CN106318039A

CN106318039A - Air-purifying ceramic ink with dermatoglyphs effect and preparation method thereof

Info

Publication number: CN106318039A
Application number: CN201610748802.XA
Authority: CN
Inventors: 于庆九; 邱杰华
Original assignee: FOSHAN CITY GAOMING DISTRICT HAIDI CERAMIC MATERIALS Co Ltd
Current assignee: FOSHAN CITY GAOMING DISTRICT HAIDI CERAMIC MATERIALS Co Ltd
Priority date: 2016-08-29
Filing date: 2016-08-29
Publication date: 2017-01-11

Abstract

The invention discloses an air-purifying ceramic ink with dermatoglyphs effect and preparation method thereof. The preparation method includes the following steps: step A. preparing dermatoglyph glaze ; step B. weighing by proportion dermatoglyph glaze, dispersant, surface additive, defoamer, bonding agent, the rest is solvent, grinding to obtain the ink semi-product; step C. filtering to obtain the ink finished product. Compared with current ceramic ink with dermatoglyphs effect, the present invention has scientific ingredients, reasonable preparation, and good stable quality. Used in connection with the color ink of ceramic ink-jet printing, the vivid concave-convex lines are more fully visualized and revealed for dermatoglyph ceramics. The 3-D effect is strong, further enhancing the decorative effect of ceramics. The present invention can also be widely applied in such fields as tiles and archaized brick, meanwhile through reasonably combining negative ion compound with deodorant and antibacterial compound material, the ceramic ink has superior antibacterial, antifouling, air-purifying function, further broadening the application scope of sinkable ceramic ink.

Description

A kind of purification air ceramic ink with leather pattern effect and preparation method thereof

Technical field

The present invention relates to ceramic technology field, particularly relate to a kind of purification air ceramic ink with leather pattern effect Water and preparation method thereof.

Background technology

Antibacterial, mycete has the biggest harm as pathogen to the mankind and animals and plants, and the health affecting people even jeopardizes life Life, brings great economic loss.Therefore the research of anti-biotic material and goods thereof causes the concern of people, antibacterial product day by day Demand will constitute huge market.

For environmental conservation aspect, negative aeroion can eliminate foreign flavor indoors and various harmful gas.In interior decoration During leftovers leftovers in the art work that the uses benzene, formaldehyde, ketone, the irritative gas such as ammonia and the daily life that evaporate Acid smell, the harmful abnormal flavour such as medicated cigarette, with the material rich in anion, negative aeroion of its release can be effectively Eliminated, reach to purify the purpose of air, and golden staphylococci, escherichia coli, candidiasis and mycete etc. are had well press down Make and use.

Ceramic ink jet technology is as a kind of new contactless, no pressure, printing technology without forme, undoubtedly by current ceramic tile Fashion, personalization, development trend art up, small lot, multi-color, low-carbon environment-friendly have pushed a new height to.From Since within 2009, China introduces First ceramic ink jet machine, the development of ceramic ink jet printing technology is advanced by leaps and bounds, and obtains a large amount of Application.Through development in a few years, the market share of ceramic ink jet product is more and more higher, also the advantage of ceramic ink jet technology is sent out Wave incisively and vividly.

Hard and the ice-cold impression of traditional ceramic tile broken by leather pattern effect brick, and nano level dermatoglyph glaze can more abundant shape Elephant show the texture that dermatoglyph brick is concavo-convex, skin texture true to nature, soft texture, make ceramic tile the most ice-cold, allow people from vision and The texture of skin can be experienced in sense of touch.With ceramic ink jet printing paint ink with the use of, be possible not only to carry further The decorative effect of high ceramic tile, also adapts to digital development trend.But rarely have at present and report the leather pattern effect about functional type Ceramic ink, therefore technology has much room for improvement, and needs research and development functional type leather pattern effect ceramic ink badly, such as antibacterial, antistatic, deodorization The functions such as agent, photochromic, anion, widen its range of application further.

Summary of the invention

In order to solve above-mentioned the deficiencies in the prior art, the invention provides a kind of purification air pottery with leather pattern effect Ink and preparation method thereof.

The technical problem to be solved is achieved by the following technical programs:

A kind of preparation method purifying air ceramic ink with leather pattern effect, it comprises the following steps:

Step A, prepare dermatoglyph glaze: by 35 ~ 40%SiO2,8 ~ 10%Al2O3,1 ~ 4%(K2O+Na2O), 8 ~ 12%(CaO+MgO), 7 ~ 9%B2O3,10 ~ 15%ZrO2,12 ~ 15%V2O5 mixing sand milling are uniform；Add 0.5 ~ 5% antibiotic complex and sand milling is uniform；Add again Entering 2 ~ 8% anion complex, sand milling uniformly prepares compound；Compound is dispensed in loading fire resistant sagger, carry out 1400 ~ 1450 DEG C of high temperature meltings, obtain the slurry of molten state；By slurry water quenching cooling, and it is broken into graininess, obtains dermatoglyph glaze；

Step B, weigh 20 ~ 35% dermatoglyph glaze, 3 ~ 8% dispersants, 2 ~ 5% surface additives, 0.3 ~ 0.8% defoamer, 1 ~ 3% combine Agent, 1 ~ 5% deodorizer, surplus is solvent, carries out disperseing 30 ~ 60min in adding homogenizer；By scattered mixed liquor dress Enter in sand mill, sand milling 8 ~ 12h, obtain the ink semi-finished product that particle diameter is distributed between 200 ~ 500nm；

Step C, ink semi-finished product step B obtained, in the constant temperature a mixing bowl of 80～100 DEG C, then carry out evacuation, height Speed vibration, filtration, obtain ink.

A kind of purification air ceramic ink with leather pattern effect, it contains the component of following percentage by weight: 20 ~ 35% Dermatoglyph glaze, 3 ~ 8% dispersants, 2 ~ 5% surface additives, 0.3 ~ 0.8% defoamer, 1 ~ 3% bonding agent, 1 ~ 5% deodorizer, surplus is Solvent；Wherein, described dermatoglyph glaze contains the component of following percentage by weight: 35 ~ 40%SiO2,8 ~ 10%Al2O3,1 ~ 4%(K2O+ Na2O), 8 ~ 12%(CaO+MgO), 7 ~ 9%B2O3,10 ~ 15%ZrO2,12 ~ 15%V2O5,0.5 ~ 5% antibiotic complex and 2 ~ 8% negative Ion complex.

In the present invention, the preparation method of described deodorizer is as follows: mix the raw material of following percentage by weight: 5%ZrO₂, 10%TiO₂, 16%SiO₂, 4%V₂O₅, 3%K₂O, 2%SnO₂, 2%Cr₂O₃, 13%Al₂O₃, 12%Fe₂O₃, 18%MgO, 8%Na2O, 7% MnO₂, put into and the big flow circulation horizontal sand mill of PUHLER company exploitation carry out sand milling, control particle diameter at 10 ~ 500nm Between, prepare inorganic oxide；By the most mixed to 30 ~ 40% epoxy resin, 30 ~ 50% phenolic resin and 20 ~ 30% inorganic oxides Close, add appropriate butyl acetate and put into dispersion dispergation in ball mill, after discharge, detect, adjust the slurry being configured to apply Material；By this slurry coating on substrate, drying and forming-film；Then it is placed in nitrogen filled protection atmosphere furnace, is warmed up to 900 ~ 1000 DEG C, protect Temperature 1 ~ 2h；Film is scraped off this substrate, obtains deodorizer.

In the present invention, described anion complex preparation method is as follows: by 5 ~ 10% coral fossil, 10 ~ 15% tourmaline, 20 ~ 35% opals, 1 ~ 5% serpentine, 5 ~ 10% Maifanitums, 1 ~ 5% rare ice stone, 1 ~ 5% hokutolite, 1 ~ 5% doctor Wang Shi, 5 ~ 10% shellfishes Shell, 10 ~ 15% kieselguhr, 1 ~ 3% iron sesquioxide, 2 ~ 5% aluminium sesquioxide, 3 ~ 8% zirconium oxides and 1 ~ 5% zirconium phosphate mix homogeneously, Add in grinding equipment and carry out superfine grinding, until particle diameter distribution is at 50 ~ 80nm, sieve, be dried, can be prepared by described negative Ion powder.Taking 5 ~ 10g anion powder to be scattered in 100 ~ 200ml ultra-pure water, water bath sonicator 1 ~ 2h obtains the most even stable dividing Dissipate liquid；When the substrate with carbon nanotube mesh film is placed in about 8 DEG C, dispersion liquid is added in the substrate of concave shape, meanwhile, Roll around roller, make this homogeneous dispersion be scattered in this carbon nanotube mesh film, owing to having when CNT is near 8 DEG C Having hydrophilic, this dispersion liquid is attracted to multiple net holes of carbon nanotube mesh film；Being warming up to about 25 DEG C, CNT has thin Aqueous being driven away by hydrone leaves behind anion powder and adsorbs in multiple net holes of carbon nanotube mesh film；After drying, will inhale This substrate is scraped off, it is thus achieved that anion powder/CNT with the carbon nanotube mesh film of anion powder.

