CN106364072A - Bulletproof wood plate - Google Patents
Bulletproof wood plate Download PDFInfo
- Publication number
- CN106364072A CN106364072A CN201610846702.0A CN201610846702A CN106364072A CN 106364072 A CN106364072 A CN 106364072A CN 201610846702 A CN201610846702 A CN 201610846702A CN 106364072 A CN106364072 A CN 106364072A
- Authority
- CN
- China
- Prior art keywords
- shellproof
- layer
- plank
- film
- plywood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a bulletproof wood plate. According to the bulletproof wood plate, through arranging a first multilayer wood plate layer and a second multilayer wood plate layer, the entire bulletproof wood plate is light in weight and convenient to process; in addition, a composite material layer is arranged between the first multilayer wood plate layer and the second multilayer wood plate layer, comprises a first bulletproof rubber sheet, a carbon fiber layer and a second bulletproof rubber sheet, which are sequentially connected, and can be used for effectively converting impact kinetic energy of a bullet into elastic potential energy and crushed surface energy, so that the bulletproof aim can be achieved, and the entire bulletproof wood plate is more stable in structural performance; an anticorrosive agent and a flame retardant are arranged in the first and second multilayer wood plate layers, so that the bulletproof wood plate can be effectively fireproof, explosion-proof and anticorrosive.
Description
Technical field
The present invention relates to safety protection field, in particular to a kind of shellproof plank.
Background technology
With national economy develop rapidly and people's prevention awareness continuous improvement, bullet resistant material is by wide through melting industry
General application.Much place is required for using some bulletproof devices, such as bank, post office, insurance company and house etc. now, this
A little bulletproof devices include bulletproof glass, armour plate etc., and bulletproof glass and armour plate are because quality is big, structural behaviour is unstable
Determine, process inconvenience and give people to bring very big inconvenience in use.
Content of the invention
It is an object of the invention to provide a kind of shellproof plank, big to improve existing bulletproof device quality, processing inconvenience,
The unstable problem of structural behaviour.
Embodiments of the invention are achieved in that
A kind of shellproof plank, it includes the first shellproof composite bed, and described first shellproof composite bed includes stacking gradually connection
The first delta wood flaggy, composite layer and the second delta wood flaggy, described composite layer includes stacking gradually connection
The first shellproof film, carbon fiber layer and the second shellproof film, wherein, described first shellproof film and described first delta wood
Flaggy stacking connects, and described second shellproof film is connected with described second plywood layer stackup.
In preferred embodiments of the present invention, described first delta wood flaggy and described first shellproof film are by viscous glutinous agent
Through being hot bonding, described second delta wood flaggy is passed through by described viscous glutinous agent with the described second shellproof film and is hot bonding,
Glued through hot pressing by described viscous glutinous agent between described first shellproof film, described carbon fiber layer and described second shellproof film
Connect.
In preferred embodiments of the present invention, described first delta wood flaggy includes multi-plywood, described multilayer gluing
By viscous glutinous agent through being hot bonding between plate.
In preferred embodiments of the present invention, inside the lumber fibre of described multi-plywood, it is provided with preservative.
In preferred embodiments of the present invention, inside the lumber fibre of described multi-plywood, it is provided with fire retardant.
In preferred embodiments of the present invention, described first delta wood flaggy is arranged away from the one side of described composite layer
There is wooden lagging.
In preferred embodiments of the present invention, the structure phase of described second delta wood flaggy and described first delta wood flaggy
With.
In preferred embodiments of the present invention, described shellproof plank also includes the second shellproof composite bed, and described second is shellproof
Composite bed is identical with the described first shellproof lamination layer structure, and described second shellproof composite bed is with the described first shellproof composite bed even
Connect.
In preferred embodiments of the present invention, arrange between described second shellproof composite bed and described first shellproof composite bed
There is described composite layer.
In preferred embodiments of the present invention, described first shellproof composite bed, described composite layer and described second
By viscous glutinous agent through being hot bonding between shellproof composite bed.
The beneficial effect of the embodiment of the present invention is:
The present invention provides a kind of shellproof plank, is made whole by the first delta wood flaggy and the second delta wood flaggy of setting
Individual shellproof plank light weight, processing also aspect, in addition it is provided with multiple between the first delta wood flaggy and the second delta wood flaggy
Condensation material layer, the first shellproof film that composite layer includes being sequentially connected, carbon fiber layer, the second shellproof film, its composite wood
The bed of material can effectively by the impact kinetic energy of bullet be converted into elastic potential energy and broken after surface energy, shellproof mesh can be reached
, entirely the structural behaviour of shellproof plank is more stable.
