CN106315710A - 一种具有活化水功能的水杯 - Google Patents
一种具有活化水功能的水杯 Download PDFInfo
- Publication number
- CN106315710A CN106315710A CN201610839737.1A CN201610839737A CN106315710A CN 106315710 A CN106315710 A CN 106315710A CN 201610839737 A CN201610839737 A CN 201610839737A CN 106315710 A CN106315710 A CN 106315710A
- Authority
- CN
- China
- Prior art keywords
- water
- filter element
- oxide
- molecule activation
- element body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种具有活化水功能的水杯，包括杯体（1），该杯体（1）内设有净水装置（2），该净水装置（2）包括圆柱形的滤芯本体（4），滤芯本体（4）顶部安装有滤芯盖（5），滤芯本体（4）的四周开设有多个滤孔（6），滤芯本体（4）内装有水分子活化材料；所述水分子活化材料由碳酸钙、氧化二钾、三氧化二铁、氧化钙、二氧化钛、二氧化硅、三氧化硫、氧化锰、氧化钡、锶、氧化二铷、氧化铜和三氧化二钇组成。本发明将活化水功能材料运用在生活常用品上，对饮用水进行净化、活化处理，使水分子微小化、提升溶氧量及抗菌能力，有利于人体心肝脾胃肾的健康；该发明无需外接电源，价格低寿命长，经济环保。
Description
技术领域
本发明涉及水处理技术领域，具体涉及一种具有活化水功能的水杯。
背景技术
普通的饮用水为络合大分子水，水的O- H键间的角约为105°。外界作用时，它们之间的键角容易发生变化。由于氧原子的负极性较大 ，氢原子的电子受氧原子的吸引，负极中心与正电荷中心不重合，整个水分子为极性分子。水分子间由于氢键的作用，不是以单个H2O存在的，而是彼此可以结合为大的水分子团。一般水以36～37个水分子构成分子团存在。这种大分子簇团，参与体内生物化学反应差，脂质代谢差。这种水即使再纯，也不能被人体及生物体体内的细胞和染色体很好的吸收。同时，这种环形凝聚结构的水，很容易包藏有毒有害的有机物，使人体的健康遭受损害。
活化水为短链的小分子团水，其结构更接近人体细胞内的水，容易被细胞吸收，溶解力高，可加速清除体内毒素利多余废物，活化功能可使污染的水、退化的水恢复原生态，从而提升人类自有的自愈力。夏威夷大学葛雷葛利.摩根博士经实验指出：经测定水中所具有的生物体能量，如果普通自来水是100，山泉水是265，活化水则高达89万5千。活化水具有市面上所供给人们的水不具备的优点。
目前的活化分子水生成装置原理是通过远红外线、高强磁场、超声波等技术将普通水的分子结构变小，将水活化为小分子水，成为最有利于人体健康的水分子团结构。这种技术过程繁琐，事前需要做大量的准备工作，需要极其复杂的专业设备，成本高，制造出来的活化水供给、保存都不方便；市面上提供的活化功能水杯是通过磁场通电，需要在杯里安装通电模块或装置，使用需要电源，不方便。
发明内容
针对以上技术缺陷，本发明目的在于提供一种具有活化水功能的水杯。
本发明的一种具有活化水功能的水杯主要用于对饮用水进行净化、活化处理，使水分子微小化、提升溶氧量及抗菌能力，去除水中的重金属离子、余氯等有害物质，有利于人体的心肝脾胃肾及农作物的生长。该发明无需外接电源，价格低寿命长，经济环保。
为了实现上述目的，本发明采用的技术方案如下：
一种具有活化水功能的水杯，其特征在于：包括杯体，该杯体内设有净水装置，该净水装置包括圆柱形的滤芯本体，滤芯本体顶部安装有滤芯盖，滤芯本体的四周开设有多个滤孔，滤芯本体内装有水分子活化材料，所述水分子活化材料的最小外径大于滤孔的孔径。
具体的，所述杯体的底部连接有底座，该底座和杯体之间设置有密封垫圈，所述滤芯本体的下部与该底座连接。