In the present invention, described dispersant is water solublity and oil-soluble high score subclass, polyacrylic acid and copolymer, benzoic acid And any one of derivant.The trade name that dispersant can list include BYK161, BYK163, BYK164, BYK168, EFKA4310, EFKA 4400, EFKA4401, Nuosperse FX9086, Solsperse 24000, Tego710, Tego671, But it is not limited to this.

In the present invention, described surface additive is amino or amido and salt thereof.Surface additive is NP-4, Span-80, At least one in AEO-3 and SRE-48000.

In the present invention, described solvent is in de-aromatic hydrocarbon solvent, environmental protection hydrocarbon solvent, alcohols, cycloalkane solvent At least one.Described bonding agent generally uses polymerizing resin, such as polyethylene, polypropylene, polrvinyl chloride and polystyrene tree One in fat, polymerizing resin plays combination and scattered dual function.Described defoamer is the polymer without organosilicon Type defoamer, the trade name that defoamer can list includes BYK051, BYK052, but is not limited to this.

In the present invention, described antibiotic complex can prepare by the following method:

(1) weigh 0.3 ~ 1gC60 powder, measure the concentrated sulphuric acid that 80 ~ 100ml mass fraction is 98%, by C60 powder and concentrated sulphuric acid Mixing in beaker, beaker is placed in ice-water bath, stirs with the speed of 500 ~ 600rpm simultaneously, obtains mixed liquor；Weigh 1 ~ 3g high Potassium manganate powder, adds in above-mentioned mixed liquor slowly；Remove ice-water bath, change water-bath into, keep bath temperature 30 ~ 40 DEG C, instead Answer 3 ~ 5h；Rapidly join 100 ~ 150ml pure water, filter, then dialyse 3 ~ 5 days with the bag filter that molecular cut off is 1000, Graphene quantum dot (GQDs) suspension；100 ~ 150rpm speed stirring GQDs suspension, simultaneously laser irradiation 30 ~ 60min, swash Photoirradiation power is 0.5 ~ 2W；Standby；

(2) ultrasonic agitation 50 ~ 60mlGQDs suspension, dropping concentration is 0.001 ~ 0.01mol/L silver nitrate aqueous solution；Dropwise add Enter concentration be 0.1 ~ 0.5mol/L ammonium dihydrogen phosphate (ammonium dihydrogen phosphate and silver nitrate aqueous solution volume ratio are 2 ~ 3: 1), ultrasonic agitation 10 ~ 20min；Be added dropwise over 0.5 ~ 1mol/L sodium hydroxide solution, regulation pH value to 11, then stand, from The heart, with deionized water and ethanol alternately washing three times, vacuum drying, obtains GQDs/Ag₂O；

(3) 1 ~ 3gGQDs/Ag is taken₂O ultrasonic agitation is scattered in 80 ~ 120ml aqueous solution；Be added dropwise over concentration be 0.005 ~ 0.05mol/L cerous nitrate aqueous solution, being added dropwise over concentration after 30 ~ 60min is 0.005 ~ 0.05mol/L zinc nitrate aqueous solution, GQDs/Ag₂O aqueous solution, cerous nitrate aqueous solution and zinc nitrate aqueous solution volume ratio are 1:0.1 ~ 0.2:0.2 ~ 0.4；Continue ultrasonic Stirring, regulation mixed solution pH value is to 7.0；Limit ultrasonic agitation, it is the hydrazine hydrate of 50% that limit adds 4 ~ 8mL mass fraction, 30 ~ Reduction reaction 0.5 ~ 1h at 40 DEG C；Afterwards, the hydrazine hydrate that 40 ~ 50mL mass fraction is 50%, reduction reaction at 85 DEG C are added After 30 ~ 48h；Filter, be washed with deionized for several times, vacuum drying, obtain GQDs/Ag₂O/Ag-Zn-Ce；

(4) by 0.1 ~ 0.5gGQDs/Ag₂O/Ag-Zn-Ce ultrasonic agitation is scattered in aqueous solution；Add volume ratio 3 ~ 5:1 afterwards Water and ammonia, be stirring evenly and then adding into tetraethyl orthosilicate (with GQDs/Ag₂The mass ratio of O/Ag-Zn-Ce is 3:1 ~ 3), regulation PH value is 9 ~ 10, and reaction temperature is 20 ~ 25 DEG C, reacts 30 ~ 60min；It is centrifuged and cleans with acetone and deionized water successively Obtain precipitation；This is deposited at 80 ~ 90 DEG C and is dried 2 ~ 4h, to obtain GQDs/Ag₂O/Ag-Zn-Ce/SiO₂；By GQDs/ Ag₂O/Ag-Zn-Ce/SiO₂It is placed under argon gas atmosphere and carries out 500 ~ 800 DEG C of heat treatment 1 ~ 2h, after being cooled to room temperature, be immersed in hydrogen Fluoric acid carries out ultrasonic 10 ~ 15min with ultrasonic power 100 ~ 150W, removes local, surface silicon dioxide, be centrifuged and be dried, it is thus achieved that Antibacterial powder；

(5), under nitrogen environment, it is the ten of 0.05 ~ 0.5mol/L by protonic acid solution and the concentration that concentration is 0.05 ~ 0.5mol/L Dialkyl benzene sulfonic acids mixes with volume ratio 2 ~ 4:2, is simultaneously introduced the antibacterial powder that step (4) prepares, after magnetic agitation 60 ~ 120min Adding aniline, antibacterial powder and aniline mass ratio are 2:12 ~ 18；After continuously stirred 60 ~ 90min, dropwise drip Ammonium persulfate., aniline It is 1:1 with Ammonium persulfate. mol ratio；15 ~ 30h is reacted at 20 DEG C～30 DEG C；Acetone, deionized water wash final vacuum for several times is dried, Mill to obtain nano polyaniline/antibacterial powder complex；

(6) prepare TiO 2 sol by sol-gel process, in colloidal sol, add the nanometer polyphenyl accounting for colloidal sol 0.01 ~ 1.0wt% Amine/antibacterial powder complex, mix homogeneously；Still aging 3～5d 60 DEG C～120 DEG C of rearmounted baking oven drying；After milling by gained again Calcine 1 ~ 2h at compound 400～550 DEG C, remove polyaniline, obtain poriferous titanium dioxide/antibacterial powder complex；

(7) by the most mixed to 30 ~ 45% epoxy resin, 35 ~ 50% phenolic resin and 8 ~ 20% poriferous titanium dioxides/antibacterial powder complex Close, add appropriate butyl acetate and put into dispersion dispergation in ball mill, after discharge, detect, adjust the slurry being configured to apply Material；By this slurry coating on substrate, drying and forming-film；Then it is placed in nitrogen filled protection atmosphere furnace, is warmed up to 900 ~ 1000 DEG C, protect Temperature 1 ~ 2h；Film is scraped off this substrate, it is thus achieved that antibiotic complex.

It is preferred that increase by a step between step (4) and (5): take three-dimensional sponge shape Graphene ultrasonic agitation and be scattered in In aqueous solution, it is added dropwise over GQDs/Ag₂O/Ag-Zn-Ce/SiO₂In aqueous solution, three-dimensional sponge shape Graphene and GQDs/Ag₂O/ Ag-Zn-Ce/SiO₂Weight ratio be 1:1 ~ 5；Ultrasonic 60 ~ the 120min of 10 ~ 100W, stands, and deionized water wash for several times, is dried Obtain GQDs/Ag₂O/Ag-Zn-Ce/SiO₂/ Graphene antibiosis powder.

