CN106313798A - Graphene oxide compound electronic radiator - Google Patents
Graphene oxide compound electronic radiator Download PDFInfo
- Publication number
- CN106313798A CN106313798A CN201610631739.1A CN201610631739A CN106313798A CN 106313798 A CN106313798 A CN 106313798A CN 201610631739 A CN201610631739 A CN 201610631739A CN 106313798 A CN106313798 A CN 106313798A
- Authority
- CN
- China
- Prior art keywords
- graphene oxide
- heating
- heating layer
- complex electronic
- oxide compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a graphene oxide compound electronic radiator and relates to the technical field of radiators. A graphite oxide compound conducting adhesive prepared after grinding and mixing of graphene oxide suspension liquid, prepared through the key technology of arranging a graphene oxide compound conducting adhesive and by placing graphene oxide into purified water for ultrasonic treatment, and a compound, prepared by mixing nano-graphite powder, bamboo charcoal fibers, epoxy resin, dicyandiamide and dimethylformamide is smeared on the two sides of a gum-dipped glass cloth curing sheet and dried to make a heating layer; after electrodes are distributed on the two sides of the heating layer, the two sides of the heating layer are covered with high-temperature-resistant flame-retardant epoxy resin insulation protective layers respectively, a graphene oxide compound electronic finned radiator made after pressing-fit is carried out under 160 DEG C and 6 Mpa for 2 hours is subjected to trimming, wire bonding and frame installation, and the finished product, namely the graphene oxide compound electronic radiator is made. The graphene oxide compound electronic radiator is used for heating and is simple in process, good in effect, low in cost and convenient to popularize.
Description
Technical field
Graphene oxide complex electronic heating of the present invention, relates to heating installation technical field；It is specifically related to graphene oxide multiple
Compound electronic heating technical field.
Background technology
Existing heating installation both domestic and external mainly has resistance wire heating installation, carbon fiber heating installation, heating film heating installation etc..More than existing known
Heating installation also exists that temperature resistant range is little, service life is short, bad mechanical property in-convenience in use, low, cold and hot some temperature difference of heating efficiency
Greatly, the deficiencies such as high-power heat-emitting products, defect and drawback can not be made.Professional knowledge based on inventor and abundant work warp
Test and unremitting pursuit excelsior to cause, in conscientious and abundant investigation, understand, analyze, sum up, study known skill
On the basis of art and present situation, creative takes " arranging graphene oxide compound conductive glue " key technology, has succeeded in developing this
Invent, produced " graphene oxide complex electronic heating " new product, effectively solve existing known technology and present situation
Deficiency, defect and the drawback existed, effectively raises the technical merit of the industry.
Summary of the invention
The present invention take " graphene oxide compound conductive glue is set " key technology, provide " graphene oxide be combined
Thing electronic heating " new product, graphene oxide is put into the graphene oxide suspension that supersound process in pure water is made by the present invention
Liquid is ground with the complex that Nano graphite powder, bamboo carbon fiber, epoxy resin, dicyandiamide, dimethylformamide are mixed mixed
The graphene oxide compound conductive glue made after conjunction is applied to the two sides of impregnation glass cloth cured sheets and heating layer is made in drying, sends out
All cover heat-resistant fireproof epoxy resins insulation protective layer after the cloth electrode of thermosphere two sides, 160 DEG C, under 6Mpa after pressing 2 hours
The graphene oxide complex electronic heating sheet made through trimming, bonding wire, add frame and make graphene oxide complex electronic heating
Finished product.
