CN106298080A - A kind of production method of copper coated aluminum bus bank - Google Patents
A kind of production method of copper coated aluminum bus bank Download PDFInfo
- Publication number
- CN106298080A CN106298080A CN201610893162.1A CN201610893162A CN106298080A CN 106298080 A CN106298080 A CN 106298080A CN 201610893162 A CN201610893162 A CN 201610893162A CN 106298080 A CN106298080 A CN 106298080A
- Authority
- CN
- China
- Prior art keywords
- copper
- production method
- coated aluminum
- aluminum
- pipe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the production method of a kind of copper coated aluminum bus bank, comprise the following steps: 1. carry out scrubbing removing oxide skin by the surface of copper pipe and aluminium sheet with iron wire brush, in noble gas, aluminium sheet is loaded in copper pipe, prevent from aoxidizing for a long time；2. the copper aluminum blank molectron installed by set is put into Efco-Northrup furnace and is heated, and heating-up temperature is 500 700 DEG C, and roll compacting elongation moulding shuts out the cuprum alclad rectangular bus bar of different size；3. according to user's requirement, conventional annealing is carried out.Bi-material is perfectly combined by the production method of a kind of copper coated aluminum bus bank of the present invention, both the characteristic that copper surface oxidation-resistant is strong had been maintained, take full advantage of again the lightweight advantage of aluminum, after three roll compacting extends, good percentage elongation, copper coated aluminum bus bank good conductivity, lightweight, production efficiency is high, percent defective is low.
Description
Technical field
The present invention relates to the manufacture method of the bus bar that a kind of power industry uses, especially relate to a kind of copper wrapped aluminum bus
The production method of row.
Background technology
Copper wrapped aluminum bus-copper clad aluminum wire bus is that the row's core as bus bars arranged by a kind of fine aluminium, uses certain thickness
Copper coin material as bus bars outer contact and install contact surface, constitute copper wrapped aluminum bus busbar.Copper wrapped aluminum bus
Busbar is possible not only to replace fine copper row's bus bars, it is also possible to applies and transmits occasion with fine copper row as electric current at other
Under, replace original copper bar with copper clad aluminum wire, effectively reduce busbar cost about 50%.Copper wrapped aluminum bus-copper clad aluminum wire product is special
Point: 1, replace original copper bar with copper clad aluminum wire, effectively reduces busbar cost about 50%.2, volume ratio 17-20%, proportion 3.7,
Copper content 40%.3, conductivity reaches about the 85% of fine copper row.4, copper aluminum interface is completely combined, shearing, bending, punching, copper aluminum
Operation requirement that is not stratified, that meet copper bar processing, use, can substitute copper bar.5, contact resistance, resistance to corrosion, superficiality
Can be just the same with copper bar.6, good mechanical property, tensile strength, case hardness are more much higher, close to copper bar than aluminum row.7, proportion
Little, lightweight, use installation more convenient, service life is long.8, in various ambient temperatures, reach permanent former between copper aluminum
Sub-intergranular combines, and layers of copper (tin plating, zinc layers) is evenly distributed, and there is not physical imperfection, but present copper coated aluminum bus bank
Manufacturing process due to drawing numbers too many, cause yield rate low, of poor quality.
Summary of the invention
It is an object of the invention to provide the production method of a kind of copper coated aluminum bus bank, the copper wrapped aluminum bus produced by the method
Row's good conductivity, lightweight.
In order to solve the problem that prior art exists, the present invention is to use following technical scheme to realize:
The production method of a kind of copper coated aluminum bus bank, comprises the following steps:
1. carry out scrubbing removing oxide skin by the surface of copper pipe and aluminium sheet with iron wire brush, in noble gas, aluminium sheet is loaded copper pipe
In, prevent from aoxidizing for a long time；
2. the copper aluminum blank molectron installed by set is put into Efco-Northrup furnace and is heated, and heating-up temperature is 500-700 DEG C, rolls
Pressure elongation moulding, shuts out the cuprum alclad rectangular bus bar of different size；
3. according to user's requirement, conventional annealing is carried out.
Described roll compacting extends to three roll compacting and extends.
Thickness after described described copper roll compacting extends is 0.6mm.
Described step 1. scrub step include cleaning copper pipe step:
Copper pipe is immersed in half an hour in copper pipe abluent, with steel brush, copper pipe is scrubbed, after scrubbing clean, use overflow water
It is rinsed.
Described step 1. scrub step include cleaning aluminum pipe step:
Aluminum pipe abluent and water are mixed to form cleanout fluid according to the ratio that weight ratio is 1:5, aluminum pipe is immersed in cleanout fluid
Scrub clean with steel brush after half an hour.