In the present invention, described antibiotic complex can also prepare by the following method:

(3) 1 ~ 3gGQDs/Ag is taken₂O ultrasonic agitation is scattered in aqueous solution；Being added dropwise over concentration is 0.05 ~ 0.5g/100mlZnO Quantum dot aqueous solution, ultrasonic power mixing speed respectively halves；After 60 ~ 90min, stand, filter, be washed with deionized for several times, Vacuum drying, obtains GQDs/Ag₂O/ZnO antibacterial powder；

(4), under nitrogen environment, it is the ten of 0.05 ~ 0.5mol/L by protonic acid solution and the concentration that concentration is 0.05 ~ 0.5mol/L Dialkyl benzene sulfonic acids mixes with volume ratio 2 ~ 4:2, is simultaneously introduced the antibacterial powder that step (4) prepares, after magnetic agitation 60 ~ 120min Adding aniline, antibacterial powder and aniline mass ratio are 2:12 ~ 18；After continuously stirred 60 ~ 90min, dropwise drip Ammonium persulfate., aniline It is 1:1 with Ammonium persulfate. mol ratio；15 ~ 30h is reacted at 20 DEG C～30 DEG C；Acetone, deionized water wash final vacuum for several times is dried, Mill to obtain nano polyaniline/antibacterial powder complex；

(5) prepare TiO 2 sol by sol-gel process, in colloidal sol, add the nanometer polyphenyl accounting for colloidal sol 0.01 ~ 1.0wt% Amine/antibacterial powder complex, mix homogeneously；Still aging 3～5d 60 DEG C～120 DEG C of rearmounted baking oven drying；After milling by gained again Calcine 1 ~ 2h at compound 400～550 DEG C, remove polyaniline, obtain poriferous titanium dioxide/antibacterial powder complex；

(6) by the most mixed to 30 ~ 45% epoxy resin, 35 ~ 50% phenolic resin and 8 ~ 20% poriferous titanium dioxides/antibacterial powder complex Close, add appropriate butyl acetate and put into dispersion dispergation in ball mill, after discharge, detect, adjust the slurry being configured to apply Material；By this slurry coating on substrate, drying and forming-film；Then it is placed in nitrogen filled protection atmosphere furnace, is warmed up to 900 ~ 1000 DEG C, protect Temperature 1 ~ 2h；Film is scraped off this substrate, it is thus achieved that antibiotic complex.

It is preferred that increase by a step between step (3) and (4): take three-dimensional sponge shape Graphene ultrasonic agitation and be scattered in In aqueous solution, it is added dropwise over GQDs/Ag₂In O/ZnO aqueous solution, three-dimensional sponge shape Graphene and GQDs/Ag₂The weight ratio of O/ZnO For 1:1 ~ 5；Ultrasonic 60 ~ the 120min of 10 ~ 100W, stands, and deionized water wash for several times, is dried to obtain GQDs/Ag₂O/ZnO/ Graphene Antibacterial powder.

There is advantages that this method loads in carbon nano net and fixes antibacterial, not only prevent it Reunite, significantly improve the stability of the antibacterial such as metal nanoparticle so that it is can more preferably be dispersed in ceramic ink jet ink, and tool There are more efficient antibacterial activity and silver ion will not overflow oxidation stain；It is compounded with the anti-microbial property of multiple antibacterial simultaneously, Have a more preferable antibacterial effect compared to single silver nano antibacterial agent, antibacterial persistently；Inorganic oxide main component have magnesium, The trace element that aluminum, ferrum etc. more than 10 kind is favourable to human body, owing to it is the special polarity crystalline solid of a kind of structure, self can grow Phase produces electron ion, and forever discharges negative aeroion, reaches deodorization and purifies the effect of air；Anion complex can the most not The anion releasing being interrupted, under having light or no light condition, the uninterrupted anion releasing of equal energy, effectively purifies air, decomposing formaldehyde Deng organic gas, improve IAQ (indoor air quality), also there is antibacterial effect, be of value to health.

Comparing with existing leather pattern effect ceramic ink, dispensing science of the present invention, rationally, quality stability is good, can grow in preparation Time preserves, and has good Ink Jet Printing Performance, with ceramic ink jet printing paint ink with the use of, can more abundant shape Elephant show the concavo-convex texture true to nature of dermatoglyph ceramic tile, third dimension is strong, improves the decorative effect of ceramic tile further, also can be at ceramics Extensively apply with fields such as Antique Imitation Tiles；Simultaneously through reasonably collocation anion complex, deodorizer and antimicrobial composite material, make Ceramic ink has that excellent antibacterial is antifouling, air purification function, widened the range of application of the ceramic ink that can sink further.

Detailed description of the invention

Technical scheme is further illustrated below by concrete preferred implementation.

Embodiment 1

A kind of purification air ceramic ink with leather pattern effect and preparation method thereof, this preparation method comprises the following steps:

Step A, prepare dermatoglyph glaze: by 40%SiO2,8%Al2O3,1%(K2O+Na2O), 10%(CaO+MgO), 9%B2O3,10% ZrO2,13%V2O5 mixing sand milling is uniform；Add 1% antibiotic complex and sand milling is uniform；Add 8% anion complex, sand milling Uniformly prepare compound；Compound is dispensed in loading fire resistant sagger, carry out 1400 DEG C of high temperature meltings, obtain the slurry of molten state Material；By slurry water quenching cooling, and it is broken into graininess, obtains dermatoglyph glaze；

Step B, weigh 20% dermatoglyph glaze, 8% Solsperse 24000,5% Span-80,0.3% BYK052,3% polystyrene Resin, 1% deodorizer and 62.7% environmental protection hydrocarbon solvent, carry out in adding homogenizer disperseing 60min；By scattered mixing Liquid loads in sand mill, and sand milling 10h obtains the ink semi-finished product that particle diameter is distributed between 200 ~ 500nm；

Step C, ink semi-finished product step B obtained, in the constant temperature a mixing bowl of 90 DEG C, then carry out evacuation, shake at a high speed Dynamic, filtration, obtains ink.

Wherein, described anion complex preparation method is as follows: by 10% coral fossil, 10% tourmaline, 35% opal, 1% serpentine, 10% Maifanitum, 5% rare ice stone, 1% hokutolite, 5% doctor Wang Shi, 5% shell, 10% kieselguhr, 1% iron sesquioxide, 3% aluminium sesquioxide, 3% zirconium oxide and 1% zirconium phosphate mix homogeneously, add in grinding equipment and carry out superfine grinding, until granule is straight Footpath is distributed in 50 ~ 80nm, sieves, and is dried, can be prepared by described anion powder.Take 8g anion powder and be scattered in 120ml ultra-pure water In, water bath sonicator 2h obtains the most even stable dispersion liquid；When the substrate with carbon nanotube mesh film is placed in about 8 DEG C, will Dispersion liquid adds in the substrate of concave shape, meanwhile, rolls around roller, makes this homogeneous dispersion be scattered in this carbon nano-tube network In shape film, owing to having hydrophilic when CNT is near 8 DEG C, this dispersion liquid is attracted to the multiple of carbon nanotube mesh film Net hole；Being warming up to about 25 DEG C, CNT has hydrophobicity being driven away by hydrone and leaves behind anion powder and adsorb in carbon nanometer In multiple net holes of pipe reticular membrane；After drying, the carbon nanotube mesh film being adsorbed with anion powder is scraped off this substrate, it is thus achieved that negative Ion powder/CNT.

Wherein, the preparation method of described deodorizer is as follows: mix the raw material of following percentage by weight: 5%ZrO₂, 10%TiO₂, 16%SiO₂, 4%V₂O₅, 3%K₂O, 2%SnO₂, 2%Cr₂O₃, 13%Al₂O₃, 12%Fe₂O₃, 18%MgO, 8%Na2O, 7%MnO₂, put into Carrying out sand milling in the big flow circulation horizontal sand mill of PUHLER company exploitation, control particle diameter, between 10 ~ 500nm, prepares nothing Machine oxide；30% epoxy resin, 50% phenolic resin and 20% inorganic oxide are sufficiently mixed, add appropriate butyl acetate Put into dispersion dispergation in ball mill, after discharge, detect, adjust the slurry being configured to apply；By this slurry coating in substrate On, drying and forming-film；Then it is placed in nitrogen filled protection atmosphere furnace, is warmed up to 900 DEG C, be incubated 1h；Film is scraped off this substrate, obtains deodorization Agent.