The purpose reached by the present invention is: 1., takes " arranging graphene oxide compound conductive glue " key technology, carry
Supply " graphene oxide complex electronic heating " new product.2., the present invention takes " to arrange graphene oxide compound conductive
Glue " key technology, solve the root problem of heating；The present invention is different from the carbon crystalline substance material of existing market, but uses oxidation
The material such as Graphene, bamboo carbon fiber, the benefit that make use of the mechanical property of graphene oxide complex excellence, hot property etc. of science
Potent fruit is more excellent relative to other inorganic reinforced filling, and the addition in polymeric matrix is also filled out than traditional reinforcement simultaneously
Material to lack.3., the chemical group of surface of graphene oxide of the present invention substantial amounts of activity oxy radical and some specific function and merit
Can carry out selectivity covalent bonding by molecule, decorating molecule is to be bonded to surface of graphene oxide with the form of covalent bond thus improves
Graphene dissolubility in a solvent and dispersibility, be presented as that the distribution in compound conductive glue is more uniform, thus reduce
The cold and hot some temperature difference, within can being down to 5 DEG C, electric heating conversion ratio is up to 98%, and its technique is scientifically prepared rationally.4., the present invention uses
Two-sided being screen-printed to impregnation glass cloth cured sheets two sides, heating power doubles, and electrothermal calefactive rate is fast, can meet industry agriculture
The high-power heating demands such as industry.5., graphene oxide of the present invention can improve the heat stability of main polymer, heat-proof combustion-resistant, resistance to
Temperature is up to 118 DEG C.6., graphene oxide of the present invention can and Nano filling----Nano graphite powder combine, may result in macromolecule
Collaborative physical property superior.7., the present invention because graphene oxide distinctive six-membered cyclic structure, stable chemical nature, by force
Degree is big, is greatly prolonged appliance life, and its service life was up to 60 years.8., the temperature resistant range of the present invention is big, length in service life, machine
Tool performance is good, easy to use, heating efficiency is high, cold and hot some temperature difference is little, can make high-power heat-emitting products, has low cost, effect
Fruit is good and reliable and stable, technical process is simple and convenient to operate fast, the advantage easily promoted.9., the present invention solves known
Deficiency, defect and the drawback that technology and present situation exist, effectively raises the technical merit of the industry.
For achieving the above object, the technical scheme that the present invention provides is:
A kind of graphene oxide complex electronic heating, by the graphene oxide in units of weight, Nano graphite powder, bamboo
Carbon fibe, epoxy resin, dicyandiamide, solvent dimethylformamide are constituted；
1., the preparation of graphene oxide suspension: graphene oxide 10 weight portion that purity is more than 95% is put into 90 weights
In the pure water of amount part, process through ultrasonic disperse, be prepared as graphene oxide suspension standby；
2., the preparation of complex: by Nano graphite powder 55 weight portion, bamboo carbon fiber 15 weight portion, epoxy resin 18 weight
Part, dicyandiamide 2 weight portion, solvent dimethylformamide 90 weight portion are sufficiently mixed, and are fabricated to complex standby；
3., the preparation of graphene oxide compound conductive glue: described graphene oxide suspension is ground with described complex
After mill mixing, it is fabricated to graphene oxide compound conductive glue standby；
4., the preparation of heating layer: with screen printer with screen printing mode by equal for described graphene oxide compound conductive glue
Even be coated on impregnation glass cloth cured sheets first, with hot-air blower by first drying, then with identical method for printing screen
Described graphene oxide compound conductive glue is evenly applied to second of described impregnation glass cloth cured sheets and uses hot-air blower
By described second drying, it is fabricated to heating layer standby；
5., the preparation of graphene oxide complex electronic heating sheet: after the Copper Foil line cloth electrode of described heating layer two sides,
Two-sided covering heat-resistant fireproof epoxy resin is insulator protective layer, 160 DEG C, pressing 2 hours under the conditions of 6Mpa, is fabricated to oxygen
Functionalized graphene complex electronic heating sheet is standby；
6., the preparation of graphene oxide complex electronic heating finished product: to described graphene oxide complex electronic heating
Sheet trimming, bonding wire, add frame, be fabricated to graphene oxide complex electronic heating finished product.
Described graphene oxide complex electronic heating, is coated on the described oxidation in described impregnation glass cloth cured sheets
Graphene complex conducting resinl, after drying realizes crystallization, is made for described graphene oxide complex electronic heating sheet
Chip.
Described graphene oxide complex electronic heating, the structure of described graphene oxide complex electronic heating is by soaking
Insulating barrier, heat-resistant fireproof asphalt mixtures modified by epoxy resin on glue glass cloth cured sheets, upper heating layer, lower heating layer, heat-resistant fireproof epoxy resin
Under fat, insulating barrier, upper lead-in wire, lower lead-in wire are constituted；
The structure of described graphene oxide complex electronic heating, on it, heating layer and impregnation glass cloth cured sheets is upper
All it is connected in the way of heat seal is bonding with lower heating layer below face, impregnation glass cloth cured sheets, heating layer and resistance to height on it
On temperature fire retarding epoxide resin under insulating barrier, heat-resistant fireproof epoxy resin insulating barrier with lower heating layer all in the way of hot pressing is connected
Being connected, on it, heating layer all electrically connects with lower lead-in wire with upper lead-in wire, lower heating layer.
