CN106350802A - Hydroelectric generator rotor - Google Patents
Hydroelectric generator rotor Download PDFInfo
- Publication number
- CN106350802A CN106350802A CN201610770952.0A CN201610770952A CN106350802A CN 106350802 A CN106350802 A CN 106350802A CN 201610770952 A CN201610770952 A CN 201610770952A CN 106350802 A CN106350802 A CN 106350802A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- parts
- weight
- treatment liquid
- axle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a hydroelectric generator rotor. A metal rotor shaft of the hydroelectric generator rotor is subjected to passivating treatment and the passivating treatment comprises the following steps: 1) putting 1 to 2 parts of N-butyl naphthalene sulfonate, 1.5 parts of dodecyl dimethyl betaine, 1.5 parts of vinyl trimethoxy silane, 0.8 part of dioscorea cirrhosa residue extracts and 4.2 parts of hydroxyethylidene diphosphonic acid sequentially into 33 parts of deionized water and stirring uniformly; 2) putting 1.6 parts of sodium molybdate, 1.9 parts of polyacrylic ester, 1.1 parts of N-phenyl-2-naphthylamine, 0.8 part of waterborne fluorocarbon emulsion and 1.3 parts of N-octadecylamine oleyl sarcosinate sequentially again, and continuously stirring until the materials are mixed completely and uniformly to prepare passivating treatment liquid; and 3) putting the metal rotor shaft into the passivating treatment liquid, performing passivating treatment at 45 DEG C for 35 seconds, taking out the metal rotor shaft, washing with pure water and then drying. The metal rotor shaft of the hydroelectric generator rotor provided by the invention is subjected to passivating treatment, so that the performance and the surface smoothness are high.
Description
Technical field
The present invention relates to hydroelectric generation machine rotor.
Background technology
Existing hydroelectric generation machine rotor, including metallic rotator axle, but antirust, the corrosion-resistant, abrasion-resistant of metallic rotator axle, anti-
Oxidation, heat-resisting, cold-resistant, weather resistance have much room for improvement, and surface smoothness is also not ideal enough.
Content of the invention
It is an object of the invention to provide a kind of hydroelectric generation machine rotor, its metallic rotator axle through Passivation Treatment, in gold
Metal surface forms uniform passivation protection film, has excellent antirust, corrosion-resistant, abrasion-resistant, antioxidation, heat-resisting, cold-resistant, weather-proof
Performance, and surface smoothness is good.
For achieving the above object, the technical scheme is that a kind of hydroelectric generation machine rotor of design, it includes metal and turns
Sub- axle, through Passivation Treatment, described Passivation Treatment comprises the steps: this metallic rotator axle
1) by 1~2 weight portion normal-butyl sodium naphthalene sulfonate, 1.5 weight portion empgen BBs, 1.5 parts by weight of ethylene bases
Trimethoxy silane, 0.8 weight portion Rhizoma Dioscoreae Cirrhosae slag extract, 4.2 weight portion hydroxy ethylene diphosphonic acids put into 33 weight portions successively
In deionized water, stir;
2) 1.6 weight portion sodium molybdate, 1.9 parts by weight of polypropylene acid esters, 1.1 weight portion n- phenyl -2- naphthalenes are put into again successively
Amine, 0.8 weight portion water-base fluorocarbon emulsion, 1.3 weight portion n- N-Oleoylsarcosine 18-amine. salt, continue stirring, equal to being sufficiently mixed
Even, prepared inactivating treatment liquid;
3) metallic rotator axle is inserted and be passivated in inactivating treatment liquid processing, 45 DEG C for the treatment of temperature, process time 35 seconds,
Cleaned with pure water after taking-up and dry again.
Preferably, hydroelectric generation machine rotor, it includes metallic rotator axle, and this metallic rotator axle is through Passivation Treatment, described
Passivation Treatment comprises the steps:
1) by 1 weight portion normal-butyl sodium naphthalene sulfonate, 1.5 weight portion empgen BBs, 1.5 parts by weight of ethylene base front threes
TMOS, 0.8 weight portion Rhizoma Dioscoreae Cirrhosae slag extract, 4.2 weight portion hydroxy ethylene diphosphonic acids put into successively 33 weight portions go from
In sub- water, stir;
2) 1.6 weight portion sodium molybdate, 1.9 parts by weight of polypropylene acid esters, 1.1 weight portion n- phenyl -2- naphthalenes are put into again successively
Amine, 0.8 weight portion water-base fluorocarbon emulsion, 1.3 weight portion n- N-Oleoylsarcosine 18-amine. salt, continue stirring, equal to being sufficiently mixed
Even, prepared inactivating treatment liquid;
3) metallic rotator axle is inserted and be passivated in inactivating treatment liquid processing, 45 DEG C for the treatment of temperature, process time 35 seconds,
Cleaned with pure water after taking-up and dry again.