Wherein, described antibiotic complex prepares by the following method:

(1) weigh 0.6gC60 powder, measure the concentrated sulphuric acid that 100ml mass fraction is 98%, C60 powder and concentrated sulphuric acid are being burnt Mixing in Bei, beaker is placed in ice-water bath, stirs with the speed of 600rpm simultaneously, obtains mixed liquor；Weigh 1g potassium permanganate powder, Add slowly in above-mentioned mixed liquor；Remove ice-water bath, change water-bath into, keep bath temperature 30 ~ 40 DEG C, react 4h；Quickly add Enter 120ml pure water, filter, then dialyse 4 days with the bag filter that molecular cut off is 1000, obtain graphene quantum dot (GQDs) and hang Supernatant liquid；100rpm speed stirring GQDs suspension, simultaneously laser irradiation 40min, laser irradiation power is 1W；Standby；

(2) ultrasonic agitation 60mlGQDs suspension, dropping concentration is 0.001mol/L silver nitrate aqueous solution；Being added dropwise over concentration is 0.1mol/L ammonium dihydrogen phosphate (ammonium dihydrogen phosphate and silver nitrate aqueous solution volume ratio are 2:1), ultrasonic agitation 20min；Being added dropwise over 1mol/L sodium hydroxide solution, regulation pH value, to 11, then stands, is centrifuged, with deionized water and ethanol Alternately washing three times, vacuum drying, obtain GQDs/Ag₂O；

(3) 1gGQDs/Ag is taken₂O ultrasonic agitation is scattered in 100ml aqueous solution；Being added dropwise over concentration is 0.05mol/L cerous nitrate Aqueous solution, being added dropwise over concentration after 30min is 0.005mol/L zinc nitrate aqueous solution, GQDs/Ag₂O aqueous solution, cerous nitrate are water-soluble Liquid and zinc nitrate aqueous solution volume ratio are 1:0.1:0.4；Continuing ultrasonic agitation, regulation mixed solution pH value is to 7.0；Limit is ultrasonic to be stirred Mixing, it is the hydrazine hydrate of 50% that limit adds 6mL mass fraction, reduction reaction 0.5h at 30 DEG C；Afterwards, add 45mL mass to divide Number is the hydrazine hydrate of 50%, at 85 DEG C after reduction reaction 36h；Filter, be washed with deionized for several times, vacuum drying, GQDs/Ag₂O/Ag-Zn-Ce；

(4) by 0.5gGQDs/Ag₂O/Ag-Zn-Ce ultrasonic agitation is scattered in aqueous solution；Afterwards add volume ratio 4:1 water and Ammonia, is stirring evenly and then adding into tetraethyl orthosilicate (with GQDs/Ag₂The mass ratio of O/Ag-Zn-Ce is 3:2), regulation pH value is 9 ~ 10, reaction temperature is 20 ~ 25 DEG C, reacts 30min；It is centrifuged and cleans with acetone and deionized water successively obtaining precipitation；Will This is deposited at 90 DEG C and is dried 3h, to obtain GQDs/Ag₂O/Ag-Zn-Ce/SiO₂；By GQDs/Ag₂O/Ag-Zn-Ce/SiO₂Put Under argon gas atmosphere, carry out 600 DEG C of heat treatment 1h, after being cooled to room temperature, be immersed in Fluohydric acid. and surpass with ultrasonic power 100W Sound 10min, removes local, surface silicon dioxide, is centrifuged and is dried, it is thus achieved that antibacterial powder；

(5) under nitrogen environment, by protonic acid solution that concentration is 0.2mol/L and detergent alkylate sulphur that concentration is 0.1mol/L Acid mixes with volume ratio 3:2, is simultaneously introduced the antibacterial powder that step (4) prepares, and adds aniline, antibacterial powder after magnetic agitation 100min After being the continuously stirred 90min of 2:18 with aniline mass ratio, dropwise dripping Ammonium persulfate., aniline and Ammonium persulfate. mol ratio are 1:1； 20h is reacted at 20 DEG C～30 DEG C；Acetone, deionized water wash final vacuum for several times is dried, mill nano polyaniline/antibacterial powder is multiple Compound；

(6) prepare TiO 2 sol by sol-gel process, add in colloidal sol and account for the nano polyaniline of colloidal sol 1.0wt%/anti- Mycopowder complex, mix homogeneously；The drying of 90 DEG C of the rearmounted baking oven of still aging 4d；To calcine at gained complex 500 DEG C after milling 1h, removes polyaniline, obtains poriferous titanium dioxide/antibacterial powder complex；

(7) 30% epoxy resin, 50% phenolic resin and 20% poriferous titanium dioxide/antibacterial powder complex are sufficiently mixed, add suitable The butyl acetate of amount puts into dispersion dispergation in ball mill, after discharge, detects, adjusts the slurry being configured to apply；This is starched Material is coated on substrate, drying and forming-film；Then it is placed in nitrogen filled protection atmosphere furnace, is warmed up to 900 DEG C, be incubated 1.5h；Film is scraped From this substrate, it is thus achieved that antibiotic complex.

Embodiment 2

Step A, prepare dermatoglyph glaze: by 38%SiO2,9%Al2O3,2%(K2O+Na2O), 10%(CaO+MgO), 8%B2O3,13% ZrO2,12%V2O5 mixing sand milling is uniform；Add 3% antibiotic complex and sand milling is uniform；Add 5% anion complex, sand milling Uniformly prepare compound；Compound is dispensed in loading fire resistant sagger, carry out 1400 DEG C of high temperature meltings, obtain the slurry of molten state Material；By slurry water quenching cooling, and it is broken into graininess, obtains dermatoglyph glaze；

Step B, weigh 30% dermatoglyph glaze, 5% Solsperse 24000,3% Span-80,0.5% BYK052,2% polystyrene Resin, 3% deodorizer and 56.5% environmental protection hydrocarbon solvent, carry out in adding homogenizer disperseing 60min；By scattered mixing Liquid loads in sand mill, and sand milling 10h obtains the ink semi-finished product that particle diameter is distributed between 200 ~ 500nm；

Wherein, described anion complex preparation method is as follows: by 8% coral fossil, 12% tourmaline, 25% opal, 3% Serpentine, 8% Maifanitum, 3% rare ice stone, 3% hokutolite, 3% doctor Wang Shi, 8% shell, 12% kieselguhr, 2% iron sesquioxide, 5% 3 Al 2 O, 6% zirconium oxide and 2% zirconium phosphate mix homogeneously, add in grinding equipment and carry out superfine grinding, until particle diameter divides Cloth, at 50 ~ 80nm, sieves, and is dried, can be prepared by described anion powder.Take 8g anion powder to be scattered in 120ml ultra-pure water, water Bathe ultrasonic 2h and obtain the most even stable dispersion liquid；When the substrate with carbon nanotube mesh film is placed in about 8 DEG C, by dispersion liquid Add in the substrate of concave shape, meanwhile, roll around roller, make this homogeneous dispersion be scattered in this carbon nanotube mesh film In, owing to having hydrophilic when CNT is near 8 DEG C, this dispersion liquid is attracted to multiple nets of carbon nanotube mesh film Hole；Being warming up to about 25 DEG C, CNT has hydrophobicity being driven away by hydrone and leaves behind anion powder and adsorb at CNT In multiple net holes of reticular membrane；After drying, the carbon nanotube mesh film being adsorbed with anion powder is scraped off this substrate, it is thus achieved that bear from Sub-powder/CNT.

Wherein, the preparation method of described deodorizer is as follows: mix the raw material of following percentage by weight: 5%ZrO₂, 10%TiO₂, 16%SiO₂, 4%V₂O₅, 3%K₂O, 2%SnO₂, 2%Cr₂O₃, 13%Al₂O₃, 12%Fe₂O₃, 18%MgO, 8%Na2O, 7%MnO₂, put into Carrying out sand milling in the big flow circulation horizontal sand mill of PUHLER company exploitation, control particle diameter, between 10 ~ 500nm, prepares nothing Machine oxide；36% epoxy resin, 40% phenolic resin and 24% inorganic oxide are sufficiently mixed, add appropriate butyl acetate Put into dispersion dispergation in ball mill, after discharge, detect, adjust the slurry being configured to apply；By this slurry coating in substrate On, drying and forming-film；Then it is placed in nitrogen filled protection atmosphere furnace, is warmed up to 1000 DEG C, be incubated 2h；Film is scraped off this substrate, must remove Smelly dose.

