CN106345574A - Wet processing method of superfine mica iron oxide - Google Patents
Wet processing method of superfine mica iron oxide Download PDFInfo
- Publication number
- CN106345574A CN106345574A CN201610796889.8A CN201610796889A CN106345574A CN 106345574 A CN106345574 A CN 106345574A CN 201610796889 A CN201610796889 A CN 201610796889A CN 106345574 A CN106345574 A CN 106345574A
- Authority
- CN
- China
- Prior art keywords
- iron oxide
- processing method
- micaceous iron
- wet processing
- fine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a wet processing method of superfine mica iron oxide. The wet processing method includes the steps of firstly, adding mica iron oxide raw materials in a ball mill, adding an ethanol solution which is 95wt% ethanol to serve as the grinding medium, and adding, by the weight percentage of mica iron oxide, 1-2% of grinding auxiliaries, wherein the ethanol solution accounts for 12-15% of the weight of the mica iron oxide raw materials; secondly, performing ball milling by the ball mill in the first step, drying, and dispersing to obtain the superfine mica iron oxide, wherein the ratio of the grinding medium to the materials is (8:1)-(10:1), rotation speed is 300-500r/minute, and ball milling time is 60-120 minutes. The wet processing method has the advantages that the average fineness of the mica iron oxide can reach below 8 micrometers by optimizing operation parameters, the sheet structure of particles can be well kept, and a narrow particle size range is achieved.
Description
Technical field
The present invention relates to micaceous iron oxide processing technique field, more particularly, to a kind of ultra-fine micaceous iron oxide wet processing side
Method.
Background technology
Micaceous iron oxide, is a kind of special iron ore with iron sesquioxide as main chemical compositions in nature, its
Crystalline state is similar to Muscovitum, and structure is flakey, and grey black has metallic luster.Due to its distinctive sclay texture feature, lead to
Cross pulverizing, super-fine processing, oxidation Ferrum dust, the iron oxide red of sorting preparation are mainly used as the filler of anticorrosive paint.Current Muscovitum
Ferrum oxide pulverizes complex process, and crushing effect is bad, and particle size range is relatively wide, and can destroy micaceous iron oxide in crushing process
Laminated structure.
Content of the invention
For above-mentioned technical problem, it is an object of the invention to provide a kind of ultra-fine micaceous iron oxide wet processing method, by cloud
Female raw iron oxide material passes through ball mill grinding, by optimizing operating parameter, reduces the particle mean size of micaceous iron oxide, prepares slice
The micaceous iron oxide product that shape structural content is many, particle size range is narrow.
The technical solution used in the present invention is:
A kind of ultra-fine micaceous iron oxide wet processing method, comprises the following steps:
(1) micaceous iron oxide raw material is led to and be added in ball mill, add ethanol solution as abrasive media, described ethanol
Solution is 95wt% ethanol, and the ethanol solution of addition accounts for the 12~15% of micaceous iron oxide raw material weight, with micaceous iron oxide
Percentage by weight meter, adds 1~2% grinding aid;
(2) and then by ball mill described in step (1) carry out ball milling, ratio of grinding media to material is 8:1~10:1, setting speed is
300~500r/min, Ball-milling Time is 60~120min, dries, breaks up and can be prepared by ultra-fine micaceous iron oxide powder.
Ultra-fine micaceous iron oxide wet processing method of the present invention, wherein, the described grinding aid of step (1) is silane
Coupling agent kh560 or silane coupler kh550.
Ultra-fine micaceous iron oxide wet processing method of the present invention, wherein, the ethanol solution adding in step (1) accounts for
The 12% of micaceous iron oxide raw material weight.
Ultra-fine micaceous iron oxide wet processing method of the present invention, wherein, ratio of grinding media to material described in step (2) is 8:1.
Ultra-fine micaceous iron oxide wet processing method of the present invention, wherein, step (2) Ball-milling Time is 120min.