Preferably, hydroelectric generation machine rotor, it includes metallic rotator axle, and this metallic rotator axle is through Passivation Treatment, described
Passivation Treatment comprises the steps:
1) by 2 weight portion normal-butyl sodium naphthalene sulfonates, 1.5 weight portion empgen BBs, 1.5 parts by weight of ethylene base front threes
TMOS, 0.8 weight portion Rhizoma Dioscoreae Cirrhosae slag extract, 4.2 weight portion hydroxy ethylene diphosphonic acids put into successively 33 weight portions go from
In sub- water, stir;
2) 1.6 weight portion sodium molybdate, 1.9 parts by weight of polypropylene acid esters, 1.1 weight portion n- phenyl -2- naphthalenes are put into again successively
Amine, 0.8 weight portion water-base fluorocarbon emulsion, 1.3 weight portion n- N-Oleoylsarcosine 18-amine. salt, continue stirring, equal to being sufficiently mixed
Even, prepared inactivating treatment liquid;
3) metallic rotator axle is inserted and be passivated in inactivating treatment liquid processing, 45 DEG C for the treatment of temperature, process time 35 seconds,
Cleaned with pure water after taking-up and dry again.
Preferably, hydroelectric generation machine rotor, it includes metallic rotator axle, and this metallic rotator axle is through Passivation Treatment, described
Passivation Treatment comprises the steps:
1) by 1.2 weight portion normal-butyl sodium naphthalene sulfonates, 1.5 weight portion empgen BBs, 1.5 parts by weight of ethylene bases three
Methoxy silane, 0.8 weight portion Rhizoma Dioscoreae Cirrhosae slag extract, 4.2 weight portion hydroxy ethylene diphosphonic acids put into 33 weight portions successively and go
In ionized water, stir;
2) 1.6 weight portion sodium molybdate, 1.9 parts by weight of polypropylene acid esters, 1.1 weight portion n- phenyl -2- naphthalenes are put into again successively
Amine, 0.8 weight portion water-base fluorocarbon emulsion, 1.3 weight portion n- N-Oleoylsarcosine 18-amine. salt, continue stirring, equal to being sufficiently mixed
Even, prepared inactivating treatment liquid;
3) metallic rotator axle is inserted and be passivated in inactivating treatment liquid processing, 45 DEG C for the treatment of temperature, process time 35 seconds,
Cleaned with pure water after taking-up and dry again.
Advantages of the present invention and having the beneficial effects that: provide a kind of hydroelectric generation machine rotor, its metallic rotator axle is through blunt
Change is processed, and forms uniform passivation protection film in metal surface, has excellent antirust, corrosion-resistant, abrasion-resistant, antioxidation, resistance to
Hot, cold-resistant, weather resistance, and surface smoothness is good.
The performance of " inactivating treatment liquid " and purposes are determined by its component and proportioning, and in " inactivating treatment liquid " not
With group, branch influences each other, and component and its proportioning can determine the final performance of " inactivating treatment liquid ", such as fruit component and its proportioning not
Mutually coordinated, the beneficial effect that single component is brought, even can be eliminated by other components abatement, when serious, different groups
Split-phase is mutually conflicted, and does not have whole synthesis effect, produces negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly
Checking, obtain the optimal component of " inactivating treatment liquid " and proportioning so that multiple component combine, mutually coordinated and produce
Positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Hydroelectric generation machine rotor, it includes metallic rotator axle, this metallic rotator axle through Passivation Treatment, described Passivation Treatment
Comprise the steps:
1) by 1~2 weight portion normal-butyl sodium naphthalene sulfonate, 1.5 weight portion empgen BBs, 1.5 parts by weight of ethylene bases
Trimethoxy silane, 0.8 weight portion Rhizoma Dioscoreae Cirrhosae slag extract, 4.2 weight portion hydroxy ethylene diphosphonic acids put into 33 weight portions successively
In deionized water, stir;
2) 1.6 weight portion sodium molybdate, 1.9 parts by weight of polypropylene acid esters, 1.1 weight portion n- phenyl -2- naphthalenes are put into again successively
Amine, 0.8 weight portion water-base fluorocarbon emulsion, 1.3 weight portion n- N-Oleoylsarcosine 18-amine. salt, continue stirring, equal to being sufficiently mixed
Even, prepared inactivating treatment liquid;
3) metallic rotator axle is inserted and be passivated in inactivating treatment liquid processing, 45 DEG C for the treatment of temperature, process time 35 seconds,
Cleaned with pure water after taking-up and dry again.