Wherein, described antibiotic complex prepares by the following method:

(2) ultrasonic agitation 60mlGQDs suspension, dropping concentration is 0.005mol/L silver nitrate aqueous solution；Being added dropwise over concentration is 0.2mol/L ammonium dihydrogen phosphate (ammonium dihydrogen phosphate and silver nitrate aqueous solution volume ratio are 2:1), ultrasonic agitation 20min；Being added dropwise over 1mol/L sodium hydroxide solution, regulation pH value, to 11, then stands, is centrifuged, with deionized water and ethanol Alternately washing three times, vacuum drying, obtain GQDs/Ag₂O；

(3) 2gGQDs/Ag is taken₂O ultrasonic agitation is scattered in 100ml aqueous solution；Being added dropwise over concentration is 0.03mol/L cerous nitrate Aqueous solution, being added dropwise over concentration after 30min is 0.03mol/L zinc nitrate aqueous solution, GQDs/Ag₂O aqueous solution, cerous nitrate are water-soluble Liquid and zinc nitrate aqueous solution volume ratio are 1:0.2:0.3；Continuing ultrasonic agitation, regulation mixed solution pH value is to 7.0；Limit is ultrasonic to be stirred Mixing, it is the hydrazine hydrate of 50% that limit adds 6mL mass fraction, reduction reaction 0.5h at 30 DEG C；Afterwards, add 45mL mass to divide Number is the hydrazine hydrate of 50%, at 85 DEG C after reduction reaction 36h；Filter, be washed with deionized for several times, vacuum drying, GQDs/Ag₂O/Ag-Zn-Ce；

(4) by 0.3gGQDs/Ag₂O/Ag-Zn-Ce ultrasonic agitation is scattered in aqueous solution；Afterwards add volume ratio 4:1 water and Ammonia, is stirring evenly and then adding into tetraethyl orthosilicate (with GQDs/Ag₂The mass ratio of O/Ag-Zn-Ce is 3:2), regulation pH value is 9 ~ 10, reaction temperature is 20 ~ 25 DEG C, reacts 45min；It is centrifuged and cleans with acetone and deionized water successively obtaining precipitation；Will This is deposited at 90 DEG C and is dried 3h, to obtain GQDs/Ag₂O/Ag-Zn-Ce/SiO₂；By GQDs/Ag₂O/Ag-Zn-Ce/SiO₂Put Under argon gas atmosphere, carry out 600 DEG C of heat treatment 1h, after being cooled to room temperature, be immersed in Fluohydric acid. and surpass with ultrasonic power 100W Sound 12min, removes local, surface silicon dioxide, is centrifuged and is dried, it is thus achieved that antibacterial powder；

(5) under nitrogen environment, by protonic acid solution that concentration is 0.2mol/L and detergent alkylate sulphur that concentration is 0.1mol/L Acid mixes with volume ratio 3:2, is simultaneously introduced the antibacterial powder that step (4) prepares, and adds aniline, antibacterial powder after magnetic agitation 100min After being the continuously stirred 90min of 2:15 with aniline mass ratio, dropwise dripping Ammonium persulfate., aniline and Ammonium persulfate. mol ratio are 1:1； 20h is reacted at 20 DEG C～30 DEG C；Acetone, deionized water wash final vacuum for several times is dried, mill nano polyaniline/antibacterial powder is multiple Compound；

(6) prepare TiO 2 sol by sol-gel process, add in colloidal sol and account for the nano polyaniline of colloidal sol 0.5wt%/anti- Mycopowder complex, mix homogeneously；The drying of 90 DEG C of the rearmounted baking oven of still aging 4d；To calcine at gained complex 500 DEG C after milling 1h, removes polyaniline, obtains poriferous titanium dioxide/antibacterial powder complex；

(7) 45% epoxy resin, 35% phenolic resin and 20% poriferous titanium dioxide/antibacterial powder complex are sufficiently mixed, add suitable The butyl acetate of amount puts into dispersion dispergation in ball mill, after discharge, detects, adjusts the slurry being configured to apply；This is starched Material is coated on substrate, drying and forming-film；Then it is placed in nitrogen filled protection atmosphere furnace, is warmed up to 900 DEG C, be incubated 1.5h；Film is scraped From this substrate, it is thus achieved that antibiotic complex.

Embodiment 3

Step A, prepare dermatoglyph glaze: by 35%SiO2,10%Al2O3,3%(K2O+Na2O), 10%(CaO+MgO), 8%B2O3,15% ZrO2,12%V2O5 mixing sand milling is uniform；Add 5% antibiotic complex and sand milling is uniform；Add 2% anion complex, sand milling Uniformly prepare compound；Compound is dispensed in loading fire resistant sagger, carry out 1400 DEG C of high temperature meltings, obtain the slurry of molten state Material；By slurry water quenching cooling, and it is broken into graininess, obtains dermatoglyph glaze；

Step B, weigh 35% dermatoglyph glaze, 3% Solsperse 24000,2% Span-80,0.8% BYK052,1% polystyrene Resin, 5% deodorizer and 53.2% environmental protection hydrocarbon solvent, carry out in adding homogenizer disperseing 60min；By scattered mixing Liquid loads in sand mill, and sand milling 10h obtains the ink semi-finished product that particle diameter is distributed between 200 ~ 500nm；

Wherein, described anion complex preparation method is as follows: by 5% coral fossil, 15% tourmaline, 20% opal, 5% Serpentine, 5% Maifanitum, 1% rare ice stone, 5% hokutolite, 1% doctor Wang Shi, 10% shell, 15% kieselguhr, 3% iron sesquioxide, 2% Aluminium sesquioxide, 8% zirconium oxide and 5% zirconium phosphate mix homogeneously, add in grinding equipment and carry out superfine grinding, until particle diameter It is distributed in 50 ~ 80nm, sieves, be dried, can be prepared by described anion powder.Take 8g anion powder to be scattered in 120ml ultra-pure water, Water bath sonicator 2h obtains the most even stable dispersion liquid；When the substrate with carbon nanotube mesh film is placed in about 8 DEG C, will dispersion Liquid adds in the substrate of concave shape, meanwhile, rolls around roller, makes this homogeneous dispersion be scattered in this carbon nanotube mesh film In, owing to having hydrophilic when CNT is near 8 DEG C, this dispersion liquid is attracted to multiple nets of carbon nanotube mesh film Hole；Being warming up to about 25 DEG C, CNT has hydrophobicity being driven away by hydrone and leaves behind anion powder and adsorb at CNT In multiple net holes of reticular membrane；After drying, the carbon nanotube mesh film being adsorbed with anion powder is scraped off this substrate, it is thus achieved that bear from Sub-powder/CNT.

Wherein, the preparation method of described deodorizer is as follows: mix the raw material of following percentage by weight: 5%ZrO₂, 10%TiO₂, 16%SiO₂, 4%V₂O₅, 3%K₂O, 2%SnO₂, 2%Cr₂O₃, 13%Al₂O₃, 12%Fe₂O₃, 18%MgO, 8%Na2O, 7%MnO₂, put into Carrying out sand milling in the big flow circulation horizontal sand mill of PUHLER company exploitation, control particle diameter, between 10 ~ 500nm, prepares nothing Machine oxide；40% epoxy resin, 30% phenolic resin and 30% inorganic oxide are sufficiently mixed, add appropriate butyl acetate Put into dispersion dispergation in ball mill, after discharge, detect, adjust the slurry being configured to apply；By this slurry coating in substrate On, drying and forming-film；Then it is placed in nitrogen filled protection atmosphere furnace, is warmed up to 1000 DEG C, be incubated 1h；Film is scraped off this substrate, must remove Smelly dose.

