CN106317328A - Water-resistant acrylonitrile-butadiene rubber latex for unlined thin gloves and preparation method thereof - Google Patents
Water-resistant acrylonitrile-butadiene rubber latex for unlined thin gloves and preparation method thereof Download PDFInfo
- Publication number
- CN106317328A CN106317328A CN201610690969.5A CN201610690969A CN106317328A CN 106317328 A CN106317328 A CN 106317328A CN 201610690969 A CN201610690969 A CN 201610690969A CN 106317328 A CN106317328 A CN 106317328A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- acrylonitrile
- resistance
- unlined
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses water-resistant acrylonitrile-butadiene rubber latex for unlined thin gloves and a preparation method thereof. The water-resistant acrylonitrile-butadiene rubber latex is prepared from the following raw materials in parts by weight: 85-90 parts of butadiene, 45-50 parts of acrylonitrile, 7-9 parts of acrylic acid, 6-8 parts of ethylene glycol diacrylate, 1-2 parts of sodium pyrophosphate, 2-3 parts of N,N'-methylene bisacrylamide, 1-2 parts of n-dodecyl mercaptan, 1-2 parts of sodium pyrosulfite, 2-4 parts of polypropylene glycol diglycidyl ether, 3-5 parts of nekal, 1-2 parts of dicumyl peroxide, 4-6 parts of phosphite ester, 5-7 parts of dialkane cyclohexane dicarboxylate and the like. The acrylonitrile-butadiene gloves prepared from the acrylonitrile-butadiene rubber latex developed in the invention are soft in texture, non-rubber-permeable, comfortable to wear and good in water resistance and have the advantages of good oil resistance, solvent resistance, wear resistance and penetration resistance. The added dodecafluoroheptylpropyltrimethoxysilane, hexadecyl methacrylate, 4-chloro-N-(stearamide-methyl)pyridine and the like have excellent water resistance and are combined with the other additives to enhance the water resistance of the product.
Description
Invention field
The invention belongs to macromolecule chemical industry Material Field, concretely relate to a kind of unlined water-fast fourth of slim glove
Nitrile latex and preparation method thereof.
Background technology
NBR latex is the kind that China's middle nineteen sixties grows up, and its application is increasingly extensive, and Technology is continuous
Improve, kind seriation increasingly.The carboxylic acrylonitrile butadiene rubber latex grown up on the basis of NBR latex is butadiene, acrylonitrile
With the aqueous dispersion of polymers of carboxylic acid, it it is the modified succedaneum of NBR latex.Carboxylic acrylonitrile butadiene rubber latex is because there being carboxylic on strand
Base, performance is better than common NBR latex, and having can be with advantages such as self-crosslinkings.Obtained latex has the oil resistant of excellence, resistance toization
Learning and anti-wear performance, good fluidity, tensile strength is high and has unique adhesion strength, is widely used as oil resistant wear-resistant immersion
Goods.Although carboxylic acrylonitrile butadiene rubber latex has a lot of merit, its water resistance is the most bad, is immersed in the water for a long time and easily rises
Wrinkle, accordingly, it would be desirable to develop a kind of mechanical strength, the carboxylic acrylonitrile butadiene rubber latex of abrasion performance, simultaneously water resistance excellence.
Summary of the invention
It is an object of the invention to provide a kind of unlined slim glove water-fast NBR latex and preparation method thereof.
For reaching above-mentioned purpose, the technical solution used in the present invention is:
A kind of unlined water-fast NBR latex of slim glove, is formed by the preparation of raw material of following weight portion: butadiene 85-90,
Acrylonitrile 45-50, acrylic acid 7-9, ethylene glycol diacrylate 6-8, sodium pyrophosphate 1-2, N,N methylene bis acrylamide 2-
3, dodecyl mercaptan carbon 1-2, sodium pyrosulfite 1-2, polypropylene glycol diglycidyl ether 2-4, nekal 3-5, mistake
Oxidation diisopropylbenzene (DIPB) 1-2, phosphite ester 4-6, cyclohexane dicarboxylic acid dialkyl esters 5-7, ten difluoro heptyl propyl trimethoxy silicon
Alkane 3-4, Decahydroisoquinolinpreparation 4-6, stearmide 3-5, higher alcohol 2-4,4-chloro-N-(stearmide methyl) pyridine 3-5, methyl-prop
Olefin(e) acid cetyl ester 6-8, aerosil 8-10, deionized water 180-220.