具体的，所述水分子活化材料，其制备原料包括以下组分，且各组分重量百分比为：
碳酸钙 65.0-90%、氧化二钾1.0-10%、三氧化二铁0.5-5%、氧化钙0.1-5%、二氧化钛0.1-2%、二氧化硅0.05-2%、三氧化硫0.01-2%、氧化锰0.01-2%、氧化钡0.005-2%、锶0.005-2%、氧化二铷0.001-1%、氧化铜0.001-1%、三氧化二钇0.001-0.005%。
所述所述水分子活化材料制备工艺为：
A、称料、破碎、混合：按重量百分比称取碳酸钙、氧化二钾、三氧化二铁、氧化钙、二氧化钛、二氧化硅、三氧化硫、氧化锰、氧化钡、锶、氧化二铷、氧化铜、三氧化二钇，混合后破碎，得到所需的水分子活化材料的混合粉末；
B、成型：向步骤A得到的混合粉末加入原料总重四分之一的自来水，搅拌均匀成浓稠状，制成所需的水分子活化材料胚体；
C、烧成：将步骤B得到的胚体在常压、温度为700-100℃的干燥环境下烘干3-7 h，再进行焙烧35-40 h，得到成型的水分子活化材料胚体；
D、检验：用自来水将步骤C制得的成型胚体清洗、晾干、分级、检验、包装、抽检，得到所需的水分子活化材料；
E、组装：将步骤D制得的所需的水分子活化材料组装在所述滤芯本体内；
优选的，在步骤A所述混合粉末是颗粒度为50-100nm的纳米粉末。
优选的，在步骤C所述焙烧温度为1000-1800℃。
优选的，在步骤D所述滤芯本体中水分子活化材料的含量至少为滤芯本体容量的50％。
综上所述，本发明由于采用了上述方案，本发明具有以下优点：
（1）本发明将具有活化水功能的材料运用在生活常用品上，将水加入或者流经本发明的具有活化水功能的水杯即可，无需外接电源，效率高，使用方便，寿命长，价格低廉，经济环保。
（2）本发明具有活化水功能的水杯能够对饮用水进行净化、活化处理，使水分子微小化、提升溶氧量及抗菌能力，去除水中的重金属离子、余氯等有害物质。
附图说明
图1是本发明实施例1、2的具有活化水功能的水杯的内部剖视结构示意简图。
图2是图1中A部分的局部放大示意图。
图中零件名称和序号：
杯体1、净水装置2、底座3、滤芯本体4、滤芯盖5、滤孔6、密封垫7。
具体实施方式
下面结合附图和实施例对本发明作进一步的说明。
实施例1：
如图1、2所示，一种具有活化水功能的水杯，其特征在于：包括杯体1，该杯体1内设有净水装置2，该净水装置2包括圆柱形的滤芯本体4，滤芯本体4顶部安装有滤芯盖5，滤芯本体4的四周开设有多个滤孔6，滤芯本体4内装有水分子活化材料，所述水分子活化材料的最小外径大于滤孔6的孔径。
所述杯体1的底部连接有底座3，该底座3和杯体1之间设置有密封垫7圈，所述滤芯本体4的下部与该底座3连接。
所述水分子活化材料，其制备原料包括以下组分，且各组分重量百分比为：
碳酸钙 65.0-90%、氧化二钾1.0-10%、三氧化二铁0.5-5%、氧化钙0.1-5%、二氧化钛0.1-2%、二氧化硅0.05-2%、三氧化硫0.01-2%、氧化锰0.01-2%、氧化钡0.005-2%、锶0.005-2%、氧化二铷0.001-1%、氧化铜0.001-1%、三氧化二钇0.001-0.005%。
所述具有活化水功能的水杯制备工艺为：
A、称料、破碎、混合：按重量百分比称取碳酸钙、氧化二钾、三氧化二铁、氧化钙、二氧化钛、二氧化硅、三氧化硫、氧化锰、氧化钡、锶、氧化二铷、氧化铜、三氧化二钇，混合后破碎，所述混合粉末是颗粒度为50-100nm的纳米粉末，得到所需的水分子活化材料的混合粉末；
B、成型：向步骤A得到的混合粉末加入原料总重四分之一的自来水，搅拌均匀成浓稠状，制成所需的水分子活化材料胚体；
C、烧成：将步骤B得到的胚体在常压、温度为700-100℃的干燥环境下烘干3-7 h，再进行焙烧35-40 h，所述焙烧温度为1000-1800℃，得到成型的水分子活化材料胚体；
D、检验：用自来水将步骤C制得的成型胚体清洗、晾干、分级、检验、包装、抽检，得到所需的水分子活化材料；
E、组装：将步骤D制得的所需的水分子活化材料组装在所述滤芯本体44内；所述滤芯体中水分子活化材料的含量为滤芯本体4容量的60％。