Embodiment 2
Hydroelectric generation machine rotor, it includes metallic rotator axle, this metallic rotator axle through Passivation Treatment, described Passivation Treatment
Comprise the steps:
1) by 1 weight portion normal-butyl sodium naphthalene sulfonate, 1.5 weight portion empgen BBs, 1.5 parts by weight of ethylene base front threes
TMOS, 0.8 weight portion Rhizoma Dioscoreae Cirrhosae slag extract, 4.2 weight portion hydroxy ethylene diphosphonic acids put into successively 33 weight portions go from
In sub- water, stir;
2) 1.6 weight portion sodium molybdate, 1.9 parts by weight of polypropylene acid esters, 1.1 weight portion n- phenyl -2- naphthalenes are put into again successively
Amine, 0.8 weight portion water-base fluorocarbon emulsion, 1.3 weight portion n- N-Oleoylsarcosine 18-amine. salt, continue stirring, equal to being sufficiently mixed
Even, prepared inactivating treatment liquid;
3) metallic rotator axle is inserted and be passivated in inactivating treatment liquid processing, 45 DEG C for the treatment of temperature, process time 35 seconds,
Cleaned with pure water after taking-up and dry again.
Embodiment 3
Hydroelectric generation machine rotor, it includes metallic rotator axle, this metallic rotator axle through Passivation Treatment, described Passivation Treatment
Comprise the steps:
1) by 2 weight portion normal-butyl sodium naphthalene sulfonates, 1.5 weight portion empgen BBs, 1.5 parts by weight of ethylene base front threes
TMOS, 0.8 weight portion Rhizoma Dioscoreae Cirrhosae slag extract, 4.2 weight portion hydroxy ethylene diphosphonic acids put into successively 33 weight portions go from
In sub- water, stir;
2) 1.6 weight portion sodium molybdate, 1.9 parts by weight of polypropylene acid esters, 1.1 weight portion n- phenyl -2- naphthalenes are put into again successively
Amine, 0.8 weight portion water-base fluorocarbon emulsion, 1.3 weight portion n- N-Oleoylsarcosine 18-amine. salt, continue stirring, equal to being sufficiently mixed
Even, prepared inactivating treatment liquid;
3) metallic rotator axle is inserted and be passivated in inactivating treatment liquid processing, 45 DEG C for the treatment of temperature, process time 35 seconds,
Cleaned with pure water after taking-up and dry again.
Embodiment 4
Hydroelectric generation machine rotor, it includes metallic rotator axle, this metallic rotator axle through Passivation Treatment, described Passivation Treatment
Comprise the steps:
1) by 1.2 weight portion normal-butyl sodium naphthalene sulfonates, 1.5 weight portion empgen BBs, 1.5 parts by weight of ethylene bases three
Methoxy silane, 0.8 weight portion Rhizoma Dioscoreae Cirrhosae slag extract, 4.2 weight portion hydroxy ethylene diphosphonic acids put into 33 weight portions successively and go
In ionized water, stir;
2) 1.6 weight portion sodium molybdate, 1.9 parts by weight of polypropylene acid esters, 1.1 weight portion n- phenyl -2- naphthalenes are put into again successively
Amine, 0.8 weight portion water-base fluorocarbon emulsion, 1.3 weight portion n- N-Oleoylsarcosine 18-amine. salt, continue stirring, equal to being sufficiently mixed
Even, prepared inactivating treatment liquid;
3) metallic rotator axle is inserted and be passivated in inactivating treatment liquid processing, 45 DEG C for the treatment of temperature, process time 35 seconds,
Cleaned with pure water after taking-up and dry again.
