CN106364026B - A kind of couple yoke supporting plate wearing plate - Google Patents
A kind of couple yoke supporting plate wearing plate Download PDFInfo
- Publication number
- CN106364026B CN106364026B CN201610794095.8A CN201610794095A CN106364026B CN 106364026 B CN106364026 B CN 106364026B CN 201610794095 A CN201610794095 A CN 201610794095A CN 106364026 B CN106364026 B CN 106364026B
- Authority
- CN
- China
- Prior art keywords
- supporting plate
- wearing
- couple yoke
- adhesive layer
- yoke supporting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention discloses a kind of couple yoke supporting plate wearing plate, and the outer surface of the substrate adhesive layer is provided with, the adhesive layer outer surface is provided with wearing layer using engineering plastics as substrate for composite construction.Selection engineering plastics are substrate, with superperformances such as higher hardness, intensity, in order to preferably improve wearability, coarse surface, brushing adhesive layer are prepared by techniques such as shot-peenings on the surface of engineering plastics, adhesive layer selects polymer-based composite, and ceramic particle is added wherein, on the one hand ensure the associativity with base material, on the other hand can ensure that wearing layer is firmly arranged in couple yoke supporting plate wearing plate outer surface with the wearing layer good combination of outer surface.
Description
Technical field
The present invention relates to a kind of railway transport vehicle accessory more particularly to a kind of couple yoke supporting plate mills with wear-resisting property
Consume plate.
Background technology
Railway freight-car is equipped with couple yoke, is specified in relevant regulations with pallet support in order to protect couple yoke from wearing
The planker of support couple yoke must install wearing plate additional, using the general steel plate of A3 materials, when wearing plate residual thickness is less than 50% more
It changes, can directly be welded on couple yoke planker.Steel wearing plate is welded on couple yoke supporting plate, and couple yoke supporting plate is installed on car body
Afterwards, steel wearing plate is in direct contact with couple yoke, in lorry driving process, since many reasons such as vibrations cause wearing plate
It directly wears, difficulty is replaced after wearing plate abrasion, since wearing plate is fixedly welded on couple yoke supporting plate, wearing plate abrasion to limit
After must cut off weld seam, be easy couple yoke poppet body is caused to damage.Therefore, the wear-resisting property for effectively extending wearing plate is solution
The certainly effective means of this problem.
In view of defect existing for above-mentioned existing wearing plate, the present inventor is based on being engaged in such product design manufacture for many years
Abundant practical experience and professional knowledge, and coordinate the utilization of scientific principle, actively it is subject to research and innovation, to found a kind of novel hook
Tail frame supporting plate wearing plate makes it have more practicability.By constantly studying, designing, and after studying sample repeatedly and improving,
Finally the present invention having practical value is created.
Invention content
It is a primary object of the present invention to, overcome defect existing for existing wearing plate, and a kind of novel hook tail frame is provided
Supporting plate wearing plate improves wear-resisting property, thus more suitable for practicality, and with the utility value in industry.
The object of the invention to solve the technical problems is realized using following technical scheme.It proposes according to the present invention
Couple yoke supporting plate wearing plate, the outer surface of the substrate is provided with bonding using engineering plastics as substrate for composite construction
Layer, the adhesive layer outer surface is provided with wearing layer.
Couple yoke supporting plate wearing plate above-mentioned, the adhesive layer are polymer-based composite.
Couple yoke supporting plate wearing plate above-mentioned, the adhesive layer are grouped as by each group of following mass parts：
Couple yoke supporting plate wearing plate above-mentioned, the wearing layer are grouped as by each group of following mass parts：
Couple yoke supporting plate wearing plate above-mentioned, the engineering plastics are polyamide, polytetrafluoroethylene (PTFE), ABS plastic, polyformaldehyde
Or any one in makrolon.
Couple yoke supporting plate wearing plate above-mentioned, the solvent are methyl propanediol, Propylene Glycol, pentaerythrite, second
Any one in alcohol, methanol or acetone.
Couple yoke supporting plate wearing plate above-mentioned, the adhesion promoter are the mixing of epoxy resin and polyurethane resin
Object.
Couple yoke supporting plate wearing plate above-mentioned, the tackifier are p-methylstyrene, m-methyl styrene, adjacent methyl
Styrene or dimethyl styrene it is therein any one.
