:1.5.
Embodiment 2:
A kind of Gel redness glue for striking plate of the present embodiment description, it is solid compounds, and its composition is:PC- 12PART-A, PC-12PART-B, 920 DU 4C, LOT#A, the mixed proportion of wherein each component is:PC-12PART-A、PC- 12PART-B, 920 DU 4C, LOT#A are 0.5:0.3:1.5:1.8.
Embodiment 3:
A kind of Gel redness glue for striking plate of the present embodiment description, it is solid compounds, and its composition is:PC- 12PART-A, PC-12PART-B, 920 DU 4C, LOT#A, the mixed proportion of wherein each component is:PC-12PART-A、PC- 12PART-B, 920 DU 4C, LOT#A are 1.5:0.8:2.5:1.2.
Embodiment 4:
As Figure 1-Figure 5, the striking plate that a kind of application Gel redness glue of the present embodiment description produces, it includes filling plate 1 He Handle preform 3, pastes one layer of Gel redness glue 2 in filling plate 1 front, the outer surface after filling plate 1 and Gel redness glue 2 laminating One layer of clad 4 of parcel, the filling plate 1 surface car being enclosed with clad 4 has the consistent nylon wire of 4 stripe pitch, forms filler piece, Filler piece is docked with handle preform, and the front of filler piece and handle preform 3 junction, reverse side outside in filler piece are wrapped up If dried layer clad 4.
Described clad 4 is the carbon fiber yarn bed of material.
The width of described Gel redness glue 2 is 30mm, and length is 150mm, and thickness is 1mm.
It is 0.3g/cm that described filling plate 1 adopts density3Epoxy resin foam material make.
Embodiment 5:
The manufacture method of the striking plate that a kind of application Gel redness glue of the present embodiment description produces, comprises the steps:
(1), utilize laser cutting machine by platy structure inserts cut into some pieces be used for make filling plate pre- templates;(2)、 In the environment of temperature is 130 DEG C, to each piece of pre- template heating and dehumidification 2h;(3), pre- template is put into shaping die at 135 DEG C At a temperature of moulding 10min form the filling plate of striking plate;(4), will be moulding after filling plate edge position burr removing and fill out Fill wrench portion and root machine breaks into TAPER shape;(5), will filling plate front paste last layer embodiment 1 in Gel redness glue, Plate front and reverse side parcel last layer carbon fiber yarn material will be filled again, the width of wherein Gel redness glue is 30mm, and length is 150mm, thickness is 1mm;(6), will wrap after yarn material filling plate consistent nylon wire of 3 stripe pitch on fare machine is got on the bus, obtain To hockey filler piece;(7), the plastics membrane tube that thickness is 0.035mm and an end closure, plastics are covered on handle pre-shaped fixture Membrane tube opening inserts vacuum tube, the air between plastics membrane tube and handle pre-shaped fixture is extracted out, makes plastics membrane tube be adjacent to handss Handle pre-shaped fixture;(8)If, in handle pre-shaped fixture outer wrap dried layer carbon fiber yarn material, form the handle preform of striking plate; (9), by filler piece and handle preform to connecting, outside filler piece, the front of filler piece and handle preform connecting portion, If reverse side superscribes dried layer carbon fiber yarn material;(10), vacuum tube is removed, and extract handle pre-shaped fixture out, form striking plate pre- Type body;(11), hockey preform is put in mould, at handle end opening access wind-pressure tube, right in mould Striking plate preform fills wind and heating, and forming temperature is 100 DEG C, and molding time is 70min, obtains striking plate young bird body;(12), will Striking plate young bird body takes out from mould, burr of pruning, and striking plate completes.