Brief description
In order to be illustrated more clearly that the technical scheme of the embodiment of the present invention, below will be attached to use required in embodiment
Figure is briefly described it will be appreciated that the following drawings illustrate only certain embodiments of the present invention, and it is right to be therefore not construed as
The restriction of scope, for those of ordinary skill in the art, on the premise of not paying creative work, can also be according to this
A little accompanying drawings obtain other related accompanying drawings.
The structural representation of a kind of shellproof plank that Fig. 1 provides for first embodiment of the invention；
The structural representation of the first delta wood flaggy that Fig. 2 provides for first embodiment of the invention；
The structural representation of a kind of shellproof plank that Fig. 3 provides for second embodiment of the invention；
The structural representation of the second shellproof composite bed that Fig. 4 provides for second embodiment of the invention.
In figure: shellproof plank 100, the first delta wood flaggy 110, the second delta wood flaggy 130, composite layer 120, the
One shellproof film 122, carbon fiber layer 124, the second shellproof film 126, the 3rd shellproof film 121, the 4th shellproof film 125, the
Two composite layers 127, the second shellproof composite bed 190, multi-plywood 150.
By, shown in accompanying drawing, the above and other purpose of the present invention, feature and advantage will become apparent from, in whole accompanying drawings
Identical reference indicates identical part, does not deliberately press actual size equal proportion scaling and draws accompanying drawing, it is preferred that emphasis is shows
Go out the purport of the present invention.
Specific embodiment
Purpose, technical scheme and advantage for making the embodiment of the present invention are clearer, below in conjunction with the embodiment of the present invention
In accompanying drawing, the technical scheme in the embodiment of the present invention is clearly and completely described it is clear that described embodiment is
The a part of embodiment of the present invention, rather than whole embodiments.The present invention generally described and illustrated in accompanying drawing herein is implemented
The assembly of example can be arranged with various different configurations and design.
Therefore, below the detailed description of the embodiments of the invention providing in the accompanying drawings is not intended to limit claimed
The scope of the present invention, but be merely representative of the selected embodiment of the present invention.Based on the embodiment in the present invention, this area is common
The every other embodiment that technical staff is obtained under the premise of not making creative work, broadly falls into the model of present invention protection
Enclose.
It should also be noted that similar label and letter expression similar terms in following accompanying drawing, therefore, once a certain Xiang Yi
It is defined in individual accompanying drawing, then do not need it to be defined further and explains in subsequent accompanying drawing.
In describing the invention, it should be noted that term "left", "right", " interior ", etc. the orientation of instruction or position close
System is based on orientation shown in the drawings or position relationship, or the orientation usually put when this invention product uses or position are closed
System, is for only for ease of the description present invention and simplifies description, rather than the device of instruction or hint indication or element must have
Specific orientation, with specific azimuth configuration and operation, be therefore not considered as limiting the invention.Additionally, term " the
One ", " second ", " the 3rd ", " the 4th " etc. are only used for distinguishing description, and it is not intended that indicating or hint relative importance.
In describing the invention in addition it is also necessary to explanation, unless otherwise clearly defined and limited, term " setting ",
" connection " should be interpreted broadly, for example, it may be being fixedly connected or being detachably connected, or is integrally connected；Can be
It is mechanically connected or electrically connect；Can be to be joined directly together it is also possible to be indirectly connected to by intermediary, can be two
The connection of element internal.For the ordinary skill in the art, above-mentioned term can be understood in the present invention with concrete condition
In concrete meaning.
Other features and advantages of the present invention will illustrate in subsequent description, and, partly becomes from description
It is clear that or being understood by implementing the embodiment of the present invention.The purpose of the present invention and other advantages can be by being write
In description, claims and accompanying drawing, specifically noted structure is realizing and to obtain.
First embodiment
Refer to Fig. 1, the present embodiment provides a kind of shellproof plank 100, including the first shellproof composite bed, first is shellproof compound
Layer includes stacking gradually the first delta wood flaggy 110, composite layer 120 and the second delta wood flaggy 130 of connection, is combined
Material layer 120 includes the first shellproof film 122, carbon fiber layer 124 and the second shellproof film 126 stacking gradually connection, its
In, the stacking of the first shellproof film 122 and the first delta wood flaggy 110 is connected, the second shellproof film 126 and the second delta wood flaggy
130 stackings connect.
