CN106364244A - Decorative composite film with stereo colour pattern - Google Patents
Decorative composite film with stereo colour pattern Download PDFInfo
- Publication number
- CN106364244A CN106364244A CN201610762741.2A CN201610762741A CN106364244A CN 106364244 A CN106364244 A CN 106364244A CN 201610762741 A CN201610762741 A CN 201610762741A CN 106364244 A CN106364244 A CN 106364244A
- Authority
- CN
- China
- Prior art keywords
- layer
- parts
- sol
- substrate
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The decorative composite film with the stereoscopic colorful patterns comprises a substrate and a coating coated on the substrate, wherein the substrate is made of a fully transparent polyester film, and the coating is made of the following raw materials in percentage by weight: 32.1% of silicon dioxide dispersion liquid, 4.36% of polyvinyl alcohol 205 solution, 62.2% of polyvinyl alcohol 235 solution and 1.34% of absolute ethyl alcohol; the beneficial effects are that: printing is clear, and energy is saved: the coating technology is adopted to solve the output problem of medical images, and meanwhile, the digital medical image film can be output only by printing with a color laser printer, so that the labor intensity of doctors is greatly reduced, the waiting time of patients is reduced, the non-renewable silver resources and the waste of forest resources are effectively saved, developing, fixing and sewage are not required to be discharged to the nature, and toxic and harmful substances to the human body do not exist.
Description
Technical field
The invention belongs to a kind of compound film for decoration with 3 D colour pattern.
Background technology
With the continuous progress of social development and science and technology, people are to the beautification of environment and to cultural and handicraft product
Require also increasingly improving.In recent years, due to the appearance of metal coating technology, from this, will revolutionize various in making
Cause the huge waste of non-ferrous metal during metal board, non-ferrous metal board is replaced using metal coating.In existing metal coating skill
In art, although made various board metal-likes are very true, due to ductility and the formation pattern of metal-plated film layer
The less stable of structure, therefore, its space pattern is difficult to keep permanent.
Content of the invention
It is an object of the invention to provide a kind of energy saving, it is clear to print, and to solve medical imaging using coating technology
Output problem, only need simultaneously color laser printer print just can export digital medical image film there is stereo colour
The compound film for decoration of pattern.
The technical scheme is that
There is the compound film for decoration of 3 D colour pattern, it is characterized in that, be provided with basal membrane layer, basal membrane layer is provided with colloidal sol
Layer, sol layer is provided with patterned layer, and patterned layer top is provided with transparent film layer, and sol layer thickness is 0.8mm, patterned layer；Patterned layer
For being etched in advance after predetermined pattern, melt sol layer in the case of temperature is 240 degree and pattern is laminated on sol layer, warp
After polishing the sol layer exceeding, then complete after covering transparent film layer.
Wherein, sol layer is PUR, and it is made up of following weight portion: styrene and 25 parts of ethylacylic acid copolymer,
20 parts of paraffin, 45 parts of Petropols, 1 part of pigment, 2 parts of antioxidant, 2.5 parts of brightener, 4.5 parts of flashlight powder.
Wherein, transparent film layer its be made up of following weight portion: 55 parts of isobutanol, 40 parts of butyl glycol ether, Nano sol coagulate
5 parts of glue.
The invention has the beneficial effects as follows: the present invention also has rational in infrastructure, simple production process, easily realizes automatization's flowing water
Job type produces, and production efficiency is high, with low cost, easy to use, range of application width, the features such as long service life.
Specific embodiment
The invention will be further described:
Embodiment 1
There is the compound film for decoration of 3 D colour pattern, be provided with basal membrane layer, basal membrane layer is provided with sol layer, on sol layer
It is provided with patterned layer, patterned layer top is provided with transparent film layer, sol layer thickness is 0.8mm, patterned layer；Patterned layer is to be etched in advance
After predetermined pattern, thawing sol layer pattern is laminated on sol layer in the case of temperature is 240 degree, through polishing exceed molten
After glue-line, then complete after covering transparent film layer；Sol layer is PUR, and it is made up of following weight portion: styrene and ethyl third
25 parts of olefin(e) acid copolymer, 20 parts of paraffin, 45 parts of Petropols, 1 part of pigment, 2 parts of antioxidant, 2.5 parts of brightener, flashlight powder
4.5 part；Transparent film layer its be made up of following weight portion: 55 parts of isobutanol, 40 parts of butyl glycol ether, 5 parts of nano sol-gel.
This product adopts metal film composite material, the cold mounting technology of colored printing, you can reach the metal of all metal tags
Sense can meet the inaccessiable abundant color change of metal tag again, can save substantial amounts of mineral resources, the course of processing is no
The chemistry rotten decorations technics comparing that abnormal smells from the patient, pollution-free, noiselessness and traditional label produce is more environmentally friendly, more attractive, and production efficiency can carry
High more than 10 times.Especially with certain thickness thermosol glue-line, this thermosol glue-line is the adhesive linkage of the present invention to the present invention, and
It is that the metal film composite material of the present invention forms the casing play of permanent space pattern.
These are only presently preferred embodiments of the present invention, not in order to limit the present invention, all spirit in the present invention and
Any modification, equivalent and improvement of being made within principle etc., should be included within the scope of the present invention.
Claims (3)
1. there is the compound film for decoration of 3 D colour pattern, it is characterized in that, be provided with basal membrane layer, basal membrane layer is provided with sol layer,
Sol layer is provided with patterned layer, and patterned layer top is provided with transparent film layer, and sol layer thickness is 0.8mm, patterned layer；Patterned layer is pre-
After being first etched into predetermined pattern, melt sol layer in the case of temperature is 240 degree and pattern is laminated on sol layer, through polishing
After the sol layer exceeding, then complete after covering transparent film layer.
2. the compound film for decoration with 3 D colour pattern according to claim 1, is characterized in that, sol layer is hot melt
Glue, it is made up of following weight portion: styrene and 25 parts of ethylacylic acid copolymer, 20 parts of paraffin, 45 parts of Petropols, pigment
1 part, 2 parts of antioxidant, 2.5 parts of brightener, 4.5 parts of flashlight powder.
3. the compound film for decoration with 3 D colour pattern according to claim 2, is characterized in that, transparent film layer its by
Following weight portion composition: 55 parts of isobutanol, 40 parts of butyl glycol ether, 5 parts of nano sol-gel.