Embodiment 6:
The manufacture method of the striking plate that a kind of application Gel redness glue of the present embodiment description produces, comprises the steps:
(1), utilize laser cutting machine by platy structure inserts cut into some pieces be used for make filling plate pre- templates;(2)、 In the environment of temperature is 100 DEG C, to each piece of pre- template heating and dehumidification 3h;(3), pre- template is put into shaping die at 125 DEG C At a temperature of moulding 15min form the filling plate of striking plate;(4), will be moulding after filling plate edge position burr removing and fill out Fill wrench portion and root machine breaks into TAPER shape;(5), plate front patch last layer Gel redness glue will be filled, then plate will be filled Front and reverse side superscribe layer of glass yarn material, and the width of wherein Gel redness glue is 30mm, and length is 150mm, and thickness is 1mm;(6), will wrap after yarn material filling plate consistent carat line of 5 stripe pitch on fare machine is got on the bus, obtain hockey filling Piece;(7), the plastics membrane tube that thickness is 0.05mm and an end closure is covered on handle pre-shaped fixture, plastic foil tube opening end is inserted Enter vacuum tube, the air between plastics membrane tube and handle pre-shaped fixture is extracted out, makes plastics membrane tube be adjacent to handle pre-shaped fixture; (8)If, in handle pre-shaped fixture outer wrap dried layer glass fiber yarn material, form the handle preform of striking plate;(9), will fill out Fill piece and handle preform to connecting, outside filler piece, the front of filler piece and handle preform connecting portion, reverse side parcel If upper dried layer glass fiber yarn material;(10), vacuum tube is removed, and extract handle pre-shaped fixture out, form striking plate preform; (11), hockey preform is put in mould, at handle end opening access wind-pressure tube, to striking plate in mould Preform fills wind and heating, and forming temperature is 140 DEG C, and molding time is 50min, obtains striking plate young bird body;(12), by striking plate Young body takes out from mould, burr of pruning, and striking plate completes.
Embodiment 7:
The manufacture method of the striking plate that a kind of application Gel redness glue of the present embodiment description produces, comprises the steps:
(1), utilize laser cutting machine by platy structure inserts cut into some pieces be used for make filling plate pre- templates;(2)、 In the environment of temperature is 120 DEG C, to each piece of pre- template heating and dehumidification 2.5h;(3), pre- template put into shaping die 130 At a temperature of DEG C, moulding 12min forms the filling plate of striking plate;(4), will be moulding after filling plate edge position burr removing and Filling wrench portion and root machine break into TAPER shape;(5), plate front patch last layer Gel redness glue will be filled, then will fill Plate front and reverse side superscribe layer of glass yarn material, and the width of wherein Gel redness glue is 30mm, and length is 150mm, thickness For 1mm;(6), will wrap after yarn material filling plate consistent nylon wire of 5 stripe pitch on fare machine is got on the bus, obtain hockey and fill out Fill piece;(7), the plastics membrane tube that thickness is 0.04mm and an end closure, plastic foil tube opening end are covered on handle pre-shaped fixture Insertion vacuum tube, the air between plastics membrane tube and handle pre-shaped fixture is extracted out, makes plastics membrane tube be adjacent to handle pre-shaped fixture; (8)If, in handle pre-shaped fixture outer wrap dried layer glass fiber yarn material, form the handle preform of striking plate;(9), will fill out Fill piece and handle preform to connecting, outside filler piece, the front of filler piece and handle preform connecting portion, reverse side parcel If upper dried layer glass fiber yarn material;(10), vacuum tube is removed, and extract handle pre-shaped fixture out, form striking plate preform; (11), hockey preform is put in mould, at handle end opening access wind-pressure tube, to striking plate in mould Preform fills wind and heating, and forming temperature is 120 DEG C, and molding time is 60min, obtains striking plate young bird body;(12), by striking plate Young body takes out from mould, burr of pruning, and striking plate completes.

Claims (1)

1. a kind of Gel redness glue for striking plate, is characterized in that:It is solid compounds, and its composition is:Polyurethane resin, Polyurethane spontaneous recovery agent, foaming agent, red pigment, the mixing quality ratio of wherein each component, polyurethane resin:Polyurethane spontaneous recovery Agent:Foaming agent:Red pigment is 0.5-1.5:0.3-0.8:1.5-2.5:1.2-1.8.
CN201610842844.XA 2016-09-23 2016-09-23 Gel red rubber for stroke bat Pending CN106380827A (en)