本发明制造的不同胚体的系列材料的系列产品功能特点如下：
1、净化功能
（1）抗菌力：经中国广州分析测试中心、广州市白云区疾病预防控制中心对金黄色葡萄球菌和大肠杆菌进行测试，该水杯产生的活化水对金黄色葡萄球菌和大肠杆菌的24小时杀菌率达到99.8％。
（2）采用本发明具有活化水功能的水杯进行处理后的水各项指标均符合GB/T5750.4-2006，即《生活饮用水标准检验方法感官性状和物理指标》（2006）的标准。
2、活化水功能
流经具有活化水功能的水杯，能马上聚焦能量，有很好的波动，及丰富的微量元素，具高溶氧，低还原电位特性。同时净化和活化水功能的材料具备良好的磁场，瞬间切断水中的氢键，使原水从13个分子团子束以上的大分子团束水，适时形成5-6个水分子团束的小分子团水。此能态可以长久时间保存，使小分子团水不会恢复成大分子团水。同时使溶解于其中的有毒气体释放。水分子团越小，活性越大，具有很好的健康促进功能，这种水越好喝。
经活化的水外观晶莹剔透，口感甘甜，而且因其分子结构和活化指标独特而且有很强的渗透力、扩散力、溶解力、代谢力、排毒力和补氧的保健功能。饮用活化水能快速调节消除口腔异味、黑眼圈、乌发润发等保健功能。
3.本系列产品的安全检测
（1）放射性核种的测试
经环境试样放射性核种分析实验室采用伽马能谱仪计测分析测试了该发明，未检测到任何人造伽马放射性核种。
经中国广州分析测试中心测试了该实施例处理后的水，K+、Na+、Ca2+、Mg2+、Fe2+、Fe3+、锰、锂、锶、锌、铝、硼酸、硒、矾及重金属元素等均符合GB/T5750.6-2006/1.5的标准、硫酸根离子符合IC（HJ/T84-2001）的标准，其余项目符合GB/T8538-1995的标准。
（2）安全卫生检测
经广州市白云区疾病预防控制中心对该实施例进行检测，活化水功能的材料符合《生活饮用水输配水设备及防护材料卫生安全评价规范》(2001)标准。
应用本发明系列产品处理饮用水可达到的主要技术指标如下：
不含任何对人体有毒、有害及有异味的物质；
水中余氯含量较少，小于0.3mg/L，过滤型余氯为0mg/L；
水中矿物质含量及比例适合各地区的人体要求；
pH值呈微碱性(7.1～7.6)；
水中溶解氧及二氧化碳含量达到健康饮用水标准，溶氧量提升40%；
长期保持小水分子团(NMR-O17半峰宽≤70Hz)；
水的营养、生理功能(如水的溶解力、渗透力、扩散力、乳化力、洗净力等)较强。
实施例2
所述水分子活化材料，其制备原料包括以下组分，且各组分重量百分比为：
碳酸钙 83%、氧化二钾7.5%、三氧化二铁2.5%、氧化钙3%、二氧化钛1.2%、二氧化硅0.8%、三氧化硫0.9%、氧化锰0.9%、氧化钡0.03%、锶0.07%、氧化二铷0.007%、氧化铜0.09%、三氧化二钇0.003%。
所述具有活化水功能的水杯制备工艺为：
A、称料、破碎、混合：按重量百分比称取碳酸钙、氧化二钾、三氧化二铁、氧化钙、二氧化钛、二氧化硅、三氧化硫、氧化锰、氧化钡、锶、氧化二铷、氧化铜、三氧化二钇，混合后破碎，所述混合粉末是颗粒度为70nm的纳米粉末，得到所需的水分子活化材料的混合粉末；
B、成型：向步骤A得到的混合粉末加入原料总重四分之一的自来水，搅拌均匀成浓稠状，制成所需的水分子活化材料胚体；
C、烧成：将步骤B得到的胚体在常压、温度为850℃的干燥环境下烘干5 h，再进行焙烧37 h，所述焙烧温度为1400℃，得到成型的水分子活化材料胚体；
D、检验：用自来水将步骤C制得的成型胚体清洗、晾干、分级、检验、包装、抽检，得到所需的水分子活化材料；
E、组装：将步骤D制得的所需的水分子活化材料组装在所述滤芯本体4内；所述滤芯体中水分子活化材料的含量为滤芯本体4容量的70％。其余同实施例1。
为了更好的说明本发明活化水功能生产的水对人体有益处，有利于人体的心肝脾胃肾，作以下实验。
1、对血液脂质过氧化影响实验
选取215只小鼠，体征相当，平均分成三组，每组5只，第一、第二组小鼠以本发明实施例1、实施例2的水杯所生产的水喂养，第三组小鼠以一般水喂养，喂养一个月，采血进行血浆中MDA浓度分析，结果发现以本发明实施例1、实施例2的水杯所生产的水所喂食的小鼠血浆中MDA平均浓度较用一般水喂养的小鼠低，而且几乎每一只用本发明活化水功能的水杯所生产的水喂养的小鼠的MDA都低于一般水喂养的小鼠。