First delta wood flaggy 110 is all logical with the second delta wood flaggy 130 with composite layer 120, composite layer 120
Cross a kind of resistant to elevated temperatures viscous glutinous agent of inorganic environment-friendly through hot pressing connects so that the first delta wood flaggy 110, composite layer
120th, the connection between the second delta wood flaggy 130 is more firm and solid, the impulsive force to reduce bullet.
That is, shellproof plank 100 include being sequentially connected the first delta wood flaggy 110, the first shellproof film 122,
Carbon fiber layer 124, the second shellproof film 126, the second delta wood flaggy 130, are all logical between each structure of shellproof plank 100
Cross a kind of resistant to elevated temperatures viscous glutinous agent of inorganic environment-friendly through hot pressing connects.
Refer to Fig. 2, the first delta wood flaggy 110 includes multi-plywood 150, with its timber literary composition between adjacent plywood
Reason is crossed-over, by a kind of resistant to elevated temperatures viscous glutinous agent of inorganic environment-friendly through hot pressing connects between adjacent plywood.
As a kind of embodiment, multi-plywood 150 includes the first plywood 152 and the second plywood 154, the first glue
Plywood 152 is connected with the second plywood 154 stacking, and the machine direction of the first plywood 152 can be tilted to the left, the second glue
The machine direction of plywood 154 can be tilted to the right that is to say, that the machine direction of adjacent plywood is different, so
Enable that delta wood flaggy is more smooth, structural behaviour is more stable, due to the angled staggered company of the machine direction of plywood
Connect the penetration power of the effective ground resistance blind bullet of meeting.
As a kind of embodiment, the first delta wood flaggy 110 is provided with high-quality in fact away from the one side of composite layer 120
Wooden lagging or Recombinant Wood lagging, or other have ornamental wooden lagging so that shellproof plank 100 is more attractive in appearance, so that
Shellproof plank 100 seems attractive in appearance, good-looking, practical when being used as the bulletproof devices such as ballistic gate, bulletproof window.
As a kind of embodiment, the first delta wood flaggy 110 can be through cold by wooden lagging with multi-plywood 150
Several operation such as pressure, hot pressing, sanding, health preserving is made.
As a kind of embodiment, when shellproof plank 100 is chronically at wet environment or runs into and has corrosive medicine
During product, shellproof plank 100 is highly susceptible to corrode or damage by worms, so, in order to prevent shellproof plank 100 to be corroded or be damaged by worms,
Add preservative generally in multi-plywood 150, this preservative can be the waterborne preservative not readily dissolving, can pass through
In airtight vacuum tube, the timber of multi-plywood 150 is pressed, preservative is pressed into the timber fibre of multi-plywood 150
In dimension.
In addition can also be by, in airtight pressure anti-corrosion tank, preservative being pressed into multi-plywood with vacuum pressure
Inside 150 lumber fibre.
As a kind of embodiment, if run into fire or run into flare, shellproof plank 100 is because it has timber
Structure is it is easy to lead to shellproof plank 100 to light, so generally adding fire retardant in the inside of multi-plywood 150, permissible
In airtight vacuum tube, multi-plywood 150 is pressed, by fire retardant be pressed into multi-plywood 150 lumber fibre so that
Shellproof plank 100 can be prevented fires, and is more beneficial for the use of people.
In order to preferably stop the impulsive force of bullet, as a kind of embodiment, the thickness of the first delta wood flaggy 110 can
Think 18mm.
As a kind of embodiment, pass through between the first shellproof film 122, carbon fiber layer 124 and the second shellproof film 126
, through hot pressing connects, the first shellproof film 122 and second shellproof 126 carbon of film are fine for a kind of resistant to elevated temperatures viscous glutinous agent of inorganic environment-friendly
Dimension layer 124 be wrapped in interior through High Temperature High Pressure formed composite layer 120.
Composite layer 120 can by the impact kinetic energy of bullet be converted into elastic potential energy and broken after surface energy, and
The multilamellar bullet resistant material of shellproof plank 100 setting can more efficiently stop the impact of bullet.
As a kind of embodiment, carbon fiber layer 124 can be the inorganic polymer fiber that phosphorus content is higher than 90%.
As a kind of embodiment, the thickness of carbon fiber stratum reticulare can be 2mm.
As a kind of embodiment, in literary composition, a kind of resistant to elevated temperatures viscous glutinous agent of described inorganic environment-friendly can be refractory ceramics
Adhesivess tbd-n1 is formed, or a kind of high temperature resistant glue, or other have high temperature resistant and adhesive effect material group
Become.
As a kind of embodiment, in literary composition, the first described shellproof film 122 and the second shellproof film 126 can be a kind of
By pe material through High Temperature High Pressure make there is the film of adhesive effect or other materials is especially processed through some
The film being formed afterwards, and can be with other adhering objects through High Temperature High Pressure.
