CN106313517A - Nylon membrane, nylon membrane welding method and application of ethylene acrylic acid copolymer membrane in nylon membrane welding - Google Patents
Nylon membrane, nylon membrane welding method and application of ethylene acrylic acid copolymer membrane in nylon membrane welding Download PDFInfo
- Publication number
- CN106313517A CN106313517A CN201510395252.3A CN201510395252A CN106313517A CN 106313517 A CN106313517 A CN 106313517A CN 201510395252 A CN201510395252 A CN 201510395252A CN 106313517 A CN106313517 A CN 106313517A
- Authority
- CN
- China
- Prior art keywords
- welding
- nylon membrane
- nylon
- membrane
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a nylon membrane welding method. The nylon membrane welding method comprises the step of placing a welding assisting membrane at a joint of two to-be-welded nylon membranes for welding. The invention further provides a nylon membrane and an application of an ethylene acrylic acid copolymer membrane in nylon membrane welding. According to the nylon membrane welding method, all that is needed is to clamp the welding assisting membrane between the two to-be-welded nylon membranes during welding, welding can be performed by conventional membrane welding equipment according to a conventional welding process, and the nylon membrane welding method is simple, practical and efficient.
Description
Technical field
The present invention relates to a kind of welding method, the welding method of a kind of nylon membrane.
Background technology
Along with human social development and scientific and technological progress, nylon film is applied to work more and more widely
The every field of agricultural production, scientific research and human lives, but the interconnection technique of nylon membrane is never
Solve very well.
At present, it is usually what employing following two mode realized connecting between several nylon films: a kind of
Being to be connected together by two nylon films by the way of bonding, bonding plane time bonding is it is generally required to keep several
The high pressure of atmospheric pressure, and bonding after nylon film also need to place several hours even tens hours and treat gluing
After agent solidification, can be only achieved maximum intensity, so that the method is the longest.Additionally, it is because gluing
Agent can bring new material composition into, it is also possible to the use of glued nylon membrane can be caused to be restricted.Example
As, the diameter used on the large-scale detector of Borexino neutrino experiment is respectively 11 meters and 8.5 meters
Nylon film balloon, it is simply that with adhering method making.
Another way is welding, but owing to the melted interval of nylon is narrower, wayward, therefore, it is difficult to
Use the mode of the directly welding of similar polyethylene film.Existing welding manner is to first pass through blowing formation one
Face be nylon membrane, another side be the laminated film of welding plastic sheeting (such as polyethylene film), or will
Nylon membrane becomes composite membrane with solderable plastic sheeting dry laminating, recycles welding plastic sheeting face
Realize the welding of nylon membrane.Obviously, which needs first to prepare with compound membrane production equipment and Technology
Composite membrane, welds the most again so that welding procedure time-consumingly long, cost height.
Summary of the invention
For solving the problems referred to above, the invention provides the welding method of a kind of nylon membrane, including welding is auxiliary
Film is placed in the joint of two nylon membranes to be welded, welds.
According to an embodiment of the present invention, the auxiliary film of described welding is ethylene acrylic acid co polymer film.
According to another embodiment of the present invention, the thickness of the auxiliary film of described welding is between 0.1~0.35mm.
According to another embodiment of the present invention, the width of the auxiliary film of described welding is between 5~20mm.
According to another embodiment of the present invention, described welding method includes folding up auxiliary for described welding film
The joint of two nylon membranes to be welded, heats described joint with welding equipment and bestows pressure,
Make the fusing of described welding auxiliary film form weld seam, after cooling, obtain the nylon membrane of welding.
According to another embodiment of the present invention, the weldingvoltage of described welding equipment is 60~80V, weldering
Connecing electric current is 16~19A.
According to another embodiment of the present invention, the time heating described joint is 10~20s,
The pressure bestowing pressure is 0.25~0.35MPa, and cool time is 60~70s.
Present invention also offers a kind of nylon membrane, any of the above-described welding method prepare.
Invention further provides the application in nylon membrane welds of the ethylene acrylic acid co polymer film.
The welding method of the nylon membrane of the present invention, only needs during welding to be clipped in be welded two by welding auxiliary film
Between block nylon membrane, use existing film solder equipment to weld according to existing welding procedure, be a kind of
Simply, the welding method of nylon membrane practical, efficient.
Detailed description of the invention
Embodiment inventive features will describe the most in detail with the exemplary embodiments of advantage.It should be understood that
Be that the present invention can have various changes in different embodiments, it is all without departing from the model of the present invention
Enclose, and therein being described in substantially is treated as purposes of discussion, and be not used to limit the present invention.
An embodiment of the present invention provides the welding method of a kind of nylon membrane, is placed in including by auxiliary for welding film
The joint of two nylon membranes to be welded, welds.
In the present invention, weld auxiliary film and play the effect of " welding rod ", fold up welding auxiliary film to be welded
The joint of two nylon membranes, heats this joint with welding equipment and bestows pressure, making welding auxiliary
Film fusing forms weld seam, obtains the nylon membrane of welding after cooling.
Weld auxiliary film and be preferably ethylene acrylic acid co polymer film, such as, can be 41E687 by model
The blown film of Du Pont's raw material.The thickness welding auxiliary film can weld auxiliary film between 0.1~0.35mm
Width is advisable with the joint covering two nylon membranes to be welded, is preferably between 5~20mm, concrete
Size can select according to the width of joint.
