CN106336588A - Butyl rubber sealant plug used for aluminum electrolytic capacitor - Google Patents
Butyl rubber sealant plug used for aluminum electrolytic capacitor Download PDFInfo
- Publication number
- CN106336588A CN106336588A CN201610716354.5A CN201610716354A CN106336588A CN 106336588 A CN106336588 A CN 106336588A CN 201610716354 A CN201610716354 A CN 201610716354A CN 106336588 A CN106336588 A CN 106336588A
- Authority
- CN
- China
- Prior art keywords
- parts
- butyl rubber
- polysorbate
- carbon black
- polyvinyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a butyl rubber sealant plug used for an aluminum electrolytic capacitor. The butyl rubber sealant plug comprises the following raw materials in parts by weight: 70-85 parts of butyl rubber 301, 20-30 parts of polyvinyl alcohol, 15-28 parts of hydroxyl silicone oil, 10-15 parts of MBS resin, 5-8 parts of phthalic dimethyl anhydride, 12-18 parts of sodium polymethacrylate, 5-10 parts of vinyltriethoxysilane, 14-20 parts of ethyl p-hydroxybenzoate, 11-14 parts of tetra-(methylethylketoxime)silane, 13-16 parts of butanol, 3-9 parts of boron nitride, 11-13 parts of powdered steatile, 14-22 parts of polysorbate, and 15-20 parts of carbon black. The butyl rubber sealant plug has good airtight performance, increases the chemical resistance, solvent resistance and aging resistance performances of the product, and can prolong the usage life of the capacitor on the electric appliance products.
Description
Technical field
The invention belongs to caulking gum field is and in particular to a kind of aluminium electrolutic capacitor butyl rubber seal rubber plug.
Background technology
Capacitor is maximum using the widest, consumption, and the electronic component do not replaced, and its yield accounts for all electronic component
40%, and wherein with aluminium electrolutic capacitor for topmost capacitor classification.Aluminium electrolutic capacitor is to do negative pole by aluminum cylinder,
The inside is referred to as aluminium electrolutic capacitor equipped with liquid electrolyte, the capacitor that the aluminium strip of a piece of bending of insertion does positive pole and makes.It
Fuse be by anode aluminium foil, be soaked with electrolyte interleaving paper, cathode aluminum foil, the overlapping winding such as Natural Oxide Film, core
Enclosed with aluminum hull and Jiao Gai after son impregnation electrolyte and just constitute an electrolysis condenser.Generally, alminium electrolytic condenser
There is a plastic bushing outside the aluminum hull of device.Sleeve pipe color is colourful, and it is not only attractive in appearance, and has specific meaning.Aluminum
Electrolysis condenser is the high universal electrolysis condenser of a kind of good electrical property made of aluminum, scope of application width, reliability.
Aluminium electrolutic capacitor is widely used in the household electrical appliance such as air conditioner, radio cassette player, washing machine, communication equipment and complete electronic set, instrument, instrument
Supporting.Aluminium electrolutic capacitor its feature is that capacity is big, but electric leakage is big, and error is big, and stability is poor, is commonly used for alternating current bypass
And filtering, it is also used for signal coupling when less demanding.Electrochemical capacitor has dividing of positive and negative electrode, can not be reversed during use.Aluminium electroloysis
Capacitor when mounted, is typically necessary and core bag is placed in aluminum hull, then core is wrapped placement rubber stopper and is closed, rubber
Plug is typically all by manually rubber stopper being enclosed within pin when mounted.Aluminium electrolutic capacitor in long-term work runs,
Electrolyte can gradually decrease to external diffusion, volatilization, capacitance through encapsulant, finally results in inefficacy;The volatilization of electrolyte is not
Only relevant with the height of the sub- temperature of inner core of capacitor, the seal rubber plug of capacitor will directly affect the speed to external diffusion for the electrolyte
Degree.In aluminium electrolutic capacitor production process, need to use this material of plug and aluminium electrolutic capacitor is sealed, stop
Electrolyte passes through plug and volatilizees in high temperature.And plug is obtained with butyl rubber and there is excellent air-tightness, but its resistance to ag(e)ing,
Chemical species stability is not good, therefore limits its utilization scope.Work out a kind of alminium electrolytic condenser with more dominance energy
Device butyl rubber seal rubber plug becomes the task of top priority.
Content of the invention
It is an object of the invention to provide a kind of aluminium electrolutic capacitor butyl rubber seal rubber plug.