Described graphene oxide complex electronic heating, described impregnation glass cloth cured sheets, upper heating layer, lower heating
Layer, under insulating barrier, heat-resistant fireproof epoxy resin, insulating barrier is laminated structure on heat-resistant fireproof epoxy resin, described on draw
Line, lower lead-in wire are electricity linear structure.
The operation principle of the present invention is: the present invention takes " arranging graphene oxide compound conductive glue " key technology, will
Graphene oxide compound conductive glue connects power supply, after energising after being coated in the two sides of impregnation glass cloth cured sheets and baking and curing
Just generate heat and serve the effect of heating installation.The operation principle of the present invention is scientific and reasonable, reliable and stable.
Owing to have employed technical scheme provided by the present invention；Owing to the present invention takes " to arrange graphene oxide complex
Conducting resinl " key technology；Described in the operation principle of the present invention；Owing to graphene oxide is put in pure water super by the present invention
The graphene oxide suspension that sonication is made and Nano graphite powder, bamboo carbon fiber, epoxy resin, dicyandiamide, dimethyl formyl
The graphene oxide compound conductive glue made after the ground mixing of complex that amine is mixed is applied to the solidification of impregnation glass cloth
Heating layer is made in the two sides of sheet and drying, all covers the protection of heat-resistant fireproof epoxy resins insulation after the cloth electrode of heating layer two sides
Layer, 160 DEG C, pressing was made after 2 hours under 6Mpa graphene oxide complex electronic heating sheet through trimming, bonding wire, add frame
Make graphene oxide complex electronic heating finished product.Make the present invention compared with existing known technology and present situation, it is thus achieved that have
Benefit effect is:
1, this invention takes " graphene oxide compound conductive glue is set " key technology, provide " graphene oxide
Complex electronic heating " new product.
2, the present invention takes " arranging graphene oxide compound conductive glue " key technology, solves at all asking of heating
Topic.
3, the present invention is different from the carbon crystalline substance material of existing market, but uses the material such as graphene oxide, bamboo carbon fiber, section
That learns make use of the reinforcing effect of the mechanical property of graphene oxide complex excellence, hot property etc. relative to other inorganic reinforcement
Filler is more excellent, and the addition in polymeric matrix is also few than traditional reinforced filling simultaneously.
4, the chemical group of surface of graphene oxide of the present invention substantial amounts of activity oxy radical and some specific function and merit
Can carry out selectivity covalent bonding by molecule, decorating molecule is to be bonded to surface of graphene oxide with the form of covalent bond thus improves
Graphene dissolubility in a solvent and dispersibility, be presented as that the distribution in compound conductive glue is more uniform, thus reduce
The cold and hot some temperature difference, within can being down to 5 DEG C, electric heating conversion ratio is up to 98%, and its technique is scientifically prepared rationally.
5, the present invention uses and two-sided is screen-printed to impregnation glass cloth cured sheets two sides, and heating power doubles, heating
Speed is fast, can meet the high-power heating demands such as industry agricultural.
6, graphene oxide of the present invention can improve the heat stability of main polymer, heat-proof combustion-resistant, and heatproof is up to 118 DEG C.
7, graphene oxide of the present invention can and Nano filling----Nano graphite powder combines, may result in high molecular collaborative
Physical property is superior.
8, the present invention is because graphene oxide distinctive six-membered cyclic structure, stable chemical nature, and intensity is big, is greatly prolonged
Appliance life, its service life was up to 60 years.
9, the temperature resistant range of the present invention is big, length in service life, good mechanical property, easy to use, heating efficiency is high, cold and hot point
The temperature difference is little, can make high-power heat-emitting products.
10, the present invention can be used for the various aspects such as indoor heating, industrial heating, agricultural heating, medical treatment heating, has application
The beneficial effect that scope is wide.
11, the present invention has low cost, effective and reliable and stable, technical process is simple and convenient to operate fast, easily promotes
Advantage.
12, the present invention solves existing known technology and deficiency, defect and the drawback of present situation existence.
13, the present invention effectively raises the technical merit of the industry.
Accompanying drawing explanation
Fig. 1 is the technological process window frame schematic diagram of the specific embodiment of the invention.
