CN106366977A - High-strength carboxylic butadiene-styrene latex special for carpet and preparation method thereof - Google Patents

High-strength carboxylic butadiene-styrene latex special for carpet and preparation method thereof Download PDF

Info

Publication number
CN106366977A
CN106366977A CN201610742188.6A CN201610742188A CN106366977A CN 106366977 A CN106366977 A CN 106366977A CN 201610742188 A CN201610742188 A CN 201610742188A CN 106366977 A CN106366977 A CN 106366977A
Authority
CN
China
Prior art keywords
parts
agent
initiator
butadiene latex
styrene butadiene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610742188.6A
Other languages
Chinese (zh)
Inventor
何发丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jujube Hengtai Chemical Co Ltd
Original Assignee
Jujube Hengtai Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jujube Hengtai Chemical Co Ltd filed Critical Jujube Hengtai Chemical Co Ltd
Priority to CN201610742188.6A priority Critical patent/CN106366977A/en
Publication of CN106366977A publication Critical patent/CN106366977A/en
Pending legal-status Critical Current

Abstract

The invention discloses high-strength carboxylic butadiene-styrene latex special for carpet. The carboxylic butadiene-styrene latex is prepared from, by mass, 35-55 parts of butadiene, 45-65 parts of styrene, 0.8-1.5 parts of emulsifier, 1.1-1.8 parts of anti-aging agent, 1-2 parts of reinforcing agent, 40-85 parts of deionized water, 0.8-1.6 parts of filling agent, 1.3-2 parts of softening agent, 5-10 parts of tert-dodecylmercaptan, 20-30 parts of ammonium persulfate, 10-15 parts of caustic soda, 1-3 parts of initiator, 0.5-1.1 parts of anionic surface active agent, 1-2 parts of itaconic acid and 0.7-1.4 parts of fire retardant. The added reinforcing agent improves the strength of carboxylic butadiene-styrene latex, and the added softening agent improves the softness of carboxylic butadiene-styrene latex.