Wherein, antibiotic complex prepares by the following method:

(2) ultrasonic agitation 60mlGQDs suspension, dropping concentration is 0.01mol/L silver nitrate aqueous solution；Being added dropwise over concentration is 0.5mol/L ammonium dihydrogen phosphate (ammonium dihydrogen phosphate and silver nitrate aqueous solution volume ratio are 2:1), ultrasonic agitation 20min；Being added dropwise over 1mol/L sodium hydroxide solution, regulation pH value, to 11, then stands, is centrifuged, with deionized water and ethanol Alternately washing three times, vacuum drying, obtain GQDs/Ag₂O；

(3) 3gGQDs/Ag is taken₂O ultrasonic agitation is scattered in 100ml aqueous solution；Being added dropwise over concentration is 0.005mol/L nitric acid Cerium aqueous solution, being added dropwise over concentration after 30min is 0.05mol/L zinc nitrate aqueous solution, GQDs/Ag₂O aqueous solution, cerous nitrate water Solution and zinc nitrate aqueous solution volume ratio are 1:0.2:0.4；Continuing ultrasonic agitation, regulation mixed solution pH value is to 7.0；Limit is ultrasonic Stirring, it is the hydrazine hydrate of 50% that limit adds 6mL mass fraction, reduction reaction 0.5h at 30 DEG C；Afterwards, 45mL mass is added Mark is the hydrazine hydrate of 50%, at 85 DEG C after reduction reaction 36h；Filter, be washed with deionized for several times, vacuum drying, GQDs/Ag₂O/Ag-Zn-Ce；

(4) by 0.1gGQDs/Ag₂O/Ag-Zn-Ce ultrasonic agitation is scattered in aqueous solution；Afterwards add volume ratio 4:1 water and Ammonia, is stirring evenly and then adding into tetraethyl orthosilicate (with GQDs/Ag₂The mass ratio of O/Ag-Zn-Ce is 3:2), regulation pH value is 9 ~ 10, reaction temperature is 20 ~ 25 DEG C, reacts 60min；It is centrifuged and cleans with acetone and deionized water successively obtaining precipitation；Will This is deposited at 90 DEG C and is dried 3h, to obtain GQDs/Ag₂O/Ag-Zn-Ce/SiO₂；By GQDs/Ag₂O/Ag-Zn-Ce/SiO₂Put Under argon gas atmosphere, carry out 600 DEG C of heat treatment 1h, after being cooled to room temperature, be immersed in Fluohydric acid. and surpass with ultrasonic power 100W Sound 15min, removes local, surface silicon dioxide, is centrifuged and is dried, it is thus achieved that antibacterial powder；

(5) under nitrogen environment, by protonic acid solution that concentration is 0.2mol/L and detergent alkylate sulphur that concentration is 0.1mol/L Acid mixes with volume ratio 3:2, is simultaneously introduced the antibacterial powder that step (4) prepares, and adds aniline, antibacterial powder after magnetic agitation 100min After being the continuously stirred 90min of 2:12 with aniline mass ratio, dropwise dripping Ammonium persulfate., aniline and Ammonium persulfate. mol ratio are 1:1； 20h is reacted at 20 DEG C～30 DEG C；Acetone, deionized water wash final vacuum for several times is dried, mill nano polyaniline/antibacterial powder is multiple Compound；

(6) prepare TiO 2 sol by sol-gel process, add in colloidal sol account for the nano polyaniline of colloidal sol 0.01wt%/ Antibacterial powder complex, mix homogeneously；The drying of 90 DEG C of the rearmounted baking oven of still aging 4d；To forge at gained complex 500 DEG C after milling Burn 1h, remove polyaniline, obtain poriferous titanium dioxide/antibacterial powder complex；

(7) 40% epoxy resin, 40% phenolic resin and 20% poriferous titanium dioxide/antibacterial powder complex are sufficiently mixed, add suitable The butyl acetate of amount puts into dispersion dispergation in ball mill, after discharge, detects, adjusts the slurry being configured to apply；This is starched Material is coated on substrate, drying and forming-film；Then it is placed in nitrogen filled protection atmosphere furnace, is warmed up to 900 DEG C, be incubated 1.5h；Film is scraped From this substrate, it is thus achieved that antibiotic complex.

Embodiment 4

Preparation method based on embodiment 2, difference is: increase following steps between step (4) and (5): take three-dimensional sea Continuous shape Graphene ultrasonic agitation is scattered in aqueous solution, is added dropwise over GQDs/Ag₂O/Ag-Zn-Ce/SiO₂In aqueous solution, three-dimensional Spongy graphene and GQDs/Ag₂O/Ag-Zn-Ce/SiO₂Weight ratio be 1:3；The ultrasonic 90min of 50W, stands, deionized water Washing for several times, is dried to obtain GQDs/Ag₂O/Ag-Zn-Ce/SiO₂/ Graphene antibiosis powder.

Three-dimensional sponge shape graphene preparation method is as follows: by 3g graphite powder, 1g NaNO3 in ice-water bath with 250ml 98% concentrated sulphuric acid mix homogeneously, is slowly added to 6g KMnO4.Then heat at 35 DEG C, after stirring 40min, add 95ml and go Ionized water, is warming up to 98 DEG C of reaction 20min；Add 270ml water dilution, and with in 5ml 30% H2O2 with unnecessary KMnO4, The color of mixed solution is brown color, filtered while hot, and with deionized water cyclic washing to neutral, ultrasonic disperse obtains GO；Take 200ml mass fraction is in the discoid reaction utensil that the graphene oxide solution of 5mg/ml pours diameter 25cm, high 2cm into, adds Ascorbic acid (VC) 0.5g stirring makes it be sufficiently mixed；Then confined reaction ware is placed in 80 DEG C of hydro-thermal reactions 15h, in reaction utensil Graphene oxide Spontaneous Contraction be cross-linked into three-dimensional sponge structure, lyophilization, obtain flexibility three-dimensional sponge shape Graphene.

Embodiment 5

Preparation method based on embodiment 1, difference is: described antibiotic complex prepares by the following method:

(3) 1gGQDs/Ag is taken₂O ultrasonic agitation is scattered in aqueous solution；Being added dropwise over concentration is 0.5g/100mlZnO quantum dot Aqueous solution, ultrasonic power mixing speed respectively halves；After 60min, stand, filter, be washed with deionized for several times, vacuum drying, Obtain GQDs/Ag₂O/ZnO antibacterial powder；

(4) under nitrogen environment, by protonic acid solution that concentration is 0.2mol/L and detergent alkylate sulphur that concentration is 0.1mol/L Acid mixes with volume ratio 3:2, is simultaneously introduced the antibacterial powder that step (4) prepares, and adds aniline, antibacterial powder after magnetic agitation 100min After being the continuously stirred 90min of 2:18 with aniline mass ratio, dropwise dripping Ammonium persulfate., aniline and Ammonium persulfate. mol ratio are 1:1； 20h is reacted at 20 DEG C～30 DEG C；Acetone, deionized water wash final vacuum for several times is dried, mill nano polyaniline/antibacterial powder is multiple Compound；

(5) prepare TiO 2 sol by sol-gel process, add in colloidal sol and account for the nano polyaniline of colloidal sol 1.0wt%/anti- Mycopowder complex, mix homogeneously；The drying of 90 DEG C of the rearmounted baking oven of still aging 4d；To calcine at gained complex 500 DEG C after milling 1h, removes polyaniline, obtains poriferous titanium dioxide/antibacterial powder complex；

(6) 30% epoxy resin, 50% phenolic resin and 20% poriferous titanium dioxide/antibacterial powder complex are sufficiently mixed, add suitable The butyl acetate of amount puts into dispersion dispergation in ball mill, after discharge, detects, adjusts the slurry being configured to apply；This is starched Material is coated on substrate, drying and forming-film；Then it is placed in nitrogen filled protection atmosphere furnace, is warmed up to 900 DEG C, be incubated 1.5h；Film is scraped From this substrate, it is thus achieved that antibiotic complex.