Couple yoke supporting plate wearing plate above-mentioned, the levelling agent be clay, calcium carbonate, butadiene-styrene rubber, tetrasodium pyrophosphate and
The mixture of fluorine-containing surfactant.
Couple yoke supporting plate wearing plate above-mentioned, dispersant nano-titanium dioxide, organobentonite or the hypophosphorous acid
Aluminium it is therein any one.
Further, nano-ceramic particle selects nano calcium oxide, nano silicon oxide, nanometer silicon carbide, nano-silica
Change titanium it is therein any one.
By above-mentioned technical proposal, couple yoke supporting plate wearing plate of the invention at least has following advantages：
It is a primary object of the present invention to improve the wearability of couple yoke supporting plate wearing plate, selection engineering plastics are substrate,
With superperformances such as higher hardness, intensity, in order to preferably improve wearability, pass through shot-peening etc. on the surface of engineering plastics
Technique prepares coarse surface, brushing adhesive layer, and adhesive layer selects polymer-based composite, and addition ceramics wherein
On the one hand grain ensures the associativity with base material, on the other hand can ensure wearing layer jail with the wearing layer good combination of outer surface
Solid setting in couple yoke supporting plate wearing plate outer surface.
The adhesion promoter added in adhesive layer selects the mixture of epoxy resin and polyurethane resin, addition fluorine surface
Activating agent, high surface determine that its dosage is seldom, its high thermal stability and high chemical inertness are determined to system
Stability does not adversely affect；By controlling addition, it may make substrate surface wettability good, be convenient for drying, improve
Adhesion property.
Dispersant wherein in adhesive layer is used to improve the uniformity of adhesive layer itself, it is ensured that adhesive layer each section of preparation
Performance is consistent；Adhesion promoter is used to enhance the adhesion property between adhesive layer and base material, the aluminium powder additionally added and nanometer
Ceramic particle is ensured and the smooth combination of wearing layer to improve the workability of adhesive layer.
Wearing layer select addition ceramic composition ceramic-metal composite, in ingredient in addition to addition bonding component Ni and
Other than Cr, Pt is also added, Cr in wearing layer can be promoted to diffuse to the surface, improve the antioxygenic property of adhesive layer；But Pt
Content is too low, the effect for increasing Cr and diffusing to the surface will be not achieved, the excessively high aggregation that can cause Cr influences uniformity, therefore Pt
Content control between 1~10 mass parts.Dy is also added, the crystallite size in wearing layer can be refined, acted predominantly on
In the compactness and adhesive capacity of enhancing wearing layer.
Above description is only the general introduction of technical solution of the present invention, in order to better understand the technical means of the present invention,
And can be implemented in accordance with the contents of the specification, it is described in detail as after with presently preferred embodiments of the present invention below.
Specific implementation mode
Further to illustrate the present invention to reach the technological means and effect that predetermined goal of the invention is taken, to according to this
Couple yoke supporting plate wearing plate its specific implementation mode, feature and its effect proposed is invented, is described in detail as after.
Embodiment 1
The couple yoke supporting plate wearing plate of the present invention selects Teflon engineered plastic as baseplate material, prepares couple yoke
Supporting plate wearing plate prepares coarse surface by shot-blast process on the surface of the substrate, convenient for preparing adhesive layer, increase adhesive layer with
The adhesive property of substrate.
Adhesive layer is grouped as by each group of following mass parts：44 parts of methyl propanediol solvents, 16 parts of epoxy resin and poly- ammonia
For the mixture of ester resin as adhesion promoter, the mass ratio of epoxy resin and polyurethane resin is 1：3；Two between 8 parts
Methyl styrene tackifier, 2 parts of aluminium powders, 10 parts of clay, calcium carbonate, butadiene-styrene rubber, tetrasodium pyrophosphate and fluorine-containing surfactant
Mixture is as levelling agent, the mass ratio of wherein clay, calcium carbonate, butadiene-styrene rubber, tetrasodium pyrophosphate and fluorine-containing surfactant
1:2:1:3：3：1；4 parts of nano-titanium dioxide dispersants, 16 parts of nano silicon oxide nano-ceramic particles.Nano-ceramic particle and its
The dispersant coordinated of middle addition ensures there is better dispersion effect；Adhesion promoter can be by the binder of dispersion
It is firm to be attached to substrate surface, enhance caking property.
