CN106283676A - A kind of UV resistance, radioprotective canvas tent fabric and preparation method thereof - Google Patents
A kind of UV resistance, radioprotective canvas tent fabric and preparation method thereof Download PDFInfo
- Publication number
- CN106283676A CN106283676A CN201610680545.0A CN201610680545A CN106283676A CN 106283676 A CN106283676 A CN 106283676A CN 201610680545 A CN201610680545 A CN 201610680545A CN 106283676 A CN106283676 A CN 106283676A
- Authority
- CN
- China
- Prior art keywords
- resistance
- canvas
- radioprotective
- fibre
- colloidal sol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of UV resistance, radioprotective canvas tent fabric, it is to be prepared by the raw material of following weight parts: polyster fibre 30 40, flax fiber 10 15, bamboo fibre 10 15, stainless steel fibre 5 10, styrene-acrylic emulsion 5 10, nano zine oxide 35, blanc fixe 12, polyoxyethylene sorbitan monoleate 0.2 0.4, UV absorbent UV 531 0.5 1, hydroxyethyl cellulose 12, modified starch colloidal sol 5 10.The canvas tent fabric of the present invention had both met basic use requirement, had again good moisture-penetrable ventilated property, coating stability and the uniformity high, difficult drop-off, cracking, waterproof effect and exterior quality are good, and have good UV resistance, shielding property, and surcharge is high.
Description
Technical field
The present invention relates to tent material technical field, particularly relate to a kind of UV resistance, radioprotective canvas tent fabric and
Preparation method.
Background technology
Tent is a kind of textile with construction material function, isolates an individual secure in lowered in field environment
Space.Tent has simplicity, light and handy feature, needs have Radix Saposhnikoviae, rainproof, snow defence, cold-proof, the basic function of mosquito proof.
Recently as the development of tourist industry, the sales volume of tent is increased substantially, and market expands further, outside people are to tent
See, the demand of performance improves the most further.Tent material is made up through surface dressing of base fabric, and its performance largely affects
The serviceability of tent.Current most widely used tent material is polyester canvas, and its breathable moisture permeability is poor, serviceability
The highest with surcharge, it is impossible to meet the potential demand of city's field alignment expensive goods.Owing to tent needs to be often exposed to sunlight
Under, ultraviolet can accelerate the aging of fabric and fade, and affects serviceability and the life-span of fabric, therefore anti-ultraviolet, radioprotective
Function becomes a kind of trend of tent material development.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of UV resistance, radioprotective canvas tent face
Material and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of UV resistance, radioprotective canvas tent fabric, it is to be prepared by the raw material of following weight parts:
Polyster fibre 30-40, flax fiber 10-15, bamboo fibre 10-15, stainless steel fibre 5-10, styrene-acrylic emulsion 5-10, nanometer
Zinc oxide 3-5, blanc fixe 1-2, Tween-80 0.2-0.4, ultraviolet absorbent UV-531 0.5-1, hydroxy ethyl fiber
Element 1-2, modified starch colloidal sol 5-10;
Wherein modified starch colloidal sol is prepared by the raw materials in: corn starch 30-40, graphite powder 10-15, sodium nitrate 1-
2, potassium permanganate 2-4, acrylic acid 3-5, methyl methacrylate 6-8,15-20% concentration aqueous hydrogen peroxide solution 10-15, persulfuric acid
Ammonium 0.5-1, sodium lauryl sulphate 0.5-1, water 200-300;The preparation method of modified starch colloidal sol is by solid-liquid by graphite powder
Weight ratio 1:1.5-1:2 adds sodium nitrate, potassium permanganate, 40-50 DEG C of reaction after mixing with the concentrated sulphuric acid that mass fraction is 98%
Water, corn starch and 15-20% concentration aqueous hydrogen peroxide solution 60-80 DEG C stirring 3-4h it is sequentially added into, in being adjusted to by pH after 0.5-1h
Remaining raw material 70-80 DEG C reaction 1-2h is added, after cooling and get final product after property.
A kind of UV resistance, the preparation method of radioprotective canvas tent fabric, comprise the following steps:
(1) by polyster fibre, flax fiber, bamboo fibre and stainless steel fibre blending woven in proportion, canvas base fabric is obtained;
(2) by styrene-acrylic emulsion, modified starch colloidal sol, after Tween-80 mixes with ultraviolet absorbent UV-531 50-60 DEG C stir
Mix 1-2h, add remaining raw material co-ground after cooling to fineness≤50 μm, obtain coating agent;
(3) the canvas scrim surfaces that the coating agent in (2) is evenly applied in (1), prior to 80-90 DEG C of dry 4-6h, then at
120-140 DEG C of heat treatment 10-20min, i.e. obtains UV resistance, radioprotective canvas tent fabric after cooling.
The invention have the advantage that
The present invention is compounded by raw materials such as modified starch colloidal sol and styrene-acrylic emulsions, and the coating agent of synthesis has with tent canvas base fabric
Good associativity, generates in base fabric and has good adherence fastness, moisture-penetrable ventilated property and the film of mechanical property, makes final obtaining
To canvas tent fabric both met basic use requirement, there is again good moisture-penetrable ventilated property, coating stability and uniformly
Degree height, difficult drop-off, cracking, waterproof effect and exterior quality are good, and have good UV resistance, shielding property, additional
It is worth height.
