CN106353893A - Manufacturing method for hardened film resin lens - Google Patents
Manufacturing method for hardened film resin lens Download PDFInfo
- Publication number
- CN106353893A CN106353893A CN201510425842.6A CN201510425842A CN106353893A CN 106353893 A CN106353893 A CN 106353893A CN 201510425842 A CN201510425842 A CN 201510425842A CN 106353893 A CN106353893 A CN 106353893A
- Authority
- CN
- China
- Prior art keywords
- blue light
- conversion particles
- wavelength conversion
- lens
- hardening liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a manufacturing method for a hardened film resin lens. According to the lens, a novel hardening liquid which is manufactured by blue light wavelength conversion particles is blended and used to perform dip-coating treatment on the surface of the lens on the basis of the existing lens film coating process flow treatment, blue light with the wavelength of 400 to 480 nm which is harmful to a human body is converted into low-frequency near infrared light with the wavelength of 850 to 950 nm; the original blue light preventing capacity of the lens is remarkably improved on the premise of ensuring light transmittance of the lens; the blue light attenuation rate is increased from original 10 to 20 percent to above 80 percent; the blue light transmittance is attenuated selectively, and meanwhile, the overall light transmittance of the lens is taken into consideration; the window transfer transmittance adjustment of the blue light frequency is realized; the manufacturing method has the characteristics that the creativity is novel, the technology is unique, the process is simple, the practicability is high, and the blue light attenuation rate can be selectively adjusted.
Description
Technical field
The present invention relates to anti-blue light resin lens make applied technical field, particularly relate to a kind of anti-blue light resin lens being coated with blue light wavelength conversion particles stiffened film layer and preparation method thereof.
Background technology
The radioprotective eyeglass generally sold on glasses market now is the indium stannum alloy conductive film layer of stiffened one layer of 20 200 nano thickness of film surface vacuum evaporation in resin lens, realize the decay shielding action to high frequency electromagnetic radiation using the electric conductivity of indium stannum alloy, but indium is rare metal, excavating with exploitation in ground in the layer reserves can be fewer and feweri, when eventually having resource exhaustion, if can manage to solve the shielding problem of electromagnetic radiation as resin lens surface coating using the extremely abundant carbon series of conductive product of present on earth amount, the space of great development and application will be had.
A kind of anti-blue light resin lens manufacture method of Chinese patent 201310408405.4 and product employ to be dosed the method for blue-light absorbers (o l p melanin powder) to absorb and to scatter blue light energy in heat curing-type optical resin monomer,Decrease passing through of blue light,It is reported that,When the addition of o l p melanin powder is in 600-800ppm,The product made can stop more than 90% blue light,But o l p melanin powder belongs to the light absorbent of wide spectrum type,Its advantage is to high-frequency shortwave light such as purple light、The screening factor of blue light is more than the decay screening factor to low frequency light wave,But itself there is no window adsorption frequency,The Rectangular decay characteristic curve to blue light cannot be realized,Also reduce passing through of other frequency coloured light while decaying blue light,Reduce the integral light-transmitting rate of eyeglass.
Content of the invention
The invention provides a kind of manufacture method of stiffened film resin eyeglass, it is the use of a kind of new hardening liquid of blue light wavelength conversion particles making and dip-coating processing is carried out to lens surface, blue light between harmful wavelength 400-480nm can be converted into the near infrared light of the low frequency wavelength of wavelength 850-950nm, eyeglass original anti-blue light ability is made to significantly improve, blue light attenuation rate increases to more than 80% by 20%.