Embodiment 6

Preparation method based on embodiment 2, difference is: described antibiotic complex prepares by the following method:

(3) 2gGQDs/Ag is taken₂O ultrasonic agitation is scattered in aqueous solution；Being added dropwise over concentration is 0.2g/100mlZnO quantum dot Aqueous solution, ultrasonic power mixing speed respectively halves；After 80min, stand, filter, be washed with deionized for several times, vacuum drying, Obtain GQDs/Ag₂O/ZnO antibacterial powder；

(4) under nitrogen environment, by protonic acid solution that concentration is 0.2mol/L and detergent alkylate sulphur that concentration is 0.1mol/L Acid mixes with volume ratio 3:2, is simultaneously introduced the antibacterial powder that step (4) prepares, and adds aniline, antibacterial powder after magnetic agitation 100min After being the continuously stirred 90min of 2:15 with aniline mass ratio, dropwise dripping Ammonium persulfate., aniline and Ammonium persulfate. mol ratio are 1:1； 20h is reacted at 20 DEG C～30 DEG C；Acetone, deionized water wash final vacuum for several times is dried, mill nano polyaniline/antibacterial powder is multiple Compound；

(5) prepare TiO 2 sol by sol-gel process, add in colloidal sol and account for the nano polyaniline of colloidal sol 0.5wt%/anti- Mycopowder complex, mix homogeneously；The drying of 90 DEG C of the rearmounted baking oven of still aging 4d；To calcine at gained complex 500 DEG C after milling 1h, removes polyaniline, obtains poriferous titanium dioxide/antibacterial powder complex；

(6) 45% epoxy resin, 35% phenolic resin and 20% poriferous titanium dioxide/antibacterial powder complex are sufficiently mixed, add suitable The butyl acetate of amount puts into dispersion dispergation in ball mill, after discharge, detects, adjusts the slurry being configured to apply；This is starched Material is coated on substrate, drying and forming-film；Then it is placed in nitrogen filled protection atmosphere furnace, is warmed up to 900 DEG C, be incubated 1.5h；Film is scraped From this substrate, it is thus achieved that antibiotic complex.

Embodiment 7

Preparation method based on embodiment 3, difference is: described antibiotic complex prepares by the following method:

(3) 3gGQDs/Ag is taken₂O ultrasonic agitation is scattered in aqueous solution；Being added dropwise over concentration is 0.05g/100mlZnO quantum dot Aqueous solution, ultrasonic power mixing speed respectively halves；After 90min, stand, filter, be washed with deionized for several times, vacuum drying, Obtain GQDs/Ag₂O/ZnO antibacterial powder；

(4) under nitrogen environment, by protonic acid solution that concentration is 0.2mol/L and detergent alkylate sulphur that concentration is 0.1mol/L Acid mixes with volume ratio 3:2, is simultaneously introduced the antibacterial powder that step (4) prepares, and adds aniline, antibacterial powder after magnetic agitation 100min After being the continuously stirred 90min of 2:12 with aniline mass ratio, dropwise dripping Ammonium persulfate., aniline and Ammonium persulfate. mol ratio are 1:1； 20h is reacted at 20 DEG C～30 DEG C；Acetone, deionized water wash final vacuum for several times is dried, mill nano polyaniline/antibacterial powder is multiple Compound；

(5) prepare TiO 2 sol by sol-gel process, add in colloidal sol account for the nano polyaniline of colloidal sol 0.01wt%/ Antibacterial powder complex, mix homogeneously；The drying of 90 DEG C of the rearmounted baking oven of still aging 4d；To forge at gained complex 500 DEG C after milling Burn 1h, remove polyaniline, obtain poriferous titanium dioxide/antibacterial powder complex；

(6) 40% epoxy resin, 40% phenolic resin and 20% poriferous titanium dioxide/antibacterial powder complex are sufficiently mixed, add suitable The butyl acetate of amount puts into dispersion dispergation in ball mill, after discharge, detects, adjusts the slurry being configured to apply；This is starched Material is coated on substrate, drying and forming-film；Then it is placed in nitrogen filled protection atmosphere furnace, is warmed up to 900 DEG C, be incubated 1.5h；Film is scraped From this substrate, it is thus achieved that antibiotic complex.

Embodiment 8

Preparation method based on embodiment 6, difference is: increase such as next step between step (3) and (4): take three-dimensional Spongy graphene ultrasonic agitation is scattered in aqueous solution, is added dropwise over GQDs/Ag₂In O/ZnO aqueous solution, three-dimensional sponge shape stone Ink alkene and GQDs/Ag₂The weight ratio of O/ZnO is 1:3；The ultrasonic 90min of 50W, stands, and deionized water wash for several times, is dried GQDs/Ag₂O/ZnO/ Graphene antibiosis powder.

Comparative example 1

Preparation method based on embodiment 1, difference is: described antibiotic complex is the titanium dioxide carrying metal antibacterial agent Titanium；It is not added with anion complex；The preparation method of described deodorizer is as follows: mix the raw material of following percentage by weight: 5% ZrO₂, 10%TiO₂, 16%SiO₂, 4%V₂O₅, 3%K₂O, 2%SnO₂, 2%Cr₂O₃, 13%Al₂O₃, 12%Fe₂O₃, 18%MgO, 8%Na2O, 7%MnO₂, put in the big flow circulation horizontal sand mill of PUHLER company exploitation and carry out sand milling, control particle diameter 10 ~ Between 500nm, prepare inorganic oxide, i.e. deodorizer.

Comparative example 2

Preparation method based on embodiment 5, difference is: described antibiotic complex is the mixing of zinc oxide and titanium dioxide Thing；It is not added with deodorizer；Described anion complex preparation method is as follows: by 5% coral fossil, 15% tourmaline, 20% albumen Stone, 5% serpentine, 5% Maifanitum, 1% rare ice stone, 5% hokutolite, 1% doctor Wang Shi, 10% shell, 15% kieselguhr, 3% 3 oxidation two Ferrum, 2% aluminium sesquioxide, 8% zirconium oxide and 5% zirconium phosphate mix homogeneously, add in grinding equipment and carry out superfine grinding, until Grain diameter Distribution, at 50 ~ 80nm, is sieved, and is dried,.

The ceramic ink preparing embodiment 1 ~ 8 and comparative example 1,2 carries out performance test, test result display ink viscosity Be 15 ~ 35mPa s, surface tension at 25 ~ 40mN/m, even particle size distribution, mean diameter between 200 ~ 400nm, maximum grain Footpath is less than 1 μm, has good stability and Ink Jet Printing Performance.With ceramic ink jet printing paint ink with the use of, profit The direct spray printing on ceramic tile blank with ink jet printer, after burning till, brick face has been createed the effect that lines is the most orderly, uneven Really, the third dimension being a splendid legacy, feel is fine and smooth, more common wallpaper class ornament materials more texture and solid sense.

Embodiment 1 ~ 8 and comparative example 1,2 are carried out the performance tests such as antibacterial, test result such as following table:

Sterilization rate: take 10⁵The escherichia coli 0.1ml of individual/ml, is spread evenly across spraying and burns till the ceramic tile face of ceramic ink On, at indoor placement 2h, then bacterium solution sterilized water is eluted in culture medium, at 37 DEG C, cultivates 24h, then detection bacterium number, Calculate sterilization rate.

Heat stability is tested: is placed in electric furnace by the ceramic tile spraying and burning till ceramic ink, is raised to 200 DEG C from room temperature, Insulation 20min, puts into rapidly in 25 DEG C of water, takes out and dry after 10min, and glaze layer is without temperature shock crackle and tests its sterilization rate.

Wear testing: selecting Mohs' hardness is the abrasive material of 3～4, is rubbing by spraying and burn till on the ceramic tile of ceramic ink Wipe and imitate the effect after paving uses 2 years for 1000 times.

Antifouling test: selection chrome green is pollutant.

Sterilizing Evaluation for Uniformity: spray at same and burn till and choose 100 regions on the ceramic tile of ceramic ink and carry out Sterilizing is tested, and the data recorded is carried out Uniformity Analysis, by the uniformity=100* (1-standard deviation/meansigma methods).When uniformly Degree is more than 97%, then be labeled as ▲；When the uniformity is more than 90% and less than 97%, then it is labeled as ☆；When the uniformity is less than 90%, then mark It is designated as.

Deodorizing test: prepare two 51PVF resin airbags, put into one piece of sample print in an air bag, another tree Fat air bag not setting-out sheet.Then in two air bags, it is blown into 500ppmNH3-air gas mixture respectively and seals.At interval of 30min uses gas detecting tube to measure the concentration of NH3 in air bag, until terminating after 2 hours on-tests, calculates deodorization rate.

Anion burst size: use Japan to produce COM-3010PRO type ion detector test anion burst size, by this sample Product are positioned over 1m³Test box (length is 1m) in, record air-anion concentration in air (initial and 24h)；Adopt Test with Han Wang M1 type haze table, PM2.5 concentration (1h and 24h) in test box；(formaldehyde is dense to drip 0.1mg formaldehyde in test box Degree 0.1mg/m³), record concentration of formaldehyde after 24h.