The welding equipment used is not limited by the present invention, and existing welding equipment is used equally to the present invention.
Wherein, the weldingvoltage of welding equipment is preferably 60~80V;Welding current is preferably 16~19A.Right
The time that joint carries out heating can be 10~20s;Bestow the pressure of pressure can be 0.25~
0.35MPa, such as 0.3MPa;Cool time can be 60~70s.
The welding of the nylon membrane of an embodiment of the present invention can be achieved by the steps of:
1) with Du Pont 41E687 as raw material, made by small-sized inflation film manufacturing machine and weld auxiliary film: can be according to 41E687
Raw material technology requirement, the corresponding parameter adjusting inflation film manufacturing machine, and it is auxiliary to adjust welding with equipment situation as required
The thickness of film.
2) width of auxiliary film is welded in cutting as required, auxiliary film width more than two nylon films to be welded it
Between joint width.
3) preheating heat-sealing machine, set heating voltage, add pressure between thermocurrent, heating plate, heat time heating time and
Cool time.
4) put between two pieces of nylon membranes welding auxiliary film, put into the most together the upper and lower heating plate of heat-sealing machine it
Between, alignment joint falls heating plate, begins to warm up welding.
5) observe weldquality and carry out weld seam heat sealing strength quantitative test.
6) adjust above heat-sealing machine parameter, do multiple welding test, each weld strength is done quantitative test,
Assess each weldquality, determine optimal welding parameter, carry out formal batch welding.
The welding method of the present invention can be used for all kinds of nylon membrane, below, in conjunction with the film welded enforcement of nylon 6
The welding method of the nylon membrane of the present invention is described further by example:
Embodiment
Embodiment 1,2 all makes the auxiliary film of welding, weldering according to aforesaid operations step with Du Pont's 41E687 raw material
Meet relevant parameter such as table 1 institute of the nylon 6 after two nylon 6 thin film, involved process conditions and welding
Show.
Table 1
Wherein, the thickness of the nylon membrane welded is 0.125mm, and the thickness welding auxiliary film is 0.135mm,
Weld width 8mm.The average weld strength of embodiment 1,2 all reaches the 80% of nylon membrane bulk strength
Above, weld seam percentage elongation all reaches more than the 85% of nylon membrane body percentage elongation.
The welding method of the nylon film of the present invention, compared with prior art, has the advantages that
It is different from the method that the nylon membrane used at present is bonding or utilizes coextrusion nylon film to weld, the present invention's
The welding method of nylon film is a kind of brand-new solder technology, and welding effect is good, and weld strength is permissible
Reach the level of composite membrane welding.
The welding method of the nylon film of the present invention utilizes the auxiliary film of special welding to realize the welding of nylon film,
This welding can complete according to conventional soldering techniques with traditional films welding equipment, and auxiliary film raw material is easy to get, valency
Lattice are low, little to auxiliary film width requirement (more than nylon film joint width), and do not have auxiliary film thickness
There are special requirement, auxiliary film can be blown with a small-sized inflation film manufacturing machine.Therefore, the nylon film of the present invention
Welding method is with low cost, simple, convenient quick, efficiently.
The welding method of the nylon film of the present invention, bonding with nylon membrane compared with, process conditions are gentleer,
And substantially reduce the operating time.Bonding plane when nylon membrane is bonding is it is generally required to keep the height of several atmospheric pressure
Pressure, bonding complete after also need be dried within about 4 hours, just can obtain bonding nylon membrane.
Compared with coextrusion nylon film welding, though the welding method of the nylon film of the present invention increases when welding
Auxiliary film places program together, but eliminates the step that composite membrane produces, enormously simplify technique.
Unless limited otherwise, term used herein is the implication that those skilled in the art are generally understood that.
Embodiment described in the invention is merely for exemplary purpose, and is not used to limit the guarantor of the present invention
Protecting scope, those skilled in the art can be made within the scope of the invention various other and replace, change and change
Enter, thus, the invention is not restricted to above-mentioned embodiment, and be only defined by the claims.
Claims (9)
1. a welding method for nylon membrane, is placed in connecing of two nylon membranes to be welded including by welding auxiliary film
At conjunction, weld.
Method the most according to claim 1, the auxiliary film of wherein said welding is ethylene acrylic acid co polymer
Film.
Method the most according to claim 1, the thickness of the auxiliary film of wherein said welding between 0.1~
0.35mm。
Method the most according to claim 1, the width of the auxiliary film of wherein said welding is between 5~20mm.
Method the most according to claim 1, folds up to be welded two including by auxiliary for described welding film
The joint of nylon membrane, heats described joint with welding equipment and bestows pressure, making described welding
The fusing of auxiliary film forms weld seam, obtains the nylon membrane of welding after cooling.
Method the most according to claim 5, the weldingvoltage of wherein said welding equipment is 60~80V,
Welding current is 16~19A.
Method the most according to claim 5, the time wherein described joint heated be 10~
20s, the pressure bestowing pressure is 0.25~0.35MPa, and cool time is 60~70s.
8. a nylon membrane, is prepared by the method according to any one of claim 1 to 7.
9. ethylene acrylic acid co polymer film application in nylon membrane welds.