Description

A kind of carpet Special high-strength carboxylic styrene butadiene latex and preparation method thereof
Technical field
The present invention relates to chemical technology field, specially a kind of carpet Special high-strength carboxylic styrene butadiene latex and its preparation side Method.
Background technology
Carboxylic styrene butadiene latex is to add a small amount of carboxylic acid and other auxiliary agent with butadiene, styrene, is generated by emulsion polymerization Copolymer, is a kind of milky aqueous dispersion with bluish violet gloss.Combinated styrene content ratio is higher, has higher bonding Power and conjunctiva intensity, machinery and chemical stability are good, and mobility, bin stability are all good, the advantages of loading is big.Residual benzene class Monomer is little, belongs to environmentally friendly machine.
Carboxylic styrene butadiene latex is also used for carpet backing and applies application adhesive, fixing carpet pile, stablizes size of carpet, makes Carpet use during have good ruggedness, present carpet carboxylic styrene butadiene latex intensity difference, lead to carpet intolerant to With flexibility is bad, and user's comfort is poor.
Content of the invention
It is an object of the invention to provide a kind of carpet Special high-strength carboxylic styrene butadiene latex and preparation method thereof, possess strong The advantage that degree is high, pliability is good, solves the problems, such as existing carpet carboxylic styrene butadiene latex intensity difference, not softness.
For achieving the above object, the present invention provides a kind of following technical scheme: carpet Special high-strength carboxylic styrene butadiene latex, Described carboxylic styrene butadiene latex is made up of the raw material of following mass fraction: butadiene 35-55 part, styrene 45-65 part, emulsifying agent 0.8-1.5 part, age resistor 1.1-1.8 part, reinforcing agent 1-2 part, deionized water 40-85 part, filler 0.8-1.6 part, softening agent 1.3-2 part, tert-dodecyl mercaptan 5-10 part, Ammonium persulfate. 20-30 part, Caustic soda 10-15 part, initiator 1-3 part, anionic table Face activating agent 0.5-1.1 part, itaconic acid 1-2 part and fire retardant 0.7-1.4 part.
Preferably, described carboxylic styrene butadiene latex is made up of the raw material of following mass fraction: butadiene 30-50 part, styrene 50-70 part, emulsifying agent 0.9-1.6 part, age resistor 1.0-1.7 part, reinforcing agent 1.1-2.1 part, deionized water 50-100 part, filling Agent 1-1.8 part, softening agent 1.4-2.1 part, tert-dodecyl mercaptan 4.8-9.8 part, Ammonium persulfate. 21-31 part, Caustic soda 9-14 part, Initiator 1.2-3.2 part, anionic surfactant 0.6-1.2 part, itaconic acid 1.1-2.1 part and fire retardant 0.8-1.5 part.
Preferably, described carboxylic styrene butadiene latex is made up of the raw material of following mass fraction: 45 parts of butadiene, styrene 60 Part, 1.3 parts of emulsifying agent, 1.3 parts of age resistor, 1.5 parts of reinforcing agent, 75 parts of deionized water, 1.4 parts of filler, 1.8 parts of softening agent, 7 parts of tert-dodecyl mercaptan, Ammonium persulfate. 19-29 part, Caustic soda 11-16 part, 2 parts of initiator, anionic surfactant 0.9 Part, 1.6 parts of itaconic acid and 1.3 parts of fire retardant.
Preferably, one of described initiator initiator system of ammonium persulfate, potassium peroxydisulfate and methyl ethyl ketone peroxide.
Preferably, described emulsifying agent is sodium lauryl sulphate.
Preferably, described anionic surfactant is dodecylbenzene sodium sulfonate.
Preferably, described filler is preferably one of Calcium Carbonate, lignin and Pulvis Talci.
The invention allows for a kind of carpet Special high-strength carboxylic styrene butadiene latex and preparation method thereof, walk including following Rapid:
S1, reaction vessel vacuum state puts into 90% butadiene, 85% benzene second in composition of raw materials into container Alkene, the deionized water of 75-90%, the emulsifying agent of 30-40%, tert-dodecyl mercaptan 45-65%, 60-75% itaconic acid, 70- 85% filler and 80-90% fire retardant;
S2, reacting by heating container, to 70-80 DEG C, adds the initiator of 20-30%, 70-85% age resistor, 60-80% Reinforcing agent, 65-80% softening agent, 66-77% anionic surfactant;