Embodiment described above only have expressed embodiments of the present invention, and it describes more concrete and detailed, but can not Therefore the restriction to the scope of the claims of the present invention it is interpreted as, as long as using the skill that the form of equivalent or equivalent transformation is obtained Art scheme, all should fall within the scope and spirit of the invention.

Claims

1. having the preparation method purifying air ceramic ink of leather pattern effect, it comprises the following steps:

The preparation method purifying air ceramic ink with leather pattern effect the most according to claim 1, it is characterised in that The preparation method of described antibiotic complex is as follows:

(1) weigh 0.3 ~ 1gC60 powder, measure the concentrated sulphuric acid that 80 ~ 100ml mass fraction is 98%, by C60 powder and concentrated sulphuric acid Mixing in beaker, beaker is placed in ice-water bath, stirs with the speed of 500 ~ 600rpm simultaneously, obtains mixed liquor；Weigh 1 ~ 3g high Potassium manganate powder, adds in above-mentioned mixed liquor slowly；Remove ice-water bath, change water-bath into, keep bath temperature 30 ~ 40 DEG C, instead Answer 3 ~ 5h；Rapidly join 100 ~ 150ml pure water, filter, then dialyse 3 ~ 5 days with the bag filter that molecular cut off is 1000, GQDs suspension；100 ~ 150rpm speed stirring GQDs suspension, simultaneously laser irradiation 30 ~ 60min, laser irradiation power is 0.5~2W；Standby；

(2) ultrasonic agitation 50 ~ 60mlGQDs suspension, dropping concentration is 0.001 ~ 0.01mol/L silver nitrate aqueous solution；Dropwise add Entering concentration is 0.1 ~ 0.5mol/L ammonium dihydrogen phosphate, ultrasonic agitation 10 ~ 20min；It is added dropwise over 0.5 ~ 1mol/L hydroxide Sodium solution, regulation pH value, to 11, then stands, is centrifuged, and with deionized water and ethanol alternately washing three times, is vacuum dried, GQDs/Ag₂O；

(4) by 0.1 ~ 0.5gGQDs/Ag₂O/Ag-Zn-Ce ultrasonic agitation is scattered in aqueous solution；Add volume ratio 3 ~ 5:1 afterwards Water and ammonia, be stirring evenly and then adding into, regulation pH value be 9 ~ 10, reaction temperature is 20 ~ 25 DEG C, react 30 ~ 60min；Carry out It is centrifuged and cleans with acetone and deionized water successively and obtain precipitation；This is deposited at 80 ~ 90 DEG C and is dried 2 ~ 4h, to obtain GQDs/Ag₂O/Ag-Zn-Ce/SiO₂；By GQDs/Ag₂O/Ag-Zn-Ce/SiO₂It is placed under argon gas atmosphere and carries out 500 ~ 800 DEG C of heat Process 1 ~ 2h, after being cooled to room temperature, be immersed in Fluohydric acid. and carry out ultrasonic 10 ~ 15min with ultrasonic power 100 ~ 150W, remove table Local, face silicon dioxide, is centrifuged and is dried, it is thus achieved that antibacterial powder；

The preparation method purifying air ceramic ink with leather pattern effect the most according to claim 2, it is characterised in that Increase by a step between step (4) and (5): take three-dimensional sponge shape Graphene ultrasonic agitation and be scattered in aqueous solution, be added dropwise over GQDs/Ag₂O/Ag-Zn-Ce/SiO₂In aqueous solution, three-dimensional sponge shape Graphene and GQDs/Ag₂O/Ag-Zn-Ce/SiO₂Weight Amount ratio is 1:1 ~ 5；Ultrasonic 60 ~ the 120min of 10 ~ 100W, stands, and deionized water wash for several times, is dried to obtain GQDs/Ag₂O/Ag-Zn- Ce/SiO₂/ Graphene antibiosis powder.

4. having the preparation method purifying air ceramic ink of leather pattern effect, it comprises the following steps:

Step C, ink semi-finished product step B obtained, in the constant temperature a mixing bowl of 80～100 DEG C, then carry out evacuation, height Speed vibration, filtration, obtain ink；

Wherein, the preparation method of described antibiotic complex is as follows:

The preparation method purifying air ceramic ink with leather pattern effect the most according to claim 4, it is characterised in that Increase by a step between step (3) and (4): take three-dimensional sponge shape Graphene ultrasonic agitation and be scattered in aqueous solution, be added dropwise over GQDs/Ag₂In O/ZnO aqueous solution, three-dimensional sponge shape Graphene and GQDs/Ag₂The weight ratio of O/ZnO is 1:1 ~ 5；10 ~ 100W surpasses Sound 60 ~ 120min, stands, and deionized water wash for several times, is dried to obtain GQDs/Ag₂O/ZnO/ Graphene antibiosis powder.

6., according to the preparation method purifying air ceramic ink with leather pattern effect described in claim 1 or 4, its feature exists In, the preparation method of described deodorizer is as follows: mix the raw material of following percentage by weight: 5%ZrO₂, 10%TiO₂, 16%SiO₂, 4% V₂O₅, 3%K₂O, 2%SnO₂, 2%Cr₂O₃, 13%Al₂O₃, 12%Fe₂O₃, 18%MgO, 8%Na2O, 7%MnO₂, put into PUHLER company Carrying out sand milling in the big flow circulation horizontal sand mill of exploitation, control particle diameter, between 10 ~ 500nm, prepares inorganic oxide；Will 30 ~ 40% epoxy resin, 30 ~ 50% phenolic resin and 20 ~ 30% inorganic oxides are sufficiently mixed, and add appropriate butyl acetate and put Enter dispersion dispergation in ball mill, after discharge, detect, adjust the slurry being configured to apply；By this slurry coating on substrate, Drying and forming-film；Then it is placed in nitrogen filled protection atmosphere furnace, is warmed up to 900 ~ 1000 DEG C, be incubated 1 ~ 2h；Film is scraped off this substrate, Deodorizer.

7., according to the preparation method purifying air ceramic ink with leather pattern effect described in claim 1 or 4, its feature exists In, described anion complex preparation method is as follows: by 5 ~ 10% coral fossil, 10 ~ 15% tourmaline, 20 ~ 35% opals, 1 ~ 5% serpentine, 5 ~ 10% Maifanitums, 1 ~ 5% rare ice stone, 1 ~ 5% hokutolite, 1 ~ 5% doctor Wang Shi, 5 ~ 10% shells, 10 ~ 15% kieselguhr, 1 ~ 3% iron sesquioxide, 2 ~ 5% aluminium sesquioxide, 3 ~ 8% zirconium oxides and 1 ~ 5% zirconium phosphate mix homogeneously, add in grinding equipment Row superfine grinding, until particle diameter distribution is at 50 ~ 80nm, sieves, and is dried, can be prepared by described anion powder.

8. taking 5 ~ 10g anion powder to be scattered in 100 ~ 200ml ultra-pure water, water bath sonicator 1 ~ 2h obtains the most even stable dispersion Liquid；When the substrate with carbon nanotube mesh film is placed in about 8 DEG C, dispersion liquid is added in the substrate of concave shape, come meanwhile Return scroll wheel, make this homogeneous dispersion be scattered in this carbon nanotube mesh film, owing to having when CNT is near 8 DEG C Hydrophilic, this dispersion liquid is attracted to multiple net holes of carbon nanotube mesh film；Being warming up to about 25 DEG C, CNT has hydrophobic Property and hydrone is driven away leave behind anion powder adsorb in multiple net holes of carbon nanotube mesh film；After drying, will absorption The carbon nanotube mesh film having anion powder scrapes off this substrate, it is thus achieved that anion powder/CNT.

9. a purification air ceramic ink with leather pattern effect, it is characterised in that it contains the group of following percentage by weight Part: 20 ~ 35% dermatoglyph glaze, 3 ~ 8% dispersants, 2 ~ 5% surface additives, 0.3 ~ 0.8% defoamer, 1 ~ 3% bonding agent, 1 ~ 5% deodorization Agent, surplus is solvent；Wherein, described dermatoglyph glaze contain the component of following percentage by weight: 35 ~ 40%SiO2,8 ~ 10%Al2O3,1 ~ 4%(K2O+Na2O), 8 ~ 12%(CaO+MgO), 7 ~ 9%B2O3,10 ~ 15%ZrO2,12 ~ 15%V2O5,0.5 ~ 5% antibiotic complex And 2 ~ 8% anion complex.