It is additionally provided with one layer of wearing layer in the outer surface of adhesive layer, is grouped as by each group of following mass parts：44 parts of ZrO2,
4 parts of Y2O3, 2 parts of MoSi2, 3 parts of Ni, 7 parts of Cr, 21 parts of SiC, 8 parts of TiC, 7 parts of Pt, 4 parts of Dy.
Increasing Pt in wearing layer is improved to ensure that the aggregation of Cr, Dy can refine the crystallite size in wearing layer
Wear-resisting property.
Embodiment 2
The couple yoke supporting plate wearing plate of the present invention selects polycarbonate engineering plastic as baseplate material, prepares couple yoke support
Plate wearing plate prepares coarse surface by shot-blast process on the surface of the substrate, convenient for preparing adhesive layer, increases adhesive layer and base
The adhesive property of plate.
Adhesive layer is grouped as by each group of following mass parts：38 parts of acetone solvents, 16 parts of epoxy resin and polyurethane resin
Mixture as adhesion promoter, the mass ratio of epoxy resin and polyurethane resin is 2:2；8 parts to methylbenzene second
Alkene tackifier, 8 parts of aluminium powders, 13 parts of clay, calcium carbonate, butadiene-styrene rubber, tetrasodium pyrophosphate and fluorine-containing surfactant mixture make
For levelling agent, the wherein mass ratio of clay, calcium carbonate, butadiene-styrene rubber, tetrasodium pyrophosphate and fluorine-containing surfactant is 2:2:3:3：
2：1；4 parts of hypo-aluminum orthophosphate dispersants, 17 parts of nano calcium oxide nano-ceramic particles.Nano-ceramic particle and the dispersion wherein added
Agent coordinated ensures there is better dispersion effect；The binder of dispersion can be firmly attached to by adhesion promoter
Substrate surface enhances caking property.
It is additionally provided with one layer of wearing layer in the outer surface of adhesive layer, is grouped as by each group of following mass parts：35 parts of ZrO2,
2 parts of Y2O3, 3 parts of MoSi2, 6 parts of Ni, 4 parts of Cr, 25 parts of SiC, 6 parts of TiC, 9 parts of Pt, 10 parts of Dy.
Increasing Pt in wearing layer is improved to ensure that the aggregation of Cr, Dy can refine the crystallite size in wearing layer
Wear-resisting property.
Embodiment 3
The couple yoke supporting plate wearing plate of the present invention selects Polyamide Engineering Plastic as baseplate material, prepares couple yoke supporting plate
Wearing plate prepares coarse surface by shot-blast process on the surface of the substrate, convenient for preparing adhesive layer, increases adhesive layer and substrate
Adhesive property.
Adhesive layer is grouped as by each group of following mass parts：40 parts of pentaerythrite solvents, 11 parts of epoxy resin and polyurethane
For the mixture of resin as adhesion promoter, the mass ratio of epoxy resin and polyurethane resin is 3:4；5 parts of adjacent methyl
Styrene tackifier, 14 parts of aluminium powders, the mixing of 15 parts of clay, calcium carbonate, butadiene-styrene rubber, tetrasodium pyrophosphate and fluorine-containing surfactant
Object is 2 as levelling agent, the wherein mass ratio of clay, calcium carbonate, butadiene-styrene rubber, tetrasodium pyrophosphate and fluorine-containing surfactant:4:
3:1：2：1；2 parts of organobentonite dispersants, 13 parts of nanometer silicon carbide nano-ceramic particles.Nano-ceramic particle with wherein add
Dispersant coordinated, ensure have better dispersion effect；Adhesion promoter can be firm by the binder of dispersion
It is attached to substrate surface, enhances caking property.
It is additionally provided with one layer of wearing layer in the outer surface of adhesive layer, is grouped as by each group of following mass parts：42 parts of ZrO2,
1 part of Y2O3,1 part of MoSi2,2 parts of Ni, 6 parts of Cr, 28 parts of SiC, 5 parts of TiC, 9 parts of Pt, 6 parts of Dy.
Increasing Pt in wearing layer is improved to ensure that the aggregation of Cr, Dy can refine the crystallite size in wearing layer
Wear-resisting property.
