Content of the invention
Based on this it is necessary to the problem existing for sole processing method, provide one kind can improve sole aesthetics, sample
The good assembled shoe bottom processing method of formula diversification, non-skid property.
A kind of assembled shoe bottom processing method, comprises the steps:
S1, mould is placed on forming machine, starts described forming machine and preheated;
S2, the raw material of different colours is added separately in described mould, described forming machine carries out processing and forming
Obtain the big bottom of footwear that model is identical, color is single;
S3, the big bottom of described footwear of different colours is placed in cutting machine, big bottom is entered to described footwear to start described cutting machine
Row severing obtains default cutting cube, and described cutting cube is collected arranging according to code section, color;
S4, carry out sole color matching, by different code sections, color described cutting cube assembling combination in assembling die;
S5, the described assembling die being placed with described cutting cube is placed on hot press, on described cutting cube successively
Place transparent hot melt, release paper and heat-insulated stereotype plate, described hot press pushes afterwards;
S6, hot press rise, and take off described heat-insulated stereotype plate, release paper, are sequentially placed heat on described transparent hot melt
Melten gel mutispandex, release paper and heat-insulated stereotype plate, afterwards described hot press push and obtain assembled shoe bottom;
S7, described assembled shoe bottom is placed on household freezer is processed.
Wherein in an embodiment, in described step s1, preheating temperature is set as 177~183 DEG C.
Wherein in an embodiment, described step s2 also includes cooling treatment, heat treatment and Product checking, described cold
But process and be divided into first stage, second stage, phase III, the chilling temperature of described first stage is 67~69 DEG C, described the
The chilling temperature of two-stage is 53~55 DEG C, and the chilling temperature of described phase III is 44~46 DEG C.
Wherein in an embodiment, the time of described cooling treatment is 13~17min altogether.
Wherein in an embodiment, described heat treatment adopts pressing mold to shape, and is applied more than being equal on described pressing mold
The pressure of 10kg.
Wherein in an embodiment, described step s3 will carry out hardness, Thickness sensitivity in big bottom to described footwear before severing,
So that severing is normally carried out.
Wherein in an embodiment, after different code sections in described step s4, the described cutting cube assembling combination of color
Surface smoothes out.
Wherein in an embodiment, the temperature of the described hot press in described step s5 is 123~127 DEG C, and pressure is
4.5kg/cm, pressing time is 2~4s.
Wherein in an embodiment, the temperature of the described hot press in described step s6 is 123~127 DEG C, and pressure is
4.5kg/cm, pressing time is 13~17s.
Wherein in an embodiment, also comprise the steps: after step s7 s8, described assembled shoe bottom is carried out left and right join
Double pack is processed.
Combinations thereof sole processing method, first passes through raw material and completes on forming machine that specification is identical, different colours footwear
Big bottom processing and forming, then severing is carried out to the big bottom of footwear of different colours by cutting machine obtain cutting cube, and by cutting cube according to code
Section, color are collected arranging.The cutting cube of different code sections, color is assembled in assembling die, starts hot press simultaneously afterwards
Complete to push laminating process by transparent hot melt, PUR mutispandex, obtain assembled shoe bottom.Whole assembled shoe bottom processing method
Each flow process compact, transparent hot melt, PUR mutispandex be used in combination can allow different code sections, color cutting cube fast
Speed laminating forms a complete sole, is not readily separated, is closely pasted together, this sole has easily between each cutting cube
Bend, skid resistance is good, firm characteristic.Because each assembled shoe bottom is to be fitted by after the cutting cube assembling combination of different colours
Formed, make assembled shoe bottom more attractive in appearance, pattern variation, very useful.
Specific embodiment
For the ease of understanding the present invention, below with reference to relevant drawings, the present invention is described more fully.In accompanying drawing
Give presently preferred embodiments of the present invention.But, the present invention can realize in many different forms however it is not limited to this paper institute
The embodiment of description.On the contrary, providing the purpose of these embodiments to be to make the understanding to the disclosure more thorough
Comprehensively.
It should be noted that when element is referred to as " being fixed on " another element, it can be directly on another element
Or can also there is element placed in the middle.When an element is considered as " connection " another element, it can be directly connected to
To another element or may be simultaneously present centering elements.
Unless otherwise defined, all of technology used herein and scientific terminology and the technical field belonging to the present invention
The implication that technical staff is generally understood that is identical.The term being used in the description of the invention herein is intended merely to description tool
The purpose of the embodiment of body is it is not intended that in limiting the present invention.
Refer to Fig. 1, be the flow chart of the assembled shoe bottom processing method of a preferred embodiment of the present invention, walk including following
Rapid:
S1, provide mould, forming machine, raw material, cutting machine, assembling die, transparent hot melt, PUR mutispandex,
Release paper, heat-insulated stereotype plate, hot press, household freezer are standby, check and check numbering, the size of mould, by mould
It is placed on forming machine, start forming machine and preheated, preheating temperature is set as 177~183 DEG C, is preferably 180 DEG C.
