CN106280849A - Glass coating - Google Patents
Glass coating Download PDFInfo
- Publication number
- CN106280849A CN106280849A CN201510283106.1A CN201510283106A CN106280849A CN 106280849 A CN106280849 A CN 106280849A CN 201510283106 A CN201510283106 A CN 201510283106A CN 106280849 A CN106280849 A CN 106280849A
- Authority
- CN
- China
- Prior art keywords
- glass
- coating
- glass coating
- wetting agent
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to technical field of paint preparation, particularly relate to glass coating, this glass coating, including aldehyde resin and the wetting agent with emulsification, the glass paint brush of the present invention is at glass article surface, can effectively keep the cleaning of glass article surface, if there being oil pollution glass, wetting agent can gradually penetrate into greasy surfaces, oil is emulsified into droplet, can wipe easily, it is not left in inside glass, decoration and defencive function for a long time are provided, it is desirable to provide a kind of glass coating, this kind of coating is waterproof except having traditional coating, etch-proof effect, also there is preferable antifouling property, it is with a wide range of applications, be suitable to popularization and application.
Description
Technical field
The invention belongs to technical field of paint preparation, particularly relate to glass coating.
Background technology
It is applied to body surface and can form a class I liquid I or the general name of solid material of the solid-state film with protection, decoration or property, including paint, water paint, powdery paints.Paint is flowable liquid coating, including paint and water paint.Paint is with organic solvent as medium or high solid, solvent-free oil paint.Water paint is that available water is dissolved or with water-dispersible coating.Coating, as one of the main material of house decoration, the large percentage accounted in decorations, is bought whether qualified overall finishing effect and the environment in room of directly influencing of coating, the most even the healthy of human body can be produced harm greatly.
Summary of the invention
It is desirable to provide a kind of glass coating, this kind of coating, except having traditional coating effect waterproof, etch-proof, also has preferable antifouling property, is with a wide range of applications, be suitable to popularization and application.
To achieve these goals, the technical solution used in the present invention is as follows:
Glass coating, it is characterised in that this glass coating, at least includes consisting of composition, the ratio of each component respectively: aldehyde resin: 55%；Dispersant: 1%；Pigment: 5%；Emulsion: 8%；Wetting agent: 1%；Filler: 30%；
Wherein, described wetting agent contains organosilicon, has preferable pollution resistance.
The present invention is further arranged to, and described emulsion uses VAE emulsion, has the most viscous and effect.
The present invention is further arranged to, and described filler uses one or both combinations in heavy calcium carbonate, Pulvis Talci and mica powder.
The present invention is further arranged to, and described filler contains a small amount of methyl silanol potassium, and methyl silanol potassium needs, through shielding processing, to be coated with inert substance, is allowed to when storing not react.
Compared with prior art, glass coating of the present invention has the beneficial effect that this kind of coating except having traditional coating effect waterproof, etch-proof, also there is preferable antifouling property, wetting agent in the glass coating of the present invention has good emulsification and antifouling capacity, greasy dirt can be stoped to penetrate into inside glass, it is ensured that glass cleans for a long time.
Detailed description of the invention
Embodiment: glass coating, it is characterised in that this glass coating, at least includes consisting of composition, the ratio of each component respectively: aldehyde resin: 55%；Dispersant: 1%；Pigment: 5%；Emulsion: 8%；
Wetting agent: 1%；Filler: 30%；Wherein, described wetting agent contains organosilicon, has preferable pollution resistance。
The present invention is further arranged to, and described emulsion uses VAE emulsion, has the most viscous and effect.
The present invention is further arranged to, and described filler uses one or both combinations in heavy calcium carbonate, Pulvis Talci and mica powder.
The present invention is further arranged to, and described filler contains a small amount of methyl silanol potassium, and methyl silanol potassium needs, through shielding processing, to be coated with inert substance, is allowed to when storing not react.
Utilize technical solutions according to the invention, or those skilled in the art is under the inspiration of technical solution of the present invention, design similar technical scheme, and reach above-mentioned technique effect, all fall into protection scope of the present invention.
Claims (4)
1. glass coating, it is characterised in that this glass coating, at least includes consisting of composition, the ratio of each component respectively: aldehyde resin: 55%；Dispersant: 1%；Pigment: 5%；Emulsion: 8%；Wetting agent: 1%；
Filler: 30%；Wherein, described wetting agent contains organosilicon, has preferable pollution resistance.
Glass coating the most according to claim 1, it is characterised in that: described emulsion uses VAE emulsion.
Glass coating the most according to claim 1, it is characterised in that: described filler uses one or both combinations in heavy calcium carbonate, Pulvis Talci and mica powder.
Glass coating the most according to claim 1, it is characterised in that: described filler contains a small amount of methyl silanol potassium.