To achieve these goals, the invention provides a kind of aluminium electrolutic capacitor butyl rubber seal rubber plug, by following
The raw material of weight portion is obtained: butyl rubber 301 70-85 part, polyvinyl alcohol 20-30 part, hydroxy silicon oil 15-28 part, mbs resin 10-
15 parts, phthalic acid diformazan acid anhydride 5-8 part, sodium polymethacrylate 12-18 part, VTES 5-10 part, right
Nipagin A 14-20 part, four butanone oximino silane 11-14 parts, butanol 13-16 part, boron nitride 3-9 part, Pulvis Talci 11-
13 parts, polysorbate 14-22 part, white carbon black 15-20 part.
A kind of above-mentioned aluminium electrolutic capacitor butyl rubber seal rubber plug, is made up of the raw material of following weight portion: butyl rubber
301 70 parts, 20 parts of polyvinyl alcohol, 15 parts of hydroxy silicon oil, 10 parts of mbs resin, 5 parts of phthalic acid diformazan acid anhydride, polymethyl
12 parts of sour sodium, 5 parts of VTES, 14 parts of ethylparaben, 11 parts of four butanone oximino silane, butanol 13
Part, 3 parts of boron nitride, 11 parts of Pulvis Talci, 14 parts of polysorbate, 15 parts of white carbon black.
A kind of above-mentioned aluminium electrolutic capacitor butyl rubber seal rubber plug, is made up of the raw material of following weight portion: butyl rubber
301 75 parts, 25 parts of polyvinyl alcohol, 22 parts of hydroxy silicon oil, 13 parts of mbs resin, 7 parts of phthalic acid diformazan acid anhydride, polymethyl
15 parts of sour sodium, 7 parts of VTES, 17 parts of ethylparaben, 12 parts of four butanone oximino silane, butanol 15
Part, 6 parts of boron nitride, 12 parts of Pulvis Talci, 18 parts of polysorbate, 17 parts of white carbon black.
A kind of above-mentioned aluminium electrolutic capacitor butyl rubber seal rubber plug, is made up of the raw material of following weight portion: butyl rubber
301 85 parts, 30 parts of polyvinyl alcohol, 28 parts of hydroxy silicon oil, 15 parts of mbs resin, 8 parts of phthalic acid diformazan acid anhydride, polymethyl
18 parts of sour sodium, 10 parts of VTES, 20 parts of ethylparaben, 14 parts of four butanone oximino silane, butanol
16 parts, 9 parts of boron nitride, 13 parts of Pulvis Talci, 22 parts of polysorbate, 20 parts of white carbon black.
Beneficial effect: the butyl rubber seal rubber plug of the present invention has good air-tightness, improves resistance toization of product simultaneously
The property learned, solvent resistance and ageing-resistant performance, thus extend service life in electric equipment products for the capacitor.
Specific embodiment
Embodiment 1
A kind of aluminium electrolutic capacitor butyl rubber seal rubber plug that the present embodiment provides, is obtained by the raw material of following weight portion: fourth
301 70 parts of base rubber, 20 parts of polyvinyl alcohol, 15 parts of hydroxy silicon oil, 10 parts of mbs resin, 5 parts of phthalic acid diformazan acid anhydride, poly- methyl
12 parts of sodium acrylate, 5 parts of VTES, 14 parts of ethylparaben, 11 parts of four butanone oximino silane, fourth
13 parts of alcohol, 3 parts of boron nitride, 11 parts of Pulvis Talci, 14 parts of polysorbate, 15 parts of white carbon black.
Embodiment 2
A kind of aluminium electrolutic capacitor butyl rubber seal rubber plug that the present embodiment provides, is obtained by the raw material of following weight portion: fourth
301 75 parts of base rubber, 25 parts of polyvinyl alcohol, 22 parts of hydroxy silicon oil, 13 parts of mbs resin, 7 parts of phthalic acid diformazan acid anhydride, poly- methyl
15 parts of sodium acrylate, 7 parts of VTES, 17 parts of ethylparaben, 12 parts of four butanone oximino silane, fourth
15 parts of alcohol, 6 parts of boron nitride, 12 parts of Pulvis Talci, 18 parts of polysorbate, 17 parts of white carbon black.
Embodiment 3
A kind of aluminium electrolutic capacitor butyl rubber seal rubber plug that the present embodiment provides, is obtained by the raw material of following weight portion: fourth
301 85 parts of base rubber, 30 parts of polyvinyl alcohol, 28 parts of hydroxy silicon oil, 15 parts of mbs resin, 8 parts of phthalic acid diformazan acid anhydride, poly- methyl
18 parts of sodium acrylate, 10 parts of VTES, 20 parts of ethylparaben, 14 parts of four butanone oximino silane,
16 parts of butanol, 9 parts of boron nitride, 13 parts of Pulvis Talci, 22 parts of polysorbate, 20 parts of white carbon black.