The invention has the advantages that:
Ultra-fine micaceous iron oxide wet processing method of the present invention, micaceous iron oxide raw material is ground by ball mill
Mill, by optimizing operating parameter, makes the average fineness of micaceous iron oxide all can reach less than 8 μm, and can preferably keep granule
Laminated structure, the micaceous iron oxide product laminated structure content prepared is many, particle mean size is thinner, particle size range is narrower.
Specific embodiment
The present invention is further illustrated with reference to embodiments, and in following examples, Muscovitum raw iron oxide material is Tongling
Minute surface ironworks Raymond mill product, iron oxide content is 84%.
Embodiment 1
A kind of ultra-fine micaceous iron oxide wet processing method, comprises the following steps:
(1) micaceous iron oxide raw material is led to and be added in ball mill, add ethanol solution as abrasive media, described ethanol
Solution is 95wt% ethanol, and the ethanol solution of addition accounts for the 12% of micaceous iron oxide raw material weight, with the weight of micaceous iron oxide
Percentages, add 2% grinding aid, and described grinding aid is silane coupler kh550;
(2) and then by ball mill described in step (1) carry out ball milling, ratio of grinding media to material is 8:1, setting speed is 300r/
Min, Ball-milling Time is 120min, then dries under the conditions of 30 DEG C in vacuum drying oven, breaks up and can be prepared by ultra-fine cloud
Female brown iron oxide.
Embodiment 2
A kind of ultra-fine micaceous iron oxide wet processing method, comprises the following steps:
(1) micaceous iron oxide raw material is led to and be added in ball mill, add ethanol solution as abrasive media, described ethanol
Solution is 95wt% ethanol, and the ethanol solution of addition accounts for the 15% of micaceous iron oxide raw material weight, with the weight of micaceous iron oxide
Percentages, add 1% grinding aid, and described grinding aid is silane coupler kh560;
(2) and then by ball mill described in step (1) carry out ball milling, ratio of grinding media to material is 10:1, setting speed is 500r/
Min, Ball-milling Time is 60min, then dries under the conditions of 40 DEG C in vacuum drying oven, breaks up and can be prepared by ultra-fine Muscovitum
Brown iron oxide.
Embodiment described above is only that the preferred embodiment of the present invention is described, the not model to the present invention
Enclose and be defined, on the premise of without departing from design spirit of the present invention, the technical side to the present invention for the those of ordinary skill in the art
Various modifications and improvement that case is made, all should fall in the protection domain of claims of the present invention determination.
Claims (5)
1. a kind of ultra-fine micaceous iron oxide wet processing method it is characterised in that: comprise the following steps:
(1) micaceous iron oxide raw material is led to and be added in ball mill, add ethanol solution as abrasive media, described ethanol solution
For 95wt% ethanol, the ethanol solution of addition accounts for the 12~15% of micaceous iron oxide raw material weight, with the weight of micaceous iron oxide
Percentages, add 1~2% grinding aid;
(2) and then by ball mill described in step (1) carry out ball milling, ratio of grinding media to material be 8:1~10:1, setting speed be 300~
500r/min, Ball-milling Time is 60~120min, dries, breaks up and can be prepared by ultra-fine micaceous iron oxide powder.
2. ultra-fine micaceous iron oxide wet processing method according to claim 1 it is characterised in that: step is ground described in (1)
Milling aid is silane coupler kh560 or silane coupler kh550.
3. ultra-fine micaceous iron oxide wet processing method according to claim 1 it is characterised in that: add in step (1)
Ethanol solution account for the 12% of micaceous iron oxide raw material weight.
4. ultra-fine micaceous iron oxide wet processing method according to claim 1 it is characterised in that: described in step (2)
Ratio of grinding media to material is 8:1.
5. the ultra-fine micaceous iron oxide wet processing method according to claim 1-4 any one it is characterised in that: step
(2) Ball-milling Time is 120min.