Technical scheme is realized by following technological means: a kind of manufacture method of stiffened film resin eyeglass it is characterised in that: comprise the following steps:
1), weigh 50 grams of the blue light wavelength conversion particles powder of 5 15 microns of particle diameter, grind 30 minutes to 2 hours in high-energy planetary formula nanon ball-mill;
2), measure 20 liters of silica resin eyeglass hardening liquid with plastic containers, liquid is inserted into high speed electric blender stirring-head, 1800 rotating speed strong stirring per minute 30 minutes, add the nanoscale blue light wavelength conversion particles powder of 0.1-2% part by weight in whipping process according to specific needs successively, be all dispersed in silicon dioxide hardening liquid to conversion particles;
3), the silicon dioxide hardening liquid of mixing blue light wavelength conversion particles is poured into ultrasonic disperse 1 hour in the stainless steel tank of 200 watts of ultrasonic oscillators;
4), the hardening liquid of blue light wavelength conversion particles good for dispersion mixing is put in vacuum tank and start evacuator after standing 2-4 hour, extract bubble in clean liquid;
5), the hardening liquid extracting the mixing blue light wavelength conversion particles of clean bubble is poured in the immersion groove on plated film flow production line, in slow agitation, routinely plate the czochralski method of stiffened film in resin lens surface dip-coating hardening liquid;
6), resin lens surface dip-coating hardening liquid is put into after processing and is heated up to 120 degree in infrared drying case and carries out heat cure in 2 hours, forms, on resin lens surface, the anti-blue light resin lens being coated with blue light wavelength conversion particles stiffened film layer that a layer thickness is 2-5 micron.
The present invention, has the function of antistatic, anti-blue light and anti-electromagnetic-radiation, and blue light attenuation rate increases to more than 80% by 20%.Simple and practical, of many uses.
Specific embodiment
A kind of manufacture method of present invention stiffened film resin eyeglass, comprises the following steps:
1), weigh 50 grams of the blue light wavelength conversion particles powder of 5 15 microns of particle diameter, grind 30 minutes to 2 hours in high-energy planetary formula nanon ball-mill;
2), measure 20 liters of silica resin eyeglass hardening liquid with plastic containers, liquid is inserted into high speed electric blender stirring-head, 1800 rotating speed strong stirring per minute 30 minutes, add the nanoscale blue light wavelength conversion particles powder of 0.1-2% part by weight in whipping process according to specific needs successively, be all dispersed in silicon dioxide hardening liquid to conversion particles;
3), the silicon dioxide hardening liquid of mixing blue light wavelength conversion particles is poured into ultrasonic disperse 1 hour in the stainless steel tank of 200 watts of ultrasonic oscillators;
4), the hardening liquid of blue light wavelength conversion particles good for dispersion mixing is put in vacuum tank and start evacuator after standing 2-4 hour, extract bubble in clean liquid;
5), the hardening liquid extracting the mixing blue light wavelength conversion particles of clean bubble is poured in the immersion groove on plated film flow production line, in slow agitation, routinely plate the czochralski method of stiffened film in resin lens surface dip-coating hardening liquid;
6), resin lens surface dip-coating hardening liquid is put into after processing and is heated up to 120 degree in infrared drying case and carries out heat cure in 2 hours, forms, on resin lens surface, the anti-blue light resin lens being coated with blue light wavelength conversion particles stiffened film layer that a layer thickness is 2-5 micron.
Claims (1)
1. a kind of manufacture method of stiffened film resin eyeglass, comprises the following steps:
1), weigh 50 grams of the blue light wavelength conversion particles powder of 5 15 microns of particle diameter, grind 30 minutes to 2 hours in high-energy planetary formula nanon ball-mill;
2), measure 20 liters of silica resin eyeglass hardening liquid with plastic containers, liquid is inserted into high speed electric blender stirring-head, 1800 rotating speed strong stirring per minute 30 minutes, add the nanoscale blue light wavelength conversion particles powder of 0.1-2% part by weight in whipping process according to specific needs successively, be all dispersed in silicon dioxide hardening liquid to conversion particles;
3), the silicon dioxide hardening liquid of mixing blue light wavelength conversion particles is poured into ultrasonic disperse 1 hour in the stainless steel tank of 200 watts of ultrasonic oscillators;
4), the hardening liquid of blue light wavelength conversion particles good for dispersion mixing is put in vacuum tank and start evacuator after standing 2-4 hour, extract bubble in clean liquid;
5), the hardening liquid extracting the mixing blue light wavelength conversion particles of clean bubble is poured in the immersion groove on plated film flow production line, in slow agitation, routinely plate the czochralski method of stiffened film in resin lens surface dip-coating hardening liquid;
6), resin lens surface dip-coating hardening liquid is put into after processing and is heated up to 120 degree in infrared drying case and carries out heat cure in 2 hours, forms, on resin lens surface, the anti-blue light resin lens being coated with blue light wavelength conversion particles stiffened film layer that a layer thickness is 2-5 micron.