The present invention has a following remarkable advantage:
The production method of a kind of copper coated aluminum bus bank of the present invention due to comprise the following steps that 1. with iron wire brush by copper pipe and aluminium sheet
Surface carry out scrubbing removing oxide skin, in noble gas, aluminium sheet is loaded in copper pipe, prevents from aoxidizing for a long time；2. will suit
Good copper aluminum blank molectron is put into Efco-Northrup furnace and is heated, and heating-up temperature is 500-700 DEG C, roll compacting elongation moulding,
Shut out the cuprum alclad rectangular bus bar of different size；3. according to user's requirement, carrying out conventional annealing, the method is complete by bi-material
Beautiful combines, and has both maintained the characteristic that copper surface oxidation-resistant is strong, has taken full advantage of again the lightweight advantage of aluminum, scrub
Step enables copper pipe preferably to combine with aluminum pipe, after three roll compacting extends, and good percentage elongation, copper coated aluminum bus bank
Good conductivity, lightweight, production efficiency is high, percent defective is low.
Detailed description of the invention
Below in conjunction with the embodiment of the present invention, technical scheme is clearly and completely described, it is clear that institute
The embodiment described is only a part of embodiment of the present invention rather than whole embodiments.Based on the embodiment in the present invention,
The every other embodiment that those of ordinary skill in the art are obtained under not making creative work premise, broadly falls into this
The scope of bright protection.
Embodiment 1:
The production method of a kind of copper coated aluminum bus bank, comprises the following steps:
1. carry out scrubbing by the surface of copper pipe and aluminium sheet with iron wire brush and remove oxide skin, after oxide skin is all disposed, in inertia
Aluminium sheet is loaded in copper pipe by gas, prevents from aoxidizing for a long time；
Described step 1. in scrub step include cleaning copper pipe step:
Copper pipe is immersed in half an hour in copper pipe abluent, with steel brush, copper pipe is scrubbed, after scrubbing clean, use overflow water
It is rinsed.
Described step 1. in scrub step also include cleaning aluminum pipe step:
Aluminum pipe abluent and water are mixed to form cleanout fluid according to the ratio that weight ratio is 1:5, aluminum pipe is immersed in cleanout fluid
Scrub clean with steel brush after half an hour.
2. the copper aluminum blank molectron installed by set is put into Efco-Northrup furnace and is heated, and heating-up temperature is 500 DEG C, rolls
Pressure elongation moulding, shuts out the cuprum alclad rectangular bus bar of different size；
3. according to user's requirement, conventional annealing is carried out.
Described roll compacting extends to three roll compacting and extends.
Thickness after described described copper roll compacting extends is 0.6mm.
The copper coated aluminum bus bank prepared of production method using a kind of copper coated aluminum bus bank of the present embodiment has a following parameter:
| Density | Tensile strength | Elongation percentage | Relative electric conductivity |
| 3.7g/cm3 | 110 MPA | Soft state 15 %；Hard state 1.5 % | 85 % |
Embodiment 2:
The present embodiment and the difference of embodiment 1 are that step step 2. middle heating-up temperature is 700 DEG C, and remaining is with embodiment 1.
Embodiment 3:
The present embodiment and the difference of embodiment 1 are that step step 2. middle heating-up temperature is 600 DEG C, and remaining is with embodiment 1.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, permissible
Understand and these embodiments can be carried out multiple change without departing from the principles and spirit of the present invention, revise, replace
And modification, the scope of the present invention be defined by the appended.
Claims (5)
1. the production method of a copper coated aluminum bus bank, it is characterised in that comprise the following steps:
1. carry out scrubbing removing oxide skin by the surface of copper pipe and aluminium sheet with iron wire brush, in noble gas, aluminium sheet is loaded copper pipe
In, prevent from aoxidizing for a long time；
2. the copper aluminum blank molectron installed by set is put into Efco-Northrup furnace and is heated, and heating-up temperature is 500-700 DEG C, rolls
Pressure elongation moulding, shuts out the cuprum alclad rectangular bus bar of different size；
3. according to user's requirement, conventional annealing is carried out.
The production method of a kind of copper coated aluminum bus bank the most according to claim 1, it is characterised in that: described roll compacting extends
It is that three roll compacting extends.
The production method of a kind of copper coated aluminum bus bank the most according to claim 1, it is characterised in that: described described copper rolls
Thickness after calendering is stretched is 0.6mm.
The production method of a kind of copper coated aluminum bus bank the most according to claim 1, it is characterised in that: 1. described step brushes
Wash step include cleaning copper pipe step:
Copper pipe is immersed in half an hour in copper pipe abluent, with steel brush, copper pipe is scrubbed, after scrubbing clean, use overflow water
It is rinsed.
The production method of a kind of copper coated aluminum bus bank the most according to claim 1, it is characterised in that: 1. described step brushes
Wash step include cleaning aluminum pipe step:
Aluminum pipe abluent and water are mixed to form cleanout fluid according to the ratio that weight ratio is 1:5, aluminum pipe is immersed in cleanout fluid
Scrub clean with steel brush after half an hour.