S2, the raw material of different colours is added separately in mould, forming machine is to solid color in mould
Raw material carry out processing and forming and obtain the big bottom of footwear that model is identical, color is single, finally give that multiple colors are different but model phase
The same big bottom of footwear.
S3, to footwear, big bottom carries out hardness, Thickness sensitivity, big for the footwear of different colours bottom is placed in cutting machine, to severing
Machine is set, and adjusts die position, and big bottom carries out severing and obtains default cutting cube to footwear to start cutting machine, will cut tuber
It is collected arranging according to code section, color, can numbering placement one by one in order.
S4, carry out sole color matching, by different code sections, color cutting cube assembling combination in assembling die, make in combination
Surface smooth-going after different code sections in mould, the cutting cube assembling combination of color.
S5, the described assembling die being placed with described cutting cube is placed on hot press, on described cutting cube successively
Place transparent hot melt, release paper and heat-insulated stereotype plate, hot press pushes afterwards, the temperature of hot press is 123~127 DEG C, excellent
Elect 125 DEG C as, pressure is 4.5kg/cm, pressing time is 2~4s, preferably 3s.
S6, hot press rise, and take off described heat-insulated stereotype plate, release paper, are sequentially placed heat on described transparent hot melt
Melten gel mutispandex, release paper and heat-insulated stereotype plate, afterwards described hot press push and obtain assembled shoe bottom, the temperature of hot press is
123~127 DEG C, preferably 125 DEG C, pressure is 4.5kg/cm, and pressing time is 13~17s, preferably 15s.
S7, described assembled shoe bottom be placed on household freezer processed, make mutispandex pass through PUR quick firmly with
Cutting cube is fitted.
S8, described assembled shoe bottom is carried out left and right join double pack process.
In step s1, mould passes through screw locking on forming machine, to avoid having vibrations in production process, impact
The quality producing.In step s2, forming machine includes to the concrete steps carrying out processing and forming: a, verification raw material numbering, with true
Protect and use correct raw material, the laggard material of advancing of confirmation;B, the type of being set as determine machine board to adapt to different processing conditionss;c、
Close mould d, shot material to mould by projecting shower nozzle;E, after forming machine completes processing and forming, open molding
Mould;F, manually take out footwear big bottom cleaning mould, return to step c and be continuing with.
Also include cooling treatment, heat treatment and the Product checking successively carrying out in step s2, described cooling treatment is divided
For first stage, second stage, phase III, the time of cooling treatment is 13~17min, preferably 15min altogether.First stage
Chilling temperature be 67~69 DEG C, preferably 68 DEG C, the chilling temperature of second stage is 53~55 DEG C, preferably 54 DEG C, the 3rd
The chilling temperature in stage is 44~46 DEG C, preferably 45 DEG C, successively goes through the cooling treatment of three phases, the big bottom of footwear is progressively terraced
Degree cooling, thus will not damage footwear bottom matter, the chi at the big bottom of the footwear after cooling treatment because of the larger very fast cooling of the temperature difference
Very little can reduce a bit.Heat treatment adopts pressing mold to shape, and is applied more than the pressure equal to 10kg, makes the footwear at the big bottom of footwear on pressing mold
Head keeps 5~15 degree of set-back, by natural cooling under indoor temperature, controls cool time more than 15 minutes.Product checking
Including carrying out size detection with ground plate it is allowed to the error of length+1~3mm is it is allowed to the error of width ± 0.5mm;Afterwards with card
Chi toe-cap and followed by thickness it is allowed to the error of ± 1mm;Carry out repair flash afterwards;Finally carry out color join double, it is to avoid because of not equality of temperature
Spend the aberration causing.
Step s3 before severing will to footwear big bottom carry out hardness, Thickness sensitivity it is ensured that the big bottom of each footwear toe-cap, after
With conformance with standard it is ensured that severing is normally carried out.
Step s4 is matched colors according to Production requirement, different code sections.Can not after the cutting cube assembling combination of color
Have dislocation, rugged phenomenon, the side edge of a knife at assembled shoe bottom needs to smooth out, and can not have zigzag.
Transparent hot melt film is the same with the size of PUR mutispandex, PUR mutispandex hot melt under the hot pressing of hot press
Glue melts, make mutispandex pass through PUR and different code sections, color cutting cube fit, release paper plays and avoids hot press
Pressure head is bonding with transparent hot melt, PUR mutispandex, prevent mutispandex be contaminated it is ensured that laminating processing quality.
Each technical characteristic of embodiment described above can arbitrarily be combined, for making description succinct, not to above-mentioned reality
The all possible combination of each technical characteristic applied in example is all described, as long as however, the combination of these technical characteristics is not deposited
In contradiction, all it is considered to be the scope of this specification record.
Embodiment described above only have expressed the several embodiments of the present invention, and its description is more concrete and detailed, but simultaneously
Can not therefore be construed as limiting the scope of the patent.It should be pointed out that coming for those of ordinary skill in the art
Say, without departing from the inventive concept of the premise, some deformation can also be made and improve, these broadly fall into the protection of the present invention