Through in the various embodiments described above, the metallic rotator axle of hydroelectric generation machine rotor through Passivation Treatment, in metal surface shape
Uniformly passivation protection film, has excellent antirust, corrosion-resistant, abrasion-resistant, antioxidation, heat-resisting, cold-resistant, weather resistance, and
Surface smoothness is good.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1., it is characterised in that it includes metallic rotator axle, this metallic rotator axle is through Passivation Treatment, institute for hydroelectric generation machine rotor
State Passivation Treatment to comprise the steps:
1) by 1~2 weight portion normal-butyl sodium naphthalene sulfonate, 1.5 weight portion empgen BBs, 1.5 parts by weight of ethylene base front threes
TMOS, 0.8 weight portion Rhizoma Dioscoreae Cirrhosae slag extract, 4.2 weight portion hydroxy ethylene diphosphonic acids put into successively 33 weight portions go from
In sub- water, stir;
2) put into successively again 1.6 weight portion sodium molybdate, 1.9 parts by weight of polypropylene acid esters, 1.1 weight portion n- phenyl-2-naphthylamines,
0.8 weight portion water-base fluorocarbon emulsion, 1.3 weight portion n- N-Oleoylsarcosine 18-amine. salt, continue stirring, uniform to being sufficiently mixed,
Prepared inactivating treatment liquid;
3) metallic rotator axle is inserted and be passivated in inactivating treatment liquid processing, 45 DEG C for the treatment of temperature, process time 35 seconds, take out
Cleaned with pure water afterwards and dry again.
2. it is characterised in that it includes metallic rotator axle, this metal turns hydroelectric generation machine rotor according to claim 1
Through Passivation Treatment, described Passivation Treatment comprises the steps: sub- axle
1) by 1 weight portion normal-butyl sodium naphthalene sulfonate, 1.5 weight portion empgen BBs, 1.5 parts by weight of ethylene base trimethoxies
Silane, 0.8 weight portion Rhizoma Dioscoreae Cirrhosae slag extract, 4.2 weight portion hydroxy ethylene diphosphonic acids put into 33 parts by weight of deionized water successively
In, stir;
2) put into successively again 1.6 weight portion sodium molybdate, 1.9 parts by weight of polypropylene acid esters, 1.1 weight portion n- phenyl-2-naphthylamines,
0.8 weight portion water-base fluorocarbon emulsion, 1.3 weight portion n- N-Oleoylsarcosine 18-amine. salt, continue stirring, uniform to being sufficiently mixed,
Prepared inactivating treatment liquid;
3) metallic rotator axle is inserted and be passivated in inactivating treatment liquid processing, 45 DEG C for the treatment of temperature, process time 35 seconds, take out
Cleaned with pure water afterwards and dry again.
3. it is characterised in that it includes metallic rotator axle, this metal turns hydroelectric generation machine rotor according to claim 1
Through Passivation Treatment, described Passivation Treatment comprises the steps: sub- axle
1) by 2 weight portion normal-butyl sodium naphthalene sulfonates, 1.5 weight portion empgen BBs, 1.5 parts by weight of ethylene base trimethoxies
Silane, 0.8 weight portion Rhizoma Dioscoreae Cirrhosae slag extract, 4.2 weight portion hydroxy ethylene diphosphonic acids put into 33 parts by weight of deionized water successively
In, stir;
2) put into successively again 1.6 weight portion sodium molybdate, 1.9 parts by weight of polypropylene acid esters, 1.1 weight portion n- phenyl-2-naphthylamines,
0.8 weight portion water-base fluorocarbon emulsion, 1.3 weight portion n- N-Oleoylsarcosine 18-amine. salt, continue stirring, uniform to being sufficiently mixed,
Prepared inactivating treatment liquid;
3) metallic rotator axle is inserted and be passivated in inactivating treatment liquid processing, 45 DEG C for the treatment of temperature, process time 35 seconds, take out
Cleaned with pure water afterwards and dry again.
4. it is characterised in that it includes metallic rotator axle, this metal turns hydroelectric generation machine rotor according to claim 1
Through Passivation Treatment, described Passivation Treatment comprises the steps: sub- axle
1) by 1.2 weight portion normal-butyl sodium naphthalene sulfonates, 1.5 weight portion empgen BBs, 1.5 parts by weight of ethylene base trimethoxies
Base silane, 0.8 weight portion Rhizoma Dioscoreae Cirrhosae slag extract, 4.2 weight portion hydroxy ethylene diphosphonic acids put into 33 weight portion deionizations successively
In water, stir;
2) put into successively again 1.6 weight portion sodium molybdate, 1.9 parts by weight of polypropylene acid esters, 1.1 weight portion n- phenyl-2-naphthylamines,
0.8 weight portion water-base fluorocarbon emulsion, 1.3 weight portion n- N-Oleoylsarcosine 18-amine. salt, continue stirring, uniform to being sufficiently mixed,
Prepared inactivating treatment liquid;
3) metallic rotator axle is inserted and be passivated in inactivating treatment liquid processing, 45 DEG C for the treatment of temperature, process time 35 seconds, take out
Cleaned with pure water afterwards and dry again.