S3, carries out continuous heating to reaction vessel and is warmed up to 75-85 DEG C, into reaction vessel at the uniform velocity in Deca composition of raw materials 20-30% Ammonium persulfate., 10-25% Caustic soda and remaining butadiene, styrene, deionized water, itaconic acid, emulsifying agent, initiation Agent, tert-dodecyl mercaptan, age resistor, filler, fire retardant, anionic surfactant, softening agent and reinforcing agent;
S4, the temperature of reaction vessel is maintained between 80-90 DEG C, is incubated 3-4h, when conversion ratio reaches more than 95%, It is cooled to 65-75 DEG C, add the Caustic soda of 50-60% in remaining Ammonium persulfate. and composition of raw materials;
S5 moves to reaction vessel in degassing container and is de-gassed, and control degassing container vacuum is -0.07-- 0.09mpa, vacuum flashing degassing 3-5 hour, after the completion of degassing, temperature is reduced to 25-45 degree, carries out discharging of packing, obtain carboxylic Base styrene-butadiene latex.
Compared with prior art, beneficial effects of the present invention are as follows:
1st, the present invention passes through to add reinforcing agent in the preparation process of carboxylic styrene butadiene latex, can improve latex using reinforcing agent Anti-wear performance, tear resistance and tensile strength properties, for improving the intensity of carpet carboxylic styrene butadiene latex.
2nd, the present invention passes through to add softening agent in the preparation process of carboxylic styrene butadiene latex, can improve adding of glue based article Work performance and serviceability, it is possible to increase the tensile strength of latex, percentage elongation and wearability, make carboxylic styrene butadiene latex finished product more Soft.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical solution of the present invention is clearly and completely described it is clear that being retouched The embodiment stated is only a part of embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, this The every other embodiment that field those of ordinary skill is obtained under the premise of not making creative work, broadly falls into the present invention The scope of protection.
Embodiment one
45 parts of butadiene, 50 parts of styrene, 1.3 parts of emulsifying agent, 1.5 parts of age resistor, 1.5 parts of reinforcing agent, deionized water 60 Part, 1.2 parts of filler, 1.5 parts of softening agent, 7 parts of tert-dodecyl mercaptan, 22 parts of Ammonium persulfate., 12 parts of Caustic soda, 1.5 parts of initiator, 0.9 part of anionic surfactant, 1.7 parts of itaconic acid and 1 part of fire retardant.
Its preparation method comprises the following steps:
S1, reaction vessel vacuum state puts into 85% butadiene, 75% benzene second in composition of raw materials into container Alkene, 80% deionized water, 35% emulsifying agent, tert-dodecyl mercaptan 50%, 70% itaconic acid, 75% filler and 85% resistance Combustion agent;
S2, reacting by heating container to 75 DEG C, add 25% initiator, 75% age resistor, 70% reinforcing agent, 75% Softening agent, 70% anionic surfactant;
S3, carries out continuous heating to reaction vessel and is warmed up to 80 DEG C, into reaction vessel at the uniform velocity in Deca composition of raw materials 25% Ammonium persulfate., 15% Caustic soda and remaining butadiene, styrene, deionized water, itaconic acid, emulsifying agent, initiator, uncle ten Two carbon mercaptan, age resistor, filler, fire retardant, anionic surfactant, softening agent and reinforcing agent;
S4, the temperature of reaction vessel is maintained between 85 DEG C, is incubated 3h, when conversion ratio reaches more than 95%, cooling To 70 DEG C, add in remaining Ammonium persulfate. and composition of raw materials 55% Caustic soda;
S5 moves to reaction vessel in degassing container and is de-gassed, and control degassing container vacuum is -0.08mpa, subtracts Temperature is reduced to 30 degree after the completion of degassing by pressure flash liberation 4 hours, carries out discharging of packing, obtains carboxylic styrene butadiene latex.
Embodiment two
40 parts of butadiene, 66 parts of styrene, 1.5 parts of emulsifying agent, 1.4 parts of age resistor, 2 parts of reinforcing agent, 70 parts of deionized water, 1.7 parts of filler, 1.6 parts of softening agent, 6 parts of tert-dodecyl mercaptan, 27 parts of Ammonium persulfate., 13 parts of Caustic soda, 1.7 parts of initiator, the moon 1 part of ionic surfactant, 1.8 parts of itaconic acid and 1.4 parts of fire retardant.