Detailed description of the invention
A kind of UV resistance, radioprotective canvas tent fabric, it is to be prepared by the raw material of following weight parts:
Polyster fibre 30, flax fiber 10, bamboo fibre 10, stainless steel fibre 5, styrene-acrylic emulsion 5, nano zine oxide 3, blanc fixe
1, Tween-80 0.2, ultraviolet absorbent UV-531 0.5, hydroxyethyl cellulose 1, modified starch colloidal sol 5;
Wherein modified starch colloidal sol is prepared by the raw materials in: corn starch 30, graphite powder 10, sodium nitrate 1, permanganic acid
Potassium 2, acrylic acid 3, methyl methacrylate 6,15% concentration aqueous hydrogen peroxide solution 10, Ammonium persulfate. 0.5, sodium lauryl sulphate
0.5, water 200;Graphite powder is 98% by solid-liquid weight ratio 1:1.5 and mass fraction by the preparation method of modified starch colloidal sol
Add sodium nitrate, potassium permanganate after concentrated sulphuric acid mixing, be sequentially added into water, corn starch and 15% concentration after 40 DEG C of reaction 0.5h double
Oxygen water aqueous solution 60 DEG C stirring 3h, adds remaining raw material 70 DEG C reaction 1h, after cooling and get final product after pH is adjusted to neutrality.
A kind of UV resistance, the preparation method of radioprotective canvas tent fabric, comprise the following steps:
(1) by polyster fibre, flax fiber, bamboo fibre and stainless steel fibre blending woven in proportion, canvas base fabric is obtained;
(2) styrene-acrylic emulsion, modified starch colloidal sol, Tween-80 are mixed rear 50 DEG C of stirrings with ultraviolet absorbent UV-531
1h, adds remaining raw material co-ground to fineness≤50 μm, obtains coating agent after cooling;
(3) the canvas scrim surfaces being evenly applied in (1) by the coating agent in (2), prior to 80 DEG C of dry 4h, then at 120 DEG C
Heat treatment 10min, i.e. obtains UV resistance, radioprotective canvas tent fabric after cooling.
Above-mentioned prepared canvas tent fabric performance index test result is as follows:
Project | Unit | Index |
Ultimate strength (warp-wise) | N | 2760 |
Ultimate strength (broadwise) | N | 2490 |
Vapor transfer rate | g/m2d | 1716 |
Colour fastness to rubbing | Level | 6 |
Anti-ultraviolet property | 50+ |
Claims (2)
1. a UV resistance, radioprotective canvas tent fabric, it is characterised in that it is to be prepared by the raw material of following weight parts:
Polyster fibre 30-40, flax fiber 10-15, bamboo fibre 10-15, stainless steel fibre 5-10, styrene-acrylic emulsion 5-10, nanometer
Zinc oxide 3-5, blanc fixe 1-2, Tween-80 0.2-0.4, ultraviolet absorbent UV-531 0.5-1, hydroxy ethyl fiber
Element 1-2, modified starch colloidal sol 5-10;
Described modified starch colloidal sol is prepared by the raw materials in: corn starch 30-40, graphite powder 10-15, sodium nitrate
1-2, potassium permanganate 2-4, acrylic acid 3-5, methyl methacrylate 6-8,15-20% concentration aqueous hydrogen peroxide solution 10-15, over cure
Acid ammonium 0.5-1, sodium lauryl sulphate 0.5-1, water 200-300;The preparation method of modified starch colloidal sol is by solid by graphite powder
Liquid weight ratio 1:1.5-1:2 adds sodium nitrate, potassium permanganate, 40-50 DEG C of reaction after mixing with the concentrated sulphuric acid that mass fraction is 98%
Water, corn starch and 15-20% concentration aqueous hydrogen peroxide solution 60-80 DEG C stirring 3-4h it is sequentially added into, in being adjusted to by pH after 0.5-1h
Remaining raw material 70-80 DEG C reaction 1-2h is added, after cooling and get final product after property.
A kind of UV resistance the most according to claim 1, the preparation method of radioprotective canvas tent fabric, it is characterised in that
Comprise the following steps:
(1) by polyster fibre, flax fiber, bamboo fibre and stainless steel fibre blending woven in proportion, canvas base fabric is obtained;
(2) by styrene-acrylic emulsion, modified starch colloidal sol, after Tween-80 mixes with ultraviolet absorbent UV-531 50-60 DEG C stir
Mix 1-2h, add remaining raw material co-ground after cooling to fineness≤50 μm, obtain coating agent;
(3) the canvas scrim surfaces that the coating agent in (2) is evenly applied in (1), prior to 80-90 DEG C of dry 4-6h, then at
120-140 DEG C of heat treatment 10-20min, i.e. obtains UV resistance, radioprotective canvas tent fabric after cooling.