Embodiment 4
The production technology that above-described embodiment 1-3 uses is conventional production process, is followed successively by:
A. dispensing, is adjusted weighing and burden by the range of formula proportion;
B. knead, the material preparing is put in sealed rubber mixing machine and is kneaded;
C. thin logical, the material after mixing is proceeded to opening rubber mixing machine, for thin logical uniform inner material, and park cooling 24~
72 hours;
D. rolling out film, carries out rolling out film using open refining glue roller calender, and this open refining glue roller calender is also
Incidentally conveying conveyer belt and positioning cutting knife;
E. one-shot forming vulcanization crosslinking, carries out compression molding using vacuum type vulcanizing press, is carried out once by production mould
Vulcanization crosslinking molding, its molding temperature is controlled to 175~195 DEG C, and vacuum is not less than 700mmhg, vacuum type vulcanizing press
Stress control be 100~150 kilograms per square centimetres, the production time be 180~360 seconds;
F. thick burr removing, by manually using the little blunt shovelling blade of steel by unnecessary burr on shaped article, scurf and protrusion
Burr tail remove;
G. rinse and cut out, by manual or automaticization water under high pressure, the fine-powder of shaped article in the hole is rinsed well, Ran Houtong
Cross roller cutting device to be cut out;
H. faulty materials in shaped article are removed by artificial visual, then shaped article are moved on press machine by thin burr removing
Carry out punching press, unnecessary burr in shaped article are carried out separating;
I. packaging and storing, is carried out to product by using water purification machine, and is dehydrated by dewaterer, recycles nature electricity
Wind carries out packaging and storing using pe plastic bag after carrying out air-drying.
Claims (4)
1. a kind of aluminium electrolutic capacitor with butyl rubber seal rubber plug it is characterised in that being made up of the raw material of following weight portion: butyl
Glue 301 70-85 part, polyvinyl alcohol 20-30 part, hydroxy silicon oil 15-28 part, mbs resin 10-15 part, phthalic acid diformazan acid anhydride
5-8 part, sodium polymethacrylate 12-18 part, VTES 5-10 part, ethylparaben 14-20 part,
Four butanone oximino silane 11-14 parts, butanol 13-16 part, boron nitride 3-9 part, Pulvis Talci 11-13 part, polysorbate 14-22
Part, white carbon black 15-20 part.
2. a kind of aluminium electrolutic capacitor according to claim 1 with butyl rubber seal rubber plug it is characterised in that by following
The raw material of weight portion is made: 301 70 parts of butyl rubber, 20 parts of polyvinyl alcohol, 15 parts of hydroxy silicon oil, 10 parts of mbs resin, adjacent benzene two
5 parts of formic acid diformazan acid anhydride, 12 parts of sodium polymethacrylate, 5 parts of VTES, 14 parts of ethylparaben,
Four 11 parts of butanone oximino silanes, 13 parts of butanol, 3 parts of boron nitride, 11 parts of Pulvis Talci, 14 parts of polysorbate, 15 parts of white carbon black.
3. a kind of aluminium electrolutic capacitor according to claim 1 with butyl rubber seal rubber plug it is characterised in that by following
The raw material of weight portion is made: 301 75 parts of butyl rubber, 25 parts of polyvinyl alcohol, 22 parts of hydroxy silicon oil, 13 parts of mbs resin, adjacent benzene two
7 parts of formic acid diformazan acid anhydride, 15 parts of sodium polymethacrylate, 7 parts of VTES, 17 parts of ethylparaben,
Four 12 parts of butanone oximino silanes, 15 parts of butanol, 6 parts of boron nitride, 12 parts of Pulvis Talci, 18 parts of polysorbate, 17 parts of white carbon black.
4. a kind of aluminium electrolutic capacitor according to claim 1 with butyl rubber seal rubber plug it is characterised in that by following
The raw material of weight portion is made: 301 85 parts of butyl rubber, 30 parts of polyvinyl alcohol, 28 parts of hydroxy silicon oil, 15 parts of mbs resin, adjacent benzene two
8 parts of formic acid diformazan acid anhydride, 18 parts of sodium polymethacrylate, 10 parts of VTES, 20 parts of ethylparaben,
Four 14 parts of butanone oximino silanes, 16 parts of butanol, 9 parts of boron nitride, 13 parts of Pulvis Talci, 22 parts of polysorbate, 20 parts of white carbon black.