A kind of unlined slim glove preparation method of water-fast NBR latex, comprises the following steps:
(1) by acrylonitrile, acrylic acid, ethylene glycol diacrylate, sodium pyrophosphate, N,N methylene bis acrylamide, positive 12
Carbon mercaptan, deionized water join mix homogeneously in reactor, then add butadiene, peroxidating diisopropyl after nitrogen charging evacuation
Benzene, polypropylene glycol diglycidyl ether mix, and regulate temperature to 35-45 DEG C of insulation reaction 3-4h, are subsequently adding pyrosulfurous acid
Sodium, nekal, insulation reaction 4-5h after being continuously heating to 50-60 DEG C, stop when conversion ratio reaches more than 97%
Reaction, obtains NBR latex emulsion;
(2) by phosphite ester, cyclohexane dicarboxylic acid dialkyl esters, ten difluoro heptyl propyl trimethoxy silicanes, Decahydroisoquinolinpreparation
Add dispersion agitator tank in dispersion stirring 80-100min, be subsequently adding 4-chloro-N-(stearmide methyl) pyridine, metering system
Acid cetyl ester, aerosil are circulated grinding 3-5h, and to dispersion liquid, powder particle size is less than 5 μm, obtains latex
Modifying agent;
(3) after the raw materials such as NBR latex emulsion, latex modified agent, stearmide, higher alcohol being mixed at a temperature of 65-75 DEG C
Stirring 50-60min, obtains described NBR latex.
Beneficial effects of the present invention:
The present invention develop NBR latex prepare butyronitrile gloves quality softness not strike-through, wearing comfort, water resistance is good, also has
There is good oil resistivity, solvent resistance, wearability and paracentesis resistance.Ten difluoro heptyl propyl trimethoxy silicanes of interpolation, first
Base aliphatic acrylate, 4-chloro-N-(stearmide methyl) pyridine etc. has good water repelling property, with other interpolation
Agent combines the resistance to water enhancing goods.
Detailed description of the invention
Below in conjunction with specific embodiment, technical scheme of the present invention is further described.
Embodiment 1:
A kind of unlined water-fast NBR latex of slim glove, is formed by the preparation of raw material of following weight portion (kg): butadiene 85,
Acrylonitrile 45, acrylic acid 7, ethylene glycol diacrylate 6, sodium pyrophosphate 1, N,N methylene bis acrylamide 2, positive 12 carbon sulfur
Alcohol 1, sodium pyrosulfite 1, polypropylene glycol diglycidyl ether 2, nekal 3, cumyl peroxide 1, phosphorous acid
Ester 4, cyclohexane dicarboxylic acid dialkyl esters 5, ten difluoro heptyl propyl trimethoxy silicane 3, Decahydroisoquinolinpreparation 4, stearmide 3,
Higher alcohol 2,4-chloro-N-(stearmide methyl) pyridine 3, methacrylic acid cetyl ester 6, aerosil 8, deionization
Water 180.
A kind of unlined slim glove preparation method of water-fast NBR latex, comprises the following steps:
(1) by acrylonitrile, acrylic acid, ethylene glycol diacrylate, sodium pyrophosphate, N,N methylene bis acrylamide, positive 12
Carbon mercaptan, deionized water join mix homogeneously in reactor, then add butadiene, peroxidating diisopropyl after nitrogen charging evacuation
Benzene, polypropylene glycol diglycidyl ether mix, and regulate temperature to 35-45 DEG C of insulation reaction 3-4h, are subsequently adding pyrosulfurous acid
Sodium, nekal, insulation reaction 4-5h after being continuously heating to 50-60 DEG C, stop when conversion ratio reaches more than 97%
Reaction, obtains NBR latex emulsion;
(2) by phosphite ester, cyclohexane dicarboxylic acid dialkyl esters, ten difluoro heptyl propyl trimethoxy silicanes, Decahydroisoquinolinpreparation
Add dispersion agitator tank in dispersion stirring 80-100min, be subsequently adding 4-chloro-N-(stearmide methyl) pyridine, metering system
Acid cetyl ester, aerosil are circulated grinding 3-5h, and to dispersion liquid, powder particle size is less than 5 μm, obtains latex
Modifying agent;
(3) after the raw materials such as NBR latex emulsion, latex modified agent, stearmide, higher alcohol being mixed at a temperature of 65-75 DEG C
Stirring 50-60min, obtains described NBR latex.
