CN106281193A - Novel non-formaldehyde, benzene-free and environment-friendly glue - Google Patents
Novel non-formaldehyde, benzene-free and environment-friendly glue Download PDFInfo
- Publication number
- CN106281193A CN106281193A CN201610654815.0A CN201610654815A CN106281193A CN 106281193 A CN106281193 A CN 106281193A CN 201610654815 A CN201610654815 A CN 201610654815A CN 106281193 A CN106281193 A CN 106281193A
- Authority
- CN
- China
- Prior art keywords
- parts
- glue
- benzene
- formaldehyde
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention open a kind of novel non-formaldehyde, benzene-free and environment-friendly glue.Count by weight, this glue is by including that following raw material prepares: polyether Glycols 70~100 parts, 2,6 toluene di-isocyanate(TDI)s 30~50 parts, chain extender 10~20 parts, acetone 50~80 parts, vinyl acetate acrylic acid ester copolymer emulsion 20~30 parts, thickening agent 2~4 parts, firming agent 1~3 parts, zinc oxide 1~3 parts, 100 parts of water.Compared with existing glue, the glue of the present invention does not contains formaldehyde and benzene, is a kind of environment-friendly water-based glue, and has higher adhesion strength.
Description
Technical field
The invention belongs to adhesive field, be specifically related to a kind of novel non-formaldehyde, benzene-free and environment-friendly glue.
Background technology
Because timber day lacks, wood-based plate is used to replace many conventional use of sawn timber, and its yield increases sharply.With sawn timber phase
Ratio, the advantage of wood-based plate is: breadth is big, structural good, easy construction;Dilation rate is low, dimensionally stable, and material is equal compared with sawn timber
Even, it is unlikely to deform cracking;Veneer and various particle as raw material of artifical plate are prone to dipping, thus can make various functional processing
(such as fire-retardant, anticorrosion, nonshrink, wear-resisting etc.);Thickness level and the density level suitability of wider range are strong;Brake forming performance compares sawn timber
Good.
Wood-based plate is with timber or other non-wood plants as raw material, is separated into various unit material through certain machining
After, stick with glue agent gluing and form.And the adhesive major part being currently used for wood-based plate is containing formaldehyde products, use this kind of gluing
Agent easily causes indoor formaldehyde pollution, is unfavorable for health.
Summary of the invention
The technical problem to be solved in the present invention is to overcome existing defect, it is provided that a kind of novel non-formaldehyde, benzene-free and environment-friendly glue
Water.
In order to solve above-mentioned technical problem, the invention provides following technical scheme:
Novel non-formaldehyde, benzene-free and environment-friendly glue, count by weight, by including that following raw material prepares:
Polyether Glycols 70~100 parts, 2,6-toluene di-isocyanate(TDI) 30~50 parts, chain extender 10~20 parts, acetone 50~80
Part, vinyl acetate-acrylic copolymer emulsion 20~30 parts, thickening agent 2~4 parts, firming agent 1~3 parts, zinc oxide 1~3 parts,
100 parts of water.
Preferably, described chain extender is ethylenediamine base ethyl sulfonic acid sodium and/or dimethylolpropionic acid.
Preferably, described firming agent is vinyl triamine or m-xylene diamine.
The preparation method of above-mentioned glue, comprises the steps step:
(1) by polyether Glycols, 2,6-toluene di-isocyanate(TDI), chain extender and acetone add in reactor, are heated with stirring to 80
~90 DEG C, insulation reaction 1~3 hours, cooling, regulate pH to 7;
(2) under agitation, in the system of step (1) add vinyl acetate-acrylic copolymer emulsion, firming agent, zinc oxide,
Thickening agent and water, be uniformly mixed so as to obtain described glue.