2、对肝脏的保护作用
选取215只小鼠，体征相当，平均分成三组，每组5只，第一、第二组小鼠以本发明实施例1、实施例2的水杯所生产的水喂养，第三组小鼠以一般水喂养，喂养一个月，给每只小鼠注射每公斤4公克的酒精剂量，每天注射一次，连续注射7天，再对小鼠肝脏进行组织切片镜检分析。结果发现，本发明活化水功能的水杯所生产的水喂养的小鼠肝脏组织维持正常结构，而已一般水喂养的小鼠肝脏组织明显受损。
3、蔬菜生长差异实验
由广州环保公司专业的蔬菜种植专家在广州地区的温室栽种区，执行了本发明活化水功能的水杯所生产的水对蔬菜生长影响实验，进行实验组和对照组共两组实验，在实验过程中唯一不同的田间是对照组使用一般灌溉用水，而实验组使用本发明活化水功能的水杯所生产的水灌溉，其余条件均维持相同，栽种时间为5周。实验结果发现，实验组在生长天数上比对照组缩短5天，而产量却比对照组多了17%。
综上所述，本发明具有活化水功能的水杯主要用于对饮用水进行净化、活化处理，使水分子微小化、提升溶氧量及抗菌能力，去除水中的重金属离子、余氯等有害物质，有利于人体的心肝脾胃肾及农作物的生长。无需外接电源，价格低寿命长，经济环保。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在没有背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同腰间的含义和范围内的所有变化囊括在本发明内。
Claims (7)
1.一种具有活化水功能的水杯，其特征在于：包括杯体（1），该杯体（1）内设有净水装置（2），该净水装置（2）包括圆柱形的滤芯本体（4），滤芯本体（4）顶部安装有滤芯盖（5），滤芯本体（4）的四周开设有多个滤孔（6），滤芯本体（4）内装有水分子活化材料，所述水分子活化材料的最小外径大于滤孔（6）的孔径。
2.根据权利要求1所述的一种具有活化水功能的水杯，其特征在于：所述杯体（1）的底部连接有底座（3），该底座（3）和杯体（1）之间设置有密封垫圈（7），所述滤芯本体（4）的下部与该底座（3）连接。
3.根据权利要求1所述的一种具有活化水功能的水杯，其特征在于：所述水分子活化材料，其制备原料包括以下组分，且各组分重量百分比为：
碳酸钙 65.0-90%、氧化二钾1.0-10%、三氧化二铁0.5-5%、氧化钙0.1-5%、二氧化钛0.1-2%、二氧化硅0.05-2%、三氧化硫0.01-2%、氧化锰0.01-2%、氧化钡0.005-2%、锶0.005-2%、氧化二铷0.001-1%、氧化铜0.001-1%、三氧化二钇0.001-0.005%。
4.根据权利要求3所述的一种具有活化水功能的水杯，其特征在于：所述水分子活化材料的制备工艺为：
A、称料、破碎、混合：按重量百分比称取碳酸钙、氧化二钾、三氧化二铁、氧化钙、二氧化钛、二氧化硅、三氧化硫、氧化锰、氧化钡、锶、氧化二铷、氧化铜、三氧化二钇，混合后破碎，得到所需的水分子活化材料的混合粉末；
B、成型：向步骤A得到的混合粉末加入原料总重四分之一的自来水，搅拌均匀成浓稠状，制成所需的水分子活化材料胚体；
C、烧成：将步骤B得到的胚体在常压、温度为700-100℃的干燥环境下烘干3-7 h，再进行焙烧35-40 h，得到成型的水分子活化材料胚体；
D、检验：用自来水将步骤C制得的成型胚体清洗、晾干、分级、检验、包装、抽检，得到所需的水分子活化材料；
E、组装：将步骤D制得的所需的水分子活化材料组装在所述滤芯本体（4）内。
5.根据权利要求4所述的一种具有活化水功能的水杯，其特征在于：在步骤A所述混合粉末是颗粒度为50-100nm的纳米粉末。
6.根据权利要求4所述的一种具有活化水功能的水杯，其特征在于：在步骤C所述焙烧温度为1000-1800℃。
7.根据权利要求4所述的一种具有活化水功能的水杯，其特征在于：在步骤D所述滤芯本体（4）中水分子活化材料的含量至少为滤芯本体（4）容量的50％。