Embodiment 2:
A kind of unlined water-fast NBR latex of slim glove, is formed by the preparation of raw material of following weight portion (kg): butadiene
87.5, acrylonitrile 47.5, acrylic acid 8, ethylene glycol diacrylate 7, sodium pyrophosphate 1.5, N,N methylene bis acrylamide
2.5, dodecyl mercaptan carbon 1.5, sodium pyrosulfite 1.5, polypropylene glycol diglycidyl ether 3, nekal 4, peroxide
Change diisopropylbenzene (DIPB) 1.5, phosphite ester 5, cyclohexane dicarboxylic acid dialkyl esters 6, ten difluoro heptyl propyl trimethoxy silicane 3.5,
Decahydroisoquinolinpreparation 5, stearmide 4, higher alcohol 3,4-chloro-N-(stearmide methyl) pyridine 4, methacrylic acid cetyl ester
7, aerosil 9, deionized water 190.
Preparation method is with embodiment 1.
Embodiment 3:
A kind of unlined water-fast NBR latex of slim glove, is formed by the preparation of raw material of following weight portion (kg): butadiene 90,
Acrylonitrile 50, acrylic acid 9, ethylene glycol diacrylate 8, sodium pyrophosphate 2, N,N methylene bis acrylamide 3, positive 12 carbon sulfur
Alcohol 2, sodium pyrosulfite 2, polypropylene glycol diglycidyl ether 4, nekal 5, cumyl peroxide 2, phosphorous acid
Ester 6, cyclohexane dicarboxylic acid dialkyl esters 7, ten difluoro heptyl propyl trimethoxy silicane 4, Decahydroisoquinolinpreparation 6, stearmide 5,
Higher alcohol 4,4-chloro-N-(stearmide methyl) pyridine 5, methacrylic acid cetyl ester 8, aerosil 10, go from
Sub-water 220.
Preparation method is with embodiment 1.
The unlined slim glove that above-described embodiment 1-3 the prepares performance test results such as following table institute of water-fast NBR latex
Show:
Embodiment 1 | Embodiment 2 | Embodiment 3 | |
Solid content, % | 48.6 | 49.5 | 51.5 |
Viscosity, mPa.s | 96.3 | 97.8 | 103.2 |
PH value | 8.4 | 8.8 | 8.7 |
Particle diameter, nm | 118 | 135 | 126 |
Resistance to water (immerses distilled water 240h) | Unchanged | Unchanged | Unchanged |
Claims (2)
1. the unlined water-fast NBR latex of slim glove, it is characterised in that formed by the preparation of raw material of following weight portion:
Butadiene 85-90, acrylonitrile 45-50, acrylic acid 7-9, ethylene glycol diacrylate 6-8, sodium pyrophosphate 1-2, N, N-methylene
Bisacrylamide 2-3, dodecyl mercaptan carbon 1-2, sodium pyrosulfite 1-2, polypropylene glycol diglycidyl ether 2-4, dibutyl naphthalene
Sodium sulfonate 3-5, cumyl peroxide 1-2, phosphite ester 4-6, cyclohexane dicarboxylic acid dialkyl esters 5-7, ten difluoro heptyl third
Base trimethoxy silane 3-4, Decahydroisoquinolinpreparation 4-6, stearmide 3-5, higher alcohol 2-4,4-chloro-N-(stearmide methyl) pyrrole
Pyridine 3-5, methacrylic acid cetyl ester 6-8, aerosil 8-10, deionized water 180-220.
A kind of unlined slim glove preparation method of water-fast NBR latex the most according to claim 1, its feature exists
In, comprise the following steps:
(1) by acrylonitrile, acrylic acid, ethylene glycol diacrylate, sodium pyrophosphate, N,N methylene bis acrylamide, positive 12
Carbon mercaptan, deionized water join mix homogeneously in reactor, then add butadiene, peroxidating diisopropyl after nitrogen charging evacuation
Benzene, polypropylene glycol diglycidyl ether mix, and regulate temperature to 35-45 DEG C of insulation reaction 3-4h, are subsequently adding pyrosulfurous acid
Sodium, nekal, insulation reaction 4-5h after being continuously heating to 50-60 DEG C, stop when conversion ratio reaches more than 97%
Reaction, obtains NBR latex emulsion;
(2) by phosphite ester, cyclohexane dicarboxylic acid dialkyl esters, ten difluoro heptyl propyl trimethoxy silicanes, Decahydroisoquinolinpreparation
Add dispersion agitator tank in dispersion stirring 80-100min, be subsequently adding 4-chloro-N-(stearmide methyl) pyridine, metering system
Acid cetyl ester, aerosil are circulated grinding 3-5h, and to dispersion liquid, powder particle size is less than 5 μm, obtains latex
Modifying agent;
(3) after the raw materials such as NBR latex emulsion, latex modified agent, stearmide, higher alcohol being mixed at a temperature of 65-75 DEG C
Stirring 50-60min, obtains described NBR latex.