Label in figure: 1, impregnation glass cloth cured sheets, 2, upper heating layer, 3, lower heating layer, 4, heat-resistant fireproof epoxy
Insulating barrier on resin, 5, insulating barrier under heat-resistant fireproof epoxy resin, 6, upper lead-in wire, 7, lower lead-in wire.
Detailed description of the invention
Detailed description of the invention one
Below in conjunction with Figure of description, the present invention is described in detail.As shown in Figure of description:
A kind of graphene oxide complex electronic heating, by the graphene oxide in units of weight, Nano graphite powder, bamboo
Carbon fibe, epoxy resin, dicyandiamide, solvent dimethylformamide are constituted；
1., the preparation of graphene oxide suspension: graphene oxide 10 weight portion that purity is more than 95% is put into 90 weights
In the pure water of amount part, process through ultrasonic disperse, be prepared as graphene oxide suspension standby；
2., the preparation of complex: by Nano graphite powder 55 weight portion, bamboo carbon fiber 15 weight portion, epoxy resin 18 weight
Part, dicyandiamide 2 weight portion, solvent dimethylformamide 90 weight portion are sufficiently mixed, and are fabricated to complex standby；
3., the preparation of graphene oxide compound conductive glue: described graphene oxide suspension is ground with described complex
After mill mixing, it is fabricated to graphene oxide compound conductive glue standby；
4., the preparation of heating layer: with screen printer with screen printing mode by equal for described graphene oxide compound conductive glue
Even be coated on impregnation glass cloth cured sheets first, with hot-air blower by first drying, then with identical method for printing screen
Described graphene oxide compound conductive glue is evenly applied to second of described impregnation glass cloth cured sheets and uses hot-air blower
By described second drying, it is fabricated to heating layer standby；
5., the preparation of graphene oxide complex electronic heating sheet: after the Copper Foil line cloth electrode of described heating layer two sides,
Two-sided covering heat-resistant fireproof epoxy resin is insulator protective layer, 160 DEG C, pressing 2 hours under the conditions of 6Mpa, is fabricated to oxygen
Functionalized graphene complex electronic heating sheet is standby；
6., the preparation of graphene oxide complex electronic heating finished product: to described graphene oxide complex electronic heating
Sheet trimming, bonding wire, add frame, be fabricated to graphene oxide complex electronic heating finished product.
Described graphene oxide complex electronic heating, is coated on the described oxidation in described impregnation glass cloth cured sheets
Graphene complex conducting resinl, after drying realizes crystallization, is made for described graphene oxide complex electronic heating sheet
Chip.
Described graphene oxide complex electronic heating, the structure of described graphene oxide complex electronic heating is by soaking
Insulating barrier 4, heat-resistant fireproof ring on glue glass cloth cured sheets 1, upper heating layer 2, lower heating layer 3, heat-resistant fireproof epoxy resin
Under epoxy resins, insulating barrier 5, upper lead-in wire 6, lower lead-in wire 7 are constituted；
The structure of described graphene oxide complex electronic heating, on it, heating layer 2 and impregnation glass cloth cured sheets 1 is upper
All being connected in the way of heat seal is bonding with lower heating layer 3 below face, impregnation glass cloth cured sheets 1, on it, heating layer 2 is with resistance to
On high temperature flame-proof epoxy resin, under insulating barrier 4, heat-resistant fireproof epoxy resin, insulating barrier 5 is all connected with hot pressing with lower heating layer 3
Mode be connected, on it, heating layer 2 all electrically connects with lower lead-in wire 7 with upper lead-in wire 6, lower heating layer 3.
Described graphene oxide complex electronic heating, described impregnation glass cloth cured sheets 1, upper heating layer 2, lower heating
On layer 3, heat-resistant fireproof epoxy resin, under insulating barrier 4, heat-resistant fireproof epoxy resin, insulating barrier 5 is laminated structure, described
Upper lead-in wire 6, lower lead-in wire 7 are electricity linear structure.
Detailed description of the invention two
Implement by detailed description of the invention one, simply: change into weight portion gram being carried out, have received intended good
Good effect.