As a kind of embodiment, in literary composition, the first described plywood 152 and the second plywood 154 are to be peeled into by juggle
Veneer or become veneer by flitch slicing, the first multi-plywood 150 is exactly three layers with adhesive gluing veneer or veneer
Or the board-like material of multilamellar, generally use odd-level veneer, and make adjacent layer veneer machine direction is orthogonal or machine direction
Mutually angled gluing forms.Plywood can improve timber utilization rate, is a main path saving timber.
It should be strongly noted that the second delta wood flaggy 130 also includes multi-plywood 150, its multi-plywood 150
Arrangement architecture and the arrangement architecture of multi-plywood 150 of connected mode and the first delta wood flaggy 110 and connection side
Formula is identical, and it is also equipped with high-quality solid wood veneer or Recombinant Wood lagging away from the one side of composite layer 120, or other have
The wooden lagging of ornamental effect.
In order to be able to preferably play shellproof, the explosion-proof of shellproof plank 100, as a kind of embodiment, shellproof plank
100 gross thickness can be 40mm.
The operation principle of shellproof plank 100 is: the first delta wood flaggy 110 is all by many with the second delta wood flaggy 130
Layer plywood 150 composition, it is provided with preservative and fire retardant in the lumber fibre of multi-plywood 150 so that it is tied
Structure stable performance is moreover it is possible to fire prevention, insect protected, anti-corrosion effectively, and its multi-plywood 150 structure makes entirely shellproof plank
100 is lightweight, easy to process；And the first adjacent plywood 152 is different with the machine direction of its timber with the second plywood 154
It is cross-linked, this is just effectively improved the bulletproof ability of shellproof plank 100；First delta wood flaggy 110 and the second delta wood
Flaggy 130 is provided with wooden lagging away from the one side of composite layer 120, makes shellproof plank 100 more attractive, practical.By first
The composite layer 120 that shellproof film 122, carbon fibre web, the second shellproof film 126 are made through High Temperature High Pressure can effectively
The impact kinetic energy of bullet be converted into elastic potential energy and broken after surface energy, its shellproof plank 100 is made up of multilamellar bullet resistant material,
Can shellproof to a great extent, fire prevention, explosion-proof.
Second embodiment
Refer to Fig. 3, the present embodiment provides a kind of shellproof plank 100, the shellproof plank of this enforcement row and first embodiment
100 is roughly the same, and the shellproof plank 100 differring primarily in that the present embodiment of the two also includes the second shellproof composite bed 190, the
Two shellproof composite beds 190 are identical with the first shellproof lamination layer structure, and the second shellproof composite bed 190 and the first shellproof composite bed are even
Connect.
It is provided with the second composite layer 127 between second shellproof composite bed 190 and the first shellproof composite bed.
Pass through inorganic environment-friendly between first shellproof composite bed, the second composite layer 127 and the second shellproof composite bed 190
Resistant to elevated temperatures viscous glutinous agent is through being hot bonding.
Refer to Fig. 4, as a kind of embodiment, the composition structure of the second shellproof composite bed 190 and the company of its structure
Connect mode identical with the composition structure of the first shellproof composite bed and the connected mode of its structure.
It should be strongly noted that the second composite layer 127 include stacking gradually connection the 3rd shellproof film 121,
Carbon fiber layer 124, the 4th shellproof film 123, pass through the resistant to elevated temperatures viscous glutinous agent of inorganic environment-friendly through hot pressing connects between them.
Second shellproof composite bed 190 and the 4th shellproof film 123, the first shellproof composite bed 140 and the 3rd shellproof film 121
All pass through the resistant to elevated temperatures viscous glutinous agent of inorganic environment-friendly through hot pressing connects.
Second shellproof composite bed 190 and the first shellproof composite bed are both provided with away from the one side of the second composite layer 127
High-quality solid wood veneer or Recombinant Wood lagging, or other have the wooden lagging of ornamental effect, make shellproof plank 100 more beautiful
Sight, practicality.
As a kind of embodiment, the composition structure of the second composite layer 127 and the connected mode of its structure with multiple
The connected mode of the composition structure of condensation material layer 120 and its structure is identical.
That is, shellproof plank 100 includes the first shellproof composite bed, the second composite layer stacking gradually connection
127th, the second shellproof composite bed 190, passes through the resistant to elevated temperatures viscous glutinous agent of inorganic environment-friendly through hot pressing connects between them.