It takes 4 point test hardness respectively in wearing layer, its average hardness value, the final result is asked to be used as and detected
The hardness of sample, load 0.9807N used in test protect lotus time 15s, and wearing layer Rockwell hardness number prepared by each embodiment is such as
Shown in table 1.
1 hardness test result of table
| Wearing layer | Hardness number 1 | Hardness number 2 | Hardness number 3 | Hardness number 4 | Average value |
| Embodiment 1 | 1219 | 1100 | 1005 | 1228 | 1138 |
| Embodiment 2 | 1100 | 1243 | 1030 | 1008 | 1095 |
| Embodiment 3 | 1008 | 1222 | 1267 | 1026 | 1130 |
The wear-resistant coating hardness of preparation has reached 1000 Rockwell hardness or more, and the hardness of general metal-cermic coating exists
Between 900~1000, hardness is to reflect one of the important indicator of wear-resisting property, it is seen that wearing layer wearability of the invention is preferable.
The quality of the height of porosity and the consistency and coating of low intuitively reflection coating.Porosity is high, and coating combines tight
It is close, it is high-quality；Otherwise coating combine it is loose, it is of poor quality.DT2000 metallographics point are carried using OLMPUS-BX51M light microscopes
Analyse software, specimen cross section randomly select region take 10 photos are averaged, measure the porosity of coating, such method base
Gray value in light microscope tests porosity.The voidage of each embodiment wearing layer is as shown in table 2.
2 voidage test result of table
The above described is only a preferred embodiment of the present invention, be not intended to limit the present invention in any form, though
So the present invention has been disclosed as a preferred embodiment, and however, it is not intended to limit the invention, any technology people for being familiar with this profession
Member, without departing from the scope of the present invention, when the technology contents using the disclosure above make a little change or modification
For the equivalent embodiment of equivalent variations, as long as being the content without departing from technical solution of the present invention, according to the technical essence of the invention
To any simple modification, equivalent change and modification made by above example, in the range of still falling within technical solution of the present invention.
Claims (7)
1. a kind of couple yoke supporting plate wearing plate, it is characterised in that：For composite construction, using engineering plastics as substrate, in the substrate
Outer surface be provided with adhesive layer, the adhesive layer outer surface is provided with wearing layer, passes through shot-peening work on the surface of the substrate
Skill prepares coarse surface, to increase the adhesive property of the adhesive layer and the substrate；
The adhesive layer is polymer-based composite；
The adhesive layer is grouped as by each group of following mass parts：
Solvent 20 ~ 45
Adhesion promoter 5 ~ 20
Tackifier 5 ~ 20
Aluminium powder 1 ~ 15
Levelling agent 8 ~ 25
Dispersant 1 ~ 5
Nano-ceramic particle 2 ~ 20；
The wearing layer is grouped as by each group of following mass parts：
ZrO2 30~50
Y2O3 1~5
MoSi2 1~5
Ni 2~8
Cr 2~8
SiC 20~40
TiC 1~10
Pt 1~10
Dy 1~10。
2. couple yoke supporting plate wearing plate according to claim 1, it is characterised in that：The engineering plastics are polyamide, gather
Any one in tetrafluoroethene, ABS plastic, polyformaldehyde or makrolon.
3. couple yoke supporting plate wearing plate according to claim 1, it is characterised in that：The solvent be methyl propanediol,
Any one in Propylene Glycol, pentaerythrite, ethyl alcohol, methanol or acetone.
4. couple yoke supporting plate wearing plate according to claim 1, it is characterised in that：The adhesion promoter is epoxy
The mixture of resin and polyurethane resin.
5. couple yoke supporting plate wearing plate according to claim 1, it is characterised in that：The tackifier are to methylbenzene second
Alkene, m-methyl styrene, o-methyl styrene or dimethyl styrene it is therein any one.
6. couple yoke supporting plate wearing plate according to claim 1, it is characterised in that：The levelling agent is clay, carbonic acid
The mixture of calcium, butadiene-styrene rubber, tetrasodium pyrophosphate and fluorine-containing surfactant.
7. couple yoke supporting plate wearing plate according to claim 1, it is characterised in that：The dispersant is nanometer titanium dioxide
Titanium, organobentonite or hypo-aluminum orthophosphate it is therein any one.