The novel non-formaldehyde of the present invention, benzene-free and environment-friendly glue instead of traditional use containing aldehyde glue completely, formaldehydeless release,
It is adapted to the processing technique of particieboard, there is adhesive strength and the nail-holding ability of excellence, and extra-high frost resistance (0 degree to 5 degree Celsius
Viscosity is almost unchanged, does not glue press).
Detailed description of the invention
Hereinafter the preferred embodiments of the present invention are illustrated, it will be appreciated that preferred embodiment described herein is only used
In the description and interpretation present invention, it is not intended to limit the present invention.
Embodiment 1
(1) polyether Glycols 100g, 2,6-toluene di-isocyanate(TDI) 50g, ethylenediamine base ethyl sulfonic acid sodium 20g and acetone 80g are added
Entering in reactor, be heated with stirring to 80 DEG C, insulation reaction 3 hours, cooling, by triethylamine regulation system pH to 7;
(2) under agitation, in the system of step (1), vinyl acetate-acrylic copolymer emulsion 30g, vinyl triamine are added
3g, zinc oxide 3g, thickening agent (commercially available TT935) 2g and water 100g, mixing i.e. obtains described glue.
Embodiment 2
(1) polyether Glycols 70g, 2,6-toluene di-isocyanate(TDI) 30g, dimethylolpropionic acid 10g and acetone 50g are added reaction
In still, being heated with stirring to 90 DEG C, insulation reaction 1 hour, cooling, by triethylamine regulation system pH to 7;
(2) under agitation, in the system of step (1) add vinyl acetate-acrylic copolymer emulsion 20g, benzene dimethylamine 1g,
Zinc oxide 1g, thickening agent (commercially available DT-205) 4g and water 100g, mixing i.e. obtains described glue.
The mean molecule quantity of polyether Glycols used by the present invention is 1000-5000.
Used by the present invention, vinyl acetate-acrylic copolymer emulsion is produced in conventional fashion, and its viscosity is 1500-
2500mPa/s, solid content is 40-50%.
The initial adhesive strength of the adhesion strength of the glue of the present invention: 5min is 3.0~3.3N/mm, and the most viscous intensity of 24h is
3.2~3.5N/mm, 70 DEG C × 95% relative humidity adhesive strength after aging 7 days is 2.0~2.5N/mm.Method of testing reference
GB/T2791-1995。
Finally it is noted that the foregoing is only the preferred embodiments of the present invention, it is not limited to the present invention,
Although being described in detail the present invention with reference to previous embodiment, for a person skilled in the art, it still may be used
So that the technical scheme described in foregoing embodiments to be modified, or wherein portion of techniques feature is carried out equivalent.
All within the spirit and principles in the present invention, any modification, equivalent substitution and improvement etc. made, should be included in the present invention's
Within protection domain.
Claims (4)
1. novel non-formaldehyde, benzene-free and environment-friendly glue, count by weight, by including that following raw material prepares:
Polyether Glycols 70~100 parts, 2,6-toluene di-isocyanate(TDI) 30~50 parts, chain extender 10~20 parts, acetone 50~80
Part, vinyl acetate-acrylic copolymer emulsion 20~30 parts, thickening agent 2~4 parts, firming agent 1~3 parts, zinc oxide 1~3 parts,
100 parts of water.
Glue the most according to claim 1, it is characterised in that: described chain extender is ethylenediamine base ethyl sulfonic acid sodium and/or two
Hydroxymethylbutyrate.
Glue the most according to claim 1, it is characterised in that: described firming agent is vinyl triamine or m-xylene diamine.
4. the preparation method of glue described in claim 1-3, comprises the steps step:
(1) by polyether Glycols, 2,6-toluene di-isocyanate(TDI), chain extender and acetone add in reactor, are heated with stirring to 80
~90 DEG C, insulation reaction 1~3 hours, cooling, regulate pH to 7;
(2) under agitation, in the system of step (1) add vinyl acetate-acrylic copolymer emulsion, firming agent, zinc oxide,
Thickening agent and water, be uniformly mixed so as to obtain described glue.