As a kind of embodiment, the thickness of the first delta wood flaggy 110 and the second delta wood flaggy 130 is 9mm.
In order to be able to preferably play shellproof, the explosion-proof of shellproof plank 100, as a kind of embodiment, shellproof plank
100 gross thickness is 48mm.
And it is possible to shellproof as needed, explosion-proof rank is arranging the number of the second shellproof composite bed 190, it second
Shellproof composite bed 190 arranges more, and it is shellproof, explosion proof ratings are higher.
The operation principle of shellproof plank 100 is: the first delta wood flaggy 110, the second delta wood flaggy 130 are all by multilamellar
Plywood 150 composition, it is provided with preservative and fire retardant in the lumber fibre of multi-plywood 150 so that its structure
Moreover it is possible to fire prevention, insect protected, anti-corrosion effectively, its multi-plywood 150 structure makes entirely shellproof plank 100 weight for stable performance
Gently, easy to process；And adjacent multi-plywood 150 is cross-linked with its grain direction difference, this is just effectively improved shellproof
The bulletproof ability of plank 100；First shellproof composite bed and the second shellproof composite bed 190 are away from the one of the second composite layer 127
Face is provided with wooden lagging, makes shellproof plank 100 more attractive, practical.Composite layer 120, the second composite layer 127 can have
Surface energy after effect the impact kinetic energy of bullet being converted into elastic potential energy and crushes, its shellproof plank 100 is by the shellproof material of multilamellar
Material composition, can shellproof to a great extent, fire prevention, explosion-proof.
In sum, the present invention provides a kind of shellproof plank 100, by the first delta wood flaggy 110 and second of setting
Delta wood flaggy 130 makes whole shellproof plank 100 light weight, and processing is also convenient for, in addition in the first delta wood flaggy 110 and the
It is provided with composite layer 120, composite layer 120 includes the first shellproof glue being sequentially connected between two delta wood flaggies 130
Piece 122, carbon fiber layer 124, the second shellproof film 126, the impact kinetic energy of bullet can be converted by its composite layer 120 effectively
For elastic potential energy and broken after surface energy, shellproof purpose can be reached, make the structural behaviour of entirely shellproof plank 100 more
Stable.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, for the skill of this area
For art personnel, the present invention can have various modifications and variations.All within the spirit and principles in the present invention, made any repair
Change, equivalent, improvement etc., should be included within the scope of the present invention.
Claims (10)
1. it is characterised in that including the first shellproof composite bed, described first shellproof composite bed includes layer successively to a kind of shellproof plank
Folded the first delta wood flaggy connecting, composite layer and the second delta wood flaggy, described composite layer includes layer successively
Folded the first shellproof film connecting, carbon fiber layer and the second shellproof film, wherein, described first shellproof film and described first
Plywood layer stackup connects, and described second shellproof film is connected with described second plywood layer stackup.
2. shellproof plank according to claim 1 is it is characterised in that described first delta wood flaggy is shellproof with described first
, by viscous glutinous agent through being hot bonding, described second delta wood flaggy and described second shellproof film are by described viscous glutinous agent for film
Through being hot bonding, pass through described viscous glutinous between described first shellproof film, described carbon fiber layer and described second shellproof film
Agent is through being hot bonding.
3. shellproof plank according to claim 1 is it is characterised in that described first delta wood flaggy includes multilayer gluing
Plate, by viscous glutinous agent through being hot bonding between described multi-plywood.
4. shellproof plank according to claim 3 is it is characterised in that be provided with inside the lumber fibre of described multi-plywood
Preservative.
5. shellproof plank according to claim 3 is it is characterised in that be provided with inside the lumber fibre of described multi-plywood
Fire retardant.
6. shellproof plank according to claim 1 is it is characterised in that described first delta wood flaggy is away from described composite wood
The one side of the bed of material is provided with wooden lagging.
7. according to the shellproof plank described in arbitrary one of claim 1-6 it is characterised in that described second delta wood flaggy and institute
The structure stating the first delta wood flaggy is identical.
8. shellproof plank according to claim 1 it is characterised in that described shellproof plank also to include second shellproof compound
Layer, described second shellproof composite bed is identical with the described first shellproof lamination layer structure, described second shellproof composite bed and described the
One shellproof composite bed connects.
9. shellproof plank according to claim 8 is it is characterised in that described second shellproof composite bed is shellproof with described first
It is provided with described composite layer between composite bed.
10. shellproof plank according to claim 8 is it is characterised in that described first shellproof composite bed, described composite
By viscous glutinous agent through being hot bonding between layer and described second shellproof composite bed.