Detailed description of the invention three
Detailed description of the invention one, two practice processes is implemented, simply: to graphene oxide, Nano graphite powder, bamboo
Carbon fibe, epoxy resin, dicyandiamide, solvent dimethylformamide, the consumption of pure water, respectively to reduce 1,2,3,4,5,6,7,
8,9,10,15,20,25,30 times are carried out, the most respectively to expand 1,2,3,4,5,6,7,8,9,10,15,20,25,30 times
It is carried out, all have received intended good result.The present invention is made to have small test, laboratory test, expanding test, life
The solid foundation of producing property test, has the operability of theoretical direction and production application.
These are only presently preferred embodiments of the present invention, not the present invention is made any pro forma restriction；All industry skills
Art personnel all can smooth and easy implement；But make the equivalent variations modified with develop without departing from technical solution of the present invention, be this
Bright technical scheme.
Claims (4)
1. a graphene oxide complex electronic heating, it is characterised in that: by the graphene oxide in units of weight, nanometer
Graphite powder, bamboo carbon fiber, epoxy resin, dicyandiamide, solvent dimethylformamide are constituted；
1., the preparation of graphene oxide suspension: graphene oxide 10 weight portion that purity is more than 95% is put into 90 weight portions
Pure water in, through ultrasonic disperse process, be prepared as graphene oxide suspension standby；
2., the preparation of complex: by Nano graphite powder 55 weight portion, bamboo carbon fiber 15 weight portion, epoxy resin 18 weight portion, double
Cyanamide 2 weight portion, solvent dimethylformamide 90 weight portion are sufficiently mixed, and are fabricated to complex standby；
3., the preparation of graphene oxide compound conductive glue: described graphene oxide suspension and described complex are ground mixed
After conjunction, it is fabricated to graphene oxide compound conductive glue standby；
4., the preparation of heating layer: with screen printing mode, described graphene oxide compound conductive glue is uniformly coated with screen printer
It is overlying on first of impregnation glass cloth cured sheets, with hot-air blower by first drying, then with identical method for printing screen by institute
State graphene oxide compound conductive glue and be evenly applied to second of described impregnation glass cloth cured sheets and with hot-air blower by institute
State second drying, be fabricated to heating layer standby；
5., the preparation of graphene oxide complex electronic heating sheet: after the Copper Foil line cloth electrode of described heating layer two sides, two-sided
Covering heat-resistant fireproof epoxy resin is insulator protective layer, 160 DEG C, pressing 2 hours under the conditions of 6Mpa, is fabricated to aoxidize stone
Ink alkene complex electronic heating sheet is standby；
6., the preparation of graphene oxide complex electronic heating finished product: described graphene oxide complex electronic heating sheet is cut
Limit, bonding wire, add frame, be fabricated to graphene oxide complex electronic heating finished product.
Graphene oxide complex electronic heating the most according to claim 1, it is characterised in that: it is coated on described impregnation glass
Described graphene oxide compound conductive glue in glass cloth cured sheets, after drying realizes crystallization, is made for described oxidation
The chip of graphene complex electronic heating sheet.
Graphene oxide complex electronic heating the most according to claim 1, it is characterised in that: described graphene oxide is multiple
The structure of compound electronic heating is by impregnation glass cloth cured sheets (1), upper heating layer (2), lower heating layer (3), heat-resistant fireproof ring
In epoxy resins, under insulating barrier (4), heat-resistant fireproof epoxy resin, insulating barrier (5), upper lead-in wire (6), lower lead-in wire (7) are constituted；
The structure of described graphene oxide complex electronic heating, on it, heating layer (2) and impregnation glass cloth cured sheets (1) is upper
All it is connected in the way of heat seal is bonding with lower heating layer (3) below face, impregnation glass cloth cured sheets (1), heating layer on it
(2) with insulating barrier (5) under insulating barrier (4), heat-resistant fireproof epoxy resin on heat-resistant fireproof epoxy resin and lower heating layer (3)
All it is connected in the way of hot pressing connection, heating layer (2) and upper lead-in wire (6), lower heating layer (3) and lower lead-in wire (7) all electricity on it
Connect.
Graphene oxide complex electronic heating the most according to claim 3, it is characterised in that: described impregnation glass cloth is solid
Change insulating barrier (4), heat-resistant fireproof epoxy on sheet (1), upper heating layer (2), lower heating layer (3), heat-resistant fireproof epoxy resin
Under resin, insulating barrier (5) is laminated structure, and described upper lead-in wire (6), lower lead-in wire (7) are electricity linear structure.