Its preparation method comprises the following steps:
S1, reaction vessel vacuum state puts into 86% butadiene, 83% benzene second in composition of raw materials into container Alkene, 77% deionized water, 31% emulsifying agent, tert-dodecyl mercaptan 51%, 73% itaconic acid, 79% filler and 85% resistance Combustion agent;
S2, reacting by heating container, to 77 DEG C, adds 23% initiator, 71% age resistor, 63% reinforcing agent, 73% soft Agent, 67% anionic surfactant;
S3, carries out continuous heating to reaction vessel and is warmed up to 77 DEG C, into reaction vessel at the uniform velocity in Deca composition of raw materials 23% Ammonium persulfate., 13% Caustic soda and remaining butadiene, styrene, deionized water, itaconic acid, emulsifying agent, initiator, uncle ten Two carbon mercaptan, age resistor, filler, fire retardant, anionic surfactant, softening agent and reinforcing agent;
S4, the temperature of reaction vessel is maintained between 87 DEG C, is incubated 3.1h, when conversion ratio reaches more than 93%, fall Temperature, to 73 DEG C, adds in remaining Ammonium persulfate. and composition of raw materials 55% Caustic soda;
S5 moves to reaction vessel in degassing container and is de-gassed, and control degassing container vacuum is -0.07mpa, subtracts Temperature is reduced to 41 degree after the completion of degassing by pressure flash liberation 3.5 hours, carries out discharging of packing, obtains carboxylic styrene butadiene latex.
Embodiment three
Carboxylic styrene butadiene latex is made up of the raw material of following mass fraction: 45 parts of butadiene, 60 parts of styrene, emulsifying agent 1.3 Part, 1.3 parts of age resistor, 1.5 parts of reinforcing agent, 75 parts of deionized water, 1.4 parts of filler, 1.8 parts of softening agent, tert-dodecyl mercaptan 7 Part, Ammonium persulfate. 19-29 part, Caustic soda 11-16 part, 2 parts of initiator, 0.9 part of anionic surfactant, 1.6 parts of itaconic acid With 1.3 parts of fire retardant.
Its preparation method comprises the following steps:
S1, reaction vessel vacuum state puts into 82% butadiene, 74% benzene second in composition of raw materials into container Alkene, 76% deionized water, 34% emulsifying agent, tert-dodecyl mercaptan 46%, 64% itaconic acid, 82% filler and 84% resistance Combustion agent;
S2, reacting by heating container, to 76 DEG C, adds 22% initiator, 75% age resistor, 70% reinforcing agent, 66% soft Agent, 68% anionic surfactant;
S3, carries out continuous heating to reaction vessel and is warmed up to 77 DEG C, into reaction vessel at the uniform velocity in Deca composition of raw materials 26% Ammonium persulfate., 14% Caustic soda and remaining butadiene, styrene, deionized water, itaconic acid, emulsifying agent, initiator, uncle ten Two carbon mercaptan, age resistor, filler, fire retardant, anionic surfactant, softening agent and reinforcing agent;
S4, the temperature of reaction vessel is maintained between 84 DEG C, is incubated 4h, when conversion ratio reaches more than 91%, cooling To 72 DEG C, add in remaining Ammonium persulfate. and composition of raw materials 55% Caustic soda;
S5 moves to reaction vessel in degassing container and is de-gassed, and control degassing container vacuum is -0.09mpa, subtracts Temperature is reduced to 40 degree after the completion of degassing by pressure flash liberation 5 hours, carries out discharging of packing, obtains carboxylic styrene butadiene latex.
In sum: this carpet Special high-strength carboxylic styrene butadiene latex and preparation method thereof, by carboxylic styrene butadiene latex Preparation process in add reinforcing agent, in the preparation process of carboxylic styrene butadiene latex add softening agent, solve existing carboxyl fourth Benzene latex intensity difference, the problem of pliability difference.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, permissible Understand and can carry out multiple changes, modification, replacement to these embodiments without departing from the principles and spirit of the present invention And modification, the scope of the present invention be defined by the appended.

Claims (8)

1. a kind of carpet Special high-strength carboxylic styrene butadiene latex it is characterised in that: described carboxylic styrene butadiene latex is by following mass parts The raw material of number is made: butadiene 35-55 part, styrene 45-65 part, emulsifying agent 0.8-1.5 part, age resistor 1.1-1.8 part, reinforcement Agent 1-2 part, deionized water 40-85 part, filler 0.8-1.6 part, softening agent 1.3-2 part, tert-dodecyl mercaptan 5-10 part, over cure Sour ammonium 20-30 part, Caustic soda 10-15 part, initiator 1-3 part, anionic surfactant 0.5-1.1 part, itaconic acid 1-2 part and Fire retardant 0.7-1.4 part.
2. a kind of carpet Special high-strength carboxylic styrene butadiene latex according to claim 1 it is characterised in that: described carboxyl fourth Benzene latex is made up of the raw material of following mass fraction: butadiene 30-50 part, styrene 50-70 part, emulsifying agent 0.9-1.6 part, anti- Old agent 1.0-1.7 part, reinforcing agent 1.1-2.1 part, deionized water 50-100 part, filler 1-1.8 part, softening agent 1.4-2.1 part, Tert-dodecyl mercaptan 4.8-9.8 part, Ammonium persulfate. 21-31 part, Caustic soda 9-14 part, initiator 1.2-3.2 part, anionic surface Activating agent 0.6-1.2 part, itaconic acid 1.1-2.1 part and fire retardant 0.8-1.5 part.
3. a kind of carpet Special high-strength carboxylic styrene butadiene latex according to claim 1 it is characterised in that: described carboxyl fourth Benzene latex is made up of the raw material of following mass fraction: 45 parts of butadiene, 60 parts of styrene, 1.3 parts of emulsifying agent, 1.3 parts of age resistor, 1.5 parts of reinforcing agent, 75 parts of deionized water, 1.4 parts of filler, 1.8 parts of softening agent, 7 parts of tert-dodecyl mercaptan, Ammonium persulfate. 19- 29 parts, Caustic soda 11-16 part, 2 parts of initiator, 0.9 part of anionic surfactant, 1.6 parts of itaconic acid and 1.3 parts of fire retardant.
4. a kind of carpet Special high-strength carboxylic styrene butadiene latex according to claim 1 it is characterised in that: described initiator One of initiator system of ammonium persulfate, potassium peroxydisulfate and methyl ethyl ketone peroxide.
5. a kind of carpet Special high-strength carboxylic styrene butadiene latex according to claim 1 it is characterised in that: described emulsifying agent For sodium lauryl sulphate.
6. a kind of carpet Special high-strength carboxylic styrene butadiene latex according to claim 1 it is characterised in that: described anion Type surfactant is dodecylbenzene sodium sulfonate.
7. a kind of carpet Special high-strength carboxylic styrene butadiene latex according to claim 1 it is characterised in that: described filler It is preferably one of Calcium Carbonate, lignin and Pulvis Talci.
8. a kind of carpet Special high-strength carboxylic styrene butadiene latex and preparation method thereof it is characterised in that: this preparation method include with Lower step:
S1, reaction vessel vacuum state puts into 80-90% butadiene, 70-85% benzene second in composition of raw materials into container Alkene, the deionized water of 75-90%, the emulsifying agent of 30-40%, tert-dodecyl mercaptan 45-65%, 60-75% itaconic acid, 70- 85% filler and 80-90% fire retardant;
S2, reacting by heating container, to 70-80 DEG C, adds the initiator of 20-30%, 70-85% age resistor, 60-80% reinforcement Agent, 65-80% softening agent, 66-77% anionic surfactant;
S3, carries out continuous heating to reaction vessel and is warmed up to 75-85 DEG C, the 20- at the uniform velocity in Deca composition of raw materials into reaction vessel 30% Ammonium persulfate., 10-25% Caustic soda and remaining butadiene, styrene, deionized water, itaconic acid, emulsifying agent, initiator, Tert-dodecyl mercaptan, age resistor, filler, fire retardant, anionic surfactant, softening agent and reinforcing agent;
S4, the temperature of reaction vessel is maintained between 80-90 DEG C, is incubated 3-4h, when conversion ratio reaches more than 95%, cooling To 65-75 DEG C, add the Caustic soda of 50-60% in remaining Ammonium persulfate. and composition of raw materials;
S5 moves to reaction vessel in degassing container and is de-gassed, and control degassing container vacuum is -0.07--0.09mpa, Temperature is reduced to 25-45 degree after the completion of degassing, carries out discharging of packing, obtain carboxy styrene-butadiene rubber by vacuum flashing degassing 3-5 hour Breast.
CN201610742188.6A 2016-08-26 2016-08-26 High-strength carboxylic butadiene-styrene latex special for carpet and preparation method thereof Pending CN106366977A (en)